Practical issues for testing thin film PV modules at standard test conditions.

Thin film photovoltaic (TF) modules have gained importance in the photovoltaic (PV) market. New PV plants increasingly use TF technologies. In order to have a reliable sample of a PV module population, a huge number of modules must be measured. There is a big variety of materials used in TF technology. Some of these modules are made of amorphous or microcrystalline silicon. Other are made of CIS or CdTe. Not all these materials respond the same under standard test conditions (STC) of power measurement. Power rates of the modules may vary depending on both the extent and the history of sunlight exposure. Thus, it is necessary a testing method adapted to each TF technology. This test must guarantee repeatability of measurements of generated power. This paper shows responses of different commercial TF PV modules to sunlight exposure. Several test procedures were performed in order to find the best methodology to obtain measurements of TF PV modules at STC in the easiest way. A methodology for indoor measurements adapted to these technologies is described.

Estudio experimental sobre la reacción álcali-sílice en el hormigón producida por áridos de reacción lenta

La finalidad de esta investigación se enmarca dentro de los estudios sobre hormigones de presas llevados a cabo en el Laboratorio Central de Estructuras y Materiales del CEDEX. En España se han diagnosticado 18 obras afectadas tanto por la reacción álcali-sílice de tipo rápido como por la de tipo lento. Dos de de las obras, fabricadas con áridos graníticos, no presentan signos de deterioro pero en laboratorio se han hallado productos expansivos. En las 16 presas españolas restantes, el hormigón de 10 de ellas estaba fabricado con áridos graníticos, de las cuales, 7 están afectadas por la reacción de tipo lento. Sin embargo, en las clasificaciones internacionales de las rocas potencialmente reactivas se establece habitualmente que las rocas graníticas son inocuas o de reactividad muy baja. En los casos puntuales encontrados en la literatura, la reactividad de este tipo de áridos se encuentra frecuentemente asociada al cuarzo microcristalino que contienen y ocasionalmente se asocia esta reactividad también al cuarzo deformado y/o microfisurado. En la tesis doctoral de Víctor Daniel Lanza Fernández, también realizada en el CEDEX, se han tratado los áridos de reacción rápida, dando una descripción detallada de los componentes que intervienen en este tipo de reacción y presentando un ensayo eficaz para su detección en el laboratorio. La investigación desarrollada en la presente tesis doctoral se ha centrado en los áridos de reacción lenta, mucho menos estudiados. A partir del estudio bibliográfico realizado sobre este tipo de reacción se ha detectado ciertas lagunas, basadas principalmente en la falta de un método de detección en el laboratorio para los áridos de reacción lenta. No se ha encontrado un procedimiento en el estudio petrográfico que sea fiable y cuantificable para este tipo de áridos. El ensayo acelerado de barras de mortero, que para los áridos de reacción rápida supone un método rápido y fiable, falla en la detección de los áridos de reacción lenta al aplicar los límites normalizados. Si bien en publicaciones recientes se ha propuesto la posibilidad de ampliar el tiempo de tratamiento hasta los 90 días, la duración del ensayo es más larga de lo deseado. Para resolver estas lagunas, se han tomado áridos de obras reales afectadas por la reacción álcali-sílice (en algún caso también de las canteras de donde se extrajeron los áridos para la ejecución), con lo que la reactividad de estos áridos queda demostrada por su comportamiento en obra. Al objeto de aumentar la muestra de ensayo y utilizar también áridos inocuos, se han tomado muestras de canteras, tanto en uso como abandonadas. Sobre estos áridos se ha realizado una caracterización completa con los ensayos actualmente disponibles para el estudio de su reactividad con los álcalis del cemento: estudio petrográfico, ensayo acelerado de barras de mortero y Gel-Pat modificado. En la investigación se ha desarrollado una metodología de tinción de geles álcali-sílice para la cuantificación de los mismos en el interior de las barras de mortero. Se ha relacionado el volumen de gel generado en la reacción con la expansión producida, tanto para áridos lentos, como rápidos, estableciendo analogías y diferencias en el comportamiento de ambos. La cuantificación de este tipo de compuestos realizada en las barras de mortero, abre la posibilidad de estudiar la capacidad expansiva que presentan en testigos de hormigón de obras afectadas. Este dato podría ser una herramienta importante para el desarrollo de modelos matemáticos que puedan predecir el futuro comportamiento de las estructuras afectadas por la reacción álcali-sílice. La tinción ha sido asimismo utilizada para establecer un método de detección de áridos reactivos basado en el ensayo de Gel-Pat modificado. La metodología de detección propuesta para estos áridos es cuantitativa y proporciona los resultados en 14 días, suponiendo una ventaja importante sobre los métodos actuales, que permiten detectarlos en 90 días (de forma orientativa en 56 días). This research is part of the studies on durability of concrete dams carried out in the Laboratorio Central de Estructuras y Materiales of CEDEX during the last years. At the present time, 18 public works affected by alkali-silica reaction have been diagnosed in Spain. In 12 of them the concrete was mixed with granitic aggregates, 7 of which were damaged by the slow alkali-silica reaction, 3 by the rapid alkali-silica reaction and in the other 2 cases, although there was no visual evidence of the reaction in field, the laboratory tests showed the presence of expansive products inside the concrete. However, in the international classifications of potentially reactive aggregates granitic rocks are pointed out as innocuous or as low reactivity and usually their reactivity is attributed to the presence of microcrystalline quartz and occasionally with the strained and microcracked quartz. The rapid reactive aggregates were deeply studied in a previous research (Víctor Daniel Lanza’s Thesis) also carried out in CEDEX. In this research, a detailed description of the components involved in the rapid alkali-silica reaction was given. Also, a fast method to detect them in the laboratory was developed. The research of the present PhD Thesis is focused in the slow-reactive aggregates, much less studied. The state of the art has shown some gaps in the knowledge about this reaction, mainly the absence of a reliable method to detect slow-reactive aggregates. On one side, there is no systematic and quantitative petrographic test for these aggregates. On the other side, the accelerated mortar bar test has been proved to be effective to detect rapid reactive aggregates but the standard limits fail in the detection of the slowreactive aggregates. In recent investigations it has been proposed extending the test until 90 days, but this period is considered too long. In this research, aggregates taken from affected structures have been used in the test, so their reactivity has been shown in practice. With the aim of increasing the number of samples aggregates from quarries have been also used. A method to stain alkali-silica gels has been applied to mortar bars, thereby quantifying the volume of gel generated inside. This volume has been related to the expansion of the bars, both for rapid for slow reactive aggregates, establishing similarities and differences. The quantification of the gel volume, applied to concrete cores extracted from affected structures, could be an important tool in mathematical models to predict the future behaviour of the structures affected by the alkali-silica reaction. The staining method has been also used to develop a method to detect slow reactive aggregates, based on the optimised Gel-Pat test, obtaining results in 14 days. This represents a major improvement compared to the actual methods (accelerated mortar bar test) which give an indicative value of reactivity at 56 days, and a final result at 90 days.

