Study of thermocycling effect on the bond strength between an aluminous ceramic and a resin cement

This study evaluated the effect of thermocycling on the bond strength between Procera AllCeram (Nobel-Biocare) and a resin cement (Panavia F, Kuraray CO). Nine ceramic blocks with dimensions of 5x6x6mm were conditioned at one face with Rocatec System (Espe). After, they were luted with Panavia F to composite resin blocks (Clearfil AP-X, Kuraray CO). The nine groups formed by ceramic, cement and composite resin were split up obtaining 75 samples with dimensions of 12x1x1mm and adhesive surface presenting 1mm2±0.1mm2 of area. The samples were divided into 3 groups (n=25): G1 - 14 days in distilled water at 37ºC; G2 – 6,000 cycles in water (5ºC - 55ºC – 30s); G3 – 12,000 cycles in water (5ºC - 55ºC – 30s). The samples were tested in a universal testing machine (EMIC) at a crosshead speed of 1mm/min. Data were analyzed by ANOVA and Tukey tests. The results indicated that mean values of rupture tension (MPa) of G1 (10.71 ± 3.54) did not differ statistically (p <5%) from G2 (9.01 ± 3.90), however there was statistical difference between G1 and G3 (7.28 ± 3.00). It was concluded that thermocycling significantly reduced the bond strength values when samples were submitted to 12,000 cycles.

Effect of whitening and desensitizing dentifrices on composite surfaces treated with surface sealants

This study evaluated the effect of different dentifrices on the microhardness and surface roughness of composite surfaces covered by surface sealants. Samples of Filtek P60 were made and divided into groups, in accordance with surface treatments: G1 - Fortify; G2 - Fortify Plus; G3 - control (none). For Knoop microhardness evaluation, the specimens were placed in a microdurometer, under a load of 50 g for 15 sec. The analyses of surface roughness were carried out individually in a profilometer. The specimens were submitted to toothbrushing using dentifrices: Colgate Maximum Protection Anti-caries, Colgate Whitening or Sensodyne, diluted in distilled water (1:3) for 30 000 cycles. The results showed that the control group (G3) presented the highest microhardness values. The control group presented, before toothbrushing, the lowest surface roughness values, and after toothbrushing there were no differences among the experimental groups. The maintenance of the lowest values of microhardness demonstrated the effectiveness of these sealant materials to support the abrasive wear.

Abrasion resistance of direct and indirect resins as a function of a sealant veneer

Abrasive wear is one of the most common type of wear that not only affect teeth, as also dental restorations. Thus to investigate one of the etiological factors as tooth brushing procedure is clinical relevant in order to select the best material combination that may prevent damage of resin dental restoration's abrasion. This study evaluated the influence of tooth brushing on mass loss and surface roughness of direct Venus (Vs) and indirect Signum (Sg) resin composites, with and without a surface sealant, Fortify (F). Twenty-four specimens were prepared with each resin composite, using their proprietary curing units, according to manufacturer's instructions. All the specimens were polished and ultrasonically cleaned in distilled water for 5 minutes. Half of the specimens of each resin (n = 12) were covered with F (Vs F and Sg F ), except for the control (C) specimens (Vs C and Sg C ), which were not sealed. Mass loss (ML) as well as surface roughness (Ra ) was measured for all the specimens. Then, the specimens were subjected to toothbrush-dentifrice abrasion, using a testing machine for 67.000 brushing strokes, in an abrasive slurry. After brushing simulation, the specimens were removed from the holder, rinsed thoroughly and blot dried with soft absorbent paper. The abrasion of the material was quantitatively determined with final measurements of ML and surface roughness, using the method described above. ML data were analyzed by two-way analysis of variance (ANOVA) and the analysis indicated that resin composites were not statistically different; however, the specimens sealed with F showed higher ML. Ra mean values of the groups Vs F and Sg F significantly increased. Tooth brushing affects mainly the roughness of the direct and indirect resin composites veneered with a sealant.

