Influence of addition of calcium oxide on physicochemical properties of Portland cement with zirconium or niobium oxide

Context: Calcium oxide (CaO) may be added to mineral trioxide aggregate (MTA) or Portland cement (PC) to improve physicochemical and biological properties. Aims: To evaluate the physicochemical properties of PC associated with radiopacifiers and CaO. Materials and Methods: MTA Angelus, PC + 30% zirconium oxide (Zr), or 30% niobium oxide (Nb) associated with 10 or 20% of CaO were evaluated. Gilmore needles were used to evaluate initial and final setting time. Compressive strength was evaluated after the periods of 24 hours and 21 days. pH was analyzed after 3, 12, 24 hours, 7, 14, 21 days. Solubility and flow tests were performed based on the ISO 6876. The data obtained were submitted to analysis of variance and Tukey tests (P ≤ 0.05). Results: The associations with 10% CaO showed greater strength that the associations with 20% CaO. The shortest initial setting time was observed for the association PC + Zr + 20% CaO and MTA. All the cements presented alkaline pH. The flow of all cements was similar. The highest solubility was found in the associations with 20% CaO. Conclusion: The addition of CaO to PC favored the alkaline property and the PC + Zr + 20% CaO presented setting time similar to MTA.

Ph and antimicrobial activity of portland cement associated with different radiopacifying agents

The aim of this study was to evaluate the antimicrobial activity and pH changes induced by Portland cement (PC) alone and in association with radiopacifiers. Methods. The materials tested were pure PC, PC + bismuth oxide, PC + zirconium oxide, PC + calcium tungstate, and zinc oxide and eugenol cement (ZOE). Antimicrobial activity was evaluated by agar diffusion test using the following strains: Micrococcus luteus, Streptococcus mutans, Enterococcus faecalis, Pseudomonas aeruginosa, and Candida albicans. After 24 hours of incubation at 37°C, inhibition of bacterial growth was observed and measured. For pH analysis, material samples (n=10) were placed in polyethylene tubes and immersed in 10 mL of distilled water. After 12, 24, 48, and 72 hours, the pH of the solutions was determined using a pH meter. Results. All microbial species were inhibited by the cements evaluated. All materials composed of PC with radiopacifying agents promoted pH increase similar to pure Portland cement. ZOE had the lowest pH values throughout all experimental periods. Conclusions. All Portland cement-based materials with the addition of different radiopacifiers (bismuth oxide, calcium tungstate, and zirconium oxide) presented antimicrobial activity and pH similar to pure Portland cement.

Effect of chlorhexidine gluconate on porosity and compressive strength of a glass ionomer cement

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Influence of the addition of chlorhexidine diacetate on bond strength of a high-viscosity glass ionomer cement to sound and artificial caries-affected dentin

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Influência do tempo de endurecimento no comportamento físico e biológico de sete cimentos endodônticos

Pós-graduação em Odontologia Restauradora - ICT

Avaliação da resposta tecidual e capacidade de mineralização de cimentos que contém compostos biocerâmicos, resinosos e com hidróxido de cálcio

Pós-graduação em Ciência Odontólogica - FOA

Influência da incorporação de nanopartículas de trimeta- fosfato de sódio associado ou não à clorexidina nas proprie- dades microbiológicas, físico-mecânicas e de redução da desmineralização de cimento de ionômero de vidro

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Mechanical properties of components of the bonding interface in different regions of radicular dentin surfaces

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Study of thermocycling effect on the bond strength between an aluminous ceramic and a resin cement

This study evaluated the effect of thermocycling on the bond strength between Procera AllCeram (Nobel-Biocare) and a resin cement (Panavia F, Kuraray CO). Nine ceramic blocks with dimensions of 5x6x6mm were conditioned at one face with Rocatec System (Espe). After, they were luted with Panavia F to composite resin blocks (Clearfil AP-X, Kuraray CO). The nine groups formed by ceramic, cement and composite resin were split up obtaining 75 samples with dimensions of 12x1x1mm and adhesive surface presenting 1mm2±0.1mm2 of area. The samples were divided into 3 groups (n=25): G1 - 14 days in distilled water at 37ºC; G2 – 6,000 cycles in water (5ºC - 55ºC – 30s); G3 – 12,000 cycles in water (5ºC - 55ºC – 30s). The samples were tested in a universal testing machine (EMIC) at a crosshead speed of 1mm/min. Data were analyzed by ANOVA and Tukey tests. The results indicated that mean values of rupture tension (MPa) of G1 (10.71 ± 3.54) did not differ statistically (p <5%) from G2 (9.01 ± 3.90), however there was statistical difference between G1 and G3 (7.28 ± 3.00). It was concluded that thermocycling significantly reduced the bond strength values when samples were submitted to 12,000 cycles.

