EFFECT OF ETHYLENE-PROPYLENE COPOLYMER WITH RESIDUAL PE CRYSTALLINITY ON MECHANICAL-PROPERTIES AND MORPHOLOGY OF PP/HDPE BLENDS

Morphology and mechanical properties of polypropylene (PP)/high density polyethylene (HDPE) blends modified by ethylene-propylene copolymers (EPC) with residual PE crystallinity were investigated. The EPC showed different interfacial behavior in PP/HDPE blends of different compositions. A 25/75 blend of PP/HDPE (weight ratio) showed improved tensile strength and elongation at break at low EPC content (5 wt %). For the PP/HDPE = 50/50 blend, the presence of the EPC component tended to make the PP dispersed phase structure transform into a cocontinuous one, probably caused by improved viscosity matching of the two components. Both tensile strength and elongation at break were improved at EPC content of 5 wt %. For PP/HDPE 75/25 blends, the much smaller dispersed HDPE phase and significantly improved elongation at break resulted from compatibilization by EPC copolymers. (C) 1995 John Wiley & Sons, Inc.

CURE AND IONIC-CONDUCTIVITY OF A 2-COMPONENT EPOXY NETWORK POLYMER ELECTROLYTE

In order to raise the room temperature ionic conductivity and improve the mechanical strength of a PEO-based polymer electrolyte, a non-crystalline two-component epoxy network was synthesized by curing diglycidyl ether of polyethylene glycol (DGEPEG) with triglycidyl ether of glycerol (TGEG) in the presence of LiClO4 salt, which acts in this system as both a ring opening catalyst and a source of ionic carrier. The structure of the precursors, the curing process and the cured films have been characterized by C-13 NMR, IR, DSC and ionic conductivity measurement techniques. The electrolyte system exhibits an ionic conductivity as high as similar to 10(-5) S/cm at 25 degrees C and is mechanically self-supportable. The dependence of ionic conductivity was investigated as a function of temperature, salt content, MW of PEG segment in DGEPEG and the proportion of DGEPEG in DGEPEG/TGEG ratio.

Study on comblike polymer electrolyte

New comblike polymers(CP) have been synthesized by reacting monomethyl ether of polyethylene glycol(PEGME) with poly(methyl vinyl ether-alt-maleic anhydride)(MA) and endcapping the residual carboxylic acid with methanol. Butanone was selected as a solvent for the esterification reaction in order to obtain a completely soluble product. They were characterized by IR, C-13 NMR and elemental analysis.

YIELD BEHAVIOR AND VISCOELASTIC INTERPRETATION BY ACTIVATION VOLUMEN OF PHENOLPHTHALEIN POLYETHER KETONE

Phenolphthalein polyether ketone (PEK-C) exhibits a marked tensile yield behaviour. The yield stress depends on strain rate and the activation volume V could be evaluated from the data of the yield stress. From the creep and stress relaxation behaviour,

STUDIES ON COMPATIBILIZATION OF POLYPROPYLENE THERMOPLASTIC POLYURETHANE BLENDS AND MECHANISM OF COMPATIBILIZATION

This paper reports a study of compatibilization and the mechanism of compatibilization of polypropylene (PP)/thermoplastic polyurethane (TPU) blends with maleated polypropylene (PP-MA) and its graft copolymer with polyethylene oxide (PEO), (PP-MA)-g-PEO.

EFFECTS OF CRYSTALLIZATION RATES ON INTERFACE LAYER THICKNESS OF EPITAXIAL HDPE ON ORIENTED IPP

The effect of crystallization rate on the epitaxial interface layer thickness of high-density polyethylene (HDPE) in the epitaxial system with oriented isotactic polypropylene (iPP) has been investigated by electron microscopy. The results of bright-field

COMPATIBILIZATION OF POLYPROPYLENE POLY(ETHYLENE OXIDE) BLENDS AND CRYSTALLIZATION BEHAVIOR OF THE BLENDS

The compatibilization of incompatible polypropylene (PP)/poly(ethylene oxide) (PEO) blends was studied. The experimental results showed that the graft copolymer [(PP-MA)-g-PEO] of maleated PP (PP-MA) and mono-hydroxyl PEO (PEO-OH) was a good compatibilize

COMPATIBILIZATION AND STRUCTURE OF POLY(PROPYLENE) NYLON-12 BLENDS

In this paper, scanning electron microscopy (SEM), differential scanning calorimetry (DSC) and wide-angle X-ray diffraction (WAXD) were used to study the structure and compatibilization of poly(propylene) (PP)/nylon-12 (PA 12) blends. The compatibilizatio

