An in-situ modified sol-gel process for monolith catalyst preparation used in the partial oxidation of methane

An in-situ modified sol-gel method for the preparation of a Ni-based monolith-supported catalyst is reported. With the presence of a proper amount of plasticizer and binder, and at an optimized pH value, the stable boehmite sol was modified with metal ions (Ni, Li, La) successfully without distinct growth of the particle size. Monolith-supported Ni-based/gamma-Al2O3 catalysts were obtained using the modified sol as the coating medium with several cycles of dip-coating and calcination. Combined BET, SEM-EDS, XRD and H-2-TPR investigations demonstrated that the derived monolith catalysts had a high specific surface area, a relatively homogeneous surface composition, and a high extent of interaction between the active component and the support. These catalysts showed relatively stable catalytic activities for partial oxidation of methane (POM) to syngas under atmospheric pressure. The monolith catalysts prepared by this sol-gel method also demonstrated an improved resistance to sintering and loss of the active component during the reaction process.

Templateless synthesis of catalysts with narrow mesoporous distribution

In this study, amorphous silica-alumina nanomaterials with narrow mesoporous distribution can be obtained by two novel sol-gel processes, without the use of any templates. The results of our experiments show that the preparation method has a great influence on the precursor sol structure as well as the specific surface area and mesopore volume of the final product, but has no effect on the pore size distribution.

FTIR study of CO and NO adsorbed on nitrided CoMo/Al2O3 catalysts

The states of surface Co and Mo sites on nitrided CoMo supported on Al2O3 were studied by adsorption of CO and NO as IR probe molecules. Three IR bands at 2200, 2060 and 2025 cm(-1) were detected for adsorbed CO. These bands can be respectively attributed to the surface NCO species as a result of CO adsorbed on surface N sites, and linearly adsorbed CO on surface Co and Mo sites in low valence states. The addition of cobalt to the Mo nitride diminishes the band at 2200 cm(-1). This may be due to either the change of the surface structure of the supported nitride, or the formation of a new phase, CoxMoyNz, as suggested in the literature Kim et al., Catal. Lett., 1997, 43, 91 and Logan et al., Catal. Lett., 1998, 56, 165. Comparison of CO and NO adsorption on Mo2N/Al2O3 and CoMoNx/Al2O3 indicates that the presence of cobalt can promote the reduction and nitridation of Mo.

Epoxidation of cyclohexene on Ti/SiO2 catalysts prepared by chemical grafting TiCl4 on deboronated silica xerogel

Ti/SiO2 (or Ti/de[B]SiO2) catalysts were prepared by grafting deboronated silica xerogel with gaseous TiCl4. Using TBHP as oxidant, the Ti/de[B]SiO2 catalyst shows both catalytic activity and selectivity in epoxidation of cyclohexene better than 80%, and the activity can be comparable with that of Ti-beta. The catalytic activity of Ti/de[B]SiO2 strongly depends on the content of B of support precursor, and the pretreatment temperature of the support. IR studies show that the sites in the deboronated silica xerogel to react with TiCl4 are not only the silanol nests, but also the defect sites produced during the deboronation. (C) 2001 Elsevier Science B.V. All rights reserved.

Preparation of titania-based catalysts for formaldehyde photocatalytic oxidation from TiCl4 by the sol-gel method

Titania sols were prepared by acid hydrolysis of a TiCl4 precursor instead of titanium alkoxides. The effect of acid concentration on the particle size and stability of sol was investigated. Stable titania sols with mean particle size of 14 nm could be obtained when the H+/Ti molar ratio was 0.5. The titania sols were modified with Pt, SiO2, ZrO2, WO3 and MoO3 to prepare a series of modified catalysts, which were used for the photocatalytic oxidation of formaldehyde at 37 degreesC. They showed different photocatalytic activities due to the influence of the additives. Comparing with pure TiO2, the addition of silica or zirconia increased the photocatalytic activity, while the addition of Pt and MoO3 decreased the activity, and the addition Of WO3 had little effect on the activity. It is of great significance that the conversion of formaldehyde was increased up to 94% over the SiO2-TiO2 catalyst. The increased activity was partly due to higher surface area and porosity or smaller crystallite size. A comparison of our catalyst compositions with the literature in this field suggested that the difference in activity due to the addition of a second metal oxide maybe caused by the surface chemistry of the catalysts, particularly the acidity. (C) 2001 Elsevier Science B.V. All rights reserved.