聚β-羟基丁酸酯解聚酶的纯化及性质

对DS9701菌株产生的聚β-羟基丁酸酯(PHB)解聚酶进行了分离、纯化及有关性质的表征.通过SephadexG-100分离出两种PHB解聚酶(E1和E2),经聚丙烯酰胺凝胶电脉检测为一条谱带.E1的最适反应温度为40℃～45℃,稳定性优于E2,最适反应pH=4.0,稳定范围3.6～7.0,Km值为0.182g/L.E2的最适反应温度为40℃,pH=6.0,稳定范围4.0～8.0,Km值为0.65g/L.通过质谱仪测得E1的相对分子质量为4.5×104,E2的相对分子质量为4.4×104.

Alternating LB film of ferric oxide nanoparticles-copper phthalocyanine derivative and its gas sensitivity

Nanoparticulate ferric oxide - tris - (2,4-di-t-amylphenoxy) - (8-quinolinolyl) copper phthalocyanine Langmuir-Blodgett Z-type multilayers were obtained by using monodisperse nanoparticle ferric oxide hydrosol as the subphase. XPS data reveal that the nanoparticle ferric oxide exist as alpha -Fe2O3 phase in the films. Transition electron microscopic (TEM) image of the alternating monolayer shows that the film was highly covered by the copper phthalocyanine derivative and the nanoparticles were arranged rather closely. IR and visible spectra all give the results that the nanoparticles were deposited onto the substrate with the copper phthalocyanine derivative. The gas-sensing measurements show that the alternating LB film had very fast response-recovery characteristic to 2 ppm C2H5OH gas, and also sensitive to larger than 200 ppm NH3.

Crystal form transition during heating of solvent-induced crystalline syndiotactic polystyrene

The phase transition of two kinds of solvent-induced crystalline syndiotactic polystyrene (sPS). gamma-sPS and delta(c)-sPS, has been studied via WAXD and DSC. gamma-sPS transform to a-sPS at 195-225 degrees C before melt during heating, whereas delta(e)-sPS transform to first gamma-sPS and then a-sPS at 100-200 degrees C and 200-215 degrees C, respectively. The transition of delta(e)-gamma and gamma-a occurs for below melting point of sPS indicates they are all solid-solid transition.

TG-DTA properties of new nonlinear optical materials: K(2)Ln(NO3)(5)center dot 2H(2)O (Ln = La, Ce, Pr, Nd, Sm)

Single crystals of K(2)Ln(NO3)(5). 2H(2)O (KLnN) (Ln = La, Ce, Pr, Nd, Sm) were grown from aqueous solution. The thermogravimetric analysis and differential thermal analysis curves of KLnN demonstrate that the processes of dehydration, melting, irreversible phase transformation and decomposition of NO3- take place in sequence in the heating processes (except KCN). There are three stages in the decomposition of NO3- in KLnN (Ln = La, Nd, Sm) while two in KLnN (Ln = Ce, Pr). K(2)Ln(NO3)(5) is formed at about 225 degrees C by the reaction of KNO3 and Ln(NO3)(3). nH(2)O (Ln = La, Ce, Pr, Nd). (C) 2000 Elsevier Science Ltd. All rights reserved.

胺类化合物气相色谱保留指数与结构的相关性研究

应用Am指数和引力指数C1对在3种体系下的胺类化合物的气相色谱保留指数和结构进行了相关性研究，并运用最佳子变量集算法和人工神经网法进行了计算分析，在非极性固定相OV-101和极性固定相OV-225和NGA下均获得了比较好的相关模型。

Photochemical synthesis and crystal structure of a charge transfer salt [HMDH2][(H2PMoMo11O40)-Mo-v]center dot 2AA center dot 3H(2)O center dot DMF

The title supramolecular compound, [HMDH2][(H2PMoMo11O40)-Mo-V] . 2AA . 3H(2)O . DMF (HMD = hexamethylene diamine; AA=acetaldehyde; DMF=N,N-dimethyl formamide), has been photochemically synthesized by using elemental analysis, IR, solid diffusion reflectance, electronic spectra, ESR spectra and X-ray single-crystal analysis. The crystallographic data: triclinic, P (1) over bar, a=14.092(2), b=14.347(3), c=14.358(3)Angstrom, alpha = 75.10(3), beta = 80.70(3), gamma = 80.73(3)degrees, V = 2746.6(10)Angstrom (3), Z = 2, M-r = 2081.68, D-c=2.517g/cm(3), F(000) =1970, mu (MoK alpha) =2.766mm(-1). The structure has been refined to R =0.0832 and wR=0.2638, by full-matrix least-squares method. The title compound is composed of hexamethylene diamine, two acetaldehyde molecules, three water molecules, one N,N-dimethylformamide and [(H2PMoMo11O40)-Mo-V](2-) heteropoly anion.

