Enhanced bone apposition around biofunctionalized sandblasted and acid-etched titanium implant surfaces. A histomorphometric study in miniature pigs

Microrough titanium (Ti) surfaces of dental implants have demonstrated more rapid and greater bone apposition when compared with machined Ti surfaces. However, further enhancement of osteoblastic activity and bone apposition by bio-functionalizing the implant surface with a monomolecular adsorbed layer of a co-polymer - i.e., poly(L-lysine)-graft-poly(ethylene glycol) (PLL-g-PEG) and its derivatives (PLL-g-PEG/PEG-peptide) - has never been investigated. The aim of the present study was to examine early bone apposition to a modified sandblasted and acid-etched (SLA) surface coated with an Arg-Gly-Asp (RGD)-peptide-modified polymer (PLL-g-PEG/PEG-RGD) in the maxillae of miniature pigs, and to compare it with the standard SLA surface. Test and control implants had the same microrough topography (SLA), but differed in their surface chemistry (polymer coatings). The following surfaces were examined histomorphometrically: (i) control - SLA without coating; (ii) (PLL-g-PEG); (iii) (PLL-g-PEG/PEG-RDG) (RDG, Arg-Asp-Gly); and (iv) (PLL-g-PEG/PEG-RGD). At 2 weeks, RGD-coated implants demonstrated significantly higher percentages of bone-to-implant contact as compared with controls (61.68% vs. 43.62%; P < 0.001). It can be concluded that the (PLL-g-PEG/PEG-RGD) coatings may promote enhanced bone apposition during the early stages of bone regeneration.

Biomechanical evaluation of the interfacial strength of a chemically modified sandblasted and acid-etched titanium surface

The functional capacity of osseointegrated dental implants to bear load is largely dependent on the quality of the interface between the bone and implant. Sandblasted and acid-etched (SLA) surfaces have been previously shown to enhance bone apposition. In this study, the SLA has been compared with a chemically modified SLA (modSLA) surface. The increased wettability of the modSLA surface in a protein solution was verified by dynamic contact angle analysis. Using a well-established animal model with a split-mouth experimental design, implant removal torque testing was performed to determine the biomechanical properties of the bone-implant interface. All implants had an identical cylindrical shape with a standard thread configuration. Removal torque testing was performed after 2, 4, and 8 weeks of bone healing (n = 9 animals per healing period, three implants per surface type per animal) to evaluate the interfacial shear strength of each surface type. Results showed that the modSLA surface was more effective in enhancing the interfacial shear strength of implants in comparison with the conventional SLA surface during early stages of bone healing. Removal torque values of the modSLA-surfaced implants were 8-21% higher than those of the SLA implants (p = 0.003). The mean removal torque values for the modSLA implants were 1.485 N m at 2 weeks, 1.709 N m at 4 weeks, and 1.345 N m at 8 weeks; and correspondingly, 1.231 N m, 1.585 N m, and 1.143 N m for the SLA implants. The bone-implant interfacial stiffness calculated from the torque-rotation curve was on average 9-14% higher for the modSLA implants when compared with the SLA implants (p = 0.038). It can be concluded that the modSLA surface achieves a better bone anchorage during early stages of bone healing than the SLA surface; chemical modification of the standard SLA surface likely enhances bone apposition and this has a beneficial effect on the interfacial shear strength.

Comparison of bacterial plaque samples from titanium implant and tooth surfaces by different methods

Studies have shown similarities in the microflora between titanium implants or tooth sites when samples are taken by gingival crevicular fluid (GCF) sampling methods. The purpose of the present study was to study the microflora from curette and GCF samples using the checkerboard DNA-DNA hybridization method to assess the microflora of patients who had at least one oral osseo-integrated implant and who were otherwise dentate. Plaque samples were taken from tooth/implant surfaces and from sulcular gingival surfaces with curettes, and from gingival fluid using filter papers. A total of 28 subjects (11 females) were enrolled in the study. The mean age of the subjects was 64.1 years (SD+/-4.7). On average, the implants studied had been in function for 3.7 years (SD+/-2.9). The proportion of Streptococcus oralis (P<0.02) and Fusobacterium periodonticum (P<0.02) was significantly higher at tooth sites (curette samples). The GCF samples yielded higher proportions for 28/40 species studies (P-values varying between 0.05 and 0.001). The proportions of Tannerella forsythia (T. forsythensis), and Treponema denticola were both higher in GCF samples (P<0.02 and P<0.05, respectively) than in curette samples (implant sites). The microbial composition in gingival fluid from samples taken at implant sites differed partly from that of curette samples taken from implant surfaces or from sulcular soft tissues, providing higher counts for most bacteria studied at implant surfaces, but with the exception of Porphyromonas gingivalis. A combination of GCF and curette sampling methods might be the most representative sample method.

