Proposição de um reator fotocatalítico para destruição de microrganismos em ambientes interiores

The TiO2/UV photocatalytic reactor was investigated as an alternative system to inactivate airborne microorganisms. The experiments performed in the absence of the catalyst showed that direct photolysis was not efficient to destruct microorganisms, with only 30% of inactivation. Similar inactivation percentage was obtained using TiO2 in absence of UV radiation. The destruction of microorganisms present in a contaminated indoor atmosphere, using the combination of TiO2/UV was very efficient, reaching more than 98% of destruction.

Fotocatálise eletroquímica de atrazina sobre dióxido de titânio: efeito de diferentes parâmetros experimentais

The atrazine photoelectrochemical degradation has been examined in solutions containing TiO2 on immobilized films under a variety of experimental conditions. It was possible to observe that the supporting electrolyte nature affects the intensity of the photocurrent, being an indicative of the adsorption process. The disappearance of the organic molecule follows approximately a pseudo-first order kinetic. As mineralization product, NH4+ and NO3- ion have been identified. These results indicated that the formation of NH4+ ion can be associated to the effect of atrazine adsorption, due to need of potential adaptation together with a variation in the supporting electrolyte concentration.

Dióxido de estanho nanoestruturado: síntese e crescimento de nanocristais e nanofitas

The objectives of this work are to supply a basic background on nanostructured materials and also to report about the obtaining of nanoparticles, mainly, tin dioxide nanocrystalline particles (obtained by using the polymeric precursor method) presenting a high stability against particle growth due to the usage of a metastable solid solution. The synthesis and growth of SnO2 nanoribbons by a carbothermal reduction process are also discussed.

Inativação por oxidação fotocatalítica de Escherichia coli e Pseudomonas sp.

This study presents the bactericidal activity of titanium dioxide photocatalysis, using as model Escherichia coli and Pseudomonas sp. cells. It was observed that the process efficiency is related to initial cell concentration, light intensity, UV irradiation exposure time, TiO2 concentration increase. The ultimate removal efficiency was above 99.9%.

Tratamento de efluentes industriais por processos oxidativos na presença de ozônio

A large variety of organic and inorganic compounds may be found in wastewater which can contribute to environmental contamination. Oxidation processes with ozone (O3; O3/UV; O3/H2O2; O3/TiO2; O3/Mn+2) and the use of ozone in the pre- or post-treatment of wastewater combined with biological processes has been extensively studied for the treatment of effluents. The aim of this work was to evaluate the potential of the ozonation process in the treatment of several industrial wastewaters, namely effluents from paper mills, and textile, whey (dairy industry), pharmaceutic sand pesticides plants.

Propriedades eletrônicas e estruturais do PbTiO3: teoria do funcional de densidade aplicada a modelos periódicos

Calculations based on density functional theory at the B3LYP hybrid functional level applied to periodic models have been performed to characterize the structural and electronic properties of PbTiO3. Two different slab terminations (PbO and TiO2) have been considered to obtain and discuss the results of band structure, density of states, charge distribution on bulk and surface relaxation. It is observed that the relaxation processes are most prominent for the Ti and Pb surface atoms. The electron density maps confirm the partial covalent character of the Ti-O bonds. The calculated optical band gap and other results are in agreement with experimental data.

Preparação de eletrodos opticamente transparentes

A simple experiment for the preparation of transparent conducting glass electrodes by deposition of pure and fluorine doped SnO2 films is described. This procedure was tested in the undergraduate inorganic course at IQ-UNICAMP. The success in achieving a conducting layer was easily checked using the standard probes of a volt-ohm meter. The optical transmittance and thickness were studied by UV-vis spectrophotometry. To discuss the experimental results we place significant emphasis on molecular orbital and energy band model theories. The undergraduate students can also discuss the concepts related to the electronic properties of solids and to interesting new materials, such as transparent conducting films, which are the subject of significant current research and technological applications.

Fotodegradação de hidrocarbonetos policíclicos aromáticos em placas de sílica impregnadas com dióxido de titânio

Photodegradation of the PAHs anthracene, chrysene and benzo[k]fluoranthane on silica gel impregnated with TiO2 and over glass plates holding TiO2 was studied. Silica gel plates holding these substances were exposed to solar radiation, developed with hexane and photographed under ultra-violet light. The plates containing benzo[k]fluoranthene were also analysed by both diffuse reflectance and laser induced fluorescence. Diffuse reflectance spectra of the fluorescent spot from non irradiated plates showed small differences when compared with those obtained from irradiated plates. These spectral differences are compatible with formation of less conjugated compounds during irradiation. Fluorescence and time resolved fluorescence spectra observed after irradiation were identical to those obtained with benzo[k]fluoranthene in methanol. On plates holding silica, PAH degradation requires longer periods of solar irradiation when compared with those plates containing silica impregnated with TiO2. Glass plates impregnated with TiO2 also showed very rapid PAH degradation.

