Antimicrobial activity of highly stable silver nano particles embedded in agar-agar matrix as a thin film

Highly stable silver nanoparticles (Ag NPs) in agar-agar (Ag/agar) as inorganic-organic hybrid were obtained as free-standing film by in situ reduction of silver nitrate by ethanol. The antimicrobial activity of Ag/agar film on Escherichia coli (E. coil), Staphylococcus aureus (S. aureus), and Candida albicans (C albicans) was evaluated in a nutrient broth and also in saline solution. In particular, films were repeatedly tested for antimicrobial activity after recycling. UV-vis absorption and TEM studies were carried out on films at different stages and morphological studies on microbes were carried out by SEM. Results showed spherical Ag NPs of size 15-25 nm, having sharp surface plasmon resonance (SPR) band. The antimicrobial activity of Ag/agar film was found to be in the order, C. albicans > E. coil > S. aureus, and antimicrobial activity against C. albicans was almost maintained even after the third cycle. Whereas, in case of E. coil and S. aureus there was a sharp decline in antimicrobial activity after the second cycle. Agglomeration of Ag NPs in Ag/agar film on exposure to microbes was observed by TEM studies. Cytotoxic experiments carried out on HeLa cells showed a threshold Ag NPs concentration of 60 mu g/mL, much higher than the minimum inhibition concentration of Ag NPs (25.8 mu g/mL) for E. coli. The mechanical strength of the film determined by nanoindentation technique showed almost retention of the strength even after repeated cycle. (C) 2010 Elsevier Ltd. All rights reserved.

On the uniformity of film thickness on rotating spherical substrates on a planar work holder

Curves for the uniformity in film thickness on spherical substrates are drawn for various geometries. The optimum source-to-substrate height for maximum uniformity of the film thickness is determined. These data are approximated to achieve uniform thickness on a large number of small planar substrates loaded on a large spherical substrate holder, the appropriate geometry being selected on the basis of the radius of curvature of the substrate holder.

Thin film amorphous semiconductor microwave switches

Microwave switches operating in the X band were designed and fabricated using amorphous chalcogenide semiconductors of composition GexTeyAsz. Threshold devices were shown to operate as microwave modulators at modulation frequencies of up to 100 MHz. No delay time was observed at the highest frequency although the modulation efficiency decreased above 10 MHz owing to the finite recovery time which was approximately 0.3 × 10−8s. The devices can also be used as variolossers, the insertion loss being 0.5 dB in the OFF state and increasing on switching from 5 dB at 1 mA device current to 18 dB at 100 mA.The behaviour of the threshold switches can be explained in terms of the formation of a conducting filament in the ON state with a constant current density of 2 × 104Acm−2 that is shunted by the device capacitance. The OFF state conductivity σ varies as ωn (0.5 < n < 1) which is characteristic of hopping in localized states. However, there was evidence of a decrease in n or a saturation of the conductivity at high frequencies.As a result of phase separation memory switches require no holding current in the ON state and may be used as novel latching semiconductor phase-shifters.

Electrical switching behavior of amorphous Al23Te77 thin film sample

The electrical switching behavior of amorphous Al23Te77 thin film devices, deposited by flash evaporation, has been studied in co-planar geometry. It is found that these samples exhibit memory type electrical switching. Scanning Electron Microscopic studies show the formation of a crystalline filament in the electrode region which is responsible for switching of the device from high resistance OFF state to low resistance ON state. It is also found that the switching behavior of thin film Al-Te samples is similar to that of bulk samples, with the threshold fields of bulk samples being higher. This has been understood on the basis of higher thermal conductance in bulk, which reduces the Joule heating and temperature rise in the electrode region. (C) 2010 Elsevier B.V. All rights reserved.

Indentation of sintered alumina clay composite - an experimental discussion of a combined Boussinesq and blister stress field approach

Surface elastic strain field generated in conical indentation of sintered alumina clay composite was measured to verify the suitability of a superposed combination of Boussinesq and blister stress fields, used previously for analysing the indentation problem. The residual strain measured in the elastic hinterland is used to estimate the blister field strength without any reference to stress relation within that field. The approach may be useful in fracture studies of brittle materials.

