Effect of Resin Cement Type on the Microtensile Bond Strength to Lithium Disilicate Ceramic and Dentin Using Different Test Assemblies

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

The potential of novel primers and universal adhesives to bond to zirconia

Objectives: To investigate the adhesive potential of novel zirconia primers and universal adhesives to surface-treated zirconia substrates.Methods: Zirconia bars were manufactured (3.0 mm x 3.0 mm x 9.0 mm) and treated as follows: no treatment (C); air abrasion with 35 mu m alumina particles (S); air abrasion with 30 mu m silica particles using one of two systems (Rocatec or SilJet) and; glazing (G). Groups C and S were subsequentially treated with one of the following primers or adhesives: ZP (Z-Prime Plus), AZ (AZ Primer); MP (Monobond Plus); SU (ScotchBond Universal) and; EA (an Experimental Adhesive). Groups Rocatec and SilJet were silanized prior to cementation. Samples form group G were further etched and silanized. Bars were cemented (Multilink) onto bars of a silicate-based ceramic (3.0 mm x 3.0 mm x 9.0 mm) at 90 degrees angle, thermocycled (2.500 cycles, 5-55 degrees C, 30 s dwell time), and tested in tensile strength test. Failure analysis was performed on fractured specimens to measure the bonding area and crack origin.Results: Specimens from group C did not survive thermocycling, while CMP, CSU and CEA groups survived thermocycling but rendered low values of bond strength. All primers presented a better bond performance after air abrasion with Al2O3 particles. SilJet was similar to Rocatec, both presenting the best bond strength results, along with SMP, SSU and CEA. G promoted intermediate bond strength values. Failure mode was predominately adhesive on zirconia surface combined to cohesive of the luting agent.Conclusions: Universal adhesives (MP, SU, EA) may be a considerable alternative for bonding to zirconia, but air abrasion is still previously required. Air abrasion with silica particles followed by silane application also presented high bond strength values. (C) 2013 Elsevier Ltd. All rights reserved.

Bonding of Y-TZP to Dentin: Effects of Y-TZP Surface Conditioning, Resin Cement Type, and Aging

Purpose: To evaluate the effects of two surface treatments, aging, and two resin cements on shear bond strength between dentin and yttrium-stabilized tetragonal zirconia polycrystal ceramic (Y-TZP).Materials and Methods: Eighty human molars were embedded in acrylic resin and sectioned 3 mm below the occlusal plane. These teeth and 80 cylindrical Y-TZP specimens (height, 4 mm; diameter, 3.4 mm) were divided into eight groups (n=10) using the following factors: Y-TZP surface treatment (Vi: low-fusing porcelain [vitrification] + hydrofluoric acid etching + silanization or Si: tribochemical silicatization); cementation strategies (PF: Pan avia or CC: Clearfil); and storage (nonaging or aging). Bonding surfaces of 40 Y-TZP specimens received Vi treatment, and the rest received Si treatment. Half of the ceramic-tooth assemblies were cemented with Panavia, the rest with Clearfil. Shear tests were executed using 0.4-mm-thick wire at 0.5 mm/min. Data were analyzed by three-way analysis of variance and Tukey test (alpha=0.05). Fractures were analyzed.Results: Y-TZP surface treatments did not affect bond strength (p=0.762, Vi = Si), while resin cements (p<0.001, Panavia > Clearfil) and aging (p=0.006, nonaging > aging) showed a significant effect. Most failures were in adhesive at dentin-cement interfaces; no failure occurred between zirconia and cement.Conclusion: When Y-TZP ceramic is bonded to dentin, the weakest interface is that between dentin and resin cement. The resin cement/Y-TZP interface was less susceptible to failures, owing to Y-TZP surface treatments.

Efeito da partícula e do momento de jateamento na caracterização superficial da zircônia e na resistência de união com cimento resinoso

Pós-graduação em Reabilitação Oral - FOAR

Discrepâncias de assentamento ocorrido em coroas totais metálicas, com e sem alívio interno, variando-se os términos cervicais e os agentes cimentantes

Pós-graduação em Odontologia Restauradora - ICT

Estudo comparativo in vitro da resistência ao cisalhamento de discos metálicos de níquel-cromo, com ou sem tratamento de superfície, unidos à dentina bovina com quatro cimentos

Pós-graduação em Odontologia Restauradora - ICT

Efeito do laser Nd:Yag no pré-tratamento dentinário e selamento marginal, em restaurações de cimento de ionômero de vidro resina modificado

Pós-graduação em Odontologia Restauradora - ICT

Avaliação in vitro da resistência adesiva ao cisalhamento entre a dentina bovina, cimentos resinosos e materiais restauradores indiretos, tratados ou não com jato de óxido de alumínio, ácido fluorídrico e silano

The purpose of this study was to evaluate in vitro the shear bond strenght to bovine dentin, during 24h and 30 days with the following variables: resin cements Enforce and Panavia F; aesthetics restorative materials Art Glass, IPS Empress 2 and Targis, with surface treatment with microetching with aluminium oxide, fluoridric acid and silane. Two hundred eighty eight sound bovine teeth from 3 years old animals constituted the samples after inclusion on polyester resin box. lnstron model 430 Universal Testing Machine, a crosshead speed 0,5 mm/min and load cells of 500 Kg, was used for shear bond strenght testing (MPa). The results were statistically analysed by ANOVA The best result was obtained with /PS Empress 2, microetched with aluminium oxide, fluoridric acid and silane, cemented with Panavia F and stored in distilled water, 3f'C during 30 days

