Growth of highly crystalline CaMoO4 : Tb3+ phosphor layers on spherical SiO2 particles via sol-gel process: Structural characterization and luminescent properties

Highly crystalline CaMoO4:Tb3+ phosphor layers were grown on monodisperse SiO2 particles through a simple sol-gel method, resulting in formation of core-shell structured SiO2@CaMoO4:Tb3+ submicrospheres. The resulting SiO2@CaMoO4: Tb3+ core-shell particles were fully characterized by powder X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), field emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectra (EDS), transmission electron microscopy (TEM), photoluminescence (PL), low-voltage cathodoluminescence (CL), and kinetic decays. The XRD results demonstrate that the CaMoO4:Tb3+ layers begin to crystallize on the SiO2 spheres after annealing at 400 degrees C and the crystallinity increases with raising the annealing temperature. SEM and TEM analysis indicates that the obtained submicrospheres have a uniform size distribution and obvious core-shell structure. SiO2@CaMoO4:Tb3+ submicrospheres show strong green emission under short ultraviolet (260 nm) and low-voltage electron beam (1-3 kV) excitation, and the emission spectra are dominated by a D-5(4) -F-7(5) transition of Tb3+(544 nm, green) from the CaMoO4:Tb3+ shells.

Nanostructured CaWO4, CaWO4 : Pb2+ and CaWO4 : Tb3+ particles: Polyol-mediated synthesis and luminescent properties

Nano-submicrostructured CaWO4, CaWO4 : Pb2+ and CaWO4 : Tb3+ particles were prepared by polyol method and characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), Fourier transform infrared spectra (FT-IR), thermogravimetry-differential thermal analysis (TG-DTA), photoluminescence (PL), cathodo-luminescence (CL) spectra and PL lifetimes. The results of XRD indicate that the as-prepared samples are well crystallized with the scheelite structure of CaWO4. The FE-SEM images illustrate that CaWO4 and CaWO4 : Pb2+ and CaWO4 : Tb3+ powders are composed of spherical particles with sizes around 260, 290, and 190 nm respectively, which are the aggregates of smaller nanoparticles around 10-20 nm. Under the UV light or electron beam excitation, the CaWO4 powders exhibits a blue emission band with a maximum at about 440 nm. When the CaWO4 particles are doped with Pb2+, the intensity of luminescence is enhanced to some extent and the luminescence band maximum is red shifted to 460 nm. Tb3+-doped CaWO4 particles show the characteristic emission of Tb3+ D-5(4)-F-7(J) (J=6-3) transitions due to an energy transfer from WO42- groups to Tb3+.

Studies on the doubly charged cluster ions of sodium and potassium nitrates by electrospray ionization tandem mass spectrometry

Doubly charged cluster ions, besides singly charged cluster ions, from sodium and potassium nitrates were produced evidently under normal source capillary temperature of 200 degrees C in both positive and negative ion electrospray ionization (ESI) ion trap mass spectrometry. The fragmentation pathways for doubly charged cluster ions were studied in detail using ESI tandem mass spectrometry and two pathways were observed depending on the cluster sizes of alkali metal nitrates. In addition, factors that affect the formation of cluster ions were also interrogated.

Crystallization and orientation of syndiotactic polystyrene in nanorods

Syndiotactic polystyrene (sPS) nanorods of 200 and 80 nm diameters were prepared by infiltrating porous anodic alumina oxide templates with polymer melt, and the crystallinity and orientation of various forms of sPS crystals in the nanorods were studied by FTIR spectroscopy and electron diffraction. For sPS crystallized from amorphous state at lower temperatures, a-form crystals were found in the nanorods with random orientation and the same degree of crystallinity as that in the bulk. However, for sPS crystallized from molten state at 260 degrees C, while no preferred orientation was found for the chains in the melt, the beta-crystals formed in the nanorods oriented preferentially with the c-axis aligning perpendicular to the axial direction of the nanorod, and the degree of crystallinity was significantly lower than that in the bulk. The crystallinity decrease was more profound for nanorods of smaller diameter. These results were also supported by electron diffraction data and can be attributed to competition between nucleation and crystal growth in the nanotemplates.

Shear-enhanced crystallization of a thermoplastic polyimide derived from 3,3 ',4,4 '-oxydiphthalic dianhydride and 4,4 '-oxydianiline

The aim of this work is to investigate the effect of consecutive shear on the crystallization of an amorphous aromatic polyimide (PI) derived from 3,3',4,4'oxydiphthalic dianhydride (3,3',4,4'-ODPA) and 4,4-oxydianiline (ODA). At 260 degrees C, the increase of shear rate or shear time leads to the increase of crystallinity. Indeed, increasing shear rate can also accelerate the crystallization behavior. Moreover, it was found that a new melting peak appeared at higher temperature for long time or high rate sheared sample. The enhancement of crystallization behavior appears directly linked to the increase of crystal thickness. Particularly, the effect of shear temperature was investigated, and the results revealed that the crystallization of the PI was more sensitive to shear at 260 degrees C, which was 10 degrees above the glass transition temperature (250 degrees C) of the PI. Possible mechanism was proposed to illustrate the effect of consecutive shear on the crystallization of the PI polymer.

