Macroporous fluoropolymeric films templated by silica colloidal assembly: A possible route to super-hydrophobic surfaces

A super-hydrophobic surface was obtained on a three-dimensional (313) polyvinylidene fluoride (PVDF) macroporous film. The porous films were fabricated through self-assembled silica colloidal templates. The apparent water contact angle of the surface can be tuned from 106 degrees to 153 degrees through altering the sintering temperature and the diameter of the colloidal templates. A composite structure of micro-cavities and nanoholes on the PVDF surface was responsible for the super-hydrophobicity. The wettability of the porous surfaces was described by the use of the Cassie-Baxter model and Wenzel's equation.

One-step polyelectrolyte-based route to well-dispersed gold nanoparticles: Synthesis and insight

Polyelectrolytes have been widely used as building blocks for the creation of thickness-controllable multilayer thin films in a layer-by-layer fashion, and also been used as flocculants or stabilizer of colloids. This paper reports novel finding that a kind of polyelectrolyte, polyamines, can facilely induce HAuCl4 to spontaneously form well-stabilized gold nanoparticles without the additional step of introducing a reducing reagent during the elevation of temperature, even at room temperature in some cases. The polymer chain-confined microenvironment and the acid-induced evolution of amide of such kind of polyelectrolyte solution play an important role in the nucleation and growth of gold nanoparticles. This method would not only be helpful to gain an insight into the formation of gold nanoparticles in polyelectrolyte systems, but also provide a novel and facile one-step polyelectrolyte-based synthetic route to polyelectrolyte protected gold nanoparticles in aqueous media for potential applications. More importantly, this strategy will be general to the preparation of other nanoparticles.

Liposome-mediated conformation transition of DNA detected by molecular probe: methyl green

Recent studies have focused on the structural features of DNA-lipid assemblies. In this paper, we take methyl green (MG) as a probe molecule to detect the conformational change of DNA molecule induced by dimethyldioctadecylammonium bromide (DDAB) liposomes before the condensation process of DNA begins. DDAB-induced DNA topology changes were investigated by cyclic voltammetry (CV), circular dichroism (CD) and UV-VIS spectrometry. We find that upon binding to DNA, positively charged liposomes induce a conformational transition of DNA molecules from the native B-form to the C motif. Conformational transition in DNA results in the binding modes of MG to DNA, changing and being isolated from DNA to the solution. More stable complexes are formed between DNA and DDAB. That is also proved by the melting study of DNA.

Green electroluminescent device with a terbium beta-diketonate complex as emissive center

In this study, a terbium complex, Tb(acac)(3)bath (acac: acetylacetone, bath: 4,7-diphenyl-1,10-phenanthroline), was synthesized and its luminescent properties were investigated compared with the reported terbium complex, Tb(acac)(3)phen (phen: phenanthroline). When it was used as an emitting material in organic electroluminescent (EL) device, the triple-layer-type device with a structure of glass substrate/ITO (indium-tin oxide)/TPD (N,N'-diphenyl-N,N'-bis(3-methylphenyl)-1,1'-biphenyl-4,4'-diamine)/Tb(acac)(3)bath/Alq(3) (tris (8-hydroxyquinolinato) aluminum)/Al (aluminum) exhibited bright characteristic emission of terbium ion upon applying DC voltage. An apparent difference was observed between the photoluminescence spectrum and the EL spectrum. The EL device exhibited some characteristics of diode and the maximum luminance of 77 cd/m(2) was obtained at 17 V.

A novel route for the preparation of CdS nanocrystal-poly(acrylic acid) composites using gamma-radiation

CdS nanocrystals were synthesized through AOT/heptane/H2O reverse micelles. New stable reverse mikelles were obtained by adding an appropriate amount of acrylic. acid monomer, CdS nanocrystal-poly(acrylic acid) composites were synthesized by gamma-radiation with a reverse mi'celle route at room temperature. The US nanocrystals with narrow size distribution were, found to be dispersed homogeneously in the poly(acrylic acid) matrix. (C) 2002 Elsevier Science B.V. All rights reserved.

Sol-gel derived silicate oxyapatite phosphor films doped with rare earth ions

Rare-earth (Eu3+, Tb3+)-doped Ca2Y8(SiO4)(6)O-2 luminescent thin films were dip-coated on silicon and quartz glass substrates through a sol-gel route. X-ray diffraction (XRD), scanning electron microscopy (SEM) and luminescence excitation and emission spectra as well as luminescence decays were used to characterize the resultant films. The results of XRD reveal that these films remain amorphous below 700 degreesC, begin to crystallize at 800 degreesC, and crystallize completely around 1000 degreesC with an oxyapatite structure. The grain structure of the film can be seen clearly from SEM micrographs, where particles with various shape and average size of 250 nm can be resolved. The Eu3+ and Tb3+ ions show their characteristic red (D-5(0)-F-7(2)) and green (D-5(4)-F-7(5)) emission in the films with a quenching concentration of 10 and 6 mol% (of Y3+), respectively. The lifetime of Eu-3divided by increases with the heat treatment temperature front 700 to 1100 degreesC.