Characterization of a large-area PVDF thin film for electro-mechanical and ultrasonic sensing applications

Large-area PVDF thin films have been prepared and characterized for quasi-static and high frequency dynamic strain sensing applications. These films are prepared using hot press method and the piezoelectric phase (beta-phase) has been achieved by thermo-mechanical treatment and poling under DC field. The fabricated films have been characterized for quasi-static strain sensing and the linear strain-voltage relationship obtained is promising. In order to evaluate the ultrasonic sensing properties, a PZT wafer has been used to launch Lamb waves in a metal beam on which the PVDF film sensor is bonded at a distance. The voltage signals obtained from the PVDF films have been compared with another PZT wafer sensor placed on the opposite surface of the beam as a reference signal. Due to higher stiffness and higher thickness of the PZT wafer sensors, certain resonance patterns significantly degrade the sensor sensitivity curves. Whereas, the present results show that the large-area PVDF sensors can be superior with the signal amplitude comparable to that of PZT sensors and with no resonance-induced effect, which is due to low mechanical impedance, smaller thickness and larger area of the PVDF film. Moreover, the developed PVDF sensors are able to capture both A(0) and S-0 modes of Lamb wave, whereas the PZT sensors captures only A(0) mode in the same scale of voltage output. This shows promises in using large-area PVDF films with various surface patterns on structures for distributed sensing and structural health monitoring under quasi-static, vibration and ultrasonic situations. (C) 2010 Elsevier B.V. All rights reserved.

Micromechanics Of Fatigue Crack-Growth At Low Stress Intensities In A High-Strength Steel

An attempt to systematically investigate the effects of microstructural parameters in influencing the resistance to fatigue crack growth (FCG) in the near-threshold region under three different temper levels has been made for a high strength low alloy steel to observe in general, widely different trends in the dependence of both the total threshold stress intensity range, DELTA-K(th) and the intrinsic or effective threshold stress intensity range, DELTA-K(eff-th) on the prior austenitic grain size (PAGS). While a low strain hardening microstructure obtained by tempering at high temperatures exhibited strong dependence of DELTA-K(th) on the PAGS by virtue of strong interactions of crack tip slip with the grain boundary, a high strength, high strain hardening microstructure as a result of tempering at low temperature exhibited a weak dependence. The lack of a systematic variation of the near-threshold parameters with respect to grain size in temper embrittled structures appears to be related to the wide variations in the amount of intergranular fracture near threshold. Crack closure, to some extent provides a basis on which the increases in DELTA-K(th) at larger grain sizes can be rationalised. This study, in addition, provides a wide perspective on the relative roles of slip behaviour embrittlement and environment that result in the different trends observed in the grain size dependence of near-threshold fatigue parameters, based on which the inconsistency in the results reported in the literature can be clearly understood. Assessment of fracture modes through extensive fractography revealed that prior austenitic grain boundaries are effective barriers to cyclic crack growth compared to martensitic packet boundaries, especially at low stress intensities. Fracture morphologies comprising of low energy flat transgranular fracture can occur close to threshold depending on the combinations of strain hardening behaviour, yield strength and embrittlement effects. A detailed consideration is given to the discussion of cyclic stress strain behaviour, embrittlement and environmental effects and the implications of these phenomena on the crack growth behaviour near threshold.

Stress-strain characteristics of Tress-strain characteristics of reinforcing steel bars under cyclic loading

This paper presents test results for 22 high strength deformed bars and nine mild steel bars subjected to monotonic repeated and reversed axial loading to determine the stress-strain behavior. Equations have been proposed for the stress-strain curves and have been compared with test results. Satisfactory agreement was obtained.

Mid-urethral slings for treatment of stress urinary incontinence : long- and mid-term follow-up