Ultrasound effect in the removal of intraradicular posts cemented with different materials

This study evaluated the effect of ultrasonic vibration on the tensile strength required to remove intraradicular post cemented with different materials. Bovine teeth were selected, and 7 mm of the cervical root canals were prepared to size 5 Largo drill, the posts were cemented with zinc phosphate, Enforce (resin) or Rely X (glass ionomer). The specimens were divided into six groups (n = 10), according to the following procedures: GI-cementation with zinc phosphate associated with traction force; GII-cementation with zinc phosphate associated with ultrasonic activation and traction force; G111-cementation with Enforce associated with traction force; GIV-cementation with Enforce associated with ultrasonic activation and traction force; GV-cementation with Rely X associated with traction force; and GVI-cementation with Rely X associated with ultrasonic activation and traction force. The tensile test was conducted using the electromechanical testing machine, the force was determined by a specialized computer program and ultrasonic activation using the Jet Sonic Four Plus (Gnatus) device in 10P. Concerning to average ranking, GI showed statistically significant difference in comparison with GII and GVI (p < 0.05); there was no statistical difference in GIII and GIV when compared to other groups (p > 0.05). The ultrasound favored the intraradicular post traction regardless of the employed cement in greater or lesser extent. The post removal is a routine practice in the dental office, therefore, new solutions and better alternatives are need to the practitioner. We did not find in the literature many articles referring to this practice. Thus, the results from this study are relevant in the case planning and to promote more treatment options.

Análise da espessura da película de cimentos de ionômero vítreo e fosfato de zinco, empregados na cimentação de coroas totais metálicas, preparadas in vivo

Pós-graduação em Odontologia Restauradora - ICT

Estudo comparativo in vitro do efeito da ciclagem térmica sobre a resistência à tração de copings metálicos cimentados sobre dentes naturais, utilizando se de dois agentes cimentantes

Pós-graduação em Odontologia Restauradora - ICT

Resistência de união entre um cimento resinoso e uma cerâmica aluminizada submetida a diferentes tratamentos de superfície

Pós-graduação em Odontologia Restauradora - ICT

Microhardness of luting agents used for fiber post cementation submitted to thermo cycling

Aims and Objectives: The aim of this study was to analyze the microhardness of three resin cements used in cementing glass fiber posts in bovine incisor. The microhardness was analyzed in cervical, middle and apical thirds before and after thermocycling process. Materials and Methods: Bovine teeth were instrumented and divided into 3 groups composed of 10 teeth each. Then, the teeth were sectioned and obturated and had their canals prepared at a depth of 12mm. Once proceeded the desobturation, the roots and glass fiber posts were prepared for adhesive cementation. After cementation, the microhardness reading was carried out. After initial reading, the samples were placed in a thermocycler and subjected to 2,000 cycles and a new microhardness reading. The data collected were subjected to analysis of variance (ANOVA) and Turkey’s test. Results: It was observed a statistical difference among the microhardness of resin cements. However, the statistical difference of microhardness before and after thermocycling appeared only in group U-200. Conclusion: Thermocycling reduced microhardness values in all cements evaluated in this study. The autopolymerizing cement Multilink presented the most stable microhardness mean values after thermocycling in the coronal, middle and apical thirds.

Atividade antimicrobiana de cimentos endodônticos

The antimicrobial activity is a fundamental property of root-canal sealers due to persistence of residual microorganisms in the root canal system, even after the chemo-mechanical preparation and using of intracanal dressing. The aim of this study is to review the literature about the antimicrobial properties of some of the main root-canal sealers. Although there is controversy regarding this property, probably due to differences in the methodologies used in the studies, it was concluded that the sealers with the best antimicrobial activity were (in ascending order): Endofill, Ketac Endo, Sealapex, AH Plus, Endo CPM Sealer, Sealer 26 and Epiphany. Activ GP still needs scientific research to evaluate this property.