Maternal separation on the ethanol-preferring adult rat liver structure

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Bond strength of artificial teeth attached to a microwave-polymerized denture base resin after immersion in disinfectant solutions

To evaluate the bond strength between two types of acrylic resin teeth and a microwave denture base resin after immersion in disinfectant solutions for 180 days. Eighty specimens made of acrylic resin teeth (Biotone and Biotone IPN) attached to a microwave polymerized denture base resin (Nature-Cryl MC) were divided into eight groups (n = 10) according to the treatment (distilled water-control, 2% chlorhexidine digluconate, 1% sodium hypochlorite and sodium perborate solution-Corega Tabs). The shear strength tests (MPa) were carried out using a universal testing machine with a 0.5 mm/min speed. Data analysis was performed using ANOVA and multiple comparison Student-Newman-Keuls post hoc test (α = 0.05). Biotone IPN showed similar results among the groups (distilled water, 8.25 ± 1.81 MPa; chlorhexidine, 7.81 ± 3.34 MPa; hypochlorite, 7.75 ± 3.72 MPa; and Corega Tabs, 7.58 ± 2.27 MPa, whereas Biotone showed significantly lower shear bond strength values for the groups immersed in Corega Tabs (5.25 ± 3.27 MPa) and chlorhexidine (6.08 ± 2.35 MPa). Soaking the dentures in 1% sodium hypochlorite could be recommended as a disinfectant solution for dentures fabricated with conventional acrylic resin denture teeth and microwave denture base resin. For dentures fabricated with IPN teeth and microwave denture base resin, all the soaking solutions evaluated in this study could be suggested to denture wearers.

Resistência ao cisalhamento de diferentes sistemas adesivos no esmalte dental

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Resistência de união entre um cimento resinoso e uma cerâmica aluminizada submetida a diferentes tratamentos de superfície

Pós-graduação em Odontologia Restauradora - ICT

Pré tratamento dentinário influência do condicionamento ácido, irradiação laser e hipermineralização na resistência ao cisalhamento de sistema adesivo multi uso

The disadvantages generated by the acid etching of the dentin, such as an increase in its permeability, in the surface moisture and in the potential to denature the external dentinal collagen, the formation of a fragility zone and the citotoxicity of the adhesive monomers; which are all aggravated by the depth of the dentin, have stimulated new and different treatment philosophies of the dentin. The purpose of the present study, therefore, was to investigate the effects of three dentin treatments: laser irradiation, acid etching and hypermineralization, in the shear bond strength of the SMP Plus bonding system. Sixty bovine incisors were extracted and randomly selected immediatly alter the animal's death. They were kept frozen (-18°C) for no longer than 14 days. After buccal dentinal surface had been exposed, X-Rays were taken to control the dentin thickness. The specimens were separated into two groups: (1) Control, kept in distilled water at 4ºC; (2) Mineralized, kept in hypermineralized solution at 4°C for 14 days. Each group was divided into three sub-groups according to the type of dentin treatment used: group F - followed the manufacturer instructions (acid-etching + primer + bond), group AL (acid-etching + primer + bond + laser) and group LA (laser + (laser + acid-etching + primer + bond). A composite resin standard cylinder (Z100-3M) was bond to the dentinal surface and the shear bond strength performed on a Universal lnstron machine 4301, with 500 Kg load and at 0,5mm/min. speed. The analysis of variance (ANOVA) determined that the treatments influenced the shear bond strength values (p<0,05) with the following average shearing load at failure: AL (9,96 MPa), F (7,28MPa) e LA (4,87 MPa). The interaction between the two factors analyzed Group (control and mineralized) and treatment (F, AL, LA) also influenced the shear bond strength (p<0,05). The highest values were obtained...