An eco-friendly way to fire retardant flexible polyurethane foam: layer-by-layer assembly of fully bio-based substances

The objective of the present study is to develop fully renewable and environmentally benign techniques for improving the fire safety of flexible polyurethane foams (PUFs). A multilayered coating made from cationic chitosan (CS) and anionic alginate (AL) was deposited on PUFs through layer-by-layer assembly. This coating system exhibits a slight influence on the thermal stability of PUF, but significantly improves the char formation during combustion. Cone calorimetry reveals that 10 CS-AL bilayers (only 5.7% of the foams weight) lead to a 66% and 11% reduction in peak heat release rate and total heat release, respectively, compared with those of the uncoated control. The notable decreased fire hazards of PUF are attributed to the CS-AL coatings being beneficial to form an insulating protective layer on the surface of burning materials that inhibits the oxygen and heat permeation and slows down the flammable gases in the vapor phase, and thereby improves the flame resistance. This water-based, environmentally benign natural coating will stimulate further efforts in improving fire safety for a variety of polymer substrates.

Myelin basic protein kinase activity in tomato leaves is induced systemically by wounding and increases in response to systemin and oligosaccharide elicitors

In response to wounding, a 48-kDa myelin basic protein (MBP) kinase is activated within 2 min, both locally and systemically, in leaves of young tomato plants. The activating signal is able to pass through a steam girdle on the stem, indicating that it moves through the xylem and does not require intact phloem tissue. A 48-kDa MBP kinase is also activated by the 18-amino acid polypeptide systemin, a potent wound signal for the synthesis of systemic wound response proteins (swrps). The kinase activation by systemin is strongly inhibited by a systemin analog having a Thr-17 → Ala-17 substitution, which is a powerful antagonist of systemin activation of swrp genes. A 48-kDa MBP kinase activity also increases in response to polygalacturonic acid and chitosan but not in response to jasmonic acid or phytodienoic acid. In def1, a mutant tomato line having a defective octadecanoid pathway, the 48-kDa MBP kinase is activated by wounding and systemin as in the wild-type plants. This indicates that MBP kinase functions between the perception of primary signals and the DEF1 gene product. In response to wounding, the MBP kinase is phosphorylated on phosphotyrosine residues, indicating a relationship to the mitogen-activated protein kinase family of protein kinases.

