Photoluminescence of core-shell nanoparticles made from yttrium stabilized zirconia powder grain coated with alumina

A YSZ@Al2O3 nanocomposite was obtained by Al2O3 coating on the surface of yttrium stabilized zirconia via a polymeric precursor method. The resulting core–shell structures were characterized by X-ray diffraction, scanning electron microscopy, transmission electronic microscopy and PL spectra. The TEM micrographs clearly show a homogeneous Al2O3 shell around the ZrO2 core. The observed PL is related to surface–interface defects. Such novel technologies can, in principle, explore materials which are not available in the bulk single crystal form but their figure-of-merit is dramatically dependent on the surface–interface defect states.

The grain-scale distribution and behaviour of melt and fluid in crystalline analogue systems

The production, segregation and migration of melt and aqueous fluids (henceforth called liquid) plays an important role for the transport of mass and energy within the mantle and the crust of the Earth. Many properties of large-scale liquid migration processes such as the permeability of a rock matrix or the initial segregation of newly formed liquid from the host-rock depends on the grain-scale distribution and behaviour of liquid. Although the general mechanisms of liquid distribution at the grain-scale are well understood, the influence of possibly important modifying processes such as static recrystallization, deformation, and chemical disequilibrium on the liquid distribution is not well constrained. For this thesis analogue experiments were used that allowed to investigate the interplay of these different mechanisms in-situ. In high-temperature environments where melts are produced, the grain-scale distribution in “equilibrium” is fully determined by the liquid fraction and the ratio between the solid-solid and the solid-liquid surface energy. The latter is commonly expressed as the dihedral or wetting angle between two grains and the liquid phase (Chapter 2). The interplay of this “equilibrium” liquid distribution with ongoing surface energy driven recrystallization is investigated in Chapter 4 and 5 with experiments using norcamphor plus ethanol liquid. Ethanol in contact with norcamphor forms a wetting angle of about 25°, which is similar to reported angles of rock-forming minerals in contact with silicate melt. The experiments in Chapter 4 show that previously reported disequilibrium features such as trapped liquid lenses, fully-wetted grain boundaries, and large liquid pockets can be explained by the interplay of the liquid with ongoing recrystallization. Closer inspection of dihedral angles in Chapter 5 reveals that the wetting angles are themselves modified by grain coarsening. Ongoing recrystallization constantly moves liquid-filled triple junctions, thereby altering the wetting angles dynamically as a function of the triple junction velocity. A polycrystalline aggregate will therefore always display a range of equilibrium and dynamic wetting angles at raised temperature, rather than a single wetting angle as previously thought. For the deformation experiments partially molten KNO3–LiNO3 experiments were used in addition to norcamphor–ethanol experiments (Chapter 6). Three deformation regimes were observed. At a high bulk liquid fraction >10 vol.% the aggregate deformed by compaction and granular flow. At a “moderate” liquid fraction, the aggregate deformed mainly by grain boundary sliding (GBS) that was localized into conjugate shear zones. At a low liquid fraction, the grains of the aggregate formed a supporting framework that deformed internally by crystal plastic deformation or diffusion creep. Liquid segregation was most efficient during framework deformation, while GBS lead to slow liquid segregation or even liquid dispersion in the deforming areas.

I materiali ceramici trasparenti: preparazione, caratterizzazione e correlazione microstruttura-proprietà

This thesis focuses on the ceramic process for the production of optical grade transparent materials to be used as laser hosts. In order to be transparent a ceramic material must exhibit a very low concentration of defects. Defects are mainly represented by secondary or grain boundary phases and by residual pores. The strict control of the stoichiometry is mandatory to avoid the formation of secondary phases, whereas residual pores need to be below 150 ppm. In order to fulfill these requirements specific experimental conditions must be combined together. In addition powders need to be nanometric or at least sub-micrometric and extremely pure. On the other hand, nanometric powders aggregate easily and this leads to a poor, not homogeneous packing during shaping by pressing and to the formation of residual pores during sintering. Very fine powders are also difficult to handle and tend to absorb water on the surface. Finally, the powder manipulation (weighting operations, solvent removal, spray drying, shaping, etc), easily introduces impurities. All these features must be fully controlled in order to avoid the formation of defects that work as scattering sources thus decreasing the transparency of the material. The important role played by the processing on the transparency of ceramic materials is often underestimated. In the literature a high level of transparency has been reported by many authors but the description of the experimental process, in particular of the powder treatment and shaping, is seldom extensively described and important information that are necessary to reproduce the described results are often missing. The main goal of the present study therefore is to give additional information on the way the experimental features affect the microstructural evolution of YAG-based ceramics and thus the final properties, in particular transparency. Commercial powders are used to prepare YAG materials doped with Nd or Yb by reactive sintering under high vacuum. These dopants have been selected as the more appropriate for high energy and high peak power lasers. As far as it concerns the powder treatment, the thesis focuses on the influence of the solvent removal technique (rotavapor versus spray drying of suspensions in ethanol), the ball milling duration and speed, suspension concentration, solvent ratio, type and amount of dispersant. The influence of the powder type and process on the powder packing as well as the pressure conditions during shaping by pressing are also described. Finally calcination, sintering under high vacuum and in clean atmosphere, and post sintering cycles are studied and related to the final microstructure analyzed by SEM-EDS and HR-TEM, and to the optical and laser properties.

Microincapsulazione di nanoparticelle di argento tramite tecnica spray-freeze-drying

Per limitare gli effetti tossici delle Ag-NPs, si è pensato che esse possano essere utilizzate in forma di microincapsulati, in quanto le microcapsule possono avere una certa velocità di rilascio sotto specifiche condizioni. Incapsulando quindi le Ag-NPs, posso ottenere un rilascio controllato di esse, in modo da ottenere una concentrazione di esse utile allo scopo per cui vengono impiegate, evitando un sovradosaggio che non porterebbe alcun beneficio ma solo a una maggior probabilità di causare effetti tossici.

Hydraulic sustainability of soil-bentonite cutoff walls subjected to cyclic wetting and drying

This study investigated the effect of cyclic wetting and drying on the backfill used in soil-bentonite (SB) cutoff walls. For this purpose, model SB vertical cutoff wall backfills were prepared comprising of a fine grained mortar sand and 2% bentonite (by total weight) and 4% bentonite (by total weight). Results of the study indicate that the volume change is influenced by the bentonite content, that is, the increase in volume change increased with increasing bentonite content.