Influence of milling time on mechanically assisted synthesis of Pb0.91Ca0.1TiO3 powders

Pb0.91Ca0.1TiO3 powders (PCT) were prepared by mechanochemical synthesis from high-energy ball milling process. The influence of milling time on the phase formation, crystal structure, specific surface area, density and powder morphology was observed. We adopted the Rietveld refinement technique to investigate the crystal structure of the PCT powders. Scanning electron microscopy (SEM) analysis revealed that PCT powders milled for 5 h showed a wide distribution of particle agglomerates while milled for 35 h showed a decrease in agglomerates size. Further prolongation of milling time resulted in the agglomerates growth. (C) 2006 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Thermogravimetric investigations during the synthesis of silica-based MCM-41

MCM-41 material was synthesized starting from hydrogel containing colloidal fumed silica, sodium silicate, cetyltetramethylammonium bromide (CTMABr) as surfactant, and distilled water as solvent. These reactants were mixed to obtain a gel with the following composition: 4SiO(2):1Na(2)O:1CTMABr:200H(2)O. The hydrogel with pH=14 was hydrothermally treated at 100 degreesC, for 4 days. Each day, the pH was measured, and then adjusted to 9.5-10 by using 30% acetic acid solution. Thermogravimetry was the main technique, which was used to monitor the participation of the surfactant on the MCM-41 nanophase, being possible to determine the temperature ranges relative to water desorption as well as the surfactant decomposition and silanol condensation.

Correlation between the mobility of spin-labeled peptide chains and resin solvation: An approach to optimize the synthesis of aggregating sequences

Resin solvation properties affect the efficiency of the coupling reactions in solid-phase peptide synthesis. Here we report a novel approach to evaluate resin solvation properties, making use of spin label electron paramagnetic resonance (EPR) spectroscopy. The aggregating VVLGAAIV and ING sequences were assembled in benzhydrylamine-resin with different amino group contents (up to 2.6 mmol/g) to examine the extent of chain association within the beads. These model peptidyl-resins were first labeled at their N-terminus with the amino acid spin label 2,2,6,6-tetramethylpiperidine-N-oxyl-4-amino-4-carboxylic acid (Toac). Their solvation properties in different solvents were estimated, either by bead swelling measurement or by assessing the dynamics of their polymeric matrixes through the analysis of Toac EPR spectra, and were correlated with the yield of the acylation reaction. In most cases the coupling rate was found to depend on bead swelling. Comparatively, the EPR approach was more effective. Line shape analysis allowed the detection of more than one peptide chain population, which influenced the reaction. The results demonstrated the unique potential of EPR spectroscopy not only for improving the yield of peptide synthesis, even in challenging conditions, but also for other relevant polymer-supported methodologies in chemistry and biology.

Stereoselective synthesis of 8,9-licarinediols

The total synthesis of 8,9-licarinediols was selectively carried out from licarin A, previously obtained by oxidative coupling of (E)-isoeugenol. The corresponding enantiomerically pure (+)- and(-)-licarin A ester derivatives were subjected to Sharpless oxidation to yield the asymmetric C-8, C-9 dihydroxylation products, whose absolute configurations were established by means of the CD and NMR spectroscopic analyses of their Mosher ester derivatives. (C) 2000 Elsevier B.V. Ltd. All rights reserved.

mer-[RuCl3(P-P)H2O] (P-P=dppb or diop) as a starting material for the synthesis of binuclear complexes. Crystallographic structures of [(dppb)ClRu-mu(Cl)(3)-RuCl(dppb)] and [(eta(6)-C6H6)Ru-mu(Cl)(3)-RuCl(dppb)]. Imine hydrogenation using mono- and binuclear ruthenium complexes