Hydrogen peroxide is generated systemically in plant leaves by wounding and systemin via the octadecanoid pathway

Hydrogen peroxide (H2O2) generated in response to wounding can be detected at wound sites and in distal leaf veins within 1 hr after wounding. The response is systemic and maximizes at about 4–6 hr in both wounded and unwounded leaves, and then declines. The timing of the response corresponds with an increase in wound-inducible polygalacturonase (PG) mRNA and enzyme activity previously reported, suggesting that oligogalacturonic acid (OGA) fragments produced by PG are triggering the H2O2 response. Systemin, OGA, chitosan, and methyl jasmonate (MJ) all induce the accumulation of H2O2 in leaves. Tomato plants transformed with an antisense prosystemin gene produce neither PG activity or H2O2 in leaves in response to wounding, implicating systemin as a primary wound signal. The antisense plants do produce both PG activity and H2O2 when supplied with systemin, OGA, chitosan, or MJ. A mutant tomato line compromised in the octadecanoid pathway does not exhibit PG activity or H2O2 in response to wounding, systemin, OGA, or chitosan, but does respond to MJ, indicating that the generation of H2O2 requires a functional octadecanoid signaling pathway. Among 18 plant species from six families that were assayed for wound-inducible PG activity and H2O2 generation, 14 species exhibited both wound-inducible PG activity and the generation of H2O2. Four species, all from the Fabaceae family, exhibited little or no wound-inducible PG activity and did not generate H2O2. The time course of wound-inducible PG activity and H2O2 in Arabidopsis thaliana leaves was similar to that found in tomato. The cumulative data suggest that systemic wound signals that induce PG activity and H2O2 are widespread in the plant kingdom and that the response may be associated with the defense of plants against both herbivores and pathogens.

Comparison of the Ability of Partially N-Acetylated Chitosans and Chitooligosaccharides to Elicit Resistance Reactions in Wheat Leaves1

Chitin, a linear polysaccharide composed of (1→4)-linked 2-acetamido-2-deoxy-β-d-glucopyranose (GlcNAc) residues, and chitosan, the fully or partially N-acetylated, water-soluble derivative of chitin composed of (1→4)-linked GlcNAc and 2-amino-2-deoxy-β-d-glucopyranose (GlcN), have been proposed as elicitors of defense reactions in higher plants. We tested and compared the ability of purified (1→4)-linked oligomers of GlcNAc (tetramer to decamer) and of GlcN (pentamer and heptamer) and partially N-acetylated chitosans with degrees of acetylation (DA) of 1%, 15%, 35%, 49%, and 60% and average degrees of polymerization between 540 and 1100 to elicit phenylalanine ammonia-lyase (PAL) and peroxidase (POD) activities, lignin deposition, and microscopically and macroscopically visible necroses when injected into the intercellular spaces of healthy, nonwounded wheat (Triticum aestivum L.) leaves. Purified oligomers of (1→4)-linked GlcN were not active as elicitors, whereas purified oligomers of (1→4)-linked GlcNAc with a degree of polymerization ≥ 7 strongly elicited POD activities but not PAL activities. Partially N-acetylated, polymeric chitosans elicited both PAL and POD activities, and maximum elicitation was observed with chitosans of intermediate DAs. All chitosans but not the chitin oligomers induced the deposition of lignin, the appearance of necrotic cells exhibiting yellow autofluorescence under ultraviolet light, and macroscopically visible necroses; those with intermediate DAs were most active. These results suggest that different mechanisms are involved in the elicitation of POD activities by GlcNAc oligomers, and of PAL and POD activities by partially N-acetylated chitosan polymers and that both enzymes have to be activated for lignin biosynthesis and ensuing necrosis to occur.