己二胺-12-钼磷酸电荷转移盐的光化学合成与晶体结构

采用光化学法合成一种有机-无机电荷转移盐，（HMDH2）[H2PMo12O40]·AA·3H2O·DMF（HMD = 1,6-己二胺，AA = 乙醛，DMF = N,N-二甲基甲酰胺）超分子化合物。用元素分析，IR，固体漫反射电子光谱，ESR进行了表征。X-射线四圆衍射测定其晶体结构属三斜晶系，空间群 Pī，Mr=2081.68，晶胞参数a = 14.092(3)，b =14.347(3)，c =14.358(3)?，α=75.10(3)，β=80.70(3)，γ=80.73(3)°,V=2746.6(10)?3，Z=2，Dc=2.517g/cm3，F(000)=1970，μ(MoKα)=2.766mm- 1，全矩阵最小二乘法修正至R=0.0832，wR=0.2638。标题化合物是由1个质子化的1,6-己二胺、12-钼磷混合价杂多阴离子 [PMo12O40]4ˉ、3个水分子、2个乙醛分子和1个二甲基甲酰胺分子构成。

Synthesis, crystal structure and properties of H-8[P4W14O58Na4 (H2O)(20)] center dot 16H(2)O

A novel heteropoly tungstophosphates, H-8[P4W14O58Na4(H2O)(20)] . 16H(2)O, was synthesized by hydrothermal method and characterized by elemental analysis, IR spectrum and single-crystal X-ray structure analysis. The thermal stability of the compound was investigated by using TG-DTA. The crystal is triclinic system with space group P (1) over bar, a = 1. 137 9(2) nm, b=1. 363 2(3) nm, c=1. 627 1(3) nm; alpha=78. 20(3)degrees, beta=71, 20(3)degrees, gamma= 71. 62(3)degrees; V = 2. 252 5(8) nm(3), Z=1, M-r= 4 374. 38, D-c = 3. 225 mg/cm(3), mu = 18. 007 mm(-1), F(000)=1 972, R=0. 074 2, R-w=0. 200 4. The result of structure analysis shows that the anion of the compound consists of two PW7O29Na2(H2O)(10) subunits and two linked phosphorous atoms. A kind of microporous with size of 0. 661 4 nm X 0. 318 9 nm was formed in the crystal structure.

用仪器化冲击仪研究HIPS/SBS共混物的冲击性能

用JJ-20型仪器化冲击仪研究了HIPS/SBS共混物在组成为100/0、100/5、100/10、100/15、100/20和100/25质量比下样品的Izod缺口冲击性能。结果表明，在组成范围内，随着SBS含量的增加，样品的Izod缺口冲击强度随之增加。质量比为100/25样品的Izod缺口冲击强度值(225.9J/m)比质量比为100/0的样品(108.7J/m)增加了1倍以上。通过对冲击断裂过程的分析表明，冲击强度的提高主要是由于缺口根部应力集中产生塑性区所消耗的裂纹引发能的提高引起的，而裂纹扩展能基本没有多大变化

等离子体平板显示用发光材料

本文介绍了PDP用荧光粉的基本情况及其应用特性。归纳出基团敏化带位置的一般规律及阳离子对基团敏化带波长位移的影响。并指出，提高发光效率，改善荧光粉的热稳定性和辐照稳定性，开发新型稀土荧光粉等具有重要意义。

Crystal growth and TG-DTA properties of K(2)Ln(NO3)(5).2H(2)O (Ln = La, Ce, Pr, Nd, Sm)

Single crystals of KLnN(Ln=La, Ce, Pr, Nd, Sm) can be grown in water solution with pH approximate to 1 similar to 2 at about 40 degrees C. Crystals of KLnN (Ln=La, Ce, Pr, Nd) are orthorhombic with space group Fdd2. KPrN crystal was grwon and its crystal structure was determined for the first time. The KPrN crystal parameters obtained by the direct method are as follows: a=21.411(3) Angstrom, b=11.2210(10)Angstrom, c=12.208(2) Angstrom, Z=6, R=0.0240. The TG-DTA curves of KLnN(Ln=La,Ce, Pr, Nd, Sm) demonstrate that the processes of dehydration, melt, irreversible phase transition and decomposition of NO3- take place in sequence with the temperature increasing(except KCN). There are three steps in the decomposition of NO3- in KLnN(Ln=La, Nd, Sm) while two steps in KLnN (Ln=Ce, Pr). K(2)Ln(NO3)(5). 2H(2)O are formed at about 225 degrees C by the reaction of the starting materials of KNO3 and Ln(NO3)(3). nH(2)O.