The reactivity of the mer-[RuCl3(dppb)H2O] complex (1) with di-hydrogen shows that the products formed depend on the conditions of the reaction, i.e., solvents and presence or absence of a base. The new mixed-valence complexes [(diop)ClRu-(h-Cl)(3)-RuCl(dppb)] (3), [(binap)CIRu-(p-Cl)(3)-RuCl(dppb)] (4), [(PPh3)(2)ClRu-(mu-Cl)(3)-RuCl(dppb)] (6), [(dppn)ClRu-(mu-Cl)(3)-RuCl(dppb)] (7), [(P-ptol(3))(2)ClRu-(mu-Cl)(3)-RuCl(dppb)] (8), [(SbPh3)(2)ClRu-(mu-Cl)(3)-RuCl(dppb)] (9), [(eta(6)-C6H6)Ru-(mu-Cl)(3)-RuCl(dppb)] (11) and the known mixed-valence [(dppb)CIRu-(mu-Cl)(3)-RuCl(dppb)] (5) and [(diop)ClRu-(mu-Cl)(3)-RuCl(diop)] (10) were synthesized from complexes (1) or (2) using a methodology developed in our research group. The known complexes [(dppb)ClRu-(mu-Cl)(2)-RuCl(dppb)] (12), [(dppb)(CO)Ru-(mu-Cl)(3)-RuCl(dppb)] (13) and [H2NEt2][(dppb)ClRu-(mu-Cl)(3)-RuCl(dppb)] (14) were synthesized by changing the reaction conditions between mer-[RuCl3(dppb)H2O] (1) and dihydrogen. The crystal structures of (5) and (11) were determined by single-crystal X-ray diffraction. Some of the complexes described here are effective pre-catalysts for the hydrogenation of imines. Preliminary results on the homogeneous hydrogenation of the imines Ph-CH2-N=CH-Ph and Ph-N=CH-Ph are presented. (C) 2004 Elsevier Ltd. All rights reserved.

Synthesis of hybrid silicates containing porphyrins incorporated by a sol-gel process and their properties

Porphyrin was incorporated in a silicate network, via a covalent bond, by grafting a functional group with 3-aminopropyltriethoxysilane, using a sol-gel process. We have carried out the synthesis and measured the absorption spectra, nuclear magnetic resonance spectra, infrared (IR) spectra, luminescence spectra and lifetime of these hybrid silicates, porphyrinosilicas. These samples contained the following free-base porphyrins: meso-tetrakis-p-chlorobenzoylporphyrin, meso-tetrakis-2,6-dichloro-3-chlorosulfonylphenylporphyrin. The obtained porphyrinosilicas have similar absorption and luminescence spectra to the free base porphyrins in solution. IR spectra confirm the formation of monomeric species. Lifetime measurement for porphyrinosilica reveals that 32% +/- 2% of porphyrin is covalently bonded to the silica network. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Comparative investigation of the cleavage step in the synthesis of model peptide resins: Implications for N-alpha-9-fluorenylmethyloxycarbonyl-solid phase peptide synthesis

Based on our studies of the stability of model peptide-resin linkage in acid media, we previously proposed a rule for resin selection and a final cleavage protocol applicable to the N-alpha-tert-butyloxycarbonyl (Boc)-peptide synthesis strategy. We found that incorrect choices resulted in decreases in the final synthesis yield, which is highly dependent on the peptide sequence, of as high as 30%. The present paper continues along this line of research but examines the N-alpha-9-fluorenylmethyloxycarbonyl (Fmoc)-synthesis strategy. The vasoactive peptide angiotensin II (All, DRVYIHPF) and its [Gly(8)]-All analogue were selected as model peptide resins. Variations in parameters such as the type of spacer group (linker) between the peptide backbone and the resin, as well as in the final acid cleavage protocol, were evaluated. The same methodology employed for the Boc strategy was used in order to establish rules for selection of the most appropriate linker-resin conjugate or of the peptide cleavage method, depending on the sequence to be assembled. The results obtained after treatment with four cleavage solutions and with four types of linker groups indicate that, irrespective of the circumstance, it is not possible to achieve complete removal of the peptide chains from the resin. Moreover, the Phe-attaching peptide at the C-terminal yielded far less cleavage (50-60%.) than that observed with the Gly-bearing sequences at the same position (70-90%). Lastly, the fastest cleavage occurred with reagent K acid treatment and when the peptide was attached to the Wang resin.

