Synthesis of Cuprates of Perovskite Structure in the Ba-Pb-Cu-O, Ba-Bi-Cu-O, and Ba-Pb-Tl-Cu-O Systems: Possible High Tc Superconductivity in a Perovskite-like Phase in the Ba-Pb-Tl-Cu-O System

Cubic cuprates (a not, vert, similar 18.6 Å) with a BaCuO2-type structure were obtained in the Ba-Pb-Cu-O and Ba-Bi-Cu-O systems by the reaction of the component oxides at a high temperature (1370-1420 K), followed by quenching. By annealing these phases in oxygen at 1070-1120 K, perovskite-like phase (a not, vert, similar 4.3 Å) of the formulae BaPb1-xCuxO3-y and BaBi1-xCuxO3-y (0 < x ? 0.5) were obtained. A perovskite of nominal composition BaPb0.25Tl0.25 Cu0.5O3-y, prepared by a similar procedure, was found to be superconducting with a Tc of not, vert, similar 70 K.

Neutron diffraction study of the coupling between spin, lattice, and structural degrees of freedom in 0.8BiFeO(3)-0.2PbTiO(3)

A powder neutron diffraction study was carried out on 0.8BiFeO(3)-0.2PbTiO(3) in the temperature range 27-1000 degrees C. The system exhibits magnetic transition at similar to 300 degrees C and a rhombohedral (R3c)-cubic (Pm3m) ferroelectric phase transition at similar to 650 degrees C. Anomalous variation in the lattice parameters and the octahedral tilt angle is observed across the magnetic transition temperature. In the magnetic phase, the c parameter is contracted and the octahedral tilt angle is slightly increased. The results suggest coupling between the spin, lattice and structural degrees of freedom. (C) 2011 American Institute of Physics. doi:10.1063/1.3555093]

A transfer matrix approach for evaluation of the response of a multi-layer infinite plate to a two-dimensional pressure excitation

A 6 X 6 transfer matrix is presented to evaluate the response of a multi-layer infinite plate to a given two-dimensional pressure excitation on one of its faces or, alternatively, to evaluate the acoustic pressure distribution excited by the normal velocity components of the radiating surfaces. It is shown that the present transfer matrix is a general case embodying the transfer matrices of normal excitation and one-dimensional pressure excitation due to an oblique incident wave. It is also shown that the present transfer matrix obeys the necessary checks to categorize the physically symmetric multi-layer plate as dynamically symmetric. Expressions are derived to obtain the wave propagation parameters, such as the transmission, absorption and reflection coefficients, in terms of the elements of the transfer matrix presented. Numerical results for transmission loss and reflection coefficients of a two-layer configuration are presented to illustrate the effect of angles of incidence, layer characteristics and ambient media.

Towards the total synthesis of tashironin related allo-cedrane natural products: further exploitation of the oxidative dearomatization-IMDA-RCM triad based strategy

Synthetic studies directed towards allo-cedrane based, tashironin sibling natural products, involving some deft functional group manipulations on a preformed tetracyclic scaffold, are delineated. (C) 2011 Elsevier Ltd. All rights reserved.

Low electric field, easily reversible electrical set and reset processes in a Ge15Te83Si2 glass for phase change memory applications

We report here an easily reversible set-reset process in a new Ge15Te83Si2 glass that could be a promising candidate for phase change random access memory applications. The I-V characteristics of the studied sample show a comparatively low threshold electric field (E-th) of 7.3 kV/cm. Distinct differences in the type of switching behavior are achieved by means of controlling the on state current. It enables the observation of a threshold type for less than 0.7 mA beyond memory type (set) switching. The set and reset processes have been achieved with a similar magnitude of 1 mA, and with a triangular current pulse for the set process and a short duration rectangular pulse of 10 msec width for the reset operation. Further, a self-resetting effect is seen in this material upon excitation with a saw-tooth/square pulse, and their response of leading and trailing edges are discussed. About 6.5 x 10(4) set-reset cycles have been undertaken without any damage to the device. (C) 2011 American Institute of Physics. doi: 10.1063/1.3574659]

