Facile preparation of ZnTiO3 ceramic powders in sodium/potassium chloride melts

A facile molten salt synthesis route was developed to prepare ZnTiO3 ceramic powders with simple oxides ZnO and TiO2 using sodium and potassium chloride eutectic salts as flux. The role of calcination temperature and time and the amount of salt addition to ZnTiO3 formation was investigated by thermogravimetry-differential thermal analysis, X-ray diffraction and Fourier transformation-infrared spectroscopy measurements. Pure hexagonal phase of ZnTiO3 could be obtained from the mixture of the simple oxides and the chlorides (50 mol% KCl, 20 times to oxides in molar ratio) heating at 800 degrees C for 6 h. The scanning electron microscopy images revealed the products were hexagonal sheets of about 1-3 mu m size. Increasing the amount of salt aids in reducing the crystal sizes of final ceramic powders because of diluting the solution.

New double-ceramic-layer thermal barrier coatings based on zirconia-rare earth composite oxides

A series of La2O3-ZrO2-CeO2 composite oxides were synthesized by solid-state reaction. The final product keeps fluorite structure when the molar ratio Ce/Zr >= 0.7/0.3, and below this ratio only mixtures of La2Zr2O7 (pyrochlore) and La2O3-CeO2 (fluorite) exist. Averagely speaking, the increase of CeO2 content gives rise to the increase of thermal expansion coefficient and the reduction of thermal conductivity, but La-2(Zr0.7Ce0.3)(2)O-7 has the lowest sintering ability and the lowest thermal conductivity which could be explained by the theory of phonon scattering. Based on the large thermal expansion coefficient of La2Ce3.25O9.5, the low thermal conductivities and low sintering abilities of La2Zr2O7 and La-2(Zr0.7Ce0.3)(2)O-7, double-ceramic-layer thermal barrier coatings were prepared. The thermal cycling tests indicate that such a design can largely improve the thermal cycling lives of the coatings. Since no single material that has been studied so far satisfies all the requirements for high temperature thermal barrier coatings, double-ceramic-layer coating may be an important development direction of thermal barrier coatings.

Fe(2-EHA)(3)/Al(i-Bu)(3)/hydrogen phosphite catalyst for preparing syndiotactic 1,2-polybutadiene

Polymerizing 1,3-butadiene into syndiotactic 1,2-polybutadiene with art iron(III) catalyst system has been investigated. Activity of the catalyst was affected by the type of cocatalyst alkylaluminum and the phosphorus compound as an electron donor, molar ratio of catalyst components, and their aging sequence and aging time of the catalyst. The microstructure and configuration of the polymer was decided by the catalyst components, the higher [Al]/[Fe] molar ratio tending to yield syndiotactic 1,2-polybutadiene, while the higher [P]/[Fe] molar ratio favors the formation of amorphous 1,2-polybutadiene.

Study on QSPR of alcohols with a novel edge connectivity index F-m

A novel edge degree f(i) for heteroatom and multiple bonds in molecular graph is derived on the basis of the edge degree delta(e(r)). A novel edge connectivity index F-m is introduced. The multiple linear regression by using the edge connectivity index F-m and alcohol-type parameter delta, alcohol-distance parameter L can provide high-quality QSPR models for the normal boiling points (BPs), molar volumes (MVs), molar refraction (MRs), water solubility(log(1/S)) and octanol/water partition (logP) of alcohols with up to 17 non-hydrogen atoms. The results imply that these physical properties may be expressed as a liner combination of the edge connectivity index and alcohol-type parameter, 6, alcohol-distance parameter, L. For the models of the five properties, the correlation coefficient r and the standard errors are 0.9969,3.022; 0.9993, 1.504; 0.9992, 0.446; 0.9924,0.129 and 0.9973,0.123 for BPs, MVs, MRs, log(1/S) and logP, respectively. The cross-validation by using the leave-one-out method demonstrates the models to be highly reliable from the point of view of statistics.

Effects of acetic acid on product selectivity in gas phase oxidative dehydrogenation of cyclohexane

The effect of adding acetic acid on the product distribution in gas phase oxidative dehydrogenation of cyclohexane over alpha(1)-VOPO4 catalyst was investigated. The role of acetic acid in the reaction process was put forward. The proposed mechanism is that acetic acid take precedence of cyclohexane adsorbing on the active sites of alpha(1)-VOPO4 catalyst to form isolated active site. Thus, cyclohexene species can desorb quickly from the active sites, avoiding its deep oxidation dehydrogenation. Almost 100% selectivity to cyclohexene could be obtained when the molar ratio of acetic acid to cyclohexane was 12.9:1 at 450 degrees C, the conversion of cyclohexane was 6.9%.