Cutin Monomers and Surface Wax Constituents Elicit H2O2 in Conditioned Cucumber Hypocotyl Segments and Enhance the Activity of Other H2O2 Elicitors1

Hypocotyls from etiolated cucumber (Cucumis sativus L.) seedlings were gently abraded at their epidermal surface and cut segments were conditioned to develop competence for H2O2 elicitation. Alkaline hydrolysates of cutin from cucumber, tomato, and apple elicited H2O2 in such conditioned segments. The most active constituent of cucumber cutin was identified as dodecan-1-ol, a novel cutin monomer capable of forming hydrophobic terminal chains. Additionally, the cutin hydrolysates enhanced the activity of a fungal H2O2 elicitor, similar to cucumber surface wax, which contained newly identified alkan-1,3-diols. The specificity of elicitor and enhancement activity was further elaborated using some pure model compounds. Certain saturated hydroxy fatty acids were potent H2O2 elicitors as well as enhancers. Some unsaturated epoxy and hydroxy fatty acids were also excellent H2O2 elicitors but inhibited the fungal elicitor activity. Short-chain alkanols exhibited good elicitor and enhancer activity, whereas longer-chain alkan-1-ols were barely active. The enhancement effect was also observed for H2O2 elicitation by ergosterol and chitosan. The physiological significance of these observations might be that once the cuticle is degraded by fungal cutinase, the cutin monomers may act as H2O2 elicitors. Corrosion of cutin may also bring surface wax constituents in contact with protoplasts and enhance elicitation.

The cellulose-binding domain of the major cellobiohydrolase of Trichoderma reesei exhibits true reversibility and a high exchange rate on crystalline cellulose.

Cellulose-binding domains (CBDs) bind specifically to cellulose, and form distinct domains of most cellulose degrading enzymes. The CBD-mediated binding of the enzyme has a fundamental role in the hydrolysis of the solid cellulose substrate. In this work we have investigated the reversibility and kinetics of the binding of the CBD from Trichoderma reesei cellobiohydrolase I on microcrystalline cellulose. The CBD was produced in Escherichia coli, purified, and radioactively labeled by reductive alkylation with 3H. Sensitive detection of the labeled CBD allowed more detailed analysis of its behavior than has been possible before, and important novel features were resolved. Binding of the CBD was found to be temperature sensitive, with an increased affinity at lower temperatures. The interaction of the CBD with cellulose was shown to be fully reversible and the CBD could be eluted from cellulose by simple dilution. The rate of exchange measured for the CBD-cellulose interaction compares well with the hydrolysis rate of cellobiohydrolase I, which is consistent with its proposed mode of action as a processive exoglucanase.

Imobilização do fungo Penicillium citrinum CBMAI 1186 e lipase de Pseudomonas fluorescens em biopolímeros para aplicações em biocatálise

Diversos biomateriais podem ser aplicados como suportes na imobilização de células totais de fungos filamentosos ou enzimas isoladas, visando a manutenção e o prolongamento da atividade enzimática em processos biocatalíticos. Exemplos promissores de biomateriais são a fibroína da seda e o alginato de sódio. A fibroína é um material protéico com alta estabilidade térmica, elasticidade, resistência à tensão, não sofre ataque microbiano, baixo custo de purificação e alta tenacidade, o alginato é um biopolímero versátil, devido a suas propriedades gelificantes em soluções aquosas. Assim, neste trabalho empregou-se micélios do fungo derivado de ambiente marinho, Penicillium citrinum CBMAI 1186, livres e imobilizados em biopolímeros (fibra de algodão, fibra de fibroína da seda e fibra de paina) na biorredução quimiosseletiva, regiosseletiva e enantiosseletiva da ligação α,β-C=C de enonas α,β-, α,β,γ,δ- e di-α,β-insaturadas previamente sintetizados pela a reação de condensação aldólica. Foi possível a utilização do fungo P. citrinum CBMAI 1186 na redução quimiosseletiva, regiosseletiva e enantiosseletiva da ligação dupla carbono-carbono de sistemas α,β-insaturados. A imobilização do fungo P. citrinum CBMAI 1186 em biopolímeros (algodão, fibroína da seda, paina e quitosana) permitiu a prolongamento da atividade celular do fungo. O protocolo desenvolvido foi capaz de obter compostos até então descritos apenas por síntese clássica. Também foi realizado reações de resolução enzimática de derivados de haloidrinas por diferentes lipases microbianas de: Pseudomonas fluorescens, Candida cylindracea, Rhizopus niveus e Aspergillus niger. A lipase de P. fluorescens foi imobilizada em esferas de fibroína do bicho da seda (método 1, via adsorção) e em blenda com alginato de cálcio (método 2, via encapsulação) em diferentes condições, tais como, variação de solvente, variação da quantidade de enzima imobilizada e tempo de reação. As condições otimizadas foram empregadas em diferentes haloidrinas, rendendo elevados excessos enantioméricos (ee > 99%) e alta razão enanantiomérica (E > 200) para os produtos acetilados. Foi possível desenvolver um protocolo simples, barato e prático para a síntese enantiosseletiva de haloidrina reforçando a versatilidade da fibroína e do alginato como suportes de imobilização para catalisadores heterogêneos. Também foi possível utilizar a lipase imobilizada (método 2) na reação de transesterificação para obtenção do biodiesel etílico. As melhores condições para o bom funcionamento do biocatalisador foram: 30% do biocatalisador, 20% de n-hexano, relação óleo e etanol de 1:4 a 32 ºC por 48 h em agitação magnética (400 rpm). Essas condições permitiram a formação de 42% de rendimento do biodiesel etílico. O biocatalisador apresentou algumas limitações reacionais, tais como, fragilidade frente a elevadas temperaturas (> 32 ºC) e prolongado tempo de agitação magnética. Porém, permaneceu apto no meio por 4 ciclos consecutivas. Conclui-se que os biomateriais (fibroína, alginato e quitosana) podem ser utilizados como alternativas versáteis na imobilização de micélios de fungos filamentoso e de enzimas isoladas para aplicações em biocatalíticas.

