Accelerated ageing methodologies for the evaluation of particulate matter role in the corrosion of outdoor-exposed bronzes

Deterioration phenomena occurring on outdoor cultural heritage have been the subject of several studies, but relatively few works investigated the specific role of Particulate Matter (PM) in the corrosion of metals. This topic is really complex and, besides field exposures, accelerated ageing tests are also necessary to isolate and understand deterioration mechanisms due to PM. For this reason, the development of a methodology that allows to reproduce and analyze the effect of PM on alloys through accelerated ageing in climatic chamber has been started. On quaternary bronze specimens, single salts and a mix of them were deposited via two deposition methods: dry (directly depositing the salt on the surface) and wet (dropping a salt solution and drying it), simulating the initial chemical activation of the salts by RH% variations or by raindrops, respectively. Then, to better mimic the composition of real PM, a mixture containing a soluble salts, a mineral, a black carbon and an organic fraction was formulated and spread on the samples. The samples were placed in a climatic chamber and exposed to cyclic variations of T and RH for three weeks. The ageing cycles were set according to predictions on salt deliquescence/recrystallization through E-AIM model and to the evaluation of regional climatic data. The surface evolution was followed by SEM-EDX, Raman, AT-IR and UV-Vis Spectrophotometry. At the end of the test, mass losses were determined and corroded metals removed by pickling were analyzed by AAS. On the basis of the obtained results, the tested procedures seem to be promising in accelerating and mimicking realistic corrosion phenomena, as under the selected conditions, corrosion products typically found at different exposure time (from days to years) on outdoor bronzes were able to progressively form and evolve. Moreover, the two deposition modes simulating different condition of chemical activation of PM deposits allow to obtain complementary information.

Historic and modern alloys: atmospheric corrosion and development of accelerated ageing methodologies

The atmospheric corrosion of modern and historic alloys used in cultural heritage has been investigated by applying specific accelerated ageing methods. Three main research lines were carried out, involving different materials. In the first part, the atmospheric corrosion of a modern Cu-3Si-1Mn bronze was investigated through accelerated ageing tests simulating outdoor runoff conditions. The corrosion processes were evaluated through different analyses, and the results obtained were compared to those of a traditional quaternary bronze. The second line was carried out to characterise historic aluminium alloys used in aeronautics to develop and apply innovative protection strategies for their conservation. Historic wrecks were identified and characterised through micro and macroscale observations. Moreover, accelerated ageing tests were performed on both historic and modern alloys to compare their behaviour and select the best modern substrate to be used for the development of effective coatings. The third research line aimed to develop accelerate sampling and ageing methods to investigate the role of particulate matter (PM) in the atmospheric corrosion of bronzes and metals in general. The first approach consisted in the fine-tuning of an efficient accelerated method for ambient PM sampling on bronze specimens followed by their accelerated ageing, in order to establish a correlation between the PM and the substrate’s corrosion. After the accelerated ageing of the specimens, the corrosion was evaluated by surface characterisation and correlated to the PM features. The second approach consisted in the development of a synthetic PM formulation and of an artificial deposition method, which was performed by spraying mixtures containing the main PM inorganic fractions on a G-85 bronze with an airbrush. The deposition efficiency was assessed, and the effect of synthetic PM on the bronze corrosion was evaluated. The results were compared to those obtained by ambient PM deposition.

Effects of Accelerated Hygroscopic Ageing on Interlaminar Shear Strength and Glass Transition Temperature of CFRP

This study, which is undertaken in cooperation with Riba-COMPOSITES, investigates the effects of hygroscopic ageing on the Interlaminar Shear Strength and Glass Transition Temperature of short-beams made of carbon fibre reinforced polymer (CFRP) composites provided by two different vendors. The materials have the same weave pattern but differ in the epoxy resin formulation. The tests are done in accordance with ASTM. Accelerated ageing techniques are carried out by immersion of the specimens in deionized water at 70°C for different periods of time, developing different degrees of ageing. The results of the tests confirm that hygroscopic ageing causes a loss of properties and a depression of the glass transition temperature in both the materials. However, since one of the two materials shows more constant property degradation, its behaviour in service conditions should be more easily predictable.