Detection and characterization of non-covalent complex between lappaconitine and beta-cyclodextrin by electrospray ionization tandem mass spectrometry

The non-covalent complexes between lappaconitine (LA) and beta-cyclodextrin (beta-CD) have been detected and characterized by electrospray ionization combined with ion trap tandem mass spectrometry (ESI-MSn). The experimental results showed that only 1:1 non-covalent complex can be formed in different starting molar ratios of LA to beta-CD. Furthermore, the diagnostic fragmentation of the beta-CD-LA complex, with a significant contribution of covalent fragmentation of LA leaving the N-acetyl anthranoyl (AN) moiety inserted to beta-CD, provided the convincing evidence for the formation of non-covalent complex between LA and beta-CD and the cite of LA molecule included to cavity of beta-CD assigned to AN residue.

One-step synthesis and size control of dendrimer-protected gold nanoparticles: A heat-treatment-based strategy

Dendrimer-protected gold nanoparticles have been facilely obtained by heating an aqueous solution containing third generation poly(propyleneimine) dendrimers and HAuCl4 without the additional step of introducing other reducing agents. Transmission electron microscopy (TEM) and UV vis data indicate the size the nucleation and growth kinetics of gold nanoparticles thus formed which can be tuned by changing the initial molar ratio of dendrimer to gold.

Synthesis of the complex fluoride LiBaF3 and optical spectroscopy properties of LiBaF3 : M(M = Eu,Ce) through a solvothermal process

The complex fluoride LiBaF3 and LiBaF3:M(M = Eu, Ce) is solvothermally synthesized at 180 degreesC and characterized by means of X-ray powder diffraction, scanning electron microscopy, thermogravimetric analysis and infrared spectroscopy. In the solvothermal process, the solvents, molar ratios of initial mixtures and reaction temperature play important roles in the formation of products. The excitation and emission spectra of the LiBaF3:M(M= Eu,Ce) have been measured by fluorescence spectrophotometer. In the LiBaF3: Eu emission spectra, there is one sharp line emission located at 360 nm arising from f --> f transition of Eu2+ in the host lattice, and typical doublet 5d-4f emission of Ce3+ in LiBaF3 powder is shown.

Hydrothermal and solvothermal synthesis of the complex fluoride alpha '-SrAlF5

The complex fluoride alpha'-SrAlF5 has been synthesized through hydrothermal and solvothermal methods under mild conditions. The effects of the molar ratio of starting materials, temperature, reaction time and solvents on the synthesis of alpha'-SrAlF5 were discussed. The final products were characterized by XRD and SEM. The rod-like shape of alpha'-SrAlF5 is shown in SEM images.

Functionalization of an ethylene-propylene copolymer with allyl (3-isocyanate-4-tolyl) carbamate

An ethylene-propylene copolymer (EPM) was functionalized with an iso cyanate-bearing unsaturated monomer, allyl(3-isocyanate-4-tolyl) carbamate (TAI), with dicumyl peroxide as an initiator in a xylene solution. Fourier transform infrared (FTIR) was used to confirm the formation of EPM-g-TAI. The peak at 2273 cm(-1), characteristic of -NCO groups in EPM-g-TAI, revealed evidence of grafting. The grafting degree was determined with both chemical titration and FTIR. The grafting degree could be adjusted, and the maximum was over 6 wt % without any gelation. The molar mass distribution of EPM-g-TAI was narrower than that of EPM. The rheological behavior of both EPM-g-TAI and EPM was investigated with a rotational rheometer. The apparent viscosity of EPM-g-TAI was higher than that of EPM and increased with an increasing grafting degree of TAI. Surface analysis by contact-angle measurements showed that contact angles of EPM-g-TAI samples to a given polar liquid decreased with an increasing grafting degree of TAI. We also obtained the dispersion component of the surface free energy (gamma(S)(d)), the polar component of the surface free energy (gamma(S)(d)), and the total surface free energy (gamma(S) = gamma(S)(d) + gamma(S)(p)) of the grafted EPM. These parameters increased with the enhancement of the grafting degree, which gave us a quantitative estimation of the polar contribution of the grafted TAI to the total surface free energy of EPM-g-TAI.

