Evaluation of molar weight and deacetylation degree of chitosan during chitin deacetylation reaction: Used to produce biofilm

Chitosan is a polysaccharide derived from chitin, mainly of crustacean shells and shrimp wastes. The utilization of chitosan is related to the molar weight and deacetylation degree of the biopolymer. The aim of this work is to study the chitin deacetylation reaction, by the viscosity average molar weight and deacetylation degree of chitosan as a function of reaction time. Deacetylation was carried out in concentrated alkaline solution, 421 g L−1, at 130◦C and the reaction occurred during 4 h. Chitosan paste obtained after 20, 90 and 240 min was used to produce biofilms, which were characterized according water vapor permeability and mechanical properties (tensile strength and percentage tensile elongation at break). During the reaction time deacetylation degree reached 93%, and a 50% reduction in the viscosity average molar weight value in relation to the value of the first 20 min of reaction was found Both reactions presented a kinetic behavior of the pseudo-first order. Biofilm produced from the paste of chitosan with high deacetylation degree showed higher water vapor permeability (WVP), tensile strength (TS) and elongation (E) when compared to films with a low deacetylation.

Characterization of Non-linear Polymer Properties to Predict Process Induced Warpage and Residual Stress of Electronic Packages

Nonlinear thermo-mechanical properties of advanced polymers are crucial to accurate prediction of the process induced warpage and residual stress of electronics packages. The Fiber Bragg grating (FBG) sensor based method is advanced and implemented to determine temperature and time dependent nonlinear properties. The FBG sensor is embedded in the center of the cylindrical specimen, which deforms together with the specimen. The strains of the specimen at different loading conditions are monitored by the FBG sensor. Two main sources of the warpage are considered: curing induced warpage and coefficient of thermal expansion (CTE) mismatch induced warpage. The effective chemical shrinkage and the equilibrium modulus are needed for the curing induced warpage prediction. Considering various polymeric materials used in microelectronic packages, unique curing setups and procedures are developed for elastomers (extremely low modulus, medium viscosity, room temperature curing), underfill materials (medium modulus, low viscosity, high temperature curing), and epoxy molding compound (EMC: high modulus, high viscosity, high temperature pressure curing), most notably, (1) zero-constraint mold for elastomers; (2) a two-stage curing procedure for underfill materials and (3) an air-cylinder based novel setup for EMC. For the CTE mismatch induced warpage, the temperature dependent CTE and the comprehensive viscoelastic properties are measured. The cured cylindrical specimen with a FBG sensor embedded in the center is further used for viscoelastic property measurements. A uni-axial compressive loading is applied to the specimen to measure the time dependent Young’s modulus. The test is repeated from room temperature to the reflow temperature to capture the time-temperature dependent Young’s modulus. A separate high pressure system is developed for the bulk modulus measurement. The time temperature dependent bulk modulus is measured at the same temperatures as the Young’s modulus. The master curve of the Young’s modulus and bulk modulus of the EMC is created and a single set of the shift factors is determined from the time temperature superposition. The supplementary experiments are conducted to verify the validity of the assumptions associated with the linear viscoelasticity. The measured time-temperature dependent properties are further verified by a shadow moiré and Twyman/Green test.

Design of unique composites based on aromatic thermosetting copolyesters

Aromatic thermosetting copolyester (ATSP) has promise in high-temperature applications. It can be employed as a bulk polymer, as a coating and as a matrix for carbon fiber composites (ATSP/C composites). This work focuses on the applications of high performance ATSP/C composites. The morphology of the ATSP matrix in the presence of carbon fiber was studied. The effect of liquid crystalline character of starting oligomers used to prepare ATSP on the final crystal structure of the ATSP/C composite was evaluated. Matrices obtained by crosslinking of both liquid crystalline oligomers (ATSP2) and non-liquid crystalline oligomers (ATSP1) tend to crystallize in presence of carbon fibers. The crystallite size of ATSP2 is 4 times that of ATSP1. Composites made from ATSP2 yield tougher matrices compared to those made from ATSP1. Thus toughened matrices could be achieved without incorporating any additives by just changing the morphology of the final polymer. The flammability characteristics of ATSP were also studied. The limiting oxygen index (LOI) of bulk ATSP was found to be 40% whereas that of ATSP/C composites is estimated to be 85%. Thus, ATSP shows potential to be used as a flame resistant material, and also as an aerospace reentry shield. Mechanical properties of the ATSP/C composite were characterized. ATSP was observed to bond strongly with reinforcing carbon fibers. The tensile strength, modulus and shear modulus were comparable to those of conventionally used high temperature epoxy resins. ATSP shows a unique capability for healing of interlaminar cracks on application of heat and pressure, via the Interchain Transesterification Reaction (ITR). ITR can also be used for reduction in void volume and healing of microcracks. Thus, ATSP resin systems provide a unique intrinsic repair mechanism compared to any other thermosetting systems in use today. Preliminary studies on measurement of residual stresses for ATSP/C composites indicate that the stresses induced are much lower than that in epoxy/C composites. Thermal fatigue testing suggests that ATSP shows better resistance to microcracking compared to epoxy resins.

