Fracture toughness of a series of high chromium abrasion resistant alloys

The fracture properties of a series of alloys containing 15% chromium and 0.8 to 3.4% carbon are investigated using strain fracture toughness testing techniques. The object of the work is to apply a quantitative method of measuring toughness to abrasion resistant materials, which have previously been assessed on an empirical basis; and to examine the relationship between microstructure and K10 in an attempt to improve the toughness of inherently brittle materials. A review of the relevant literature includes discussion of the background to the alloy series under investigation, a survey of the development of fracture mechanics and the emergence of K10 as a toughness parameter. Metallurgical variables such as composition, heat treatment, grain size, and hot working are ???? to relate microstructure to toughness, and fractographic evidence is used to substantiate the findings. The results are applied to a model correlating ductile fracture with plastic strain instability, and the nucleation of voids. Strain induced martensite formation in austenitic structures is analysed in terms of the plastic energy dissipation mechanisms operating at the crack tip. Emphasis is placed on the lower carbon alloys in the series, and a composition put forward to optimise wear resistance and toughness. The properties of established competitive materials are compared to the proposed alloy on a toughness and cost basis.

The strength and fracture of engineering alloys at high temperature a collection of papers

DUE TO COPYRIGHT RESTRICTIONS ONLY AVAILABLE FOR CONSULTATION AT ASTON UNIVERSITY LIBRARY AND INFORMATION SERVICES WITH PRIOR ARRANGEMENT

The application of finite element analysis to fracture mechanics.

DUE TO COPYRIGHT RESTRICTIONS ONLY AVAILABLE FOR CONSULTATION AT ASTON UNIVERSITY LIBRARY AND INFORMATION SERVICES WITH PRIOR ARRANGEMENT

Fracture toughness of some high density PM steels

Tensile strengths, impact energies, and fracture toughness data are presented for pure Fe-0.5 C, Astaloy A with 0.2 and 0.6%C, and for Distaloy AB-0.6%C at relative densities of about 0.9, achieved by conventional pressing and sintering, and at close to 1.0, achieved by powder forging. At low relative density, properties are controlled by sizes of sinter necks; it is postulated that toughness scales as (x/a)4, x/a being the ratio of neck diameter to particle diameter. At high relative density, microvoid coalescence and good toughness is observed for low strength microstructures whereas cleavage and poor toughness is a concomitant of high strength.

Fracture toughness of SIC, Si3N4, and sialon ceramics using controlled surface flaws

Knoop and Vickers indentation cracks have frequently been used as model 'precracks' in ceramic bend specimens for fracture toughness (K1c) determination. Indentation residual stress reduces the measured K1c but can be removed or accounted for by grinding, annealing, or modelling. Values of K1c are obtained for four materials using Vickers indentations and an improved stress intensity factor. Methods for residual stress removal or incorporation are compared, and the most reliable stress removal alternative is identified for each material. © 1996 The Institute of Materials.

Interfacial effects on fatigue and fracture in discontinuously reinforced metal matrix composites

Interfaces in conventional monolithic alloys exert an important influence on fatigue and fracture behavior. In discontinuously reinforced metal matrix composites (MMCs), the role of interface is even more dominant. The interfacial is higher in MMCs and the interfaces are generally of high energy and chemically unstable. This paper reviews the factors which can affect interfacial strength in discontinuously reinforced MMCs, and the ways in which interfacial strength can be controlled. The effects of interfacial strength on fatigue crack propagation and fracture behavior are then illustrated.

