The influence of gun transverse speed on electrochemical behaviour of thermally sprayed Cr3C2-NiCr coatings in 0.5 M H2SO4 solution

In the present study, different types of 75% Cr3C2-25% NiCr coatings were applied on a steel substrate by means of high velocity oxygen fuel spraying (HVOF), and studied using ac and dc electrochemical measurements in an aerated and unstirred 0.5 M H2SO4 solution. Structural characterization was determined before and after electrochemical tests. Differences between all sprayed systems are related to the gun transverse speed and number of deposited layers, which strongly affected the electrochemical characteristics of the coated steels. The coating obtained with a higher torch speed showed better resistance against corrosion. The electrochemical impedance results were analyzed using an equivalent circuit where porosity of the coatings and substrate oxidation were considered. (C) 2003 Elsevier Ltd. All rights reserved.

Electrochemical behavior of thermally sprayed stainless steel coatings in 3.4% NaCl solution

Four types of stainless steel coatings prepared by a high velocity oxy-fuel spraying system (HVOF) were studied. Differences among coated steels were related to the spraying parameters, which influenced the behavior of the samples against the corrosion. The electrochemical behavior of the stainless steel coatings was strongly influenced by porosity, the presence of micro- and macro-cracks, and also of un-melted particles. Once the electrolyte reached the steel substrate via these defects, the galvanic pair formed between the coating and substrate-accelerated corrosion, leading to the depletion of the coating. (C) 2004 Elsevier Ltd. All rights reserved.

Effect of welding on the microstructure and electrochemical corrosion of Al-Zn-Mg-Fe alloys

The effect of gas tungsten are welding on the microstructure and electrochemical corrosion of Al-Zn-Mg-Fe alloys submitted to different heat treatments (as fabricated, annealed and aged) has been studied using optical microscopy, SEM, TEM, EDX, cyclic voltammetry and corrosion potential measurements in chloride solutions. The electrochemical techniques were very sensitive to the change in the phase compositions produced by welding. Welding caused a decrease in the mean grain size, in the hardness and in the corrosion resistance of the age-hardened alloys. The structure of the latter became strongly altered by welding to lead to phase compositions very close to those of the cold rolled and annealed specimens. (C) 2000 Elsevier B.V. Ltd. All rights reserved.

Corrosion of dental amalgams: electrochemical study of Ag-Hg, Ag-Sn and Sn-Hg phases

Dental amalgams, formed by reaction of mercury with a powder alloy containing mainly Ag, Sn, Cu and Zn, have a complex metallurgical structure which can contain up to six phases. Their observed corrosion is thus a complex process, which involves contributions from each of the phases present as well as intergranular corrosion. It is thus of interest to investigate the corrosion of individual phases present in dental amalgams. In this work the corrosion behaviour in 0.9% NaCl solution of Ag-Hg, Ag-Sn and Sn-Hg phase components of dental amalgams was investigated by electrochemical methods. The corrosion resistance was found to decrease in the order gamma (1)-Ag2\Hg3, gamma -Ag3Sn and gamma (2)-Sn7Hg. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Comparative study of Cr3C2-NiCr coatings obtained by HVOF and hard chromium coatings

In the present work the corrosion resistance of micro-cracked hard chromium and Cr3C2-NiCr (HVOF) coatings applied on a steel substrate have been compared using open-circuit potential (E-OC) measurements, electrochemical impedance spectroscopy (EIS) and polarization curves. The coatings surfaces and cross-section were characterized before and after corrosion tests using optical microscopy (OM) and scanning electron microscopy (SEM). After 18 h of immersion, the open-circuit potential values were around -0.50 and -0.25V/(Ag vertical bar AgCl vertical bar KClsat) for hard chromium and Cr3C2- NiCr, respectively. The surface analysis done after 12 h of immersion showed iron on the hard chromium surface inside/near surface cracks, while iron was not detected on the Cr3C2-NiCr surface even after 18 h. For longer immersion time hard chromium was more degraded than thermal sprayed coating. For hard chromium coating a total resistance values between 50 and 80 k Omega cm(2) were measured and two well-defined time constants were observed, without significant change with the immersion time. For Cr3C2-NiCr coating the total impedance diminished from around 750 to 25 k Omega cm(2) as the immersion time increased from 17 up to 132 h and two overlapped time constants were also observed. Polarization curves recorded after 18 h of immersion showed a lower current and higher corrosion potential for Cr3C2-NiCr coating than other samples studied. (c) 2005 Elsevier Ltd. All rights reserved.

