Structural and magnetic properties of Ni1-xZnxFe2O4 (x=0, 0.5 and 1) nanopowders prepared by sol-gel method

A series of nanostructured Ni-Zn ferrites Ni1-xZnxFe2O4 (x=0, 0.5 and 1) with a grain size from 24 to 65 nm have been prepared with a sol-gel method. The effect of composition and sintering temperature on morphology, magnetic properties, Curie temperature, specific heating rate at 295 kHz and hysteresis loss have been studied. The highest coercivity of 50 and 40 Oe, were obtained for NiFe2O4 and Ni0.5Zn0.5Fe2O4 samples with the grain size of 35 and 29 nm, respectively. The coercivity of Ni and Ni-Zn mixed ferrites decreased with temperature. The Bloch exponent was 1.5 for all samples. As the grain size increased, the Curie temperature of NiFe2O4 increased from 849 to 859 K. The highest saturation magnetization of 70 emu/g at 298 K and the highest specific heating rate of 1.6 K/s under radiofrequency heating at 295 kHz were observed over NiFe2O4 calcined at 1073 K. Both the magnitude of the hysteresis loss and the temperature dependence of the loss are influenced by the sintering temperature and composition.

Spin-wave modes in Ni nanorod arrays studied by Brillouin light scattering

Dynamic magnetic properties of arrays of Ni nanorods with a low aspect ratio have been investigated. It has been shown that the spectra of spin-wave resonances localized on nanorods with a low aspect ratio typically feature the presence of zones with high density of states resulting in a characteristic two-peak pattern of Stokes and anti-Stokes lines of magneto-optical (MO) Brillouin light scattering with pronounced Stokes–anti-Stokes (S-AS) asymmetry. A simple theoretical model based on the analysis of the elliptic character of the polarization of the optical wave interacting with a dipole magnetostatic wave has been proposed. It has been shown that the S-AS asymmetry is due entirely to the asymmetry of the MO interaction efficiency with respect to time reversal of the magnetic precession in a magnon.

Potassium-doped Ni-MgO-ZrO catalysts for dry reforming of methane to synthesis gas

Ni/K-MgO-ZrO catalysts for dry reforming of methane, with a range of Mg/Zr ratios and each containing about 10 wt% Ni, were prepared via Ni nitrate impregnation on MgO-ZrO supports synthesized by co-precipitation using KCO. It was found that a proportion of the potassium of the precipitant remained in the samples and improved the stability of the catalysts in the reaction. It was also shown that reduction of the catalysts at 1,023 K without calcination in air is necessary for stable and high activity; calcination in air at 1,073 K gives a deterioration of the catalytic properties, leading to rapid deactivation during the reaction. The order of the CH conversions of the reduced catalysts after 14 h on stream was as follows: Ni/K-MgZr ~ Ni/K-Mg ≥ Ni/K-MgZr Ni/K-Zr. A catalyst with 0.95 wt% K on MgO-ZrO with a Mg:Zr mole ratio of 5:2 showed the best resistance to deactivation. Experiments in a microbalance system showed that there was only negligible coke deposition on the surface of this sample. This behaviour was attributed to the presence of Ni nanoparticles with a diameter of less than 10 nm located on a MgO/NiO solid solution shell doped by K ions; this in turn covers a core of tetragonal ZrO and/or a MgO/ZrO solid solution. This conclusion was supported by EDS/TEM, XPS, XRD and H chemisorption measurements. © 2013 Springer Science+Business Media New York.

Water efficiency as a means of reducing carbon emissions in Northern Ireland (NI) Water

The water and sewerage sectors' combined emissions account for just over 1% of total UK emissions, while household water heating accounts for a further 5%. Energy use, particularly electricity, is the largest source of emissions in the sector. Water efficiency measures should therefore result in reduced emissions from a lower demand for water and wastewater treatment and pumping, as well as from decreased domestic water heating. Northern Ireland Water (NI Water) is actively pursuing measures to reduce its carbon footprint. This paper investigated the carbon impacts of implementing a household water efficiency programme in Northern Ireland. Assuming water savings of 59.6 L/prop/day and 15% uptake among households, carbon savings of 0.6% of NI Water's current net operational emissions are achievable from reduced treatment and pumping. Adding the carbon savings from reduced household water heating gives savings equivalent to 6.2% of current net operational emissions. Cost savings to NI Water are estimated as 300,000 per year. The cost of the water efficiency devices is approximately 1.6 million, but may be higher depending on the number of devices distributed relative to the number installed. This paper has shown clear carbon benefits to water efficiency, but further research is needed to examine social and cost impacts. © IWA Publishing 2013.

Ferromagnetism in DyRh and DyRhX (X = Fe, Ni, Co, Gd) thin films

In an effort to achieve large high-field magnetization and increased Curie temperature, polycrystalline DyRh, (DyRh)95X5 and (DyRh)85X15 (X = Fe, Co, Ni, Gd) thin films have been prepared via ultra-high vacuum DC co-sputtering on SiO2 and Si wafers, using Ta as seed and cap material. A body-centred cubic CsCl-like crystal formation (B2 phase) was achieved for DyRh around the equiatomic equilibrium, known from single crystals. The maximum in-plane spontaneous magnetization at T = 4K in fields of μ0H = 5T of was found to be μ0MS,4K = (1.50 ± 0.09)T with a ferromagnetic transition at TC = (5 ± 1)K and a coercivity of μ0HC,4K[D] = (0.010 ± 0.001)T (at T = 4K) for layers deposited on substrates heated to 350°C. Samples prepared at room temperature exhibited poorer texture, smaller grains and less B2-phase content; this did impact on the Curie temperature which was higher compared to those layers with best crystallisation; however the maximal magnetization stayed unaffected. Ferromagnetic coupling was observed in ternary alloys of DyRhGd and DyRhNi with an increased Curie temperature, larger initial permeability, and
high-field magnetization which was best for (DyRh)85Gd15 with μ0MS,4K[Gd15] = (2.10 ± 0.13)T. DyRhFe and DyRhCo showed antiparallel coupling of the spontaneous magnetic moments.