Urinary incontinence is a common problem, affecting one third of the women at least at some time during their lives. The prevalence of urinary incontinence increases with advancing age, and the everyday impact of incontinence on women and on health services is enormous. Urinary incontinence is usually divided into three different subtypes, of which stress urinary incontinence (SUI) is the most common. Surgical treatment is often needed to cure SUI, and modern mid-urethral sling procedures give the possibility to cure this condition with a low risk of adverse events, a problem often associated with the so-called traditional incontinence operations. Life expectancy among women in Western countries has grown beyond 80 years of age. Long-term efficacy of treatment options for urinary incontinence therefore becomes an important issue in a world with limited eco-nomic resources. The purpose of the present study was to prospectively evaluate the long-term efficacy and safety of the first minimally invasive mid-urethral tape procedure, the Tension-free Vaginal Tape (TVT) procedure. The long-term (5-year) follow-up results of the TVT procedure as a repeat operation af-ter an unsuccessful mid-urethral tape operation were studied and the reasons for failure of the first operation were analyzed. Another purpose was to compare the original TVT procedure with a newer modification, the Tension-free Vaginal Tape Obturator (TVT-O) procedure within a multi-centre, randomized context in order to find out possible differences between these procedures re-garding efficacy and complications and the effects on symptoms of urgency. The first study of the present thesis is a prospective, Nordic, three-centre follow-up study of 90 women suffering from SUI, who were treated by means of the TVT procedure. The mean follow-up time was more than eleven years, and the study is the first to be published in connection with more than ten years of follow-up. The second study is a retrospective analysis of 26 women who were treated with a repeat TVT procedure after an unsuccessful primary mid-urethral tape procedure. The third and fourth studies concern 273 women in seven centres in Finland who were ran-domly assigned to the TVT and TVT-O procedures, the 3-year follow-up results of which are pre-sented in this thesis. After eleven years of follow-up, 90% of the women had a negative cough stress test result and a negative 24-h pad test result. The subjective cure rate measured as the women s global impression of cure was 77%, the rate of improvement 20%, and only 3% thought that the treatment had failed. No late-onset adverse effects were found. The repeat TVT procedure was successful in 75% of the cases when women who were cured and women who were significantly improved were included. The reasons for failure of the first operation could be separated into four different groups: tape material-related, operation technique-related, concomitant illness-related and a group with no identifiable reason. There were no intra-operative complications during the repeat operation. In the randomized trial comparing the TVT with the TVT-O procedure a cough stress test results were negative in 94.6% and 89.5% of the women in the two groups, respectively, after a 3-year follow-up period. There were no statistical differences in the cure rate or the rate of complications be-tween the two procedures. Symptoms of urgency were analyzed more closely and the main finding was that the prevalence of urgency symptoms decreased significantly after both mid-urethral sling procedures. The TVT operation was found to be an effective and safe procedure even after eleven years of follow-up. Long-term follow-up after a repeat TVT procedure revealed that the TVT procedure can well be considered after an unsuccessful mid-urethra tape procedure, because 75% of the patients showed significantly improvement of their incontinence. The TVT and TVT-O procedures showed no statistically significant differences in efficacy and rate of complications after three years of follow-up. In most cases these procedures alleviate preoperative symptoms of urgency and the risk of developing de novo urgency is low.

Stress-Strain Characteristics of Reinforcing Steel Bars Under Cyclic Loading

This paper presents test results for 22 high strength deformed bars and nine mild steel bars subjected to monotonic repeated and reversed axial loading to determine the stress-strain behavior. Equations have been proposed for the stress-strain curves and have been compared with test results. Satisfactory agreement was obtained.

Stress and strength analysis of pin joints in laminated anisotropic plates

Mechanical joints in composites can be tailored to achieve improved performance and better life by appropriately selecting the laminate parameters. In order to gain the best advantage of this possibility of tailoring the laminate, it is necessary to understand the influence of laminate parameters on the behaviour of joints in composites. Most of the earlier studies in this direction were based on simplified assumptions regarding load transfer at the pin-plate interface and such studies were only carried out on orthotropic and quasi-isotropic laminates. In the present study, a more rigorous analysis is carried out to study pin joints in laminates with anisotropic properties. Two types of laminates with (0/ + ?4/90)s and (0/ ± ?2/90)s layups made out of graphite epoxy T300/5208 material system are considered. The analysis mainly concentrates on clearance fit in which the pin is of smaller diameter compared to the hole. The main aspect of the analysis of pin joints is the changing contact between the pin and the plate with increasing load levels. The analysis is carried out by an iterative finite element technique and a computationally efficient routine is developed for this purpose. Numerical studies indicate that the location and magnitude of the peak stresses along the hole boundary are functions of fibre angle and the overall anisotropic properties. It is also shown that the conventional assumption of cosine distribution for the contact pressure between pin and the plate in the analysis lead to underestimation of bearing failure load and overestimation of shear and tensile failure loads in typical (0/905)s cross-ply laminates.