Effects of a postweld heat treatment on a submerged arc welded ASTM A537 pressure vessel steel

Postweld heat treatment (PWHT) is frequently applied to steel pressure vessels, following the requirements of the ASME code (section VIII), which establishes the parameters of the PWHT based on the thickness and chemical composition of the welded section. This work shows the results of an analysis undertaken on a sample of ASTM A537 C1 steel subjected to qualifying welding procedure tests including PWHT (650 degreesC/5 h), the results obtained showed that this PWHT practice promoted a reduction in the mechanical properties of the base metal and the heat-affected zone (HAZ).

Electrochemical behavior of cobalt oxide coatings on cold-rolled steel in alkaline sodium sulfate

The electrochemical behavior of a coating of cobalt oxide on cold-rolled steel in alkaline sodium sulfate was Studied using the electrochemical techniques of open-circuit potential measurements and electrochemical impedance spectroscopy. The coating was prepared at different annealing temperatures ranging from 350 to 750 degreesC and characterized by SEM, EDX and XRD. Below 550 degreesC the composition of the coating was basically of Co3O4. At 750 degreesC CoO was formed and big cracks appeared on the film exposing an inner layer of iron oxides. Analysis of the EIS data is very difficult because of the complexity of the interface structure. It can be inferred that the charge transfer resistance of the coatings prepared at 350 and 450 C were higher than those for the coatings prepared at temperatures above 550 degreesC. (C) 2002 Published by Elsevier B.V. Ltd.

Effects of milling condition on the surface integrity of hot forged steel

This paper presents a study on the influence of milling condition on workpiece surface integrity focusing on hardness and roughness. The experimental work was carried out on a CNC machining center considering roughing and finishing operations. A 25 mm diameter endmill with two cemented carbide inserts coated with TiN layer were used for end milling operation. Low carbon alloyed steel Cr-Mo forged at 1200 degrees C was used as workpiece on the tests. Two kinds of workpiece conditions were considered, i.e. cur cooled after hot forging and normalized at 950 degrees C for 2 h. The results showed that finishing operation was able to significantly decrease the roughness by at least 46% without changing the hardness. on the other hand, roughing operation caused an increase in hardness statistically significant by about 6%. The machined surface presented deformed regions within feed marks, which directly affected the roughness. Surface finish behavior seems to correlate to the chip ratio given the decrease of 25% for roughing condition, which damaged the chip formation. The material removal rate for finishing operation 41% greater than roughing condition demonstrated to be favorable to the heat dissipation and minimized the effect on material hardness.

SAE 1045 steel/WC-Co/Ni-Cu-Ni/SAE 1045 steel joints prepared by dynamic diffusion bonding: Microelectrochemical studies in 0.6 M NaCl solution

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Corrosion protection of stainless steel by polysiloxane hybrid coatings prepared using the sol-gel process

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

The minimum quantity of lubricant (MQL) technique in the surface grinding of steel

This research aimed to analyze the viability of the minimum quantity of lubricant (MQL) technique towards different methods of lubri-refrigeration in surface grinding of steel, considering process quality, wheel life and the viability of using cutting fluids The proposal methods were the conventional (abundant fluid flow), the minimum quantity lubrication (MQL) and the optimized method with Webster nozzle (rounded) This analysis was carried out in equal machining conditions, through the assessment of variables such as grinding force, surface roughness, G ratio (volume of removed material/volume of wheel wear), and microhardness The results showed the possibility of improvement of the grinding process Besides, there is the opportunity for production of high quality workpieces with lower costs The MQL technique showed efficiency in machining with lower depths of cut The optimized method with Webster nozzle applies the fluid in a rational way, without considerable waste Hence, the results show that industry can rationalize and optimize the application of cutting fluids, avoiding inappropriate disposal, inadequate use and consequently environment pollution

Selective UV-filter detection with sensors based on stainless steel electrodes modified with polyaniline doped with metal tetrasulfonated phthalocyanine films

This work describes the construction and application of two amperometric sensors for sensitive UV-filter determination. The sensors were prepared using stainless steel electrodes in which polyaniline (PANI) was electrochemically polymerized in the presence of nickel (NiPcTS) or iron (FePcTS) tetrasulfonated phthalocyanines. The sensor surface characterizations were carried out using atomic force microscopy (AFM). The PANI/NiPcTS sensor was selective for the chemical UV-filter p-aminobenzoic acid (PABA) and the PANI/FePcTS sensor was selective for octyldimethyl-PABA (ODP), both in a mixture of tetrahydrofuran (THF) and 0.1 mol L(-1) H(2)SO(4) at a volume ratio of 30 : 70, and with an applied potential of 0.0 mV vs. Ag vertical bar AgCl. A detailed investigation of the selectivity was carried out for both sensors, in order to determine their responses for ten different UV filters. Finally, each sensor was successfully applied to PABA or ODP quantification in sunscreen formulations and water from swimming pools.