Electrochemical and structural characterization of heat-treated Cr3C2-NiCr coatings

The influence of heat-treatments on the electrochemical behavior of thermal spray Cr3C2-NiCr coatings prepared by high velocity oxygen fuel (HVOF) was studied in NaCl solution, at 25 degrees C, using open-circuit potential (E-OC) and electrochemical impedance spectroscopy (EIS) measurements. Coating characterization were performed before and after the heat-treatments and electrochemical tests by scanning electron microscopy, X-ray diffraction, and Auger electron spectroscopy. In addition to the changes in the original powder composition occurring during HVOF process, heat-treatment performed at 450 degrees C caused no significant changes in electrochemical response compared with untreated sample, and at 760 degrees C the main difference was the formation of a thin and defective layer of Cr2O3 at the coating surface, which increased the total impedance at the first day of immersion. Higher influence on the electrochemical was noted for samples treated at 880 degrees C, which also showed higher E-OC and total impedance, and lower corrosion current. This behavior was interpreted considering the formation of a chromium oxide layer on the coating surface, dissolution and decomposition of smaller carbide particles and their surface enrichment with Cr due to C diffusion and dissolution into the matrix, and possible Ni, Cr, and Fe diffusion to coating/substrate interface. (c) 2006 the Electrochemical Society.

Resistência à corrosão das fases presentes em amálgamas dentários

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Optimization of the use of carbon paste electrodes (CPE) for electrochemical study of the chalcopyrite

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Electrochemical behavior of Ti-Mo alloys applied as biomaterial

Electrochemical investigation on the as-cast Ti-Mo alloys (4-20 Mo wt.%) applied as biomaterials in Na2SO4 and Ringer physiological solutions is reported. Analyses of the open-circuit potential indicated that all alloys present spontaneous passivation. SEM and cyclic voltammograms obtained in the Ringer solution showed that the samples studied do not present pitting corrosion at potentials up to 8 V (SCE), indicating high corrosion resistance. Open-circuit potential profiles of the anodic oxides growth in both solutions show that the presence of chloride ions during the anodization does not influence the oxides' chemical stability, and also clearly indicate that adding Mo to pure Ti improves the stability of the anodic oxides. All these results suggest Ti-Mo alloys promissory to be applied as biomaterials. (c) 2008 Elsevier Ltd. All rights reserved.

Cr3C2-NiCr and WC-Ni thermal spray coatings as alternatives to hard chromium for erosion-corrosion resistance

Cr3C2-NiCr and WC-Ni coatings are widely used for wear applications at high and room temperature, respectively. Due to the high corrosion resistance of NiCr binder, Cr3C2-NiCr coatings are also used in corrosive environments. The application of WC-Ni coatings in corrosive media is 14 not recommended due to the poor corrosion resistance of the (pure Ni) metallic matrix. It is well known that the addition of Cr to the metallic binder improves the corrosion properties. Erosion-corrosion performance of thermal spray coatings is widely influenced by ceramic phase composition, the size of ceramic particles and also the composition of the metallic binder. In the present work, two types of HVOF thermal spray coatings (Cr3C2-NiCr and WC-Ni) obtained with different spray conditions were studied and compared with conventional micro-cracked hard chromium coatings. Both as-sprayed and polished samples were tested under two erosion-corrosion conditions with different erosivity. Tungsten carbide coatings showed better performance under the most erosive condition, while chromium carbide coatings were superior under less erosive conditions. Some of the tungsten carbide coatings and hard chromium showed similar erosion-corrosion behaviour under more and less erosive conditions. The erosion-corrosion and electrochemical results showed that surface polishing improved the erosion-corrosion properties of the thermally sprayed coatings. The corrosion behaviour of the different coatings has been compared using Electrochemical Impedance Spectroscopy (EIS) and polarization curves. Total material loss due to erosion-corrosion was determined by weight loss measurements. An estimation of the corrosion contribution to the total weight loss was also given. (c) 2007 Elsevier B.V. All rights reserved.

Influence of cerium (IV) ions on the mechanism of organosilane polymerization and on the improvement of its barrier properties

In this work, the effect of cerium (IV) ammonium nitrate (CAN) addition on the polymerization of bis-[triethoxysilyl]ethane (BTSE) film applied on carbon steel was studied. The electrochemical characterization of the films was carried out in 0.1 mol L(-1) NaCl solution by open-circuit potential measurements, anodic and cathodic polarization curves and electrochemical impedance spectroscopy (EIS). Morphological and chemical characterization were performed by atomic force microscopy (AFM), contact angle measurements, infrared-spectroscopy, nuclear magnetic resonance and thermogravimetric analysis. The results have clearly shown the improvement on the protective properties of the Ce(4+) modified film as a consequence of the formation of a more uniform and densely reticulated silane film. A mechanism is proposed to explain the accelerating role of Ce(4+) ions on the cross-linking of the silane layer. (C) 2008 Elsevier Ltd. All rights reserved.

Repeatability of corrosion parameters for titanium-molybdenum alloys in 0.9% NaCl solution

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Electrochemical Oxidation of Hydroxylamine on Gold in Aqueous Acidic Electrolytes: An in Situ SERS Investigation

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Quantum Mechanics Insight into the Microwave Nucleation of SrTiO3 Nanospheres

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of cerium (IV) ions on the anticorrosion properties of siloxane-poly(methyl methacrylate) based film applied on tin coated steel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)