Nanostructured barbed wire architecturing of organic conducting material blends by electrospinning

In this study, fibers of barbed wire structure were obtained by electrospinning blend of organic conducting crystalline material and polyethylene oxide. Thermal and structural characterization of the blend fibers has been carried out to study the fiber characteristics. An increase in crystallinity in the electrospun fibers was observed and was attributed to both electrospinning process as well as addition of organic conducting crystalline material. A mechanism for the formation of this barbed wire structure has also been proposed. (C) 2012 American Institute of Physics. [doi:10.1063/1.3673620]

Ultrasonic evaluation of delamination in quasi-isotropic CFRP laminates subjected to low-velocity impact

Ultrasonic C-Scan is used very often to detect flaws and defects in the composite components resulted during fabrication and damages resulting from service conditions. Evaluation and characterization of defects and damages of composites require experience and good understanding of the material as they are distinctly different in composition and behavior as compared to conventional metallic materials. The failure mechanisms in composite materials are quite complex. They involve the interaction of matrix cracking, fiber matrix interface debonding, fiber pullout, fiber fracture and delamination. Generally all of them occur making the stress and failure analysis very complex. Under low-velocity impact loading delamination is observed to be a major failure mode. In composite materials the ultrasonic waves suffer high acoustic attenuation and scattering effect, thus making data interpretation difficult. However these difficulties can be overcome to a greater extent by proper selection of probe, probe parameter settings like pulse width, pulse amplitude, pulse repetition rate, delay, blanking, gain etc., and data processing which includes image processing done on the image obtained by the C-Scan.

Is diatom earth a collapsible material?

Analysis of compressibility data of diatom earth and Ariake clay of similar water holding capacities has been made in this paper. Analysis suggests that in the case of clays with sheet minerals such as in Ariake clays, due to compression, cluster growth takes place, whereas with diatom earth the breakdown of cluster accounts for bilinear compression characteristics. It has been hypothesized that the interactive void ratio in the case of diatom earth is likely to be far smaller than that in the case of Ariake clay where most of the pore water is herd by micropores enclosed by clay particle clusters. In a way diatom earth reflects the behaviour of clay of very law physico-chemical potential with far reduced collapse potential. Even the compressibility at higher stress range both in undisturbed and remolded states are likely to be due to breakdown of clusters with little contribution from the physico - chemical potential. Diatom earth is not a collapsible material at stress levels of engineering interest despite the in -situ water content is at par or even higher than soft sensitive Ariake clay with comparatively low cementation consequently with pronounced collapsible potential.

Synthesis, growth, and characterization of a new NLO material 3-(2,3-dimethoxyphenyl)-1-(pyridin-2-yl)prop-2-en-1-one

3-(2,3-Dimethoxyphenyl)-1-(pyridin-2-yl)prop-2-en-1-one (DMPP) a potential second harmonic generating (SHG) has been synthesized and grown as a single crystal by the slow evaporation technique at ambient temperature. The structure determination of the grown crystal was done by single crystal X-ray diffraction study. DMPP crystallizes with orthorhombic system with cell parameters a = 20.3106(8)angstrom, b = 4.9574(2)angstrom, c = 13.4863(5)angstrom, alpha = 90 degrees, beta = 90 degrees, gamma = 90 degrees and space group Pca2(1). The crystals were characterized by FT-IR, thermal analysis, UV-vis-NIR spectroscopy and SHG measurements. Various functional groups present in DMPP were ascertained by FTIR analysis. DMPP is thermally stable up to 80 degrees C and optically transparent in the visible region. The crystal exhibits SHG efficiency comparable to that of KDP. (C) 2011 Elsevier B.V. All rights reserved.

Structural, vibrational and thermal studies of a new nonlinear optical material: L-Asparagine-L-tartaric acid

Crystals of a new nonlinear optical (NLO) material, viz., L-asparagine-L-tartaric acid (LALT)(1) were grown by slow evaporation of an aqueous solution containing equimolar concentrations of L-asparagine and t-tartaric acid. The structure of the title compound which crystallizes in the non-centrosymmetric monoclinic space group P2(1) consists of a molecule of L-asparagine and a molecule of free L-tartaric acid both of which are interlinked by three varieties of H-bonding interactions namely O-H center dot center dot center dot O, N-H center dot center dot center dot O and C-H center dot center dot center dot O. The UV-Vis-NIR spectrum of 1 reveals its transparent nature while the vibrational spectra confirm the presence of the functional groups in 1. The thermal stability and second harmonic generation (SHG) conversion efficiency of 1 were investigated. (C) 2012 Elsevier B.V. All rights reserved.