Sol-gel deposition and luminescent properties of oxyapatite Ca-2(Y,Gd)(8)(SiO4)(6)O-2 phosphor films doped with rare earth and lead ions

Rare-earth and lead ions (Eu3+, Tb3+, Dy3+, Pb2+) doped Ca2Y8 (SiO4)(6)O-2 and Ca2Gd8(SiO4)(6)O-2 thin films have been dip- coated on silicon and quartz glass substrates through the sol- gel route. X- Ray diffraction (XRD), TG- DTA, scanning electron microscopy (SEM), atomic force microscopy (AFM), FT- IR and luminescence excitation and emission spectra as well as luminescence decays were used to characterize the resulting films. The results of XRD reveal that these films remain amorphous below 700 degreesC, begin to crystallize at 800 degreesC and crystallize completely around 1000 degreesC with an oxyapatite structure. The grain structure of the film can be seen clearly from SEM and AFM micrographs, where particles with various shapes and average size of 250 nm can be resolved. Eu3+ and Tb3+ show their characteristic red (D-5(0)-F-7(2)) and green (D-5(4) - F-7(5)) emission in the films with a quenching concentration of 10 and 6 mol% (of Y3+), respectively. The lifetime and emission intensity of Eu3+ increase with the temperature treatment from 700 to 1100 degreesC, while those of Tb3+ show a maximum at 800 degreesC. Energy transfer phenomena have been observed by activating the oxyapatite film host- lattice Ca2Gd8(SiO4)(6)O-2 with Tb3+ (Dy3+). In addition, Pb2+ can sensitize the Gd3+ sublattice in Ca2Gd8(SiO4)(6)O-2.

Voltammetric and spectroscopic studies on methyl green and cationic lipid bound to calf thymus DNA

DNA interaction with cationic lipids promises to be a versatile and effective synthetic transfection agent. This paper presents the study on binding of a simple artifical cationic lipid, cetyltrimethylammonium bromide (CTAB), to calf thymus DNA (CT DNA) prior to the condensation process, taking methyl green (MG) as a probe. The results show that the CTAB binds to DNA through electrostatic interaction forming a hydrophobic complex, thus changing the micro-environment of duplex of DNA, so the binding state of MG and DNA is changed, and a complex CTAB-CT DNA-MG is formed. This fact suggests a new way to mediate the conformation of molecular assemblies of DNA and lipids. (C) 2000 Elsevier Science B.V. All rights reserved.

Green electroluminescence generated from the thin film based on a soluble lanthanide complex

Electroluminescent (EL) devices based on a soluble complex Tb(MDP)(3) [Tris-(monododecyl phthalate)Terbium] doped with poly (N-vinylcarbazole) (PVK), (2-(4-biphenyl)-5-(4-t-butylphenyl)-1,3,4-oxadiazole) (PBD) were fabricated. The device structures of ITO/PVK/PVK:PBD:Tb(MDp)(2)/Aiq(3)/Al and ITO/PVK:PBD:Tb(MDP)(3)/Alq(3)/Al were employed. The Tb(MDP), as emissive layer was spin-coated. The EL cell exhibited characteristic emission of terbium ion. (C) 2000 Elsevier Science S.A. All rights reserved.

Charge carrier mobility and electroluminescence in a green-emitting alternating block copolymer with a methoxy Bi-substituted chromophore

We determine the mobility of positive and negative charge carriers in a soluble green-emitting alternating block copolymer with, a methoxy bi-subsbituted conjugated segment. The negative charge carrier mobility of 6 x 10(-11) cm(2)/V.s is directly determined using space-charge-limited current analytical expressions. Positive charge carrier transport is also space-charge-limited, with a mobility of I x 10(-8) cm(2)/V.s. The electron trap distribution is exponential, with a characteristic energy of similar to 0.12 eV. A hole trap with energy similar to 0.4 eV was observed. This copolymer is used as emissive material in organic light-emitting diodes that present brightness of similar to 900 cd/m(2) at 12.5 V.

Sol-gel-derived amperometric biosensor for hydrogen peroxide based on methylene green incorporated in Nafion film

A hydrogen peroxide biosensor was fabricated by coating a sol-gel-peroxidase layer onto a Nafion-methylene green modified electrode. Immobilization of methylene green (MG) was attributed to the electrostatic force between MG(+) and the negatively charged sulfonic acid groups in Nafion polymer, whereas immobilization of horseradish peroxidase was attributed to the encapsulation function of the silica sol-gel network. Cyclic voltammetry and chronoamperometry were employed to demonstrate the feasibility of electron transfer between sol-gel-immobilized peroxidase and a glassy carbon electrode. Performance of the sensor was evaluated with respect to response time, sensitivity as well as operational stability. The enzyme electrode has a sensitivity of 13.5 mu A mM(-1) with a detection limit of 1.0 x 10(-7) M H2O2, and the sensor achieved 95% of the steady-state current within 20 s. (C) 2000 Elsevier Science B.V. All rights reserved.

Fabrication of layer-by-layer deposited multilayer films containing DNA and its interaction with methyl green

Multilayer films were fabricated by layer-by-layer electrostatic deposition techniques between poly(diallyIdimethylammonium chloride) (PDDA) and calf thymus DNA (CT DNA) on glassy carbon and quartz substrates. Electrochemical impedance spectroscopy (EIS), Fourier transform infrared (FTIR) spectroscopy and UV-vis spectroscopy demonstrated the uniform assembly of PDDA/DNA multilayer films, and X-ray photoelectron spectroscopy confirmed the elemental composition of the films. Moreover, the interaction of DNA in PDDA/DNA films with methyl green was investigated by UV-vis spectroscopy and circular dichroism (CD). (C) 2001 Elsevier Science B.V. All rights reserved.