Contração de polimerização e expansão higroscópica de resinas compostas: análise pela técnica de video-imagem

To evaluate the volumetric changes due to polymerization and thermocycling on different resin-composites. Methods: Thirteen A2 Universal Dentin shade resin-composites (n = 10) from eight manufacturers were evaluated (4Seasons, Grandio, Venus, Amelogen Plus, P90, Z350, Esthet-X, Amaris, Vita-l-escence, Natural-Look, Charisma, Z250 and Opallis). The polymerization shrinkage percentage (PS) was calculated using an image measurement device (ACUVOL - Bisco Dental). Equal volumes of material, standardized by a semisphere polyurethane matrix (d = 3mm) were used and, after 5 minutes of relaxation, the baseline volume measurements were obtained with 18 J of energy dose from the LED light-curing unit. Measurements were obtained after 5 minutes and PS values calculated. Specimens were stored in a drydark environment for 24 hours and re-measured. Specimens were then thermocycled in distilled water between 5oC and 55oC for 20,000 cycles, subjected to another volume measurement at 5,000 cycle intervals. Specimens were gently dried prior to each measurement. Results: Repeated measurements were made using ANOVA (α = 0.05) showed that all resin-composite volumes were influenced by the number of cycles. Volumes at 5 minutes post-polymerization (12.47 ± 0.08) were significantly lower than those at baseline (12.80 ± 0.09). Volumes at 24 hours (12.43 ± 0.19) were insignificantly lower than those at 5 minutes postpolymerization. With regards to the impact of thermocycling, all specimens showed statistically significant increases in volume after 5,000 cycles (13.04 ± 0.22). Although statistically different from those after 5,000 cycles, there was no statistically significant difference between volumes measured at 10,000 (12.87±0.21), 15,000 (12.92±0.24), and 20,000 (12.84±0.23) cycles. Conclusion: According to the video-imaging analysis, thermocycling caused a significant expansion in resin-composites tested, the volume increase was not able to...

Efeito da suplementação com boro no metabolismo ósseo de camundongos diabéticos não obesos

Pós-graduação em Alimentos e Nutrição - FCFAR

Emprego do extrato de Moringa (Moringa oleífera Lamarck) na clarificação do caldo de cana para produção de açúcar e etanol

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Chá mate melhora a resistência à natação e reduz o dano oxidativo induzido pelo exercício em ratos submetidos à única sessão de natação

Several nutritional interventions are performed in order to reduce the impact of EO induced by exercise. Some studies suggest that mate tea (CM) have compounds, which can act as antioxidants reducing EO. The aim of this study was to evaluate the effect of CM induced under the EO after a single bout of aerobic exercise. Methods: We used male Wistar rats (50 days and 200g) distributed in four experimental groups: control (CON); mate tea (CM), Swimming (N); Swimming+mate tea (N + CM) . The CM and N+CM groups received CM diluted in distilled water at 96 ° C for five days, oropharyngeal route (50 mg / kg body weight, 0.5 mL). Both groups were adapted to the aquatic environment prior to experimental day, after a single swimming session, with 5% of body weight attached to the tail, until the animals reached exhaustion. Immediately after the state of exhaustion, peripheral blood was collected for further analysis. Results: The animals of the group N + CM showed improved resistance swimming compared to group C (p < 0.0001). No increase in lipid oxidative damage and production of lactate in group N + CM , compared to group N , may be attributed to the significant increase in plasma uric acid concentrations demonstrated in this study was observed . Conclusion: Therefore, the results indicate that consumption of CM may be natural strategy for improving aerobic exercise endurance and reduce the impact of EO induced by aerobic exercise.

