The effects of CO2 addition on the partial oxidation of heptane for hydrogen generation

The effects of CO2 on the partial oxidation of heptane for hydrogen generation have been studied. Based on the experimental results and thermodynamic equilibrium calculations, the validity of CO2 addition to weaken the hot spots, and the feasibility of the autothermal operation are discussed.

Activated carbon supported bimetallic CoMo carbides synthesized by carbothermal hydrogen reduction

A carbothermal hydrogen reduction method was employed for the preparation of activated carbon supported bimetallic carbide. The resultant samples were characterized by BET surface area measurement, X-ray diffraction, and temperature-programmed reduction-mass spectroscopy. The results showed that nanostructured beta-Mo2C can be formed on the activated carbon by carbothermal hydrogen reduction above 700 degreesC. The particle sizes of beta-Mo2C increase with increasing reaction temperatures and Mo loading. The bimetallic CoMo carbide can be synthesized by the carbothermal hydrogen reduction even around 600 degreesC. The bimetallic CoMo carbide is from carbothermal hydrogen reduction of CoMoO4 precursor and is easily formed when the Co/Mo molar ratio is 1.0. Separation of the bimetallic CoMo carbide phase into Mo carbide and Co metal occurs when the temperature of the reduction is above 700 degreesC. The addition of a second metal such as Co and Ni, decreases the formation temperature of carbide because the second metal promotes formation of CHx species from reactive carbon atoms or groups on carbon material and hydrogen, which further carburizes oxide precursors. (C) 2003 Elsevier Science Ltd. All rights reserved.

The synthesis of nanostructured W2C on ultrahigh surface area carbon materials via carbothermal hydrogen reduction

Nanostructured tungsten carbides were synthesized, for the first time, with a size distribution of 5-12 nm on ultrahigh surface area carbon material, by carbothermal hydrogen reduction (CHR) at 850degreesC and metal Ni promoted CHR at 650 degreesC.

Catalytic partial oxidation of n-heptane for hydrogen production

Partial oxidation of n-heptane (POH) for hydrogen generation was studied over several catalysts between 700 and 850degreesC. Modified Ni-based/gamma-Al2O3 catalyst exhibited not only good catalytic activity but also good carbon deposition resistance ability. Under the modified reaction conditions, 100% n-heptane conversion and 93% hydrogen selectivity can be obtained.

The enhancement of TiO2 photocatalytic activity by hydrogen thermal treatment

In this study, conventional TiO2 powder was heated in hydrogen (H-2) gas at a high temperature as pretreatment. The photoactivity of the treated TiO2 samples was evaluated in the photodegradation of sulfosalicylic acid (SSA) in aqueous suspension. The experimental results demonstrated that the photodegradation rates of SSA were significantly enhanced by using the H-2-treated TiO2 catalysts and an optimum temperature for the H-2 treatment was found to be of 500-600 degreesC. The in situ electron paramagnetic resonance (EPR) signal intensity of oxygen vacancies (OV) and trivalent titanium (Ti3+) associated with the photocatalytic activity was studied. The results proved the presence of OV and Ti3+ in the lattice of the H2-treated TiO2 and indicated that both were contributed to the enhancement of photocatalytic activity. Moreover, the experimental results presented that the EPR signal intensity of OV and Ti3+ in the H-2-treated TiO2 samples after 10 months storage was still significant higher than that in the untreated TiO2 catalyst. The experiment also demonstrated that the significant enhancement occurred in the photodegradation of phenol using the H-2-treated TiO2. (C) 2002 Elsevier Science Ltd. All rights reserved.

The experimental research for production of hydrogen from n-octane through partially oxidizing and steam reforming method

The reaction of producing hydrogen for fuel cell which used normal octane as gasoline or diesel oil reactant through catalytic partial oxidizing and steam reforming method has been researched in the fixed-bed reactor. A series of catalysts that mainly used nickel supported on Al2O3 have been studied. It showed that the activity of the catalyst was increased with the content of nickel by using only nickel supported on Al2O3. However, its activity was not obviously increased when the content of nickel was over 5 wt%. The conversion ratio of normal octane and hydrogen selectivity were higher at higher reaction temperature. The single noble catalyst of palladium had better stability compared with that of platinum catalyst although their activity and selectivity were similar during the experimental reaction temperature. The prepared bimetallic catalyst consisted mainly of nickel and little noble metal of palladium supported on Al2O3. It showed that this catalyst had higher activity and selectivity, especially at lower or higher reaction temperatures compared with single nickel or palladium catalyst, and better stability. ((C) 2001 International Association for Hydrogen Energy. Published by Elsevier Science Ltd. All rights reserved.

Structure and electrochemical characteristics of melted composite Ti0.10Zr0.15V0.35Cr0.10Ni0.30-LaNi5 hydrogen storage alloys

The structure and electrochemical characteristics of melted composite Ti0.10Zr0.15V0.35Cr0.10Ni0.30+x% LaNi5 (x=0, 1, 5 and 10) hydrogen storage alloys have been investigated systematically. XRD shows that the matrix phase structure of V-based solid solution phase with a BCC structure and C14 Laves phase with hexagonal structure is not changed after adding LaNi5 alloy. However, the amount of the secondary phase increases with increasing LaNi5 content. Field emission scanning electron microscopy-energy dispersive spectroscopy (FESEM-EDS) shows that the C14 Laves phase contains more Zr and the white lard phase has a composition close to (Zr, Ti)(V, Cr, Ni, La)(2).

Structures and electrochemical characteristics of Ti0.26Zr0.07V0.24Mn0.1Ni0.33Mox (x=0-0.1) hydrogen storage alloys

Microstructures and electrochemical properties of Ti0.26Zr0.07V0.21Mn0.1Ni0.33Mox (x=0,0.025,0.05,0.075, 0.10) electrode alloys have been investigated. The results of XRD analysis show that the alloys are mainly composed of V-based solid solution phase with body centered cubic (bcc) structure and C14 Laves phase with hexagonal structure. The addition of Mo element can imp ove the activation characteristics, maximum discharge capacity and cyclic durability for the electrode alloys

Hydrogen peroxide biosensor based on horseradish peroxidase-Au nanoparticles at viologen grafted glassy carbon electrode

A novel hydrogen peroxide biosensor was fabricated that is based on horseradish peroxidase-Au nanoparticles immobilized on a viologen-modified glassy carbon electrode (GCE) by amino cation radical oxidation in basic solution. The immobilized BAPV acts as a mediator and a covalent linker between GCE and the Au nanoparticles. The biosensor exhibited fast response, good reproducibility, and long-term stability.