Comparative Histopathological Analysis of Human Pulps after Class I Cavity Preparation with a High-Speed Air-Turbine Handpiece or Er:YAG Laser

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Microtensile bond strength of different adhesive systems in dentin irradiated with Er : YAG laser

The objective this study was to evaluate in vitro the bond strength of two etch-and-rise and one self-etching adhesive system after dentin irradiation with Er:YAG (erbium: yttrium aluminum garnet) laser using microtensile test. The results revealed that the groups treated with laser Er:YAG presented less tensile bond strength, independently to the adhesive system used. The prompt L-pop adhesive presented less microtensile bond strength compared to the other adhesives evaluated. There was no difference between single bond and excite groups. The adhesive failures were predominant in all the experimental groups. The Er:YAG laser influenced negatively bond strength values of adhesive systems tested in dental substrate.

Diffusion analysis of one photosensitizer in bovine teeth using fluorescence optical imaging

Some photosensitizers (PSs) used for PACT (Antimicrobial Photodynamic Therapy) show an affinity for bacterial walls and can be photo-activated to cause the desired damage. However, on dentine bacterias may be less susceptible to PACT as a result of limited penetration of the PS. The aim of this study was to evaluate the diffusion of one PS based on hematoporphyrin on dentine structures. Twelve bovine incisors were used. Class III cavities (3 x 3 x 1 mm) were prepared on the mesial or distal surfaces using a diamond bur. Photogem (R) solution at 1 mg/mL (10 uL for each cavity) was used. The experimental Groups were divided according to thickness of dentine remaining and etched or no-etched before the PS application. The fluorescence excitation source was a VelScope (R) system. For image capture a scientific CCD color camera PixelFly (R) was coupled to VelScope. For image acquisition and processing, a computational routine was developed at Matlab (R). Fick's Law was used to obtain the average diffusion coefficient of PS. Differences were found between all Groups. The longitudinal temporal diffusion was influenced by the different times, thickness and acid etching.

Effect of temporary cements on the shear bond strength of luting cements

Objective: The purpose of this study was to evaluate, by shear bond strength (SBS) testing, the influence of different types of temporary cements on the final cementation using conventional and self-etching resin-based luting cements. Material and Methods: Forty human teeth divided in two halves were assigned to 8 groups (n=10): I and V (no temporary cementation); II and VI: Ca(OH)(2)-based cement; III and VII: zinc oxide (ZO)based cement; IV and VIII: ZO-eugenol (ZOE)-based cement. Final cementation was done with RelyX ARC cement (groups I to IV) and RelyX Unicem cement (groups V to VIII). Data were analyzed statistically by ANOVA and Tukey's test at 5% significance level. Results: Means were (MPa): I - 3.80 (+/- 1.481); II - 5.24 (+/- 2.297); III - 6.98 (+/- 1.885); IV - 6.54 (+/- 1.459); V - 5.22 (+/- 2.465); VI - 4.48 (+/- 1.705); VII - 6.29 (+/- 2.280); VIII - 2.47 (+/- 2.076). Comparison of the groups that had the same temporary cementation (Groups II and VI; III and VII; IV and VIII) showed statistically significant difference (p<0.001) only between Groups IV and VIII, in which ZOE-based cements were used. The use of either Ca(OH) 2 based (Groups II and VI) or ZO-based (Groups III and VII) cements showed no statistically significant difference (p>0.05) for the different luting cements (RelyX (TM) ARC and RelyX (TM) Unicem). The groups that had no temporary cementation (Groups I and V) did not differ significantly from each other either (p>0.05). Conclusion: When temporary cementation was done with ZO- or ZOE-based cements and final cementation was done with RelyX ARC, there was an increase in the SBS compared to the control. In the groups cemented with RelyX Unicem, however, the use of a ZOE-based temporary cement affected negatively the SBS of the luting agent used for final cementation.