Fracture behaviour of an aluminide coating on a single crystal nickel base superalloy

Measurement of the coating fracture strain of an aluminide coating on a single crystal nickel base superalloy has been performed both in three-point bending and using variable wall thickness testpieces. As-aged specimens, 28 to 33 μm in thickness, were tested at room temperature, 600, 700 and 750 °C; specimens pre-exposed for 140 h at 850 and 1100 °C in air and vacuum were tested at room temperature. Fracture strains varied from 0.52 to 0.70% for as-aged specimens tested at temperatures up to 700 °C and specimens exposed at 850 °C and tested at room temperature. The crack path for these conditions was intergranular or transgranular in the main coating, along carbide-matrix interfaces in the coating transition zone, and at an angle of 30-45° to the original crack path in the substrate. The as-aged coating tested at 750 °C was ductile; a ductile-brittle transition occurs between 700 and 750 °C for the strain rate used (1 × 10-5 s-1). Following 1100 °C pre-exposure, specimens were ductile at room temperature with fractures strains of several percent. In this condition the crack morphology changed to one of subsurface nucleation in β grains and at β-γ′ interfaces. © 1993.

The effect of microstructure on the fracture toughness of a metal-matrix composite

The fracture behaviour and plane strain fracture toughness, KIC, of four 8090-based metal-matrix composites containing 20 weight % SiC particles, 3, 6 and 23 μm in diameter, has been evaluated as a function of matrix ageing condition. Toughness values are found to be almost independent of reinforcement size. Ageing at 170°C results in a monotonic decrease in toughness with increasing strength up to the peak condition, with no subsequent recovery in toughness on overageing. However, unlike reinforced 8090, the composites are not found to be susceptible to intergranular embrittlement on overageing. The observed trends are found to be independent of reinforcement size. These findings are explained in terms of the strength, work hardening behaviour and nature and distribution of void-nucleating particles in the matrix. © 1993.

Effects of crack length and shape on the fracture toughness of a high strength steel 300m

The results of fracture toughness tests on a high strength steel 300m are presented. These results show (i) that in the presence of through-thickness cracks the toughness remains constant down to (a/W)-ratios as low as 0.01 and failure loads up to 0.85σy, and (ii) that the material is more resistant to crack growth when the cracks are semi-elliptical in shape, giving a toughness value which is almost 25 per cent higher than the through-thickness one. Three independent stress analyses are used to obtain stress intensity values for the semi-elliptical cracks and additional confirmation of the increase in toughness comes from stretch zone measurements.

Effects of hydrostatic tension on cleavage fracture of pure polycrystalline zinc

A study was made of notch effects on the cleavage fracture of polycrystalline zinc. It was seen that the nominal fracture stress of SENB specimens was independent of notch angle. The maximum tensile stress below the notch at fracture in SENB specimens was shown to be different from the tensile stress at fracture in tensile testpieces over a temperature range from −196 to −17°C. The notch root strain at fracture was found to be the same as the uniaxial tensile fracture strain over this temperature interval. These results were interpreted as showing the cleavage fracture of polycrystalline zinc to be shear-stress or initiation controlled, as predicted by Stroh's dislocation model of cleavage.

Increasing the fracture toughness of silicon by ion implantation

Previous studies have shown that moderate doses of radiation can lead to increased fracture toughness in ceramics. An experimental investigation was conducted to determine the effects of ion implantation on fracture toughness in silicon. Specimens implanted with Ne showed increased fracture toughness, over the entire range of implantations tested. Using ions of various energies to better distribute implantation damage further increased the fracture toughness even though the region of amorphous damage was slightly decreased. The implantation damage accumulated in a predictable manner so that fracture toughness could be optimized.

Effect of dopants on the fracture toughness of silicon

Fracture experiments were conducted on p-type and n-type Si in the presence and absence of hydrogen. It was found that fracture toughness is slightly less than the fracture toughness of n-type silicon. Annealing silicon in an Ar/H atmosphere gave a hydrogen concentration of less than 0.1 ppm, which did not have any measurable effect on fracture toughness. Likewise, the exposure of pre-cracked specimens to H did not cause any measurable change in fracture toughness.

Molecular dynamics simulation of brittle fracture in silicon

The fracture process involves converting potential energy from a strained body into surface energy, thermal energy, and the energy needed to create lattice defects. In dynamic fracture, energy is also initially converted into kinetic energy. This paper uses molecular dynamics (MD) to simulate brittle frcture in silicon and determine how energy is converted from potential energy (strain energy) into other forms.