Immediate bacterial colonization of titanium implants

Background: The information on bacterial colonization immediately after dental implant insertion is limited. Aims: (1) to assess the early colonization on titanium implants immediately post placement through the first12 post-surgical weeks , (2) to compare the microflora at interproximal subgingival implant and adjacent tooth sites. Material and Methods: Subgingival plaque samples from implant and neighbouring teeth were studied by checkerboard DNA-DNA hybridization before, 30 min. after implant placement , 1 week, 2 weeks, 4 weeks, 8 weeks, and 12 weerks after surgery. Results: Comparing bacterial loads at implant sites between 30 min. after placement with one week data showed that only the levels of V.parvula (p<0.05) differed with higher loads at week 1. Week 12 data demonstrated significantly higher bacterial loads for 15/40 species at tooth sites compared to pre-surgery (p < values varying between 0.05 and 0.01). Between immediately post-surgery and week 12 at implant sites 29/40 species were more commonly found at week 12. Included among these bacteria at implant sites were P.gingivalis (p< 0.05), T.forsythia, (p < 0.01), and T denticola (p<0.001). Immediately post-surgery 5.9% of implants, and 26.2% of teeth and at week 12, 15.0 % of implants, and 39.1% of teeth harbored S.aureus. Comparing tooth and implant sites, significantly higher bacterial loads were found at tooth sites for 27/40 species at the 30 minutes after placement interval. This difference increased to 35/40 species at week 12. Conclusions: The colonization of bacteria occurs within 30 minutes. Colonization patterns differed between implants and tooth surfaces.

Infection at titanium implants with or without clinical inflammation

Objectives: The aims of the present study were (1)to assess the microbiota at implants in function diagnosed as having either peri-implantitis, or mucositis, or being clinically without symptoms of inflammation, (2) to identify explanatory factors to implant status. Material and Methods: Clinical and microbiological data were collected from 138 subjects (mean age: 62.3 ± 14.9) with 524 implants in function for an average of 10.8 years (S.D. +1.5). The checkerboard DNA-DNA hybridization method was used to identify 40 bacterial species. Results: Subjects had poor oral hygiene with a mean % plaque score 53.2 ± 24.4. In 36% of cases periodontitis was reported as the cause for implant therapy. Mucositis was diagnosed in 61.6% and per-implantitis in 15.9% of all cases. Edentulous subjects had at implants with peri-implantitis significantly higher bacterial loads for Streptococcus sanguis (p<0.01), Fusobacterium nucleatum sp. nucleatum (p<0.02), and Leptothrichia buccalis (p<0.05) than did dentate implant subjects. Dentate subjects had higher bacterial loads of Porphyromonas gingivalis (p<0.02). The levels of Fusobacterium nucleatum sp.vincentii and Capnocytophaga ochracea were explanatory to mucositis. Only a history of periodontitis as cause of tooth loss and smoking were explanatory to peri-implantitis. The microbiota was not affect by supportive care patterns. Conclusions: Presence or absence of teeth partly explains the implant microbiota. A past history of periodontitis and smoking are associated with peri-implantitis. The microbiota at implants with mucositis, or peri-implantitis is similar to that of teeth. Supportive periodontal and implant therapy fails to have an impact on implant microbiota and does not prevent mucositis and peri-implantitis.

Bacterial colonization immediately after installation on oral titanium implants

BACKGROUND: Information on bacterial colonization immediately after dental implant insertion is limited. AIMS: (1) To assess the early colonization on titanium implants immediately after placement and throughout the first 12 post-surgical weeks, (2) to compare the microbiota at interproximal subgingival implant and adjacent tooth sites. MATERIAL AND METHODS: Subgingival plaque samples from implant and neighbouring teeth were studied by checkerboard DNA-DNA hybridization before surgery, 30 min after implant placement, and 1, 2, 4, 8, and 12 weeks after surgery. RESULTS: Comparing bacterial loads at implant sites between 30 min after placement with 1-week data showed that only the levels of Veillonella parvula (P<0.05) differed with higher loads at week 1 post-surgically. Week 12 data demonstrated significantly higher bacterial loads for 15/40 species at tooth sites compared with pre-surgery (P-values varying between 0.05 and 0.01). Between the period immediately after surgery and 12 weeks at implant sites, 29/40 species was more commonly found at 12 weeks. Included among these bacteria at implant sites were Porphyromonas gingivalis (P<0.05), Tannerella forsythia, (P<0.01), and Treponema denticola (P<0.001). Immediately post-surgery 5.9% of implants, and 26.2% of teeth, and at week 12, 15% of implants, and 39.1% of teeth harbored Staphylococcus aureus. Comparing tooth and implant sites, significantly higher bacterial loads were found at tooth sites for 27/40 species after 30 min following implant placement. This difference increased to 35/40 species at 12 weeks post-surgically. CONCLUSIONS: Bacterial colonization occurred within 30 min after implant placement. Early colonization patterns differed between implant and tooth surfaces.