Resposta imune do antígeno de superfície de hepatite B administrado via nasal em nanopartículas de quitosana liofilizadas

A nanotecnologia tornou possível estruturar nanopartículas (NPs), utilizando-se polímeros biodegradáveis e atóxicos, como a quitosana (QS) - capaz de carrear e disponibilizar antígenos para a mucosa, devido sua propriedade mucoadesiva. Uma vacina liofilizada, em comparação a uma formulação líquida, possui inúmeras vantagens, tais como melhora na estabilidade do produto e melhor resistência às variações de temperatura, aumentando sua vida de prateleira e possibilitando melhor logística do produto aos locais onde o acesso à rede refrigerada é difícil; ademais, um produto liofilizado tem sua mucoadesividade aumentada, possibilitando maior tempo de permanência na mucosa. O presente trabalho teve como objetivo observar a resposta imune, em camundongos, de uma vacina desenvolvida por um mecanismo de entrega intranasal do HBsAg (Antígeno de superfície da Hepatite B) encapsulado pelo método de incorporação em nanopartículas de quitosana (NPs) liofilizadas. A formação das NPs foi realizada pela interação eletroestática da quitosana e do TPP (tripolifosfato de sódio), utilizando método de geleificação iônica. Formulações de NPs com glicina 5% apresentaram boas características após reconstituição, umidade residual inferior a 1% e processo de liofilização de 13 horas. Foi avaliada a imunogenicidade da inoculação do HBsAg em formulações de NPs de quitosana líquida e liofilizada, verificando-se que a forma líquida produziu anticorpos IgG contra HBsAg.

Propriedades físico-químicas e mecânicas de membranas porosas de carboximetilquitosana e hidrogéis de quitosana para aplicação em engenharia de tecidos