Nd:YAG Laser Irradiation of Etched/Unetched Dentin Through an Uncured Two-step Etch-and-Rinse Adhesive and its Effect on Microtensile Bond Strength

Purpose: To evaluate whether Nd:YAG laser irradiation of etched and unetched dentin through an uncured adhesive affected the microtensile bond strength (pTBS).Materials and Methods: Flat dentin surfaces were created in 19 extracted human third molars. Adper Single Bond (SB) adhesive was applied over etched (groups 1 to 3) or unetched dentin (groups 4 to 6). The dentin was then irradiated with a Nd:YAG laser through the uncured adhesive, using 0.75 or 1 W power settings, except for the control groups (groups 1 and 4). The adhesive was light cured and composite crowns were built up. After 24 h, the teeth were sectioned into beams, with cross-sectional areas of 0.49 mm(2), and were stressed under tension. Data were statistically analyzed using two-way ANOVA and Tukey's test (alpha = 5%). Dentin surfaces of fractured specimens and the interfaces of untested beams were observed under scanning electron microscopy (SEM).Results: Acid etching, laser irradiation, and their interaction significantly affected bonding (p < 0.05). Laser irradiation did not improve bonding of etched dentin to resin (p > 0.05). However, higher pTBS means were found on unetched lased dentin (groups 5 and 6), but only in comparison to group 4, where neither lasing nor etching was performed. Groups 4 to 6 showed the lowest pTBS means among all groups tested (p < 0.05). Laser irradiation did not change the characteristics of the hybrid layers created, while solidification globules were observed on lased dentin surfaces under SEM.Conclusion: Laser irradiation of dentin through the uncured adhesive did not significantly improve the pTBS in comparison to the suggested manufacturer's technique.

Comparative scanning electron microscopic study of the effect of different dental conditioners on dentin micromorphology

This study evaluated comparatively by scanning electron microscopy (SEM) the effect of different dental conditioners on dentin micromorphology, when used according to the same protocol. Forty dentin sticks were obtained from 20 caries-free third human molars and were assigned to 4 groups corresponding to 3 conditioners (phosphoric acid 37%, Clearfil SE Bond and iBond) and an untreated control group. After application of the conditioners, the specimens were immersed in 50% ethanol solution during 10 s, chemically fixed and dehydrated to prepare them to SEM analysis. In the control group, dentin surface was completely covered by smear layer and all dentinal tubules were occluded. In the phosphoric acid-etched group, dentin surface was completely clean and presented exposed dentinal tubule openings; this was the only group in which the tubules exhibited the funnel-shaped aspect. In the groups conditioned with Clearfil SE Bond primer and iBond, which are less acidic than phosphoric acid, tubule openings were occluded or partially occluded, though smear layer removal was observed. SE Bond was more efficient in removing the smear layer than iBond. In the Clearfil SE Bond group, the cuff-like aspect of peritubular dentin was more evident. It may be concluded all tested conditioners were able to change dentin morphology. However, it cannot be stated that the agent aggressiveness was the only cause of the micromorphological alterations because a single morphological pattern was not established for each group, but rather an association of different aspects, according to the aggressiveness of the tested conditioner.

INFLUENCE of DIFFERENT SURFACE CONDITIONING PROTOCOLS on MICROTENSILE BOND STRENGTH of SELF-ADHESIVE RESIN CEMENTS TO DENTIN