Avaliação do desempenho das propriedades mecânicas de concretos self compacting elaborados com diferentes tipos de cimentos submetidos à cura térmica

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Resistência de união, índice de remanescente adesivo e avaliação da presença de esmalte sobre a base de braquetes após descolagem: estudo in vitro

Pós-graduação em Ciências Odontológicas - FOAR

Impacto da incorporação de substâncias químicas nas propriedades físico-químicas dos cimentos endodônticos

Pós-graduação em Odontologia - FOAR

Anatomização de pinos de fibra de vidro: estudo de propriedades mecânicas na interface restauradora adesiva

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Avaliação da eficácia de primers para metal na resistência ao cisalhamento da união entre cimentos resinosos e metais não nobres. Efeito do armazenamento em água

O sucesso das restaurações metálicas indiretas depende, dentre outros fatores, de uma união eficaz entre a estrutura metálica e o cimento dentário empregados. Sabe-se que os primers para metal atuam com comprovada eficácia na resistência adesiva dos cimentos resinosos às ligas nobres. Entretanto, pouco foi estudado sobre o efeito de tais materiais em ligas não nobres. O propósito deste estudo foi avaliar a eficácia de primers para metal na resistência ao cisalhamento da união entre cimentos resinosos e metais não nobres. Discos (9 mm de diâmetro e 3 mm de altura) foram fundidos em liga de NiCr (n=80) e em titânio comercialmente puro (Ti c.p.) (n=80) e foram incluídos em anel de PVC com resina acrílica quimicamente ativada. As superfícies dos discos foram regularizadas com lixas de carbeto de silício de granulação 320, 400 e 600 e jateadas com partículas de óxido de alumínio de 50 µm. Espécimes de cada metal foram divididos em quatro grupos (n=20). Uma matriz metálica bi-partida (5 mm de diâmetro interno e 2 mm de altura) foi posicionada na superfície do espécime. As áreas adesivas receberam um dos seguintes tratamentos: 1) Panavia F; 2) Alloy Primer e Panavia F; 3) Bistite DC e 4) Metaltite e Bistite DC. Para evitar a exposição dos cimentos à luz, estes foram espatulados e inseridos na matriz dentro de uma câmara de revelação radiográfica. Quarenta minutos após a confecção, os espécimes foram armazenados em água destilada a 37ºC por 24 horas e então termociclados (1.000 ciclos, 5ºC e 55ºC, 30 segundos cada banho). Após a termociclagem, os espécimes foram armazenados novamente nas mesmas condições descritas anteriormente por um período de 24 horas (n=10) ou de 6 meses (n=10) antes do ensaio de cisalhamento em uma máquina de ensaios mecânicos (Material Test System 810).

Análise química, citotoxicidade e biocompatibilidade de cimentos de ionômero de vidro

Objetivo: O presente trabalho, dividido em três estudos, teve como objetivo geral identificar e quantificar a liberação de componentes e avaliar a citotoxicidade e a biocompatibilidade de cimentos de ionômero de vidro (CIVs). Método: Para o estudo 1, extratos dos CIVs Vitrebond (VB), Fuji Lining LC (FL), Vitremer (VM), Fuji II LC (FII), Ketac Fil Plus (KF) e Ketac Molar Easymix (KM) foram obtidos pela imersão de corpos-de-prova em meio de cultura celular (DMEM). Esses extratos (n=9 por grupo) foram analisados por eletrodo específico quanto à presença de flúor e por espectrometria de absorção atômica quanto à presença de alumínio e zinco. HEMA e iodobenzeno foram identificados por CG/EM (n=6). Para o estudo 2, células MDPC-23 foram colocadas em contato com os extratos dos CIVs por 24 horas. Em seguida, foram avaliadas a atividade da desidrogenase succínica (SDH) (n=8), a produção de proteína total (PT) (n=8), a atividade da fosfatase alcalina (FAL) (n=8) e a morfologia celular (n=2). Para o estudo 3, tubos de polietileno (n=24 por grupo) foram preenchidos com os CIVs e implantados no tecido subcutâneo de 42 ratos. Como grupo controle foi utilizada a guta-percha. Após 7 ou 15 dias de pós-operatório, metade dos espécimes de cada grupo e período (n=6) foi preparada para análise histológica, e os demais (n=6) para análise da expressão de genes que codificam para IL-1? e TNF-?. Resultados: Os extratos de todos os CIVs apresentaram uma concentração de flúor significativamente maior do que o meio de cultura DMEM (controle), tendo o VB liberado maior quantidade, estatisticamente significante, do que os demais CIVs. O VB foi, também, o único material que liberou quantidades relativamente altas de alumínio e de zinco. O HEMA foi identificado nos extratos de todos os CIVs modificados por resina (VB, FL, VM e FII), e o iodobenzeno... (Resumo completo, clicar acesso eletrônico abaixo)

Biocompatibility of New Calcium Aluminate Cement: Tissue Reaction and Expression of Inflammatory Mediators and Cytokines

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)