Mass fractal characteristics of wet sonogels as determined by small-angle x-ray scattering and differential scanning calorimetry

Low density silica sonogels were prepared from acid sonohydrolysis of tetraethoxysilane. Wet gels were studied by small-angle x-ray scattering (SAXS) and differential scanning calorimetry (DSC). The DSC tests were carried out under a heating rate of 2 degrees C/min from -120 degrees C up to 30 degrees C. Aerogels were obtained by CO(2) supercritical extraction and characterized by nitrogen adsorption and SAXS. The DSC thermogram displays two distinct endothermic peaks. The first, a broad peak extending from about -80 degrees C up to practically 0 degrees C, was associated to the melting of ice nanocrystals with a crystal size distribution with pore diameter ranging from 1 or 2 nm up to about 60 nm, as estimated from Thomson's equation. The second, a sharp peak with onset temperature close to 0 degrees C, was attributed to the melting of macroscopic crystals. The DSC incremental nanopore volume distribution is in reasonable agreement with the incremental pore volume distribution of the aerogel as determined from nitrogen adsorption. No macroporosity was detected by nitrogen adsorption, probably because the adsorption method applies stress on the sample during measurement, leading to a underestimation of pore volume, or because often positive curvature of the solid surface is in aerogels, making the nitrogen condensation more difficult. According to the SAXS results, the solid network of the wet gels behaves as a mass fractal structure with mass fractal dimension D=2.20 +/- 0.01 in a characteristic length scale below xi=7.9 +/- 0.1 nm. The mass fractal characteristics of the wet gels have also been probed from DSC data by means of an earlier applied modeling for generation of a mass fractal from the incremental pore volume distribution curves. The results are shown to be in interesting agreement with the results from SAXS.

Purification, crystallization and preliminary X-ray diffraction analysis of carboxyhaemoglobin-II from the fish Piaractus mesopotamicus (pacu)

Carboxyhaemoglobin-II isolated from the pacu (Piaractus mesopotamicus) has been crystallized and X-ray diffraction data were collected to 2.0 Angstrom resolution using synchrotron radiation. Crystals were characterized as belonging to the space group I23; preliminary structural analysis reveals the presence of one dimer in the asymmetric unit.

Molecular modeling and small angle X-ray scattering studies of Hoplosternum littorale cathodic haemoglobin

Considerable interest is currently focused on fish haemoglobins in order to identify the structural basis for their diversity of functional behavior. Hoplosternum littorale is a catfish that presents bimodal gill (water)/gut (air) -breathing, which allows this species to survive in waters with low oxygen content. The hemolysate of this fish showed the presence of two main haemoglobins, cathodic and anodic. This work describes structural features analyzed here by integration of molecular modeling with small angle X-ray scattering. Here is described a molecular model for the cathodic haemoglobin in the unliganded and liganded states. The models were determined by molecular modeling based on the high-resolution crystal structure of fish haemoglobins. The structural models for both forms of H. littorale haemoglobin were compared to human haemoglobin. (C) 2004 Elsevier B.V. All rights reserved.

Crystallization and preliminary X-ray diffraction analysis of prephenate dehydratase from Mycobacterium tuberculosis H37Rv

Tuberculosis remains the leading cause of mortality arising from a bacterial pathogen ( Mycobacterium tuberculosis). There is an urgent need for the development of new antimycobacterial agents. The aromatic amino-acid pathway is essential for the survival of this pathogen and represents a target for structure-based drug design. Accordingly, the M. tuberculosis prephenate dehydratase has been cloned, expressed, purified and crystallized by the hanging-drop vapour-diffusion method using PEG 400 as a precipitant. The crystal belongs to the orthorhombic space group I222 or I2(1)2(1)2(1), with unit-cell parameters a = 98.26, b = 133.22, c = 225.01 angstrom, and contains four molecules in the asymmetric unit. A complete data set was collected to 3.2 angstrom resolution using a synchrotron-radiation source.