On the effect of Arabian Sea and Indian Ocean sea surface temperature anomaly on the monsoon rainfall of south-east of Iran

Southeast region of the country has hot and dry weather which causes to happen heavy rainfall in short time period of warm seasons and to occur river flooding. These precipitations are influenced by monsoon system of India ocean. In these thesis, It was tried to evaluate the relation between thermal anomaly of sea surface in India ocean and Arab sea which effects on southeast monsoon precipitations of Iran, For evaluation of this happening in southeast, data were collected from 7 synoptic observation stations of Bandar Abbas, Minab, Kerman , Bam, Chabahar, Iranshahr, Zahedan and 17 rain gauge stations during June to September of each year from 1980 to 2010. Rainy days were determine and then some information about synoptic circulation models, maps of average pressure of sea surface, geopotential height of 700hP surface, geopotential height of 500hP surface, temperature of 850 hPa surface, humidity of 700 hPa surface, vertical velocity of 700 hPa surface, vertical velocity of 500 hP and humidity of 2 meters height for 6 systems were extracted from NCEP/NCAR website for evaluation. By evaluation of these systems it was determined that the monsoon low pressure system tab brings needed humidity of these precipitations to this region from India ocean and Arab sea with a vast circulation. It is seen that warm air pool locates on Iran and cold air pool locates on west of India at 800 hPa surface. In a rainy day this warm air transfers to high latitudes and influences the temperature trough of southeast cold air pool of the country. In the middle surfaces of 700 and 500 hPa, the connection between low height system above India and low height system above the higher latitudes causes the low height system above India to be strength and developed. By evaluation of humidity at 2 meters height and 700 hPa surface we observe that humidity Increases in the southeast region. With penetrating of the low height system of India above the 700 and 500 hPa surfaces of southeast of Iran, the value of negative omega (Rising vertical velocity) is increased. In the second pace, it was shown the evaluation of how the correlation between sea surface temperature anomaly in India Ocean and Arab sea influences southeast monsoon precipitation of Iran. For this purpose the data of water surface temperature anomaly of Arab sea and India ocean, the data of precipitation anomaly of 7 synoptic stations , mentioned above, and correlation coefficient among the data of precipitation anomaly and water surface temperature anomaly of Arab Sea, east and west of India ocean were calculated. In conclusion it was shown that the maximum correlation coefficient of precipitation anomaly had belonged to India Ocean in June and no meaningful correlation was resulted in July among precipitation anomaly and sea surface temperature anomaly for three regions, which were evaluated.

Comportamento magnético de compósitos de matriz polimérica com adição de ferritas

Polymer matrix composites offer advantages for many applications due their combination of properties, which includes low density, high specific strength and modulus of elasticity and corrosion resistance. However, the application of non-destructive techniques using magnetic sensors for the evaluation these materials is not possible since the materials are non-magnetizable. Ferrites are materials with excellent magnetic properties, chemical stability and corrosion resistance. Due to these properties, these materials are promising for the development of polymer composites with magnetic properties. In this work, glass fiber / epoxy circular plates were produced with 10 wt% of cobalt or barium ferrite particles. The cobalt ferrite was synthesized by the Pechini method. The commercial barium ferrite was subjected to a milling process to study the effect of particle size on the magnetic properties of the material. The characterization of the ferrites was carried out by x-ray diffraction (XRD), field emission gun scanning electron microscopy (FEG-SEM) and vibrating sample magnetometry (VSM). Circular notches of 1, 5 and 10 mm diameter were introduced in the composite plates using a drill bit for the non-destructive evaluation by the technique of magnetic flux leakage (MFL). The results indicated that the magnetic signals measured in plates with barium ferrite without milling and cobalt ferrite showed good correlation with the presence of notches. The milling process for 12 h and 20 h did not contribute to improve the identification of smaller size notches (1 mm). However, the smaller particle size produced smoother magnetic curves, with fewer discontinuities and improved signal-to-noise ratio. In summary, the results suggest that the proposed approach has great potential for the detection of damage in polymer composites structures