Statement of problem. According to manufacturers, bonding with self-adhesive resin cements can be achieved without any pretreatment steps such as etching, priming, or bonding. However, the benefit of saving time with these simplified luting systems may be realized at the expense of compromising the bonding capacity.Purpose. The purpose of this study was to assess whether different dentin conditioning protocols influence the bond performance of self-adhesive resin cements to dentin.Material and methods. Flat dentin surfaces from 48 human molars were divided into 4 groups (n=12): 1) control, no conditioning; 2) H(3)PO(4), etching with 37% H(3)PO(4) for 15 seconds; 3) SEBond, bonding with self-etching primer adhesive (Clearfil SE Bond); and 4) EDTA, etching with 0.1M EDTA for 60 seconds. The specimens from each dentin pre-treatment were bonded using the self-adhesive cements RelyX Unicem, Maxcem or Multilink Sprint (n=4). The resin-cement-dentin specimens were stored in water at 37 degrees C for 7 days, and serially sectioned to produce beam specimens of 1.0 mm(2) cross-sectional area. Microtensile bond strength (mu TBS) testing was performed at 1.0 mm/min. Data (MPa) were analyzed by 2-way ANOVA and Tukey multiple comparisons test (alpha=.05). Fractured specimens were examined with a stereomicroscope (x40) and classified as adhesive, mixed, or cohesive. Additional bonded interfaces were evaluated under a scanning electron microscope (SEM).Results. Cement-dentin mu TBS was affected by the dentin conditioning approach (P <.001). RelyX Unicem attained statistically similar bond strengths to all pre-treated dentin surfaces. H(3)PO(4)-etching prior to the application of Maxcem resulted in bond strength values that were significantly higher than the other groups. The lowest mu TBS were attained when luting Multilink Sprint per manufacturers' recommendations, while H(3)PO(4)-etching produced the highest values followed by Clearfil SE bonding and EDTA. SEM observations disclosed an enhanced potential of the self-adhesive cements to form a hybrid layer when applied following manufacturer's instructions.Conclusions. When evaluated self-adhesive resin cements are used, selectively etching dentin with H(3)PO(4) prior to luting results in the most effective bonding. (J Prosthet Dent 2011;105:227-235)

Does Adhesive Resin Application Contribute to Resin Bond Durability on Etched and Silanized Feldspathic Ceramic?

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Does the Ultrasonic Cleaning Medium Affect the Adhesion of Resin Cement to Feldspathic Ceramic?

Purpose: To evaluate the effect of different cleaning media on the adhesion of resin cement to feldspathic ceramic after etching.Materials and Methods: The cementation surfaces of ceramic blocks (N = 20, n = 5 per group) were etched with 10% hydrofluoric acid (HF) gel for 20 s and rinsed for 60 s. They were then randomly assigned to 4 groups: G1: air-water spray+drying (control); G2: ultrasonic cleaning in distilled water for 4 min+drying; G3: ultrasonic cleaning in 99.5% acetone for 4 min+drying; G4: ultrasonic cleaning in 70% alcohol for 4 min+drying. The ceramic blocks were silanized and cemented (RelyX ARC) to the composite blocks. Subsequently, the microtensile bond strength test (mu TBS) was performed. In addition, EDS analysis was made to assess the elemental composition of the conditioned and cleaned ceramic surfaces.Results: A significantly higher mean mu TBS was obtained when specimens had been ultrasonically cleaned in distilled water (G2: 18.8 +/- 0.4 MPa) (p < 0.05) compared to other groups (G1: 16.6 +/- 0.5; G3: 16.1 +/- 0.9; G4: 15.8 +/- 1.4) (one-way ANOVA). EDS analysis indicated the presence of F- only in G1. Dissolved precipitates after HF etching were removed by ultrasonic cleaning.Conclusion: Cleaning the HF-etched ceramic surface ultrasonically in distilled water is recommended, instead of rinsing it with air-water spray only.

Bond Strength of Two Resin Cements on Dentin Using Different Cementation Strategies