Results of the ageing campaign of the photomultiplier Hamamatsu R760

Il guadagno di un PMT è il fattore di amplificazione tra la corrente generata dal fotocatodo e quella finale dell’anodo. Quando un PMT è soggetto a una sorgente luminosa per lunghi periodi di tempo (processo noto come "invecchiamento"), il suo guadagno tende a diminuire. In questa tesi sono riportati i risultati della campagna di invecchiamento di un fotomoltiplicatore Hamamatsu R760. In particolare, è stato studiato come variasse il guadagno in funzione della carica integrata dal PMT tramite due principali tipi di misure: quella del guadagno assoluto, che consiste in singole misure di guadagno nella condizione di emissione di un singolo fotoelettrone alla volta, e quelle di guadagno relativo, le quali hanno permesso di studiare la dipendenza tra guadagno e voltaggio applicato al PMT. Il PMT in esame è stato fatto invecchiare fino a una carica integrata totale pari a 342 C. Una volta raggiunti i 282 C, è stato spento per 20 giorni, in modo da studiare l’eventuale capacità di recuperare guadagno durante i periodi di inattività. É stata osservata una rapida decrescita del guadagno nei primi 40 C integrati, com- inciando da 7.79 · 10^6 fino a un valore pari a 1.68 · 10^6, seguita da oscillazioni minori attorno a una decrescita lineare media. Dopo il periodo di inattività non è stato rilevato alcun recupero significativo di guadagno. Il guadagno del PMT dipende dal voltaggio applicato tramite una legge a potenza, i cui parametri sono stati misurati. In particolare, gli esponenti di tale relazione sono stati soggetti a una decrescita rapida iniziale (nei primi 40 C di carica integrata), seguita da una stabilizzazione. Inoltre, sono stati ricavati i valori di tensione da applicare al PMT per mantenere il guadagno a un valore costante di 1.5 · 10^5 in funzione della carica integrata. Questo valore è stato scelto come punto di lavoro per il rivelatore PLUME installato nell’esperimento LHCb, che utilizzerà questo tipo di PMT per la sua campagna di misure.

Avaliação do amaciamento de carne bovina de dianteiro (Triceps brachii) pelos métodos de maturação, estimulação elétrica, injeção de ácidos e tenderização mecânica

Twenty-two Triceps brachii muscle obtained from 11 cows aged 3 and 4 years , killed in an experimental slaughter plant, were submitted to mechanical tenderization, injection with acetic acid 0,1M and lactic acid 0,2M, ageing for 9 and 14 days and electrical stimulation (250v - 60Hz - 90s), some of them were reserved as a control group, without treatment. The 14 days ageing time presented 21% of increase in subjective tenderness and 12% of reduction in shear force, these values were similar to the electrical stimulated meat. However the injection with acids and the ageing time 9 days did not present significant effect in the texture. Although the shear force values of mechanical tenderized meat was the shortest among all treatments, suspect of superestimation because of the fractures plan created by this process. Another analyses were carried out: pH reduction curve, R value; colour analysis; weight losses by cooking and by treatment; and microbiological analysis.

Treinamento físico e fatores de risco cardiovascular em homens de meia-idade

Universidade Estadual de Campinas . Faculdade de Educação Física

Atividade fisica e os dominios da qualidade de vida e do autoconceito no processo de envelhecimento

Universidade Estadual de Campinas . Faculdade de Educação Fisica

Adaptação e validação da escla ASKAS - Aging Sexual Knowledge and Attitudes Scale em idosos brasileiros

Universidade Estadual de Campinas . Faculdade de Educação Física

Variabilidade da frequencia cardiaca em trabalhadores em turnos

Universidade Estadual de Campinas . Faculdade de Educação Física

Saude fisica, indicadores antropometricos, desempenho fisico e bem-estar subjetivo em idosos atendidos no ambulatorio de geriatria do HC/UNICAMP

Universidade Estadual de Campinas . Faculdade de Educação Física

Sisal organosolv pulp as reinforcement for cement based composites

The present work describes non-conventional sisal (Agave sisalana) chemical (organosolv) pulp from residues of cordage as reinforcement to cement based materials. Sisal organosolv pulp was produced in a 1:1 ethanol/water mixture and post chemically and physically characterized in order to compare its properties with sisal kraft pulp. Cement based composites reinforced with organosolv or kraft pulps and combined with polypropylene (PP) fibres were produced by the slurry de-watering and pressing method as a crude simulation of the Hatschek process. Composites were evaluated at 28 days of age, after exposition to accelerated carbonation and after 100 soak/dry cycles. Composites containing organosolv pulp presented lower mechanical strength, water absorption and apparent porosity than composites reinforced with kraft pulp. The best mechanical performance after ageing was also achieved by samples reinforced with kraft pulp. The addition of PP fibres favoured the maintenance of toughness after ageing. Accelerated carbonation promoted the densification of the composites reinforced with sisal organosolv + PP fibres.