Infection at titanium implants with or without a clinical diagnosis of inflammation

OBJECTIVES: To assess the microbiota at implants diagnosed with peri-implantitis, implant mucositis, or being clinically healthy. MATERIAL AND METHODS: Clinical and microbiological data were collected from 213 subjects (mean age: 65.7+/-14) with 976 implants in function (mean: 10.8 years, SD+/-1.5). Forty species were identified by the checkerboard DNA-DNA hybridization method. RESULTS: Implant mean % plaque score was 41.8+/-32.4%. Periodontitis defined by bone loss was found in 44.9% of subjects. Implant mucositis was diagnosed in 59% and peri-implantitis in 14.9% of all cases. Neisseria mucosa, Fusobacterium nucleatum sp. nucleatum, F. nucleatum sp. polymorphum, and Capnocytophaga sputigena dominated the implant sub-mucosal microbiota and the sub-gingival microbiota at tooth sites. Implant probing pocket depth at the implant site with the deepest probing depth was correlated with levels of Eikenella corrodens (r=0.16, P<0.05), the levels of F. nucleatum sp. vincentii (r=0.15, P<0.05), Porphyromonas gingivalis (r=0.14, P<0.05), and Micromonas micros (r=0.17, P=0.01). E. corrodens was found in higher levels at implants with mucositis compared with implant health (P<0.05). Subjects who lost teeth due to periodontitis had higher yields of F. nucleatum sp. vincentii (P<0.02) and N. mucosa (P<0.05). Independent of implant status subjects with teeth had higher levels of P. gingivalis (P<0.05), and Leptotrichia buccalis (P<0.05). CONCLUSIONS: At implant sites studied, few bacteria differed by whether subjects were dentate or not or by implant status.

Re-evaluation of pulmonary titanium dioxide nanoparticle distribution using the "relative deposition index": Evidence for clearance through microvasculature

ABSTRACT: BACKGROUND: Translocation of nanoparticles (NP) from the pulmonary airways into other pulmonary compartments or the systemic circulation is controversially discussed in the literature. In a previous study it was shown that titanium dioxide (TiO2) NP were "distributed in four lung compartments (air-filled spaces, epithelium/endothelium, connective tissue, capillary lumen) in correlation with compartment size". It was concluded that particles can move freely between these tissue compartments. To analyze whether the distribution of TiO2 NP in the lungs is really random or shows a preferential targeting we applied a newly developed method for comparing NP distributions. METHODS: Rat lungs exposed to an aerosol containing TiO2 NP were prepared for light and electron microscopy at 1 h and at 24 h after exposure. Numbers of TiO2 NP associated with each compartment were counted using energy filtering transmission electron microscopy. Compartment size was estimated by unbiased stereology from systematically sampled light micrographs. Numbers of particles were related to compartment size using a relative deposition index and chi-squared analysis. RESULTS: Nanoparticle distribution within the four compartments was not random at 1 h or at 24 h after exposure. At 1 h the connective tissue was the preferential target of the particles. At 24 h the NP were preferentially located in the capillary lumen. CONCLUSION: We conclude that TiO2 NP do not move freely between pulmonary tissue compartments, although they can pass from one compartment to another with relative ease. The residence time of NP in each tissue compartment of the respiratory system depends on the compartment and the time after exposure. It is suggested that a small fraction of TiO2 NP are rapidly transported from the airway lumen to the connective tissue and subsequently released into the systemic circulation.

The role of macrophages in the clearance of inhaled ultrafine titanium dioxide particles

The role of macrophages in the clearance of particles with diameters less than 100 nm (ultrafine or nanoparticles) is not well established, although these particles deposit highly efficiently in peripheral lungs, where particle phagocytosis by macrophages is the primary clearance mechanism. To investigate the uptake of nanoparticles by lung phagocytes, we analyzed the distribution of titanium dioxide particles of 20 nm count median diameter in macrophages obtained by bronchoalveolar lavage at 1 hour and 24 hours after a 1-hour aerosol inhalation. Differential cell counts revealing greater than 96% macrophages and less than 1% neutrophils and lymphocytes excluded inflammatory cell responses. Employing energy-filtering transmission electron microscopy (EFTEM) for elemental microanalysis, we examined 1,594 macrophage profiles in the 1-hour group (n = 6) and 1,609 in the 24-hour group (n = 6). We found 4 particles in 3 macrophage profiles at 1 hour and 47 particles in 27 macrophage profiles at 24 hours. Model-based data analysis revealed an uptake of 0.06 to 0.12% ultrafine titanium-dioxide particles by lung-surface macrophages within 24 hours. Mean (SD) particle diameters were 31 (8) nm at 1 hour and 34 (10) nm at 24 hours. Particles were localized adjacent (within 13-83 nm) to the membrane in vesicles with mean (SD) diameters of 592 (375) nm at 1 hour and 414 (309) nm at 24 hours, containing other material like surfactant. Additional screening of macrophage profiles by conventional TEM revealed no evidence for agglomerated nanoparticles. These results give evidence for a sporadic and rather unspecific uptake of TiO(2)-nanoparticles by lung-surface macrophages within 24 hours after their deposition, and hence for an insufficient role of the key clearance mechanism in peripheral lungs.