Crystal structures of EtEDTB center dot 1.4C(2)H(5)OH center dot 5H(2)O and H4EtEDTB(ClO4)(4)center dot C2H5OH (EtEDTB=N, N, N ', N '-tetrakis[2-(1-ethylbenzimidazolyl)methyl]-1,2-ethanediamine)

The crystal structures of EtEDTB.1.4C(2)H(5)OH.5H(2)O 1 and H4EtEDTB(ClO4)(4).C2H5OH 2 (EtEDTB = N, N,N',N'-tetrakis[2-(1-ethylbenzimidazolyl)methyl]-1,2-ethanediamine) have been determined by single-crystal X-ray diffraction method. Compound 1 crystallizes in the space group P(1) over bar with a = 11.489(2), b = 11.866(3), c = 12.002(3) Angstrom, alpha = 97.47(2), beta = 114.564(13), gamma = 114.11(2)degrees, V = 1266.6(5) Angstrom(3), Z = 1, M-r = 847.48, D-c = 1.111 g/cm(3), F(000) = 456 and mu(MoKalpha) = 0.076 mm(-1). A total of 5207 reflections were measured for 1, of which 4323 were independent. The structure of 1 was solved by direct methods and refined by full-matrix least-squares technique to the final R = 0.0706 and wR = 0.1802 for 1318 observed reflections with I > 2sigma(I). In the structure of 1, centrosymmetric EtEDTB molecules are linked by hydrogen bonds through water and ethanol to form 2-dimensional network. Compound 2 crystallizes in the space group C2/c with a = 24.260(5), b = 13.040(3), c = 17.680(4) Angstrom, beta = 97.50(3)degrees, V = 5545.2(2) Angstrom(3), Z = 4, M-r = 1140.80, D-c = 1.366 g/cm(3), F(000) = 2384 and mu(MoKalpha) = 0.289 mm(-1).

Multiple morphologies and their transformation of a polystyrene-block-poly(4-vinylpyridine) block copolymer

We report the multiple morphologies and their transformation of polystyrene-block-poly(4-vinylpyridine) (PS-b-P4VP) in low-alkanol solvents. In order to improve the solubility of polystyrene block in alcohol solvents, the solution of block copolymer sample was treated at a higher temperature, and then the influence of rate of decreasing temperature on multiple morphologies (including spheres, rods, vesicles, porous vesicles, large compound vesicles, and large compound micelles) was observed. The transformation of spheres to rods, to tyre-shaped large compound micelles, and to sphere-shaped large compound micelles was also realized. The formation mechanisms of the multiple morphologies and their transformation are discussed briefly.

Field-amplified sample stacking capillary electrophoresis with electrochemiluminescence applied to the determination of illicit drugs on banknotes

Capillary electrophoresis (CE) with Ru(bpy)(3)(2+) electrochemiluminescence. (ECL) detection system was established to the determination of contamination of banknotes with controlled drugs and a high efficiency on-column field-amplified sample stacking (FASS) technique was also optimized to increase the ECL intensity. The method was illustrated using heroin and cocaine, which are two typical and popular illicit drugs. Highest sample stacking was obtained when 0.01 mM acetic acid was chosen for sample dissolution with electrokinetical injection for 6 s at 17 kV. Under the optimized conditions: ECL detection at 1.2 V, separation voltage 10.0 kV, 20 mM phosphate-acetate (pH 7.2) as running buffer, 5 mM Ru(bpy)(3)(2+) with 50 mM phosphate-acetate (pH 7.2) in the detection cell, the standard curves were linear in the range of 7.50 x 10(-8) to 1.00 x 10(-5) M for heroin and 2.50 x 10(-7) to 1.00 x 10(-4) M for cocaine and detection limits of 50 nM for heroin and 60 nM for cocaine were achieved (S/N = 3), respectively. Relative standard derivations of the ECL intensity and the migration time were 3.50 and 0.51% for heroin and 4.44 and 0.12% for cocaine, respectively.The developed method was successfully applied to the determination of heroin and cocaine on illicit drug contaminated banknotes without any damage of the paper currency.

Synthesis, crystal structure, and magnetic properties of {[Cu(oxbe)]Mn(H2O)[Cu(oxbe)(DMF)]}(n)center dot nDMF center dot nH(2)O: From dissymmetrical mononuclear entities to a 3D heterometallic supramolecular coordination polymer

Self-assembly of the building block [Cu(oxbe)](-) with Mn(II) led to a novel coordination polymer {[Cu(oxbe)]Mn(H2O)(Cu(oxbe)(DMF)]}(n).nDMF.nH(2)O, where H(3)oxbe is a new dissymmetrical ligand N-benzoato-N'-(2-aminoethyl)-oxamido and DMF = dimethylformamide. The crystal forms in the triclinic system, space group P(1)over-bar, with a = 9.260(4) angstorm, b = 12.833(5) angstrom, c = 15.274(6) angstrom , alpha = 76.18(3)degrees, beta = 82.7(3)degrees, gamma = 82.31(3)degrees, and Z = 2. The crystal structure of the title complex reveals that the two-dimensional bimetallic layers are constructed of (CuMnII)-Mn-II-Cu-II chains linked together by carboxylate bridge and hydrogen bonds help to produce a novel three-dimensional channel-like structure. The magnetic susceptibility measurements (5-300 K) were analyzed by means of the Hamiltonian (H)over-cap = -2J(S)over-cap (Mn)((S)over-cap(Cu1) + (S)over-cap(Cu2)), leading to J = -17.4 cm(-1).