Crystallization and preliminary X-ray diffraction analysis of XAC1151, a small heat-shock protein from Xanthomonas axonopodis pv. citri belonging to the alpha-crystallin family

The hspA gene (XAC1151) from Xanthomonas axonopodis pv. citri encodes a protein of 158 amino acids that belongs to the small heat-shock protein ( sHSP) family of proteins. These proteins function as molecular chaperones by preventing protein aggregation. The protein was crystallized using the sitting-drop vapour-diffusion method in the presence of ammonium phosphate. X-ray diffraction data were collected to 1.65 angstrom resolution using a synchrotron-radiation source. The crystal belongs to the rhombohedral space group R3, with unit-cell parameters a = b = 128.7, c = 55.3 angstrom. The crystal structure was solved by molecular-replacement methods. Structure refinement is in progress.

Lead-cadmium oxyfluoride glasses and glass-ceramics

Glasses and glass-ceramics have been obtained in oxyfluoride systems involving lead and cadmium fluorides and one of the well-known glass former oxides SiO2, B2O3 and TeO2. Vitreous domains were established and a wide range of compositions including high heavy metal contents lead to stable glasses. Amorphous structures have been studied by short-range order spectroscopy techniques (Raman scattering and x-ray absorption) and molecular basic structures have been identified. Besides the usual oxides, the role of glass former could also be proposed for cadmium ions. Special attention has been paid for crystallization process. Cubic lead fluoride, cubic lead tellurite, tetragonal tellurium oxide and a solid solution of the type Pb1-xCdxF2 are obtained as crystallization products depending on the composition and temperature of heat treatments. Pb1-xCdxF2 solid solutions are well known superionic materials and obtaining this solid solution as a crystal phase could be very interesting for applications concerning ionic electrical conduction properties. The addition of rare earth ions led to the control of the crystallization process. In the presence of the nucleating ion only the cubic form beta-PbF2 was identified. Rare earth ions are present in the crystal phase and crystal-like spectroscopic properties were observed suggesting interesting applications for these perfectly transparent glass ceramics in photonics.

Grazing incidence X-ray diffraction and atomic force microscopy analysis of BaBi2Ta2O9 thin films

Thin films of BaBi2Ta2O9 (BBT) composition were prepared through the metal organic decomposition method. The crystallinity, phase formation, crystallite size and morphology of the thin films were measured as a function of the type of substrate, stoichiometry of solution and process variables such as thickness and temperature. The thin films were investigated by grazing incidence X-ray diffractometry and atomic force microscopy (AFM) techniques. For the sample without excess of bismuth, diffraction peaks other than that of the BBT phase were observed. A well crystallized BBT single phase was observed for films prepared from a solution with 10% excess of bismuth, deposited on Si/Pt substrate, with a thickness up to 150 nm and sintered at temperatures of 700 degreesC. The thin BBT phase films heat-treated at 600 degreesC presented a diffraction pattern characteristic of samples with lower degree of crystallinity whereas for the thin films heat-treated at 800 degreesC, we observed the presence of other phases than the BBT. For the thin film deposited on the Sin+ substrate, we observe that the peaks corresponding to the BBT phase are broader than that observed on the samples deposited on the Pt and Si/Pt substrates. No variation of average crystallite size was observed as the excess of Bi increased from 10 to 20%. AFM images for the samples showed that the increasing the amount of bismuth promotes grain growth. The average surface roughness measured was in the range of 16-22 nm showing that the bismuth amount had no or little effect on the roughness of films. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Small-angle X-ray scattering study of gelation and aging of Eu3+-doped sol-gel-derived siloxane-poly(oxyethylene) nanocomposites