十一钼硅钴杂多蓝H_8[SiMo_(11)Co(H_2O)O_(39)]·20H_2O的合成与晶体结构

采用电解法制备了未见文献报道的杂多蓝H8[SiMo11Co（H2O）O39]·20H2O，通过X-射线衍射测定了其晶体结构，该晶体属单斜晶系，空间群P21；。晶胞参数全矩阵最小二乘法修正至中心原子Si与4个氧形成四面体结构，配原子M（M＝11／12Mo＋1／12Co）与O形成12个MO6八面体结构3个MO6共边形成4个M3O13三金属簇，4个三金属簇与SiO4四面体共角相连形成阴离子结构。

K_2Ln(NO_3)_5·2H_2O(Ln=La,Ce,Pr,Nd,Sm)的晶体生长和热重-差热分析研究

本文生长出了K2Ln（NO3）5.2H2O（Ln=La；Ce；Pr；Nd；Sm）的单晶，并对其进行了晶体结构及差热-热重分析研究．结果表明，K2Ln（NO3）5.2H2O（Ln=La；Ce；Pr；Nd）的晶体属正交晶系，Fdd2空间群．首次生长出KPrN单晶并用直接法解出其晶体结构．解得KPrN的晶胞参数为：a=11．2210（10）,b=21．411（3），c=12．208（2）,Z=6；R=0．0240．对KLnN加热，则依次出现脱水、熔化、不可逆相变和NO的分解过程（K2Ce（NO3）5·2H2O除外）K2Ln（NO3）5·2H2O（Ln＝La；Nd；Sm）的NO分三步分解，K2Ln（NO3）5·2H。O（Ln=Ce；Pr）的NO分两步分解·KNO3和Ln（NO3）3·nH2O的混合物在225℃左右生成K2Ln（NO3）5

硅钨杂多酸在中孔全硅分子筛HMS上的固载及其催化性能

用十二烷基胺代替传统的季铵盐合成了中孔全硅分子筛ＨＭＳ，并将硅钨杂多酸（ＳｉＷ１２）浸渍固载在ＨＭＳ上．用ＸＲＤ，ＦＴ－ＩＲ以及ＮＨ３－ＴＰＤ等手段对ＨＭＳ及不同负载量和焙烧温度的负载催化剂进行了表征．即使在固载量为５０％的ＳｉＷ１２／ＨＭＳ中，ＳｉＷ１２仍保持其Ｋｅｇｇｉｎ结构并均匀分布在载体表面上，没有ＳｉＷ１２晶相生成．同时，在气－固相反应体系中研究了固载在ＨＭＳ上的ＳｉＷ１２在合成乙酸丁酯中的催化性能．实验结果表明，２００℃焙烧可以增强杂多酸与ＨＭＳ内表面之间的相互作用，从而使其对酯化反应活性具有一定的影响，并且固载催化剂在较低反应温度下具有较高的酯化活性，且性能稳定，有一定的应用前景.

精细胶粉的应用研究

研究了６０，８０，１００，１２０目等４种精细胶粉（ＦＲＰ）的基本性能及其在胎面胶中的应用。结果表明，随ＦＲＰ精细化程度增加，掺用５０份ＦＲＰ后ＮＲ硫化胶的拉伸强度和扯断伸长率均有所提高；ＮＲ／ＢＲ并用胎面胶混炼胶的门尼粘度降低，胶料流动性增加，挤出物外观等级提高；ＮＲ／ＢＲ共混硫化胶的拉伸强度、扯断伸长率及热空气老化系数提高，撕裂强度和邵尔Ａ型硬度有所下降，而生热、动态疲劳和磨耗量等均在８０～１００目处出现最佳值。随着ＦＲＰ用量的增加，ＮＲ／ＢＲ硫化胶的拉伸强度、撕裂强度和弹性降低，生热增加，动态疲劳和热空气老化性能则有所改善。