Photoelastic analysis of forces generated by T-loop springs made with stainless steel or titanium-molybdenum alloy

Introduction: The purpose of this study was to use photoelastic analysis to compare the system of forces generated by retraction T-loop springs made with stainless steel and titanium-molybdenum alloy (TMA) (Ormco, Glendora, Calif) with photoelastic analysis. Methods: Three photoelastic models were used to evaluate retraction T-loop springs with the same preactivations in 2 groups. In group 1, the loop was constructed with a stainless steel wire, and 2 helicoids were incorporated on top of the T-loop; in group 2, it was made with TMA and no helicoids. Results: Upon using the qualitative analysis of the fringe order in the photoelastic model, it was observed that the magnitude of force generated by the springs in group 1 was significantly higher than that in group 2. However, both had symmetry for the active and reactive units related to the system of force. Conclusions: Both springs had the same mechanical characteristics. TMA springs showed lower force levels. (Am J Orthod Dentofacial Orthop 2011;140:e123-e128)

Evaluation of 316L Stainless Steel Corrosion Resistance in Solution Simulating the Acid Hydrolysis of Biomass

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Optimization procedures in the design of continuous induction hardening and tempering installations for magnetic steel bars

An inverse problem concerning the industrial process of steel bars hardening and tempering is considered. The associated optimization problem is formulated in terms of membership functions and, for the sake of comparison, also in terms of quadratic residuals; both geometric and electromagnetic design variables have been considered. The numerical solution is achieved by coupling a finite difference procedure for the calculation of the electromagnetic and thermal fields to a deterministic strategy of minimization based on modified Flctcher and Reeves method. © 1998 IEEE.

A comparison of molar root canal preparation using stainless-steel and nickel-titanium instruments

Fifty-four extracted human mandibular molars were embedded and sectioned at two levels. The reassembled mesial root canals were prepared with stainless-steel hand K-files (Flexofiles) and either Nitiflex or Mity nickel-titanium hand K-files using a push-pull anticurvature filing technique. Each of the three experimental groups contained 36 mesial canals randomly distributed. Superimposed pre- and postinstrumentation cross-sectional root images were magnified using a stereomicroscope and transferred to a computer for measurement and statistical analysis. The direction and extent of canal center movement were evaluated. At the apical level, the groups produced no significant difference of direction of canal center movement. In cervical sections, all groups tended to move in a distolingual direction. The three groups, however, produced no significant difference in the cervical sections in the extent of canal center movement. In apical sections, Nitiflex produced the least canal center movement. Copyright © 1999 by The American Association of Endodontists.

Key features of alumina/magnesia/graphite refractories for steel ladle lining

The corrosion resistance of resin bonded alumina/magnesia/graphite refractories containing different kinds of aggregates were investigated when submitted to the action of slags of several CaO/SiO2 ratios. The laboratory testing was performed by means of the rotary slag attack test. Specifically evaluated was the influence of alumina/carbon ratio and magnesia and silica contents on the refractories corrosion resistance. It was found that this property could be improved by increasing the refractory Al2O3/SiO2 ratio as well as by choosing the appropriate Al2O3/C ratio. © 2000 Elsevier Science Ltd.

Sand-water slurry erosion of API 5L X65 pipe steel as quenched from intercritical temperature

The objective of this study was to analyze the erosion of API 5L X65 pipe steel whose microstructure consisted of ferrite and martensite obtained by quenching from intercritical temperature (770 °C). Jet impingement tests with sand-water slurry were used. The changes in mechanical properties, caused by heat treatment carried out, did not induce changes in either the mechanism or erosion resistance. The erosion rate increased with angle of attack until 30° and later decreased until 90°. The microtexture of the eroded surfaces, at angles of attack of 30° and 90°, were similar for both conditions and were composed of craters and platelets at several stages of evolution. The erosion mechanism was by extrusion with the forming and forging of platelets.

A theoretical and experimental analysis of cold-formed steel shapes subjected to bending - Channel and simple lipped channel

Cold-formed steel shapes have been widely employed in steel construction, where they frequently offer a lower cost solution than do traditional laminated shapes. A classic application of cold-formed steel shapes is purlins in the roof panel of industrial buildings, connected to the roof panel by means of screws. The combined effect of these two elements has been the subject of investigations in some countries. Design criteria were included in the AISI Code in 1991 and 1996. This paper presents and discusses the results obtained from bending tests carried out on shapes commonly used in Brazil, i.e., the channel and the simple lipped channel, Tests were carried out on double shapes with 4.5 and 6.0 meter spans, which were subjected to concentrated loads and braced against each other on the supports and at intermediary points in three different load situations. The panel shape was also analyzed experimentally, simulating the action of wind by means of a vacuum box designed specifically for this purpose. The test results were then compared to those obtained through the theoretical analysis, enabling us to extract important information upon which to base proposed design criteria for the new Brazilian code.