Effect of rare earth dopants on structural and mechanical properties of nanoceria synthesized by combustion method

Structural characteristics of combustion synthesized, calcined and densified pure and doped nanoceria with tri-valent cations of Er, Y, Gd, Sm and Nd were analyzed by X-ray diffraction (XRD) and high resolution transmission electron microscopy (HRTEM). The results showed that the as-synthesized and calcined nanopowders were mesoporous and calculated lattice parameters were close to theoretical ion-packing model. The effect of dopants on elastic modulus, microhardness and fracture toughness of sintered pure and doped ceria were investigated. It was observed that tri-valent cation dopants increased the hardness of the ceria, whereas the fracture toughness and elastic modulus were decreased.

Pastas compósitas cimento/sílica/polímero para cimentação de poços de baixa profundidade sujeitas à injeção de vapor

The production of heavy oil fields, typical in the Northeastern region, is commonly stimulated by steam injection. High bottom hole temperatures are responsible not only for the development of deleterious stresses of the cement sheath but also for cement strength retrogression. To overcome this unfavorable scenario, polymeric admixtures can be added to cement slurries to improve its fracture energy and silica flour to prevent strength retrogression. Therefore, the objective of the present study was to investigate the effect of the addition of different concentrations of polyurethane (5-25%) to cement slurries containing 40% BWOC silica flour. The resulting slurries were characterized using standard API (American Petroleum Institute) laboratory tests. In addition to them, the mechanical properties of the slurries, including elastic modulus and microhardness were also evaluated. The results revealed that density, free water and stability of the composite cement/silica/polyurethane slurries were within acceptable limits. The rheological behavior of the slurries, including plastic viscosity, yield strength and gel strength increased with the addition of 10% BWOC polyurethane. The presence of polyurethane reduced the fluid loss of the slurries as well as their elastic modulus. Composite slurries also depicted longer setting times due to the presence of the polymer. As expected, both the mechanical strength and microhardness of the slurries decreased with the addition of polyurethane. However, at high bottom hole temperatures, the strength of the slurries containing silica and polyurethane was far superior than that of plain cement slurries. In summary, the use of polyurethane combined with silica is an interesting solution to better adequate the mechanical behavior of cement slurries to heavy oil fields subjected to steam injection

FABRICATION, CHARACTERIZATION, AND IRRADIATION OF AN AUSTENITIC OXIDE DISPERSION STRENGTHENED STEEL SUITED FOR NEXT GENERATION NUCLEAR APPLICATIONS

As nuclear energy systems become more advanced, the materials encompassing them need to perform at higher temperatures for longer periods of time. In this Master’s thesis we experiment with an oxide dispersion strengthened (ODS) austenitic steel that has been recently developed. ODS materials have a small concentration of nano oxide particles dispersed in their matrix, and typically have higher strength and better extreme temperature creep resistance characteristics than ordinary steels. However, no ODS materials have ever been installed in a commercial power reactor to date. Being a newer research material, there are many unanswered phenomena that need to be addressed regarding the performance under irradiation. Furthermore, due to the ODS material traditionally needing to follow a powder metallurgy fabrication route, there are many processing parameters that need to be optimized before achieving a nuclear grade material specification. In this Master’s thesis we explore the development of a novel ODS processing technology conducted in Beijing, China, to produce solutionized bulk ODS samples with ~97% theoretical density. This is done using relatively low temperatures and ultra high pressure (UHP) equipment, to compact the mechanically alloyed (MA) steel powder into bulk samples without any thermal phase change influence or oxide precipitation. By having solutionized bulk ODS samples, transmission electron microscopy (TEM) observation of nano oxide precipitation within the steel material can be studied by applying post heat treatments. These types of samples will be very useful to the science and engineering community, to answer questions regarding material powder compacting, oxide synthesis, and performance. Subsequent analysis performed at Queen’s University included X-ray diffraction (XRD) and inductively coupled plasma optical emission spectrometry (ICP-OES). Additional TEM in-situ 1MeV Kr2+ irradiation experiments coupled with energy dispersive X-ray (EDX) techniques, were also performed on large (200nm+) non-stoichiometric oxides embedded within the austenite steel grains, in an attempt to quantify the elemental compositional changes during high temperature (520oC) heavy ion irradiation.