Este trabalho teve como principal objetivo produzir membranas porosas de carboximetilquitosana e hidrogéis de quitosana com propriedades físico-químicas e mecânicas adequadas para aplicações em Engenharia de Tecidos. Para isso, quitosanas com diferentes graus de acetilação (4,0%<GA<40%) e de elevada massa molar média viscosimétrica (Mv>750.000 g.mol-1) foram produzidas através da aplicação de processos consecutivos de desacetilação assistida por irradiação de ultrassom de alta intensidade (DAIUS) à beta-quitina extraída de gládios de lulas Doryteuthis spp. A carboximetilação de quitosana extensivamente desacetilada (Qs-3; GA=4%) foi realizada pela reação com ácido monocloroacético em meio isopropanol/solução aquosa de NaOH, gerando a amostra CMQs-0 (GS≈0,98; Mv≈190.000 g.mol-1). A irradiação de ultrassom de alta intensidade foi empregada para tratar solução aquosa de CMQs-0 durante 1 h e 3 h, resultando nas amostras CMQs-1 (Mv≈94.000 g.mol-1) e CMQs-3 (Mv≈43.000 g.mol-1), respectivamente. Para a produção de membranas reticuladas, genipina foi adicionada em diferentes concentrações (1,0x10-4 mol.L-1, 3,0x10-4 mol.L-1 ou 5,0x10-4 mol.L-1) às soluções aquosas das CMQs, que foram vertidas em placas de Petri e a reação de reticulação procedeu por 24 h. Em seguida, as membranas reticuladas (M-CMQs) foram liofilizadas, neutralizadas, lavadas e liofilizadas novamente, resultando em nove amostras, que foram caracterizadas quanto ao grau médio de reticulação (GR), grau médio de hidratação (GH), morfologia, propriedades mecânicas e quanto à susceptibilidade à degradação por lisozima. O grau médio de reticulação (GR) foi tanto maior quanto maior a concentração de genipina empregada na reação, variando de GR≈3,3% (M-CMQs-01) a GR≈17,8% (M-CMQs-35). As análises de MEV revelaram que as membranas reticuladas M-CMQs são estruturas porosas que apresentam maior densidade de poros aparentes quanto maiores os valores de Mve GR. Entretanto, as membranas preparadas a partir de CMQs de elevada massa molar (Mv>94.000 g.mol-1) e pouco reticuladas (GR<10%), apresentaram propriedades mecânicas superiores em termos de resistência máxima à tração (>170 kPa) e elongação máxima à ruptura (>40%). Por outro lado, as membranas mais susceptíveis à degradação enzimática foram aquelas preparadas a partir de CMQs de baixa massa molar (Mv≈43.000 g.mol-1) e que exibiram baixos graus de reticulação (GR<11%). Hidrogéis estáveis de quitosana sem o uso de qualquer agente de reticulação externo foram produzidos a partir da gelificação de soluções aquosas de quitosana com solução de NaOH ou vapor de NH3. Os hidrogéis produzidos a partir de soluções de quitosana de elevada massa molar média ponderal (Mw≈640.000 g.mol-1) e extensivamente desacetilada (DA≈2,8%) em concentrações poliméricas acima 2,0%, exibiram melhores propriedades mecânicas com o aumento da concentração polimérica, devido à formação de numerosos emaranhamentos físicos das cadeias poliméricas em solução. Os resultados mostram que as propriedades físico-químicas e mecânicas dos hidrogéis de quitosana podem ser controladas variando a concentração do polímero e o processo de gelificação. A avaliação biológica de tais hidrogéis para a regeneração de miocárdio infartado de ratos revelou que os hidrogéis de quitosana preparados a partir de soluções de polímero a 1,5% foram perfeitamente incorporados sobre a superfície do epicárdio do coração e apresentaram degradação parcial acompanhada por infiltração de células mononucleares.

Estudo das propriedades térmicas e mecânicas de resinas dentárias compostas preparadas com sílica e quitosana

Neste trabalho foi estudada a influência da adição de quitosana e sílica a monômeros dimetacrílicos, BisEMA e TEGDMA, por meio das técnicas de fotocalorimetria, termogravimetria e análise dinâmico mecânica. Os resultados dos experimentos de fotocalorimetria demonstraram que a quitosana pode aumentar a velocidade de polimerização e o máximo de conversão para alguns sistemas em determinadas concentrações da mesma, já a sílica tem pouco efeito nas reações de fotopolimerização das amostras. Para os experimentos de termogravimetria, a quitosana tem pouca influência na degradação das amostras não alterando significativamente as curvas TGA/DTG, por outro lado a sílica acelerou a degradação térmica das amostras. A avaliação das propriedades mecânicas demonstrou que a quitosana diminui a temperatura de transição vítrea e a resposta elástica dos sistemas não afetando os valores dos módulos de armazenamento e módulos de perda. A sílica apresentou a tendência de aumento de temperatura de transição vítrea e não alteração da resposta elástica das amostras.