Solid Oxide-Ion Electrolytes

Solid oxide-ion electrolytes find application in oxygen sensors, oxygen pumps and in high-temperature electrolyser-fuel-cell hybrid systems. All the solid electrolytes known so Qr, however, exhibit: tow oxide-ion conductivities below 973 K. Therefore, there is a need for fast oxide-ion conductors operative at temperatures around 673 K, Recently, efforts have been directed towards developing such materials. This article summarizes various type of oxide-ton electrolytes reported in literature and outlines a strategy for the identificatiom/synthesis of improved materials.

Non-exponentiality in electron transfer kinetics: Static versus dynamic disorder models

Non-exponential electron transfer kinetics in complex systems are often analyzed in terms of a quenched, static disorder model. In this work we present an alternative analysis in terms of a simple dynamic disorder model where the solvent is characterized by highly non-exponential dynamics. We consider both low and high barrier reactions. For the former, the main result is a simple analytical expression for the survival probability of the reactant. In this case, electron transfer, in the long time, is controlled by the solvent polarization relaxation-in agreement with the analyses of Rips and Jortner and of Nadler and Marcus. The short time dynamics is also non-exponential, but for different reasons. The high barrier reactions, on the other hand, show an interesting dynamic dependence on the electronic coupling element, V-el.

First-principle description of magnonic PdnFem multilayers

Ab-initio calculations are used to determine the parameters that determine magnonic band structure of PdnFem multilayers (n = 2, m <= 8). We obtain the layer-resolved magnetization, the exchange coupling, and the magnetic anisotropy of the Pd-Fe structures. The Fe moment is 3.0 mu(B) close to the Pd layers and 2.2 mu(B) in the middle of the Fe layers. An intriguing but not usually considered aspect is that the elemental Pd is nonmagnetic, similar to Cu spacer layers in other multilayer systems. This leads to a pre-asymptotic ferromagnetic coupling through the Pd (about 40 mJ/m(2)). Furthermore, the Pd acquires a small moment due to spin polarization by neighboring Fe atoms, which translates into magnetic anisotropy. The anisotropies are large, in the range typical for L1(0) structures, which is beneficial for high-frequency applications. (C) 2011 American Institute of Physics. doi:10.1063/1.3556763]

Enhancement of uniaxial magnetic anisotropy in Fe thin films grown on GaAs(001) with an MgO underlayer

The understanding and control of anisotropy in Fe films grown on cubic systems such as GaAs and MgO has been of interest from the point of view of applications in devices. We report magnetic anisotropy studies on Fe/GaAs(001) and Fe/MgO/GaAs(001) prepared by pulsed laser deposition. In Fe/GaAs(001), magneto optical Kerr effect (MOKE) measurements revealed a dominant uniaxial anisotropy for Fe thickness less than 20 monolayers (ML) and this was confirmed by ferromagnetic resonance (FMR) studies. Multiple steps in the hysteresis loops were observed for Fe films of thickness 20 and 25 ML. Whereas, in Fe/MgO/GaAs(001), even at 25 ML of Fe, the uniaxial anisotropy remained dominant. The anisotropy constants obtained from FMR spectra have shown that the relative strength of uniaxial anisotropy is higher as compared to the cubic anisotropy constant in the case of Fe/MgO/GaAs(001). (C) 2011 American Institute of Physics. doi:10.1063/1.3556941]

Influence of the ferromagnetic layer on the pair breaking and low alternating current field magnetic response in superconductor/ferromagnet bilayer