Investigating the mesh dependency and upscaling of 3D grain-based models for the simulation of brittle fracture processes in low-porosity crystalline rock

The application of 3D grain-based modelling techniques is investigated in both small and large scale 3DEC models, in order to simulate brittle fracture processes in low-porosity crystalline rock. Mesh dependency in 3D grain-based models (GBMs) is examined through a number of cases to compare Voronoi and tetrahedral grain assemblages. Various methods are used in the generation of tessellations, each with a number of issues and advantages. A number of comparative UCS test simulations capture the distinct failure mechanisms, strength profiles, and progressive damage development using various Voronoi and tetrahedral GBMs. Relative calibration requirements are outlined to generate similar macro-strength and damage profiles for all the models. The results confirmed a number of inherent model behaviors that arise due to mesh dependency. In Voronoi models, inherent tensile failure mechanisms are produced by internal wedging and rotation of Voronoi grains. This results in a combined dependence on frictional and cohesive strength. In tetrahedral models, increased kinematic freedom of grains and an abundance of straight, connected failure pathways causes a preference for shear failure. This results in an inability to develop significant normal stresses causing cohesional strength dependence. In general, Voronoi models require high relative contact tensile strength values, with lower contact stiffness and contact cohesional strength compared to tetrahedral tessellations. Upscaling of 3D GBMs is investigated for both Voronoi and tetrahedral tessellations using a case study from the AECL’s Mine-by-Experiment at the Underground Research Laboratory. An upscaled tetrahedral model was able to reasonably simulate damage development in the roof forming a notch geometry by adjusting the cohesive strength. An upscaled Voronoi model underestimated the damage development in the roof and floor, and overestimated the damage in the side-walls. This was attributed to the discretization resolution limitations.

Quality in palliative care from the patient perspective : Instrument development, perceptions of care received and the importance of care

The overall aim was to investigate the quality of palliative care from the patient perspective, to adapt and psychometrically evaluate the Quality from Patients’ Perspective instrument specific to palliative care (QPP-PC) and investigate the relationship between the combination of person- and organization-related conditions and patients’ perceptions of care quality. Methods: In the systematic literature review (I), 23 studies from 6 databases and reference lists in 2014 were synthesized by integrative thematic analysis. The quantitative studies (II–IV) had cross-sectional designs including 191 patients (73% RR) from hospice inpatient care, hospice day care, palliative units in nursing homes and home care in 2013–2014. A modified version of QPP was used. Additionally, person- and organization-related conditions were assessed. Psychometric evaluation, descriptive and inferential statistics were used. Main findings: Patients’ preferences for palliative care included living a meaningful life and responsive healthcare personnel, care environment and organization of care (I). The QPP-PC was developed, comprising 12 factors (49 items), 3 single items and 4 dimensions: medical–technical competence, physical–technical conditions, identity–oriented approach, and socio-cultural atmosphere (II). QPP-PC measured patients’ perceived reality (PR) and subjective importance (SI) of care quality. PR differed across settings, but SI did not (III). All settings exhibited areas of strength and for improvement (II, III). Person-related conditions seemed to be related to SI, and person- and organization-related conditions to PR, explaining 18–30 and 22-29% respectively of the variance (IV). Conclusions: The patient perspective of care quality (SI and PR) should be integrated into daily care and improvement initiatives in palliative care. The QPP-PC can measure patients’ perceptions of care quality. Registered nurses and other healthcare personnel need awareness of person- and organization-related conditions to provide high-quality person-centred care.