The role of microorganisms in the formation of calcitic moonmilk deposits and speleothems in Altamira Cave

Bacteria are able to induce carbonate precipitation although the participation of microbial or chemical processes in speleothem formation remains a matter of debate. In this study, the origin of carbonate depositions such as moonmilk, an unconsolidated microcrystalline formation with high water content, and the consolidation of carbonate precipitates into hard speleothems were analyzed. The utilized methods included measurements of the composition of stable isotopes in these precipitates, fluorimetric determinations of RNA/DNA ratios and respirometric estimations in Altamira Cave. Results from isotope composition showed increases of the δ18O and δ13C ratios from moonmilk in the very first stages of formation toward large speleothems. Estimates of RNA/DNA ratios suggested an inactivation of microorganisms from incipient moonmilk toward consolidated deposits of calcium carbonate. Respiratory activity of microorganisms also showed a significant decrease in samples with accumulated calcite. These results suggest that bacterial activity induces the conditions required for calcium carbonate precipitation, initiating the first stages of deposition. Progressive accumulation of carbonate leads towards a less favorable environment for the development of bacteria. On consolidated speleothems, the importance of bacteria in carbonate deposition decreases and chemical processes gain importance in the deposition of carbonates.

Beyond the H2/CO2 upper bound: one-step crystallization and separation of nano-sized ZIF-11 by centrifugation and its application in mixed matrix membranes

The synthesis of nano-sized ZIF-11 with an average size of 36 ± 6 nm is reported. This material has been named nano-zeolitic imidazolate framework-11 (nZIF-11). It has the same chemical composition and thermal stability and analogous H2 and CO2 adsorption properties to the conventional microcrystalline ZIF-11 (i.e. 1.9 ± 0.9 μm). nZIF-11 has been obtained following the centrifugation route, typically used for solid separation, as a fast new technique (pioneering for MOFs) for obtaining nanomaterials where the temperature, time and rotation speed can easily be controlled. Compared to the traditional synthesis consisting of stirring + separation, the reaction time was lowered from several hours to a few minutes when using this centrifugation synthesis technique. Employing the same reaction time (2, 5 or 10 min), micro-sized ZIF-11 was obtained using the traditional synthesis while nano-scale ZIF-11 was achieved only by using centrifugation synthesis. The small particle size obtained for nZIF-11 allowed the use of the wet MOF sample as a colloidal suspension stable in chloroform. This helped to prepare mixed matrix membranes (MMMs) by direct addition of the membrane polymer (polyimide Matrimid®) to the colloidal suspension, avoiding particle agglomeration resulting from drying. The MMMs were tested for H2/CO2 separation, improving the pure polymer membrane performance, with permeation values of 95.9 Barrer of H2 and a H2/CO2 separation selectivity of 4.4 at 35 °C. When measured at 200 °C, these values increased to 535 Barrer and 9.1.

Performance Assessment of a Polymer Electrolyte Membrane Electrochemical Reactor under Alkaline Conditions – A Case Study with the Electrooxidation of Alcohols

A novel polymer electrolyte membrane electrochemical reactor (PEMER) configuration has been employed for the direct electrooxidation of propargyl alcohol (PGA), a model primary alcohol, towards its carboxylic acid derivatives in alkaline medium. The PEMER configuration comprised of an anode and cathode based on nanoparticulate Ni and Pt electrocatalysts, respectively, supported on carbonaceous substrates. The electrooxidation of PGA was performed in 1.0 M NaOH, where a cathode based on a gas diffusion electrode was manufactured for the reduction of oxygen in alkaline conditions. The performance of a novel alkaline anion-exchange membrane based on Chitosan (CS) and Poly(vinyl) alcohol (PVA) in a 50:50 composition ratio doped with a 5 wt.% of poly (4-vinylpyridine) organic ionomer cross-linked, methyl chloride quaternary salt resin (4VP) was assessed as solid polymer electrolyte. The influence of 4VP anionic ionomer loading of 7, 12 and 20 wt.% incorporated into the electrocatalytic layers was examined by SEM and cyclic voltammetry (CV) upon the optimisation of the electroactive area, the mechanical stability and cohesion of the catalytic ink onto the carbonaceous substrate for both electrodes. The performance of the 4VP/CS:PVA membrane was compared with the commercial alkaline anion-exchange membrane FAA −a membrane generally used in direct alcohol alkaline fuel cells- in terms of polarisation plots in alkaline conditions. Furthermore, preparative electrolyses of the electrooxidation of PGA was performed under alkaline conditions of 1 M NaOH at constant current density of 20 mA cm−2 using a PEMER configuration to provide proof of the principle of the feasibility of the electrooxidation of other alcohols in alkaline media. PGA conversion to Z isomers of 3-(2-propynoxy)-2-propenoic acid (Z-PPA) was circa 0.77, with average current efficiency of 0.32. Alkaline stability of the membranes within the PEMER configuration was finally evaluated after the electrooxidation of PGA.