Rare-earth-doped silica microchip laser fabricated by sintering nanoporous glass

We report a new method for fabricating rare-earth-doped silica glasses for laser materials obtained by sintering nanoporous silica glasses impregnated with rare-earth-doped ions. The fabricated materials have no residual pores and show good optical and mechanical properties. Good performance from a Nd3+-doped silica microchip laser operating at 1.064 mum is successfully demonstrated, suggesting that the fabricated silica glasses have potential for use as active materials for high-power solid-state lasers. (C) 2005 Optical Society of America.

Raman spectroscopic investigation of pure and ytterbium-doped rare earth silicate crystals

Raman spectroscopy was used to study the molecular structure of a series of selected rare earth (RE) silicate crystals including Y2SiO5 (YSO), LU2SiO5 (LSO), (Lu0.5Y0.5)(2)SiO5 (LYSO) and their ytterbium-doped samples. Raman spectra show resolved bands below 500 cm(-1) region assigned to the modes of SiO4 and oxygen vibrations. Multiple bands indicate the nonequivalence of the RE-O bonds and the lifting of the degeneracy of the RE ion vibration. Low intensity bands below 500 cm(-1) are an indication of impurities. The (SiO4)(4-) tetrahedra are characterized by bands near 200 cm(-1) which show a separation of the components of nu(4) and nu(2), in the 500-700 cm(-1) region which are attributed to the distorting bending vibration and in the 880-1000 cm(-1) region which are attributed to the symmetric and antisymmetric stretching vibrational modes. The majority of the bands in the 300-610 cm(-1) region of Re2SiO5 were found to arise from vibrations involving both Si and RE ions, indicating that there is considerable mixing of Si displacements with Si-O bending modes and RE-0 stretching modes. The Raman spectra of RE silicate crystals were analyzed in terms of the molecular structure of the crystals, which enabled separation of the bands attributed to distinct vibrational units. Copyright (C) 2007 John Wiley & Sons, Ltd.

Optimizing the Curie temperature of pseudo-binary RxR2-x ' Fe-17 (R, R ' = rare earth) for magnetic refrigeration

Several pseudo-binary RxR2-x'Fe-17 alloys (with R = Y, Ce, Pr, Gd and Dy) were synthesized with rhombohedral Th2Zn17-type crystal structure determined from x-ray and neutron powder diffraction. The choice of compositions was done with the aim of tuning the Curie temperature (T-C) in the 270 +/- 20 K temperature range, in order to obtain the maximum magneto-caloric effect around room temperature. The investigated compounds exhibit broad isothermal magnetic entropy changes, Delta S-M(T), with moderate values of the refrigerant capacity, even though the values of Delta S-M(Peak) are relatively low compared with those of the R2Fe17 compounds with R = Pr or Nd. The reduction on the Delta S-M(Peak) is explained in terms of the diminution in the saturation magnetization value. Furthermore, the Delta S-M(T) curves exhibit a similar caret-like behavior, suggesting that the magneto-caloric effect is mainly governed by the Fe-sublattice. A single master curve for Delta S-M/Delta S-M(Peak)(T) under different values of the magnetic field change are obtained for each compound by rescaling of the temperature axis.

Down to earth thoughts on conserving aquatic genetic diversity

A discussion is presented on the topic of maintaining genetic diversity in aquatic ecosystems, considering the various threats caused by irreversible damage or loss to the environment. The current situation in aquaculture and future prospects regarding the conservation and protection of endangered species are outlined, describing the case of tilapias in Africa as one particular example of fish conservation.

Preliminary observation on culture of Penaeus monodon in low-saline waters

The feasibility of semi-intensive culture of Penaeus monodon in low saline environment was investigated by comparing the growth and production in low (0.16-6.52 ppt) and high (4.60-19.42 ppt) saline areas at two stocking densities (10.5 and 16 individuals/m super(2)). After 135 days of culture, yield of shrimp in low and high stocking densities was 1563.37 kg/ha and 2274 kg/ha, respectively, in low saline ponds, and 1173.00 and 1974.00 kg/ha, respectively in high saline ponds. Food conversion ratio (FCR, 1.31-1.58) and specific growth rate (SGR 21.04-21.19%) were higher in low saline ponds as compared to high saline ponds (FCR, 1.35-1.68; SGR, 19.22-19.88%). Growth of shrimp was satisfactory in low saline ponds even when salinity decreased after 60 days of culture to almost freshwater level (0.16 ppt) indicating the variability of semi-intensive culture of P. monodon in low saline environment.