Energy absorption behaviours of CSM-based GFRC plates with hemispherical features

In the present study, the mechanical behaviour of CSM (chopped strand mat)-based GFRC (glass fibre-reinforced composite) plates with single and multiple hemispheres under compressive loads has been investigated both experimentally and numerically. The basic stress-strain behaviours arc identified with quasi-static tests on two-ply coupon laminates and short cylinders, and these are followed up with compressive tests in a UTM (universal testing machine) on single- and multiple-hemisphere plates. The ability of an explicit LS-DYNA solver in predicting the complex material behaviour of composite hemispheres, including failure, is demonstrated. The relevance and scalability of the present class of structural components as `force-multipliers' and `energy-multipliers' have been justified by virtue of findings that as the number of hemispheres in a panel increased from one to four, peak load and average absorbed energy rose by factors of approximately four and six, respectively. The performance of a composite hemisphere has been compared to similar-sized steel and aluminium hemispheres, and the former is found to be of distinctly higher specific energy than the steel specimen. A simulation-based study has also been carried out on a composite 2 x 2-hemisphere panel under impact loads and its behaviour approaching that of an ideal energy absorber has been predicted. In summary, the present investigation has established the efficacy of composite plates with hemispherical force multipliers as potential energy-absorbing countermeasures and the suitability of CAE (computer-aided engineering) for their design.

Synthesis and Electrochemical Characterization of LiNi0.8Co0.2O2 as Cathode Material for Aqueous Rechargeable Lithium Batteries

LiNi0.8Co0.2O2 cathode material for lithium ion batteries is synthesized by reaction under autogenic pressure at elevated temperature (RAPET) method. The simple synthesis procedure is time and energy saving, and thus is promising for commercial application. The structure and stability of the material have been characterized by means of XRD and TG-DTA. The electrochemical properties of the LiNi0.8Co0.2O2 cathode are investigated in 2 M Li2SO4 aqueous electrolyte and they are compared to that in an organic electrolyte. A battery cell consisting of LiNi0.8Co0.2O2 as cathode in 2 M Li2SO4 solution is constructed in combination with LiTi2 (PO4)(3) as anode. The cell retained almost constant discharge capacity over hundred cycles. The electrochemical impedance spectral ( EIS) studies in aqueous and nonaqueous electrolytes revealed that the mechanism of lithium ion intercalation and deintercalation processes in LiNi0.8Co0.2O2 electrode follow almost similar mechanism in both aqueous and nonaqueous electrolytes. The chemical diffusion coefficient was calculated from slow scan rate cyclic voltammetry and EIS. (C) 2012 The Electrochemical Society. DOI: 10.1149/2.075205jes] All rights reserved.

Development of a composite material with high magnetic permeability and low loss factor for high frequency application

A flexible composite suitable for MHz frequency application has been developed by combining Fe3O4 and polyvinyl alcohol (PVA). The loss factor and the permeability have been evaluated. At an optimum weight percentage of Fe3O4 in the PVA matrix, the frequency at which the loss factor gives a minimum shifts to the MHz region. The loss factor has been found to be lower by one order of magnitude at 70 MHz compared to the presently used nickel zinc ferrite. The Henkel plot and the Cole-Cole plot have been obtained for the understanding of the high magnetic permeability and the low loss factor. (C) 2012 American Institute of Physics. doi:10.1063/1.3672867]

Damage-tolerant design optimization of laminated composite structures using dispersion of ply angles by genetic algorithm

This article aims to obtain damage-tolerant designs with minimum weight for a laminated composite structure using genetic algorithm. Damage tolerance due to impacts in a laminated composite structure is enhanced by dispersing the plies such that too many adjacent plies do not have the same angle. Weight of the structure is minimized and the Tsai-Wu failure criterion is considered for the safe design. Design variables considered are the number of plies and ply orientation. The influence of dispersed ply angles on the weight of the structure for a given loading conditions is studied by varying the angles in the range of 0 degrees-45 degrees, 0 degrees-60 degrees and 0 degrees-90 degrees at intervals of 5 degrees and by using specific ply angles tailored to loading conditions. A comparison study is carried out between the conventional stacking sequence and the stacking sequence with dispersed ply angles for damage-tolerant weight minimization and some useful designs are obtained. Unconventional stacking sequence is more damage tolerant than the conventional stacking sequence is demonstrated by performing a finite element analysis under both tensile as well as compressive loading conditions. Moreover, a new mathematical function called the dispersion function is proposed to measure the dispersion of ply angles in a laminate. The approach for dispersing ply angles to achieve damage tolerance is especially suited for composite material design space which has multiple local minima.