Purpose:This study evaluated the microtensile bond strength of two resin cements to dentin either with their corresponding self-etching adhesives or employing the three-step etch-and-rinse technique. The null hypothesis was that the etch-and-rinse adhesive system would generate higher bond strengths than the self-etching adhesives.Materials and Methods:Thirty-two human molars were randomly divided into four groups (N = 32, n = 8/per group): G1) ED Primer self-etching adhesive + Panavia F; G2) All-Bond 2 etch-and-rinse adhesive + Panavia F; G3) Multilink primer A/B self-etching adhesive + Multilink resin cement; G4) All-Bond 2 + Multilink. After cementation of composite resin blocks (5 x 5 x 4 mm), the specimens were stored in water (37 degrees C, 24 hours), and sectioned to obtain beams (+/- 1 mm2 of adhesive area) to be submitted to microtensile test. The data were analyzed using 2-way analysis of variance and Tukey's test (alpha = 0.05).Results:Although the cement type did not significantly affect the results (p = 0.35), a significant effect of the adhesive system (p = 0.0001) was found on the bond strength results. Interaction terms were not significant (p = 0.88751). The etch-and-rinse adhesive provided significantly higher bond strength values (MPa) with both resin cements (G2: 34.4 +/- 10.6; G4: 33.0 +/- 8.9) compared to the self-etching adhesive systems (G1: 19.8 +/- 6.6; G3: 17.8 +/- 7.2) (p < 0.0001). Pretest failures were more frequent in the groups where self-etching systems were used.Conclusion:Although the cement type did not affect the results, there was a significant effect of changing the bonding strategy. The use of the three-step etch-and-rinse adhesive resulted in significantly higher bond strength for both resin cements on dentin.CLINICAL SIGNIFICANCEDual polymerized resin cements tested could deliver higher bond strength to dentin in combination with etch-and-rinse adhesive systems as opposed to their use in combination with self-etching adhesives.(J Esthet Restor Dent 22:262-269, 2010).

Effect of Acid Neutralization and Mechanical Cycling on the Microtensile Bond Strength of Glass-ceramic Inlays

Objectives: To evaluate the hypothesis that a process of hydrofluoric acid precipitate neutralization and fatigue load cycling performed on human premolars restored with ceramic inlays had an influence on microtensile bond strength results (MTBS). Methods: MOD inlay preparations were performed in 40 premolars (with their roots embedded in acrylic resin). Forty ceramic restorations were prepared using glass-ceramic (IPS Empress). The inner surfaces of all the restorations were etched with 10% hydrofluoric acid for 60 seconds, rinsed with water and dried. The specimens were divided into two groups (N=20): 1-without neutralization; 2-with neutralization. All the restorations were silanized and adhesively cemented (self-curing and self-etching luting composite system, Multilink). Ten premolars from each group were submitted to mechanical cycling (1,400,000 cycles, 50N, 37 degrees C). After cycling, the samples were sectioned to produce non-trimmed beam specimens (vestibular dentin-restoration-lingual dentin set), which were submitted to microtensile testing. Results: Bond strength was significantly affected by the surface treatment (p<0.0001) (no neutralization > neutralization) and mechanical cycling (p<0.0001) (control > cycling) (2-way ANOVA and Tukey test, alpha=.05). Conclusion: Hydrofluoric acid precipitate neutralization appears to significantly damage the resin bond to glass-ceramic and should not be recommended. The clinical simulation of the specimens, by using mechanical cycling, is important when evaluating the ceramic-dentin bond.

Effect of adhesive system type and tooth region on the bond strength to dentin

Purpose: This study evaluated the bond strength of two etch-and-rinse adhesive systems (two- and three-step) and a self-etching system to Coronal and root canal dentin.Materials and Methods: The root canals of 30 human incisors and canines were instrumented and prepared with burs. The posts used for luting were duplicated with dual resin cement (Duo-link) inside Aestheti Plus #2 molds. Thus, three groups were formed (n = 10) according to the adhesive system employed: All-Bond 2 (TE3) + resin cement post (rcp) + Duo-link (DI); One-Step Plus (TE2) + rcp + DI; Tyrian/One-Step Plus (SE) + rcp + DI. Afterwards, 8 transverse sections (1.5 mm) were cut from 4 mm above the CEJ up to 4 mm short of the root canal apex, comprising coronal and root canal dentin. The sections were submitted to push-out testing in a universal testing machine EMIC (1 mm/min). Bond strength data were analyzed with two-way repeated measures ANOVA and Tukey's test (p < 0.05).Results: The relationship between the adhesives was not the same in the different regions (p < 0.05). Comparison of the means achieved with the adhesives in each region (Tukey; p < 0.05) revealed that TE3 (mean standard deviation: 5.22 +/- 1.70) was higher than TE2 (2.60 +/- 1.74) and SE (1.68 +/- 1.85).Conclusion: Under the experimental conditions, better bonding to dentin was achieved using the three-step etch-and-rinse system, especially in the coronal region. Therefore, the traditional etch-and-rinse three-step adhesive system seems to be the best choice for teeth needing adhesive endodontic restorations.