EFFECTS OF STRUCTURE MULTIPLICITY ON MECHANISM OF RADIATION CROSS-LINKING OF POLYMERS

In an attempt to explore the effects of structural multiplicity of polymers on the mechanism of radiation crosslinking, the adaptability of the Charlesby-Pinner's equation and its various modified versions are examined. It is recognized that both chemical

INTERFACIAL BEHAVIOR OF COMPATIBILIZERS IN POLYMER BLENDS

From an analysis of the literature and our experimental results, we have established that interfacial tension is a function of the concentration of a compatibilizer, and put forward a 'three-stage' physical model to account for the compatibilizing behavio

RADIATION EFFECTS ON POLY(VINYLIDENE FLUORIDE)

Melt-crystallized poly(vinylidene fluoride)s (PVF2) with different crystallization histories were irradiated with gamma-rays within the range of irradiation doses 0-83 Mrad. The effects on the crystalline structure and mechanical properties have been measured, compared, and discussed. The degree of crystallinity of the samples was found to increase with radiation dose. The differential scanning calorimeter scans of the quenched samples indicate that there are two melting peaks, and that the area of the lower temperature peak increases while the area of higher temperature peak decreases with increasing dose. Yield stress and breaking stress for all samples are not significantly affected by irradiation but elongation at break is.

ENTANGLEMENT FLUCTUATION DURING PHASE-SEPARATION IN POLYMER BLENDS

For perhaps the first time, the dynamics of liquid-liquid phase separation was studied by time-resolved mechanical spectrometry in order to establish the relationship between blends' properties and the phase structures during spinodal decomposition (SD). The selected system was chlorinated polyethylene (CPE)/ethylene-vinyl acetate copolymer (EVA). It was found that in the early and intermediate stage of SD, the storage modulus (G') and the loss modulus (G'') increase with time after the initiation of the isothermal phase separation; in the later stage, G' and G'' decrease as phase separation proceeds. An entanglement fluctuation model was presented to manifest this phenomenon; it was found that the rheological behavior agrees well with the expections of the model in the early stage. For the later stage, the reduction of G' and G'' can be attributed to the increment of phase-domain size. (C) 1993 John Wiley & Sons, Inc.

MOLECULAR CHARACTERISTICS AND CRYSTALLINE-STRUCTURE OF ETHYLENE-DIMETHYLAMINOETHYL-METHACRYLATE COPOLYMERS

The relationship between molecular and crystalline structural characteristics of the ethylene -dimethylaminoethylmethacrylate copolymers (EDAM) was investigated and related to melt flow index MI and average gross content of DAM comonomer, in comparison with low density polyethylene (LDPE) produced by the common high-pressure radical polymerization process. Although the average molecular weight and its distribution are influenced predominantly by the polymerization conditions, DAM-content seems not to depend significantly on molecular weight according to the GPC-FT/IR measurement. Comonomer sequence distributions were determined quantitatively with the C-13-NMR spectra entirely assigned by DEPT and H-1-C-13 COSY techniques. The result suggests the alternating copolymerization tendency and surprisingly coincides with the simulation out-puts based on the assumption of continuous complete mixing reactor model, using Mayo-Lewis equation and the same Q-e values as previously reported on different types of copolymers such as EVA and St.DAM (VA;vinylacetate, St;styrene). It was confirmed by WAXD and SAXS analyses that the crystallinity X(c) and the thickness of lamellar crystal l(c) decreased with increasing DAM-content, whereas the a-lattice and b-lattice dimensions enlarged. X(c) and l(c) can definitely be correlated to the heats of fusion and crystallization measured by DSC. The average size of spherulites measured with light scattering photometry tends to be enlarged with decreasing molecular weight (increasing MI) and DAM-content.

MELTING BEHAVIOR OF DRAWN POLYPROPYLENE

The melting behavior of drawn, compression-molded isotactic polypropylene has been examined in terms of the influence of drawing conditions on the observed properties. Two endothermic peaks were observed on differential scanning calorimetry (DSC) for samples when high draw ratios and high heating rates were used during DSC tests. The peak at lower temperature is influenced by draw ratio, temperature, and rate, and exhibits a strong superheating effect. The species associated with this peak can partially recrystallize into another species associated with the peak at higher temperature during DSC measurements. The position of the peak at higher temperature depends only on draw ratio. It is proposed that the double-melting peaks at lower and higher temperature result from extremely thin quasi-amorphous or crystalline layers between microfibrils and the lamellar crystals within microfibrils, respectively. (C) 1993 John Wiley & Sons, Inc.