Synthesis of SnO2 by chemical routes and its use in varistors production

Tin oxide, SnO2. is a very used compound in industry and one of its uses is as varistor. For the current requirements of the technology is necessary a strict control of the chemical purity and the particle size of the raw material; for that reason the great interest that exists at the moment to develop synthesis methods that allow to get these requirements. In this work, ceramic powders of the Sn-Co-Nb-Ti-Al system using the controlled precipitation and polymeric precursor (Pechini) methods were synthesized. The raw material obtained was characterized using X-ray diffraction (XRD), thermal analysis (DTA/FG) and scanning electron microscopy (SEM). The sintering samples shown a good varistor behavior with non-linear coefficient (alpha) values similar to 22, and Er 2083 V/cm(2). (c) 2007 Elsevier Ltd. All rights reserved.

Microwave synthesis of YAG : Eu by sol-gel methodology

Yttrium-aluminum oxides are interesting compounds and they have been extensively used as host for lasers and phosphors, due to their stable physical and chemical properties. The fabrication of yttrium-aluminum garnet (YAG) has been investigated thoroughly. Single-crystal YAG is expensive and to produce it a new way has been investigated. This process consists of modifying the methodology of reagents mixture and the process of heating them. The microwave irradiation is used to heat-treat the oxide mixture. The traditional synthesis of YAG powders occurs through the reaction of aluminum and yttrium powders at high temperatures. With this work we investigated the preparation of YAG by non-hydrolytic sol-gel route as an alternative methodology to obtain yttrium-aluminum matrix from inorganic precursors (yttrium and aluminum chloride). The preparation of the gel was carried out in an oven-dried glassware. The AlCl3, YCl3 and ethanol were reacted in reflux under argon atmosphere. Europium III chloride was added as a structural probe. The powder was dried and heat-treated in modified microwaves. The samples were pre-treated at 50 and 800 C during I h and then heated in microwaves for 30 s, 2 and 4 min. The formation process and structure of the powders were studied by means of X-ray diffraction (XRD), photoluminescence (PL) and transmission electronic microscopy (TEM). XRD presents only picks corresponding to the YAG phase and confirmed by TEM. PL date showed that the YAG phase was formed in 2 min with the samples pre-treated at 50 C. For the samples pretreated at 800 degrees C, the YAG phase appears in 30s. The excitation spectra present a maximum of 394 nm corresponding to the L-5(6) level and emission spectra of Eu III ion present bands characteristic transitions arising from the D-5(0) -> F-7(J) (J= 1, 2, 3, 4) monifolds excited at their maximum. The magnetic dipole D-5(0) -> F-7(1) transition presents more intensity than the electric dipole D-5(0) -> F-7(2) transition. This methodology showed efficiency in obtaining YAG phase. (c) 2006 Elsevier B.V. All rights reserved.

An efficient and versatile synthesis of acylpolyamine spider toxins

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

pH at the micellar interface: Synthesis of pH probes derived from salicylic acid, acid-base dissociation in sodium dodecyl sulfate micelles, and Poisson-Boltzmann simulation

The study of the H+ concentration at the micellar interface is a convenient system for modeling the distribution of H+ at interfaces. We have synthesized salicylic acid derivatives to analyze the proton dissociation of both the carboxylic and phenol groups of' the probes, determining spectrophotometrically the apparent pK(a)'s (pK(ap)) in sodium dodecyl Sulfate, SDS, micelles with and without added salt. The synthesized probes were 2-hydroxy-5-(2-trimethylammoniumacetyl)benzoate; 2-hydroxy-5-(2-dimethylhexadecylammoniumacetyl)benzoate- 2-hydroxy-5-(2-dimethylhexadecylammoniumhexanoyl)benzoate-, 2-hydroxy-5-(2-diniethylhexadecylammoniumundecanoyl)betizoate; 2-hydroxy-5-acetylbenzoic acids and 2-hydroxy-5-dodecanoylbenzoic acid. Upon incorporation into SDS micelles the pK(ap)'s of both carboxylic and phenol groups increased by ca. 3 pH units and NaCl addition caused a decrease in the probe-incorporated pKap. The experimental results were fitted with a cell model Poisson-Boltzmann (P-B) equation taking in consideration the effect of salt on the aggregation number of SDS and using the distance of' the dissociating group as a parameter. The conformations of the probes were analyzed theoretically using two dielectric constants, e.g., 2 and 78. Both the P-B analysis and conformation calculations can be interpreted by assuming that the acid groups dissociate very close to, or at, the interface. Our results are consistent with the assumption that the intrinsic pK(a)'s of both carboxylic and phenol groups of the salicylic acid probes used here can be taken as those in water. Using this assumption the micellar and salt effects on the pKap's of the (trialkylammonium)benzoate probes were described accurately using a cell model P-B analysis. (c) 2005 Elsevier B.V. All rights reserved.