Use of straight and curved 3-dimensional titanium miniplates for fracture fixation at the mandibular angle

PURPOSE: The aim of this follow-up study was to evaluate the clinical usefulness of a new type of 3-dimensional (3D) miniplate for open reduction and monocortical fixation of mandibular angle fractures. PATIENTS AND METHODS: In 20 consecutive patients, noncomminuted mandibular angle fractures were treated with open reduction and fixation using a 2 mm 3D miniplate system in a transoral approach. All patients were systematically monitored until 6 months postoperatively. Among the outcome parameters recorded were infection, hardware failure, wound dehiscence, and sensory disturbance of the inferior alveolar nerve. RESULTS: The mean operation time from incision to wound closure was 65 minutes. Two patients had a mucosal wound dehiscence with no consequences. None developed an infection requiring a plate removal. All but 2 patients had normal sensory function 3 months after surgery. Plate fracture occurred in one patient in whom a preceding surgical removal of the third molar had been the reason for the mandibular fracture. In the absence of clinical symptoms, the patient declined plate removal. On final follow-up, fracture healing was considered clinically complete in all patients. CONCLUSIONS: The 3D plating system described here is suitable for fixation of simple mandibular angle fractures and is an easy-to-use alternative to conventional miniplates. The system may be contraindicated in patients in whom insufficient interfragmentary bone contact causes minor stability of the fracture.

Potential of chemically modified hydrophilic surface characteristics to support tissue integration of titanium dental implants

In the past, several modifications of specific surface properties such as topography, structure, chemistry, surface charge, and wettability have been investigated to predictably improve the osseointegration of titanium implants. The aim of the present review was to evaluate, based on the currently available evidence, the impact of hydrophilic surface modifications of titanium for dental implants. A surface treatment was performed to produce hydroxylated/hydrated titanium surfaces with identical microstructure to either acid-etched, or sand-blasted, large grit and acid-etched substrates, but with hydrophilic character. Preliminary in vitro studies have indicated that the specific properties noted for hydrophilic titanium surfaces have a significant influence on cell differentiation and growth factor production. Animal experiments have pointed out that hydrophilic surfaces improve early stages of soft tissue and hard tissue integration of either nonsubmerged or submerged titanium implants. This data was also corroborated by the results from preliminary clinical studies. In conclusion, the present review has pointed to a potential of hydrophilic surface modifications to support tissue integration of titanium dental implants.

Bone apposition around two different sandblasted and acid-etched titanium implant surfaces: a histomorphometric study in canine mandibles

PURPOSE: The aim of this study was to evaluate bone apposition to a modified sandblasted and acid-etched (SLA) implant surface (modSLA) in the canine mandible as compared with the standard SLA surface. MATERIAL AND METHODS: In this experimental study, all mandibular premolars and first molars were extracted bilaterally in five foxhounds. After a healing period of 6 months, each side of the mandible received six randomly assigned dental implants alternating between the standard SLA and modSLA surface. The dogs were sacrificed at 2 weeks (n=2) or 4 weeks (n=3) after implant placement. Histologic and histomorphometric analyses were then performed for each implant. RESULTS: The microscopic healing patterns at weeks 2 and 4 for the two implant types with the standard SLA and modSLA surfaces showed similar qualitative findings. New bone tissue had already established direct contact with implant surfaces after 2 weeks of healing. The mean percentage of newly formed bone in contact with the implant (BIC) was significantly greater for modSLA (28.2+/-7.9%) than for SLA (22.2+/-7.3%) (P<0.05). This difference was no longer evident after 4 weeks. An increase in BIC for both implant surface types occurred from weeks 2 to 4. This increase was statistically significant when compared with SLA at 2 weeks (P<0.05), but not when compared with modSLA at 2 weeks. CONCLUSION: The data from the present study demonstrate significantly more bone apposition for the modSLA surface than the standard SLA surface after 2 weeks of healing. This increased bone apposition may allow a further reduction of the healing period following implant placement for patients undergoing early loading procedures.