Anti-inflammatory effect of exercise training in subjects with type 2 diabetes and the metabolic syndrome is dependent on exercise modalities and independent of weight loss

We investigated the effect of different exercise modalities on high sensitivity-C reactive protein (hs-CRP) and other inflammatory markers in patients with type 2 diabetes and the metabolic syndrome. Eighty-two patients were randomized into 4 groups: sedentary control (A); receiving counseling to perform low-intensity physical activity (B); performing prescribed and supervised high-intensity aerobic (C) or aerobic + resistance (D) exercise (with the same caloric expenditure) for 12 months. Evaluation of leisure-time physical activity and assessment of physical fitness, cardiovascular risk factors and inflammatory biomarkers was performed at baseline and every 3 months. Volume of physical activity increased and HbA1c decreased in Groups B–D. VO2max, HOMA-IR index, HDL-cholesterol, waist circumference and albuminuria improved in Groups C and D, whereas strength and flexibility improved only in Group D. Levels of hs-CRP decreased in all three exercising groups, but the reduction was significant only in Groups C and D, and particularly in Group D. Changes in VO2max and the exercise modalities were strong predictors of hs-CRP reduction, independent of body weight. Leptin, resistin and interleukin-6 decreased, whereas adiponectin increased in Groups C and D. Interleukin-1β, tumor necrosis factor-α and interferon-γ decreased, whereas anti-inflammatory interleukin-4 and 10 increased only in Group D. In conclusion, physical exercise in type 2 diabetic patients with the metabolic syndrome is associated with a significant reduction of hs-CRP and other inflammatory and insulin resistance biomarkers, independent of weight loss. Long-term high-intensity (preferably mixed) training, in addition to daytime physical activity, is required to obtain a significant anti-inflammatory effect.

NIR spectrocospy can evaluate the crystallinity and the tensile and burst strenghts of nanocellulosic films.

The near infrared (NIR) spectroscopy presents itself as an interesting non-destructive test tool as it enables a fast, simple and reliable way for characterizing large samplings of biological materials in a short period of time. This work aimed to establish multivariate models to estimate the crystallinity indices and tensile and burst strength of cellulosic and nanocellulosic films through NIR spectroscopy. NIR spectra were recorded from the films before tensile and bursting strength, and crystallinity tests. Spectral information were correlated with reference values obtained by laboratory procedures through partial least square regression (PLS-R). The PLS-R model for estimating the crystallinity index presented a coefficient of determination in cross-validation (R2cv) of 0,94 and the ratio of performance to deviation (RPD) was 3,77. The mechanical properties of the films presented a high correlation with the NIR spectra: R2p = 0,85 (RPD = 2,23) for tensile and R2p = 0,93 (RPD = 3,40) for burst strength. The statistics associated to the models presented have shown that the NIR spectroscopy has the potential to estimate the crystallinity index and resistance properties of cellulose and nanocellulose films on in-line monitoring systems.

Behaviour and design of cold-formed steel compression members at elevated temperatures