We investigate the influence of the ferromagnetic layer on the magnetic and transport properties of YBa2Cu3O7-delta in YBa2Cu3O7-delta (YBCO)/La0.7Sr0.3MnO3 (LSMO) bilayers. The temperature dependent dc magnetization study reveals the presence of magnetic anisotropy in YBCO/LSMO bilayer as compared to the pure YBCO layer. The ac susceptibility study on YBCO/LSMO bilayers reveals stronger pinning and the temperature dependent critical current is found to be less prone to temperature. Besides, the current (I) dependent electrical transport studies on YBCO/LSMO exhibit a significant reduction in the superconducting T-c with increase in I and it follows I-2/3 dependence in accord with the pair breaking effect. The higher reduction of superconducting T-c in YBCO/LSMO is believed to be due to the enhanced pair-breaking induced by the spin polarized carriers being injected into the superconductor. (C) 2011 American Institute of Physics. doi: 10.1063/1.3560029]

Solvation dynamics of a charge bubble in water

A microscopic theory is used to calculate the solvation-time correlation function, (S(t)), of a light, non-stationary charge bubble in water. The calculated correlation function is found to be similar to the energy-time correlation function of a solvated electron. The ionic mobility of a charge bubble of the size of the hydrated electron is also calculated. It is found that the mobility of the charge plays a very important role in its own solvation.

The effect of aluminosilicate on the delayed onset of upturn voltages of zinc oxide varistor ceramics

The effect of aluminosilicate (Al2SiO5) on the upturn characteristics of ZnO varistor ceramics has been investigated. Addition of Al2SiO5 shifts the point of upturn above 10(4) A cm(-2). The extended nonlinearity in the high current density region is better correlatable to the presence of higher density of trap stales and changing pattern of trap depths at the grain boundary interface as much as the grain interior conductivity. Microstructure studies show the formation and involvement of a liquid phase during sintering. The secondary phases, predominantly are antimony spinel, Zn7Sb2O12, zinc silicate, Zn2SiO4 and magnesium aluminium silicate. MgAl2Si3O10. Energy dispersive X-ray analyses (EDAX) show that Al and Si are distributed more in the grain boundaries and within the secondary phases than in the grain interiors. Capacitance-voltage analyses and dielectric dispersion studies indicate the presence of negative capacitance and associated resonance, indicative of the oscillatory charge redistribution involving increased trapping at the interface states. The admittance spectroscopy data show that the type of trap slates remains unaltered whereas the addition of Al2SiO5 increases the density of low energy traps. (C) 1997 Published by Elsevier Science S.A.

Thermodynamic constraints along isograms in ternary systems: application to three-phase equilibria

Thermodynamic constraints on component chemical potentials in three-phase fields introduced by the various isograms suggested in the literature are derived for a ternary system containing compounds. When compositions of two compounds lie on an isogram, it is associated with specific characteristics which can be used to obtain further understanding of the interplay of thermodynamic factors that determine phase equilibria. When two compounds are shared by adjacent three-phase fields, the constraints are dictated by binary compositions generated by the intersection of a line passing through the shared compounds with the sides of the ternary triangle. Generalized expressions for an arbitrary line through the triangle are presented. These are consistent with special relations obtained along Kohler, Colinet and Jacob isograms. Five axioms are introduced and proved. They provide valuable tools for checking consistency of thermodynamic measurements and for deriving thermodynamic properties from phase diagrams. (C) 1997 Elsevier Science S.A.

Universal behaviour in erosive burning of solid propellants

This paper considers the extensive data and correlations on the erosive burning of solid propellants. A relatively simple nondimensional relationship between the ratio of the actual to nonerosive burn rate (eta) and a quantity g, which is the product of g(0)-the ratio of free stream mass flux to the mass flux from the surface for nonerosive condition-and Re-0(m), where Re-0 is the Reynolds number based on the nonerosive mass flux of the propellant and port diameter, is shown to correlate most data within the accuracies of the experiments with m = -0.125. This shows the above relationship to account for the effects of pressure, aluminum, even up to a proportion of 17%, burn rate catalysts, and motor size. It is concluded that the suggested correlation between eta and g may be adopted universally for most practical propellants. (C) 1997 by The Combustion Institute.