Effect of the curing conditions of concrete on the behaviour under freeze-thaw cycles*

The aim of this work is to relate the curing conditions of concrete and the addition of an air-entraining admixture with the damage caused by freeze–thaw cycles. In countries with a continental climate, the curing of concrete in summer is performed under climatic conditions of high temperature and low humidity, and during the winter the concrete suffers conditions of freeze–thaw, often accompanied by the use of de-icing salts. This paper shows the experimental results of the behaviour of concrete specimens cured under climatic summer conditions (high temperature and low humidity) and then subjected to freeze–thaw cycles. Curing of the specimens includes conditions of good and bad practice in relation to wetting and protection of the concrete. It also examines the effectiveness of using an air-entraining admixture in both cases. The experimental programme includes an evaluation of the mechanical properties of the concrete, the study of the cement hydration and the measurement of the volume and pore sizes of the concrete. These tests were performed before and after the application of the freeze–thaw cycles. The results obtained showed that the specimens without air-entraining admixture show a deterioration of mechanical properties after the freeze–thaw test. However, the inclusion of air bubbles benefits the behaviour of concrete against freeze–thaw cycles so even better mechanical properties after the test were observed. This anomalous behaviour is because the cement hydration process continues over the freeze–thaw tests, closing the pore structure. This aspect has been confirmed with the DTA and TG tests performed

NDT for concrete under accelerated freeze/thaw tests and surface scaling

Freezing of water or salt solution in concrete pores is a main cause for severe damage and significant reduction of the service life. Most of the freeze-thaw (F-T) accelerated tests measure the scaling of concrete by weighting. This paper presents complementary procedures based on the use of strain gages and ultrasonic pulse velocity (UPV) for measuring the deterioration of concrete due to freezing and thawing. These non-destructive testing (NDT) procedures are applied to two types of concretes, one susceptible to F-T damage and the other does not. The results show a good correlation between scaling and the measurements obtained with NDT. Showing NDT the advantage to detect before the damage and to perform continuous measurement

Study of the damage evolution of the concrete under freeze-thaw cycles using traditional and non-traditional techniques

Some experiments have been performed to investigate the cyclic freeze-thaw deterioration of concrete, using traditional and non-traditional techniques. Two concrete mixes, with different pore structure, were tested in order to compare the behavior of a freeze-thaw resistant concrete from one that is not. One of the concretes was air entrained, high content of cement and low w/c ratio, and the other one was a lower cement content and higher w/c ratio, without air-entraining agent. Concrete specimens were studied under cyclic freeze-thaw conditions according to UNE-CENT/TS 12390-9 test, using 3% NaCl solution as freezing medium (CDF test: Capillary Suction, De-icing agent and Freeze-thaw Test). The temperature and relative humidity were measured during the cycles inside the specimens using embedded sensors placed at different heights from the surface in contact with the de-icing agent solution. Strain gauges were used to measure the strain variations at the surface of the specimens. Also, measurements of ultrasonic pulse velocity through the concrete specimens were taken before, during, and after the freeze-thaw cycles. According to the CDF test, the failure of the non-air-entraining agent concrete was observed before 28 freeze-thaw cycles; contrariwise, the scaling of the air-entraining agent concrete was only 0.10 kg/m 2 after 28 cycles, versus 3.23 kg/m 2 in the deteriorated concrete, after 28 cycles. Similar behavior was observed on the strain measurements. The residual strain in the deteriorated concrete after 28 cycles was 1150 m versus 65 m, in the air-entraining agent concrete. By means of monitoring the changes of ultrasonic pulse velocity during the freeze-thaw cycles, the deterioration of the tested specimens were assessed