Tempo de vida útil de propelentes base-simples

The purpose of this work was to determine the safe shelf life of single-base propellants. The kinetic parameters relative to the consumption of the stabilizer diphenylamine (DPA) added to the propellant were determined as a function of the storage and ageing time. High Performance Liquid Chromatography (HPLC) with spectrophotometric detection was used to determine the DPA percentage before and after the artificial ageing at 60, 70 and 80 ºC. The experimental data were very well adjusted to a pseudo-first order kinetic model and the respective kinetic constants are 8.0-10-3 day-1 (60 ºC); 1.9-10-2 day-1 (70 ºC); 1.2-10-1 day-1 (80 ºC). The activation energy was calculated as 130 kJ mol-1 and the half-time for depletion of the DPA at the hypothetical temperature of 40 ºC of storage was estimated as being 6 years.

Exposição ocupacional à sílica no Brasil no ano de 2001

OBJETIVO: Estimar o número de trabalhadores brasileiros expostos à sílica no ano de 2001. MÉTODO: Informações sobre ocupações e setores econômicos foram reunidas em uma matriz de exposição ocupacional (MEO) com 347 categorias ocupacionais por 25 subsetores econômicos. Informações sobre o número de trabalhadores por ocupação foram extraídas da base de dados Relatório Anual de Informações Sociais (RAIS) do Ministério do Trabalho e Emprego. A exposição à sílica foi avaliada e classificada por dois peritos em quatro categorias, de acordo com a freqüência semanal de exposição no ambiente de trabalho. RESULTADOS: Foram considerados não expostos 31.451.594 trabalhadores (85,7%), possivelmente expostos 976.939 (2,65%), provavelmente expostos 2.404.955 (6,52%) e definitivamente expostos à sílica 2.065.929 (5,6%). Os setores com a maior prevalência de exposição foram: construção civil 65%, extração de pedras 59%, indústria de mineral não metálico 55% e indústria metalúrgica 24%. No setor de serviços de terceiros, a prevalência foi de 2%. CONCLUSÃO: A prevalência de trabalhadores brasileiros definitivamente expostos à sílica é mais alta do que aquela observada em países europeus, onde estudos semelhantes foram conduzidos.

O segredo da longevidade segundo as percepções dos próprios longevos

Estudos apontam fatores que podem aumentar a longevidade; no entanto, muitas questões pertinentes a este tema ainda não foram elucidadas. Percepções do próprio longevo a respeito dos fatores contribuintes para longevidade são importantes, permitindo levantamento de cada fator e suas interações com demais variáveis que promovem a longevidade. O presente artigo relata dados da investigação sobre "o segredo da longevidade", segundo percepções dos próprios longevos, analisados pelo referencial metodológico da grounded theory. Foram entrevistados trinta ferroviários longevos do município de Botucatu (SP). A análise das falas dos longevos possibilitou determinar que a percepção dos fatores se aglutina em torno de categorias progressivamente abrangentes que culminam na representação coletiva de que a longevidade é dependente do embate entre fatores prejudiciais que aniquilam a vida e fatores saudáveis que geram e preservam a vida, sobre o qual a falta de controle social e do Estado torna pessimista a visão do futuro.

Comparação da percepção de fadiga e de capacidade para o trabalho entre trabalhadores têxteis de empresas que se encontram em diferentes estágios de responsabilidade social empresarial no estado de São Paulo, Brasil

OBJETIVOS: Comparar as características demográficas e as percepções da capacidade para o trabalho, fadiga e condições de trabalho entre trabalhadores de indústrias têxteis que estejam em diferentes estágios de responsabilidade social empresarial (RSE). MÉTODOS: Em estudo transversal, 126 trabalhadores de três empresas e cinco fábricas responderam a questionário de caracterização demográfica, condições e estilos de vida, a autoavaliações sobre fadiga, condições de trabalho e capacidade para o trabalho. As empresas foram classificadas em dois grupos de pontuação de indicadores de RSE (o grupo um de menor pontuação e o grupo dois de maior pontuação), com base nas respostas dadas em questionário específico. RESULTADOS: Não foram encontradas diferenças (p > 0,05) nos resultados de capacidade para o trabalho, fadiga e na maior parte dos dados demográficos obtidos entre os trabalhadores dos dois grupos. As melhores condições de trabalho, no grupo de maior pontuação (p = 0,008), deveram-se principalmente ao fornecimento de refeições nas fábricas. CONCLUSÕES: O desenvolvimento e a implementação de projetos de RSE não implicam, necessariamente, em melhores condições de trabalho ou em percepções dos trabalhadores de menor fadiga ou maior capacidade para o trabalho, em relação a empresas que não dispõem desses projetos. Por tratar-se de estudo transversal com população reduzida e como a capacidade para o trabalho pode diminuir com o envelhecimento do trabalhador novos estudos, preferencialmente longitudinais, deverão ser realizados, com populações maiores.