Hygrothermal durability and failure modes of FRP for marine applications

This article deals with the durability of 2D woven mat carbon/polyester, glass/isopolyester, and gel-coated glass/isopolyester reinforced composites under hygrothermic conditions with regard to marine applications. The test coupons were exposed to 60 degrees C and 70 degrees C at 95% RH for a maximum duration of 100 h. The samples were periodically withdrawn and weighed for moisture absorption and tested for the degradation in the mechanical properties such as ultimate tensile strength, flexural strength, interlaminar shear strength, and Young's modulus and flexural modulus. Carbon/isopolyester-based specimens showed greater stability with respect to degradation in the mechanical properties than the glass/isopolyester/gel coat- and glass/isopolyester-based specimens. Glass/isopolyester exhibited the maximum moisture absorption, whereas the minimum moisture absorption was found in glass/isopolyester/gel coat. Diffusion coefficient (D) was found to be the highest for glass/isopolyester and the lowest for glass/isopolyester/gel coat, based on the Fick's law of diffusion. Diffusion coefficient increases with the increase in temperature for all the specimens. Microstructure study of fractured specimens was carried out using scanning electron microscope to compare matrix/fiber debonding and matrix-degradation of fiber-reinforced polymer composites.

A Linear S-N Curve with Load Dependent Variance and Explicit Failure Probability

We reconsider standard uniaxial fatigue test data obtained from handbooks. Many S-N curve fits to such data represent the median life and exclude load-dependent variance in life. Presently available approaches for incorporating probabilistic aspects explicitly within the S-N curves have some shortcomings, which we discuss. We propose a new linear S-N fit with a prespecified failure probability, load-dependent variance, and reasonable behavior at extreme loads. We fit our parameters using maximum likelihood, show the reasonableness of the fit using Q-Q plots, and obtain standard error estimates via Monte Carlo simulations. The proposed fitting method may be used for obtaining S-N curves from the same data as already available, with the same mathematical form, but in cases in which the failure probability is smaller, say, 10 % instead of 50 %, and in which the fitted line is not parallel to the 50 % (median) line.

Conservative Failure Criteria for Optimal Design of Composite Structures Including Effect of Shear Loading

A minimum weight design of laminated composite structures is carried out for different loading conditions and failure criteria using genetic algorithm. The phenomenological maximum stress (MS) and Tsai-Wu (TW) criteria and the micro-mechanism-based failure mechanism based (FMB) failure criteria are considered. A new failure envelope called the Most Conservative Failure Envelope (MCFE) is proposed by combining the three failure envelopes based on the lowest absolute values of the strengths predicted. The effect of shear loading on the MCFE is investigated. The interaction between the loading conditions, failure criteria, and strength-based optimal design is brought out.

Sonochemical Synthesis of Pt Ion Substituted TiO2 (Ti0.9Pt0.1O2): A High Capacity Anode Material for Lithium Battery

Doping of TiO2 with a suitable metal ion where dopant redox potential couples with that of titanium (Ti4+) and act as catalyst for additional reduction of Ti4+ to Ti2+ (Ti4+ -> Ti3+ -> Ti2+) is envisaged here to enhance lithium storage even higher than one Li/TiO2. Accordingly, 10 atom% Pt ion substituted TiO2, Ti0.9Pt0.1O2 nanocrystallites was synthesized by sonochemical method using diethylenetriamine (DETA) as complexing agent. Powder X-ray diffraction pattern (XRD), Rietveld refinement and TEM study reveals that Ti0.9Pt0.1O2 nanocrystallites of similar to 4 nm size crystallize in anatase structure. X-ray photo-electron spectroscopy (XPS) study confirms that and both Ti and Pt are in 4+ oxidation state. Due to Pt4+ ion substitution in TiO2, reducibility of TiO2 was enhanced and Ti4+ was reduced up to Ti2+ state via coupling of Pt states (Pt4+/Pt2+/Pt-0) with Ti states (Ti4+/Ti3+/Ti2+). Galvanostatic cycling of Ti0.9Pt0.1O2 against lithium showed very high capacity of 430 mAhg(-1) or exchange of similar to 1.5Li/Ti0.9Pt0.1O2. (C) 2012 The Electrochemical Society. DOI: 10.1149/2.029208jes] All rights reserved.

Hydrothermal synthesis of a monoclinic VO2 nanotube-graphene hybrid for use as cathode material in lithium ion batteries

The hydrothermal reaction of a mixture of a colloidal dispersion of graphite oxide and ammonium vanadate yielded a hybrid made of graphene and a nanotubular metastable monoclinic polymorph of VO2, known as VO2(B). The formation of VO2(B) nanotubes is accompanied by the reduction of graphite oxide. Initially the partially scrolled graphite oxide layers act as templates for the crystallization of VO2(B) in the tubular morphology. This is followed by the reduction of graphite oxide to graphene resulting in a hybrid in which VO2(B) nanotubes are dispersed in graphene. Electron microscopic studies of the hybrid reveal that the VO2(B) nanotubes are wrapped by and trapped between graphene sheets. The hybrid shows potential to be a high capacity cathode material for lithium ion batteries. It exhibits a high capacity (similar to 450 mAh/g) and cycling stability. The high capacity of the hybrid is attributed to the interaction between the graphene sheets and the VO2(B) tubes which improves the charge-transfer. The graphene matrix prevents the aggregation of the VO2(B) nanotubes leading to high cycling stability. (C) 2012 Elsevier Ltd. All rights reserved.