Cold-formed steel members have been widely used in residential, industrial and commercial buildings as primary load bearing structural elements and non-load bearing structural elements (partitions) due to their advantages such as higher strength to weight ratio over the other structural materials such as hot-rolled steel, timber and concrete. Cold-formed steel members are often made from thin steel sheets and hence they are more susceptible to various buckling modes. Generally short columns are susceptible to local or distortional buckling while long columns to flexural or flexural-torsional buckling. Fire safety design of building structures is an essential requirement as fire events can cause loss of property and lives. Therefore it is essential to understand the fire performance of light gauge cold-formed steel structures under fire conditions. The buckling behaviour of cold-formed steel compression members under fire conditions is not well investigated yet and hence there is a lack of knowledge on the fire performance of cold-formed steel compression members. Current cold-formed steel design standards do not provide adequate design guidelines for the fire design of cold-formed steel compression members. Therefore a research project based on extensive experimental and numerical studies was undertaken at the Queensland University of Technology to investigate the buckling behaviour of light gauge cold-formed steel compression members under simulated fire conditions. As the first phase of this research, a detailed review was undertaken on the mechanical properties of light gauge cold-formed steels at elevated temperatures and the most reliable predictive models for mechanical properties and stress-strain models based on detailed experimental investigations were identified. Their accuracy was verified experimentally by carrying out a series of tensile coupon tests at ambient and elevated temperatures. As the second phase of this research, local buckling behaviour was investigated based on the experimental and numerical investigations at ambient and elevated temperatures. First a series of 91 local buckling tests was carried out at ambient and elevated temperatures on lipped and unlipped channels made of G250-0.95, G550-0.95, G250-1.95 and G450-1.90 cold-formed steels. Suitable finite element models were then developed to simulate the experimental conditions. These models were converted to ideal finite element models to undertake detailed parametric study. Finally all the ultimate load capacity results for local buckling were compared with the available design methods based on AS/NZS 4600, BS 5950 Part 5, Eurocode 3 Part 1.2 and the direct strength method (DSM), and suitable recommendations were made for the fire design of cold-formed steel compression members subject to local buckling. As the third phase of this research, flexural-torsional buckling behaviour was investigated experimentally and numerically. Two series of 39 flexural-torsional buckling tests were undertaken at ambient and elevated temperatures. The first series consisted 2800 mm long columns of G550-0.95, G250-1.95 and G450-1.90 cold-formed steel lipped channel columns while the second series contained 1800 mm long lipped channel columns of the same steel thickness and strength grades. All the experimental tests were simulated using a suitable finite element model, and the same model was used in a detailed parametric study following validation. Based on the comparison of results from the experimental and parametric studies with the available design methods, suitable design recommendations were made. This thesis presents a detailed description of the experimental and numerical studies undertaken on the mechanical properties and the local and flexural-torsional bucking behaviour of cold-formed steel compression member at ambient and elevated temperatures. It also describes the currently available ambient temperature design methods and their accuracy when used for fire design with appropriately reduced mechanical properties at elevated temperatures. Available fire design methods are also included and their accuracy in predicting the ultimate load capacity at elevated temperatures was investigated. This research has shown that the current ambient temperature design methods are capable of predicting the local and flexural-torsional buckling capacities of cold-formed steel compression members at elevated temperatures with the use of reduced mechanical properties. However, the elevated temperature design method in Eurocode 3 Part 1.2 is overly conservative and hence unsuitable, particularly in the case of flexural-torsional buckling at elevated temperatures.

Structure–property relationships of silk-modified mesoporous bioglass scaffolds

Porous mesopore-bioglass (MBG) scaffolds have been proposed as a new class of bone regeneration materials due to their apatite-formation and drug-delivery properties; however, the material’s inherent brittleness and high degradation and surface instability are major disadvantages, which compromise its mechanical strength and cytocompatibility as a biological scaffold. Silk, on the other hand, is a native biomaterial and is well characterized with respect to biocompatibility and tensile strength. In this study we set out to investigate what effects blending silk with MBG had on the physiochemical, drug-delivery and biological properties of MBG scaffolds with a view to bone tissue engineering applications. Transmission electron microscopy (TEM), scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR) were the methods used to analyze the inner microstructure, pore size and morphology, and composition of MBG scaffolds, before and after addition of silk. The effect of silk modification on the mechanical property of MBG scaffolds was determined by testing the compressive strength of the scaffolds and also compressive strength after degradation over time. The drug-delivery potential was evaluated by the release of dexamethasone (DEX) from the scaffolds. Finally, the cytocompatibility of silk-modified scaffolds was investigated by the attachment, morphology, proliferation, differentiation and bone-relative gene expression of bone marrow stromal cells (BMSCs). The results showed that silk modification improved the uniformity and continuity of pore network of MBG scaffolds, and maintained high porosity (94%) and large-pore size (200–400 mm). There was a significant improvement in mechanical strength, mechanical stability, and control of burst release of DEX in silkmodified MBG scaffolds. Silk modification also appeared to provide a better environment for BMSC attachment, spreading, proliferation, and osteogenic differentiation on MBG scaffolds.

Compressive behaviour of nanocrystallilne Mg-5%Al alloys

Magnesium alloys are attracting increasing research interests due to their low density, high specific strength and good mechineability and availability as compared to other structural materials. However, the deformation and failure mechanisms of nanocrystalline Mg alloys have not been well understood. In this work, the deformation behavior of nanocrystalline Mg-5% Al alloys was investigated using compression test, with a focus on the effects of grain size. The average grain size of the Mg-Al alloy was changed from 13 µm to 50 nm via mechanical milling. The results showed that grain size had a significant influence on the yield stress and ductility of the Mg alloys, and the materials exhibited increased strain rate sensitivity with decrease of grain size. The deformation mechanisms were also strongly dependent with the grain sizes.