Copolymerization of carbon dioxide and propylene oxide with neodymium trichloroacetate-based coordination catalyst

The copolymerizations of carbon dioxide (CO2) and propylene oxide (PO) were performed using new ternary rare-earth catalyst, It was found that the rare-earth coordination catalyst consisting of Nd(CCl3COO)(3), ZnEt2 and glycerine was very effective for the copolymerization of PO with CO2. The effects of the relative molar ratio and addition order of the catalyst components, copolymerization reaction time, and operating pressure as well as temperature on the copolymerization were systematically investigated. At an appropriate combination of all variables, the yield could be as high as 6875 g/mol Nd per hour at 90 degreesC in a 8 h reaction period.

Liquid crystal alignment generated by linearly polarized UV light on photoactive low molecular mass compounds

Alignment films prepared from low molar mass photo-crosslinkable materials containing the cinnamate group can be used for aligning LCs after irradiating the films with linearly polarized UV light. The high contrast observed in the polarizing optical microscope between dark and bright images indicates that the alignment is quite uniform. As the photoreaction progresses. the average roughness of the films is increased. All the aggregate structures, 'lamellar crystals'. produced by the photo-crosslinking reaction are of a square shape.

Polymerization of acrylonitrile with (diisopropylamido) bis (indenyl) lanthanides

The polymerization of acrylonitrile was studied using ( diisopropylamido) his ( indenyl) lanthanides, Ind(2)LnN(i-Pr)(2)(Ln = Y, Yb) as a single-component catalyst. The effects of the amount of catalyst, monomer concentration and polymerization temperature on catalytic activity and molecular weight of polyacrylonitrile (PAN) were studied. The results show that the catalytic activity is raised obviously with rising polymerization temperature. The monomer conversion reaches 64% under polymerization temperature, monomer concentration and catalyst concentration are 50 degreesC, 5.1 mol . L (-1) and 0. 3 % (molar ratio) sequentially. The conversion and molecular weight of the polymer increase appreciably with adding additive, PhONa. When the molar ratio of PhONa to the catalyst is three I the conversion and the molecular weight is 76% and 1.32 x 10(4), respectively. The initiation mechanism for the polymerization of acrylonitrile was proposed.

Charge transfer across the water/nitrobenzene interface by three-electrode system

A droplet of aqueous solution containing a certain molar ratio of redox couple is first attached onto a platinum electrode surface, then the resulting drop electrode is immersed into the organic solution containing very hydrophobic electrolyte. Combined with reference and counter electrodes, a classical three-electrode system has been constructed, Ion transfer (IT) and electron transfer (ET) are investigated systematically using three-electrode voltammetry. Potassium ion transfer and electron transfer between potassium ferricyanide in the aqueous phase and ferrocene in nitrobenzene are observed with potassium ferricyanide/potassium ferrocyanide as the redox couple. Meanwhile, the transfer reactions of lithium, sodium, potassium, proton and ammonium ions are obtained with ferric sulfate/ferrous sulfate as the redox couple. The formal transfer potentials and the standard Gibbs transfer energy of these ions are evaluated and consistent with the results obtained by a four-electrode system and other methods.

Study of facilitated potassium ion transfer across a water vertical bar 1,2-dichloroethane interface using different phase volume ratio systems

A study of potassium ion transfer across a water \ 1,2-dichloroethane (W \ DCE) interface facilitated by dibenzo-18-crown-6 (DB18C6) with various phase volume ratio systems is presented. The key point was that a droplet of aqueous solution containing a redox couple, Fe(CN)(6)(3-)/Fe(CN)(6)(4-), with equal molar ratio, was first attached to a platinum electrode surface, and the resulting droplet electrode was then immersed into the organic solution containing a hydrophobic electrolyte to construct a platinum electrode/aqueous phase/organic phase system. The interfacial potential of the W \ DCE within the series could be externally controlled because the specific compositions in the aqueous droplet make the Pt electrode function like a reference electrode as long as the concentration ratio of Fe(CN)(6)(3-)/Fe(CN)(6)(4-) remains constant. In this way, a conventional three-electrode potentiostat can be used to study the ion transfer process at a liquid \ liquid (L \ L) interface facilitated by an ionophore with variable phase volume ratio (r = V-o/V-w). The effect of r on ion transfer and facilitated ion transfer was studied in detail experimentally. We also demonstrated that as low as 5 x 10(-8) M DB18C6 could be determined using this method due to the effect of the high phase volume ratio.