Construção e estudos de perfomance de um reator fotoquímico tipo CPC ("Compound Parabolic Concentrator")

A CPC (Compound Parabolic Concentrator) reactor was projected and constructed aiming to promote the degradation of the organic matter present in considerable volumes of aqueous effluents, under the action of solar radiation. The essays were done using a model effluent which consists of a mixture of fragments of a sodium salt of lignosulphonic acid possessing a mean molecular weigth of 52,000 Daltons, and a real effluent, from a chip board industry. The volume of effluent in each test was about 50 L. The tests involved heterogeneous (TiO2 P25 Degussa and formulations made from the association of TiO2 with a photosensitiser), and homogeneous (thermal and photochemical Fenton reactions) catalysis of the effluents. The results demonstrate the viability of application of this kind of reactor even when the load of organic pollutants is high.

Aplicação de radiação UV artificial e solar no tratamento fotocatalítico de efluentes de curtume

Tannery effluents are very dangerous for the environment since they contain large amounts of dangerous and biorecalcitrant contaminants (organic matter and Cr(VI)). This paper reports the efficiency of heterogeneous photocatalysis, based on the application of solar and artificial radiation, furnished by UV lamps, using TiO2 fixed on a flat plate, in the treatment of synthetic effluents. The results of COD and Cr(VI) demonstrate that the use of solar radiation is the most efficient way to perform the photocatalytic treatment of these effluents since a minimum removal of 62 and 61% was observed for Cr(VI) and organic matter, respectively.

A Comparison of the Environmental Impact of Different AOPs: Risk Indexes

Today, environmental impact associated with pollution treatment is a matter of great concern. A method is proposed for evaluating environmental risk associated with Advanced Oxidation Processes (AOPs) applied to wastewater treatment. The method is based on the type of pollution (wastewater, solids, air or soil) and on materials and energy consumption. An Environmental Risk Index (E), constructed from numerical criteria provided, is presented for environmental comparison of processes and/or operations. The Operation Environmental Risk Index (EOi) for each of the unit operations involved in the process and the Aspects Environmental Risk Index (EAj) for process conditions were also estimated. Relative indexes were calculated to evaluate the risk of each operation (E/NOP) or aspect (E/NAS) involved in the process, and the percentage of the maximum achievable for each operation and aspect was found. A practical application of the method is presented for two AOPs: photo-Fenton and heterogeneous photocatalysis with suspended TiO2 in Solarbox. The results report the environmental risks associated with each process, so that AOPs tested and the operations involved with them can be compared.

Biomateriais: deposição de hidroxiapatita sobre superfície de Ti-cp modificada por aspersão térmica

The osseointegrated titanium implants are reliable and safe alternatives to treatments for long periods of time. For surface modification, thermal aspersion of TiO2 was used. The samples with and without TiO2 were treated with NaOH and SBF in order to obtain a layer of HA. Characterization was done by SEM and FTIR. The images of HA obtained by SEM show a uniform morphology and a porous structure with spherical particles. The IR spectra show that the surface of Ticp/ TiO2 is more favorable for the HA deposit, as can be seen by the increase of the crystalline structure and the very intense and defined bands of the OH group of HA that is verified about 3571 and 630 cm-1. Thus the Ticp/ TiO2 surface presents a satisfactory nucleation of HA when compared to Ticp.

Degradação do pesticida Padron® por processos fotoquímicos utilizando luz artificial e solar

Destruction of Padron® (dye and picloram) was evaluated using a photoreactor and a solar reactor. Photolysis was observed using only a germicide lamp (GL). Black light (BL) and H2O2 (172 mmol L-1) promoted a conversion of 49% and 6% of dye and picloram, respectively. Photocatalytic processes were more efficient using TiO2/GL (96%-dye; 60%-picloram) than TiO2/BL (44%-dye; 40%-picloram). Photolysis using sunlight was not observed during PadronÒ recirculation in the reactor constructed with four borosilicate tubes. Meanwhile, adding H2O2 resulted in 12% conversion of dissolved organic compounds. Finally, the most efficient mineralization (60%) was obtained using the Fenton reaction ( H2O2-176 mmol L-1; FeSO4x6H2O-90 mmol L-1) and sunlight.

Extração líquido-líquido de ferro(III) e titânio(IV) pelo ácido bis-(2-etil-hexil) fosfórico (D2EHPA) em meio de ácido sulfúrico

This work presents a study on the separation of Fe(III) and Ti(IV) from sulfuric acid leaching solutions of ilmenite (FeTiO3) using liquid-liquid extraction with D2EHPA in n-dodecane as extracting agent. The distribution coefficients (K D) of the elements related to free acidity and concentration of Fe(III) and Ti(IV) were determined. Free acidity was changed from 3x10-2 to 11.88 mol L-1 and D2EHPA concentration was fixed at 1.5 mol L-1. Recovery of final products as well as recycling of wastes generated in the process were also investigated. The LLE process as a feasible alternative to obtain high-purity TiO2.

Degradação de corantes ácidos por processos oxidativos avançados usando um reator com disco rotatório de baixa velocidade

Three technologies were tested (TiO2/UV, H2O2/UV, and TiO2/H2O2/UV) for the degradation and color removal of a 25 mg L-1 mixture of three acid dyes: Blue 9, Red 18, and Yellow 23. A low speed rotating disc reactor (20 rpm) and a H2O2 concentration of 2.5 mmol L-1 were used. The dyes did not significantly undergo photolysis, although they were all degraded by the studied advanced oxidation processes. With the TiO2/H2O2/UV process, a strong synergism was observed (color removal reached 100%). Pseudo first order kinetic constants were estimated for all processes, as well as the respective apparent photonic efficiencies.