Durability of Microtensile Bond to Nonetched and Etched Feldspar Ceramic: Self-adhesive Resin Cements vs Conventional Resin

Purpose: The objective of this study was to evaluate the effect of thermocycling (TC), self-adhesive resin cements and surface conditioning on the microtensile bond strength (mu TBS) between feldspathic ceramic blocks and resin cements.Materials and Methods: Fifty-six feldspathic ceramic blocks (10 x 7 x 5 mm) (Vita Mark II) were divided into groups according to the factors "resin cement" (3 cements) and "surface conditioning" (no conditioning or conditioning [10% hydrofluoric acid etching for 5 min + silanization]) (n = 8): group 1: conditioning+Variolink II (control group); group 2: no conditioning+Biscem; group 3: no conditioning+RelyX U100; group 4: no conditioning+Maxcem Elite; group 5: conditioning+Biscem; group 6: conditioning+RelyX U100; group 7: conditioning+Maxcem Elite. The ceramic-cement blocks were sectioned to produce non-trimmed bar specimens (adhered cross-sectional area: 1 +/- 0.1 mm(2)), which were divided into two storage conditions: dry, mu TBS immediately after cutting; TC (12,000x, 5 degrees C/55 degrees C). Statistical significance was deterimined using two-way ANOVA (7 strategies and 2 storage conditions) and the post-hoc Tukey test (p<0.05).Results: Resin cement and thermocycling affected the mu TBS significantly (p = 0.001). In the dry condition, group 5 (18 +/- 6.5 MPa) presented the lowest values of mu TBS when compared to the other groups. TC decreased the mean mu TBS values significantly (p<0.05) for all resin cements tested (9.7 +/- 2.3 to 22.1 +/- 6.3 MPa), except for the resin cement RelyX U100 (22.1 +/- 6.3 MPa). In groups 3 and 4, it was not possible to measure mu TBS, since these groups had 100% pre-test failures during sectioning. Moreover, the same occurred in group 2 after TC, where 100% failure was observed during thermocycling (spontaneous failures).Conclusion: Hydrofluoric acid etching and silanization of the feldspathic ceramic surface are essential for bonding self-adhesive resin cement to a feldspathic ceramic, regardless of the resin cement used. Non-etched ceramic is not recommended.

Bond strength durability of a resin composite on a reinforced ceramic using various repair systems

Objectives. This study compared the durability of repair bond strength of a resin composite to a reinforced ceramic after three repair systems.Methods. Alumina-reinforced feldspathic ceramic blocks (Vitadur-alpha(R)) (N=30) were randomly divided into three groups according to the repair method: PR-Porcelain Repair Kit (Bisco) [etching with 9.5% hydrofluoric acid + silanization + adhesive]; CJ-CoJet Repair Kit (3M ESPE) [(chairside silica coating with 30 mu m SiO2 + silanization (ESPE(R)-Sil) + adhesive (Visio(TM)-Bond)]; CL-Clearfil Repair Kit [diamond surface roughening, etching with 40% H3PO4 + Clearfil Porcelain Bond Activator + Clearfil SE Bond)]. Resin composite was photo-polymerized on each conditioned ceramic block. Non-trimmed beam specimens were produced for the microtensile bond strength (mu TBS) tests. In order to study the hydrolytic durability of the repair methods, the beam specimens obtained from each block were randomly assigned to two conditions. Half of the specimens were tested either immediately after beam production (Dry) or after long-term water storage (37 degrees C, 150 days) followed by thermocyling (12,000 cycles, 5-55 degrees C) in a universal testing machine (1 mm/min). Failure types were analyzed under an optical microscope and SEM.Results. mu TBS results were significantly affected by the repair method (p=0.0001) and the aging conditions (p=0.0001) (two-way ANOVA, Tukey's test). In dry testing conditions, PR method showed significantly higher (p < 0.001) repair bond strength (19.8 +/- 3.8 MPa) than those of CJ and CL (12.4 +/- 4.7 and 9.9 +/- 2.9, respectively). After long-term water storage and thermocycling, CJ revealed significantly higher results (14.5 +/- 3.1 MPa) than those of PR (12.1 +/- 2.6 MPa) (p < 0.01) and CL (4.2 +/- 2.1 MPa) (p < 0.001). In all groups when tested in dry conditions, cohesive failure in the composite accompanied with adhesive failure at the interface (mixed failures), was frequently observed (76%, 80%, 65% for PR, CJ and CL, respectively). After aging conditions, while the specimens treated with PR and CJ presented primarily mixed failure types (52% and 87%, respectively), CL group presented mainly complete adhesive failures at the interface (70%).Significance. Hydrolytic stability of the repair method based on silica coating and silanization was superior to the other repair strategies for the ceramic tested. (C) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Surface degradation of glass ceramics after exposure to acidulated phosphate fluoride