Molhabilidade de material reembasador: efeito dos agentes químicos de limpeza

Risk of mechanical injuries contraindicate brushing and elect chemical agents as appropriate for daily cleaning of dentures relined with resilient materials. It was evaluated the effect of denture cleansers on the wettability of denture relining material (Dentusoft, Dental Medrano). We used 20 discs of acrylic resin thermoactivated VipiCril ® with 30mm diameter and 4mm thick, covered by 2mm Dentusoft ®. Divided into 4grupos were stored in artificial saliva at 37 +1 º C for 30 days, immersed daily for 15minutes in distilled water (GI), Corega ® Tabs (GII), a solution of sodium bicarbonate (GIII) or solution of sodium hypochlorite (GIV) after which, on the soft liner were poured 2 ml of type IV gypsum (Durone IV, Dentsply). Reached the final setting of the gypsum specimens were sectioned vertically and medially, settled water with sandpaper No. 400 and mounted on suitable device for reading (in the right and left) of the contact angle Carl Zeiss microscope (precision, 001). The results were submitted to analysis, showed non-normal distribution, opting for non-parametric test. Kruskal Wallis test performed at 5% significance, there was statistical difference between the groups with lower average contact angle for GII. It was concluded that the chemical cleaning Corega Tabs ® allowed a better adaptation of relining the gypsum studied.

Effect of polymerization techniques and cleaning solution on flexural resistance of acrylic resin chemically activated

The purpose of this study was to evaluate the impact of different disinfection solutions on flexural resistance of chemically-activated acrylic resin. Test pieces were made of clear acrylic resin using a rectangular mold and employing two techniques: wet polymerization under pressure (n = 20) and dry polymerization under pressure (n = 20). Test pieces were subdivided into four equal groups: distilled water (control), sodium bicarbonate, 1% sodium hypochlorite and effervescent ats. The 30-day cycling technique consisted of immersing the test pieces in 100 ml of solution for 10 min three times a day and placing them in closed containers containing artificial saliva at 37°C. Subsequently, the flexural resistance of samples was tested. Data were analyzed using two-way analysis of variance (ANOVA) with forces serving as the dependent variables and the polymerization technique and cleaning agents as independent variables. Post hoc multiple comparisons were performed using Tukey’s test. There was no statistically significant difference in the flexural strength between the two polymerization techniques. The greatest flexural strength was observed for the effervescent tablets group followed by the control and 1% sodium hypochlorite groups which were statistically similar. Thus, the sodium bicarbonate solution caused the lowest flexural resistance of the test pieces.

Corrosion resistance of Ni-Cr alloys in different mouthwashes

Several alloys have been used for prosthodontics restorations in the last years. These alloys have a number of metals that include gold, palladium, silver, nickel, cobalt, chromium and titanium and they are used in oral cavity undergo several corrosion. Corrosion can lead to poor esthetics, compromise of physical properties, or increased biological irritation. The objective of this study was evaluated corrosion resistance of two alloys Ni-Cr and Ni-Cr-Ti in three types of mouthwashes with different active ingredients: 0.5g/l cetylpyridinium chloride + 0.05% sodium fluoride, 0.05% sodium fluoride + 0.03% triclosan (with fluor) and 0.12% chlorohexidine digluconate. The potentiodynamic curves were performed by means of an EG&G PAR 283 potentiostat/galvanostat. The counter electrode was a platinum wire and reference electrode was an Ag/AgCl, KCl saturated. Before each experiment, working electrodes were mechanically polished with 600 and 1200 grade papers, rinsed with distilled water and dried in air. All experiments were carried out at 37.0oC in conventional three-compartment double wall glass cell containing mouthwashes. The microstructures of two alloys were observed in optical microscopy. Analysis of curves showed that Ni-Cr alloy was less reactive in the presence of 0.12% chlorohexidine digluconate while Ni-Cr-Ti alloy was more sensitive for others two types of mouthwashes (0.5g/l cetylpyridinium chloride + 0.05% sodium fluoride  and 0.05% sodium fluoride + 0.03% triclosan). This occurred probably due presence of titanium in this alloy. Microstructural analysis reveals the presence of dendritic and eutectic microstructures for NiCr and Ni-Cr-Ti, respectively.