Nanoparticle synthesis of La1-xSrxMnO3 (0.1, 0.2 and 0.3) perovskites

Synthesis of La1-xSrxMnO3 (x = 0.1, 0.2 and 0.3) by homogenous coprecipitation method using urea as precipitant agent Is reported. The particles are smaller than 200 nm after heating at 950 degreesC. Temperature dependence of the electrical resistivity was found to be similar to the reported value for single crystals of these manganites.

Wet-chemical synthesis of magnesium niobate nanoparticles powders

Nanosized and highly reactive magnesium mobate (MgNb2O6) powders were successfully synthesized by a new wet-chemical method by means of the dissolution of Nb2O5 center dot 5H(2)O and in a solution of oxalic acid followed by the addition of stoichiometric amounts of magnesium carbonate. The Nb-Mg-oxalic acid solution was evaporated resulting in a dry and amorphous powder that was calcined in the temperature range from 200 to 900 degrees C for 2 h. The crystallization process from the amorphous state to the crystalline MgNb2O6 was followed by thermal analysis. The calcined powders characterized by FT-Raman spectroscopy, X-ray diffraction (XRD) and their morphology examined by high resolution scanning electron microscopy (HR-SEM). Pure MgNb2O6, free from the second phases and obtained at 800 degrees C was confirmed by a combined analysis using XRD and FT-Raman. The average diameter of the particles was calculated from the HR-SEM image as 70 urn approximately. This technique allows a better mixing of the constituent elements and thus a better reactivity of the mixture to obtain pre-reaction products with high purity at lower temperatures and reducing cost. It can offer a great advantage in the PMN-PT formation with respect to the solid-state synthesis. (c) 2006 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Mechanochemical synthesis of barium titanate

A powder mixture of BaO and TiO2, was mechanochemically treated in a planetary ball mill in an air atmosphere for up to 4 h, using zirconium oxide vial and zirconium oxide balls as the milling medium. Mechanochemical reaction leads to the gradual formation of BaTiO3 phase. Phase evolution during synthesis and changes in powder size and morphology were monitored by XRD, DSC, IR and TEM analysis and it was shown that the formation of BaTiO3 phase was initiated after 60 min. Extended time of milling directed to formation of higher amount of BaTiO3 perovskite phase. Barium titanate with good crystallinity was formed after 240 min sintering without pre-calcination step was performed at 1330 degrees C for 2 It within heating rate 10 degrees C/min. (c) 2005 Elsevier Ltd. All rights reserved.

Mechanochemical synthesis of PZT powders

PZT ceramic powders were successfully prepared from the mixture of PbO, ZrO2 and TiO2 by mechanochemical synthesis in a planetary ball mill, under different milling conditions. Phase evolution during synthesis was monitored by X-ray diffraction analysis. Intensive milling resulted in formation of the nanocrystalline, perovskite PZT powders after 1 h of milling. This is a significant improvement in comparison to milling conditions reported by other authors. Depending on milling parameters the presence of some other phases, such as unreacted ZrO2, was also detected in some samples. The changes in powder size and morphology due to intensive milling, were determined by SEM and TEM, while BET analysis was used to determine specific surface area of the powders. Conclusions about processes taking place during mechanochemical synthesis of PZT powders were made based on the results of characterization. (C) 2002 Elsevier B.V. B.V. All rights reserved.