Objective: This study evaluated the surface degradation effect of acidulated phosphate fluoride (APF) gel exposure on the glassy matrix ceramics as a function of time. Material and methods: Disc-shaped ceramic specimens (N = 120, 10/per ceramic material) were prepared in stainless steel molds (inner diameter: 5 mm, height: 2 mm) using 6 dental ceramics: 3 indicated for ceramic-fused-to-metal (Vita Omega 900, Carmen and Vita Titankeramik), 2 for all-ceramic (Vitadur Alpha and Finesse (R) Low Fusing) and 1 for both types of restorations (IPS d. SIGN). The specimens were wet ground finished, ultrasonically cleaned and auto-glazed. All specimens were subjected to calculation of percentage of mass loss, surface roughness analysis and topographical description by scanning electron microscopy (SEM) before (0 min) and after exposure to 1.23 % APF gel for 4 min and 60 min representing short-and long-term etching effect, respectively. The data were analyzed using two-way ANOVA with repeated measures and Tukey` s test (alpha=0.05). Results: Significant effect of the type of the ceramics (p=0.0000, p=0.0031) and exposure time (p=0.0000) was observed in both surface roughness and percentage of mass loss values, respectively. The interaction factor between both parameters was also significant for both parameters (p=0.0904, p=0.0258). Both 4 min (0.44 +/- 0.1-0.81 +/- 0.2 mu m) and 60 min (0.66 +/- 0.1 - 1.04 +/- 0.3 mu m) APF gel exposure created significantly more surface roughness for all groups when compared to the control groups (0.33 +/- 0.2-0.68 +/- 0.2 mu m) (p<0.05). There were no significant differences in percentage of mass loss between the ceramics at 4 min (p>0.05) but at 60 min exposure, IPS d. SIGN showed the highest percentage of mass loss (0.1151 +/- 0.11). The mean surface roughness for Vita Titankeramik (0.84 +/- 0.2 mu m) and Finesse (R) Low Fusing (0.74.+/- 0.2 mu m) was significantly higher than those of the other ceramics (0.59 +/- 0.1 mu m - 0.49 +/- 0.1 mu m) and Vita Titankeramik (p<0.05) regardless of the exposure time. A positive correlation was found between surface roughness and percentage of mass loss for all ceramic materials [(r=0.518 (Vitadur Alpha), r=0.405 (Vita Omega 900), r=0.580 (Carmen), r=0.687 (IPS d. SIGN), r=0.442 (Finesse (R) Low Fusing), r=0.572 (Vita Titankeramik), Pearson's correlation coefficient)]. The qualitative SEM analysis showed evidence of corrosive attack on all of ceramics at varying degrees. Conclusions: The ceramics indicated for either metal-ceramic or all-ceramic restorations were all vulnerable to surface texture changes and mass loss after short-term and long-term APF gel exposure.