The aggregation, gelation, and aging of urea-cross-linked siloxane-poly(oxyethylene) nanohybrids [(U600)-n] containing two different amounts of europium triflate initially dissolved in an ethanol-water mixture were investigated by in situ small-angle X-ray scattering (SAXS). For both low (n = [O]/[Eu] = 80) and high (n = 25) europium contents, the SAXS intensity was attributed to the formation of siloxane clusters of about 8-11 Angstrom in size. Siloxane cluster formation and growth is a rapid process in hybrids with low Eu contents and slow in Eu-rich hybrids. An additional contribution to the scattering intensity at very low angles was attributed to the formation of a coarse structure level. At this secondary level, the structure can be described as a set of dense domains containing siloxane clusters embedded in a depleted matrix composed of unfolded polymer chains and solvent. By fitting a theoretical function for this model to the experimental SAXS curves, relevant structural parameters were determined as functions of time during the sol-gel transition and gel aging. For hybrids with low europium contents (n = 80), the size of the siloxane clusters remains essentially invariant, whereas the dense segregation domains progressively grow. In hybrids with high doping contents (n = 25), the preponderant structure variation during the first stages of the sol-gel transformation is the slow growth of siloxane clusters. For these hybrids, the segregation of siloxane clusters forming dense domains occurs only during advanced stages of the process.

X-ray powder diffraction analysis of a new palladium(II) amino acid complex

Powder X-ray diffraction data for a new palladium(II) amino acid complex, of composition PdC12H2ON2O4S2, are presented in this paper. Orthorhombic cell parameters are: a = 10.740 angstrom, b = 19.999 angstrom, and c = 5.2470 angstrom. (c) 2004 International Centre for Diffraction Data.

Morphology of alumina: a comparison between infrared spectroscopy and X-ray diffractometry

Morphology of three samples of alumina are investigated. Infrared spectra are analysed by use of their morphology through the theory of average dielectric constant. Crystal shape is obtained from X-ray diffraction patterns by reflection intensity ratio. In the case of electron scanning microscopy, shape factor was obtained by an average axial ratio of the particles. Comparison of results show that there is agreement among these techniques and infrared spectra can be used to determine the morphology of alumina particles from 2.7 to 10 mu m, even for heterogeneous samples. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Small angle X-ray scattering study of surface modified tin oxide nanoparticles prepared by sol-gel route

The surface properties of SnO2 nanoparticles were modified by grafting ionic (Tiron (R). (OH)(2)C6H2(SO3Na)(2)(H2O)-H-.) or non-ionic (Catechol (R). C6H4-1,2-(OH)(2)) capping Molecules during aqueous sol-gel processing to improve the redispersibility of powdered xerogel. The effect of the amount of grafted organic molecules on the redispersibility of powders in aqueous solution at several basic pH values was Studied. The nanostructural features of the colloidal suspensions were analyzed by small angle X-ray scattering (SAXS) measurements. Irrespective of the nature and amount of grafted molecules, complete redispersion was obtained in aqueous solution at pH = 13. The redispersion at pH = 11 results in a mixture of dispersed primary particles and aggregates. The proportion of well dispersed nanoparticles and aggregates (and their average size) can be tuned by the quantity of grafted ionic molecules.

Crystallization and preliminary X-ray diffraction analysis of a novel Arg49 phospholipase A(2) homologue from Zhaoermia mangshanensis venom

Zhaoermiatoxin, an Arg49 phospholipase A(2) homologue from Zhaoermia mangshanensis (formerly Trimeresurus mangshanensis, Ermia mangshanensis) venom is a novel member of the PLA(2)-homologue family that possesses an arginine residue at position 49, probably arising from a secondary Lys49 -> Arg substitution that does not alter the catalytic inactivity towards phospholipids. Like other Lys49 PLA(2) homologues, zhaoermiatoxin induces oedema and strong myonecrosis without detectable PLA(2) catalytic activity. A single crystal with maximum dimensions of 0.2 x 0.2 x 0.5 mm was used for X-ray diffraction data collection to a resolution of 2.05 angstrom using synchrotron radiation and the diffraction pattern was indexed in the hexagonal space group P6(4), with unit-cell parameters a = 72.9, b = 72.9, c = 93.9 angstrom.