Stability against crystallization and spectroscopic properties of Tm3+ doped fluorophosphate glasses

Fluorophosphate glasses with various content of Al(PO3)(3) were prepared. With the increment of Al(PO3)(3) content, density decreases while refractive index increases, and transition temperature, crystallization peak temperature and melt temperature increase which were suggested by differential scanning calorimetry. These glasses exhibit the best stability against crystallization with 7-9 mol'Yo Al(PO3)(3) content. Normalized Raman spectra were used to analyze structure and phonon state. The increment of Al(PO3)(3) content does not affect phonon energy but results in the augment of phonon density. Absorption spectra were measured. H-3(6) -> F-3(4) transition exhibits absorption at L band of the third communication window. Compared with the energy of Tm3+ excited states in other glass system, F-3(4) energy of Tm3+ in these glasses is considerable higher and H-3(4) energy is considerable lower, and it can be predicted that emission band of H-3(4) -> F-3(4) transition is close to the amplified band of gain-shift Tm3+ doped fiber amplifier. Analyses of Judd-Ofelt theory suggest when Al(PO3)(3) content is no more than 7 mol%, Judd-Ofelt parameters Omega(t) and the lifetime of H-3(4) energy level of TM3+ vary little with the increment of Al(PO3)(3) content, and when Al(PO3)(3) content is more than 7 mol%, Omega(2) and Omega(6) increase and radiative lifetime of H-3(4) energy level of Tm3+ drops sharply with the increment of Al(PO3)(3) content. (c) 2006 Elsevier B.V. All rights reserved.

稀土离子掺杂的多组分玻璃光纤

abstract {Rare earth ions doped multi-component glass fibers have important application in broad band fiber amplifier and up-conversion fiber lasers. In this paper, the mechanism and the progress of study on rare earth ions doped multi-component glass fibers in broad band fiber amplifier and up-conversion fiber lasers are introduced and reviewed. The questions and the applications of rare earth ions doped multi-component glass fibers in the future are also prospected. Based on the present research progress, it is suggested to further study the tellurite and bismuth glasses, which are used as fiber materials in broad band fiber amplifier. To up-conversion fiber laser, it is still need to further investigate novel glasses, which has low phonon energy and good physical and chemical properties.}

一种宽带拉曼放大碲酸盐玻璃的拉曼散射特性

The flattening and broadening effects of Ga2O3, GeO2, P2O5 in TeO2-BaCO3-SrCO3- Nb2O5 (TBSN) glass system were studied. The results showed that P2O5 can broaden the vibration band in Raman spectra and Ga2O3, GeO2 can flatten the spectra compared with TBSN glass. And also, they can extend the main vibration band and decrease the vibration intensity of 730 cm^-1 and 780 cm^-1 nonbridging oxygen connected with Te. They also make for the decrease of flatness in 600-870 cm^-1 vibration band and GeO2 has larger effect than Ga2O3 in weakening the vibration of nonbridging oxygen.

The spectroscopic properties of Er3(+)-doped TeO2-Nb2O5 glasses with high mechanical strength performance

(100 - x)TeO2 - xNb(2)O(5) (x=5-20) mobic tellurite glasses doped with 0.5 mol.% Er2O3 were synthesized, and their thermal, mechanical, and spectroscopic properties were measured and compared to the properties of the typical 75TeO(2)-20ZnO-5Na(2)O (TZN) tellurite glass. The refractive index (n(d)), density (p), and glass transition temperature (T-g) of bulk glasses increase with the Nb2O5 content. The Vickers microhardness (H-v) of bulk glass in niobic tellurite glasses also increases with the Nb2O5 content. The values (2.5-3.2 GPa) of H, in the niobic tellurite glasses are 47-88% larger than that (1.7 GPa) in TZN glass. The effect of Nb2O5 content on absorption spectra, the Judd-Ofelt parameters Omega(t) (t = 2, 4, 6), fluorescence spectra and the lifetimes of Er3+ :I-13/2 level were also investigated, and the stimulated emission crosssection was calculated from McCumber theory. With increasing Nb2O5 content in the glass composition, the Omega(t) (t = 2, 4, 6) parameters, fluorescence full width at half maximum (FWHM) Of I-13/2 of Er3+ increase, while the I-4(13/2) lifetimes of Er3+ decreases. Compared with TZN glass, the gain bandwidth properties of Er3+-doped TeO2-Nb2O5 glass is much larger than in tellurite glass based TeO2-ZnO-Na2O system, bismush-based glass, germanate, and silicate glasses, which indicates that TeO2-Nb2O5 glasses are better choice as a practical available host material for broadband Er3+-doped amplifier. (c) 2005 Elsevier B.V. All rights reserved.

Fabrication and emission properties of Er3+/Yb3+ codoped tellurite glass fiber for broadband optical amplification

Tellurite glass is proposed as a host for broadband erbium-doped fiber amplifiers because of their excellent optical and chemical properties. A new single mode Er3+/Yb3+ codoped tellurite fiber with D-shape cladding geometry is fabricated in this work. When pumped at 980 nm, a broad erbium amplified spontaneous emission (ASE) nearly 100 nm in the wavelength range of 1450-1650 ran around 1.53 mu m is observed. It was found that the emission spectrum from erbium in tellurite glass fibers is almost twice as broad as the corresponding spectrum in tellurite bulk glass. The changes in ASE with regard to fiber lengths and pumping power were measured and discussed. The output of about 2.3 mW from Er3+/Yb3+ codoped tellurite fiber ASE source is obtained under the pump power of 700 mW. The broad 1.53 mu m emission of Er3+ in Er3+/Yb3+ codoped tellurite glass fiber can be used as host material for potential broadband optical amplifier and tunable fiber lasers. (c) 2005 Elsevier B.V. All rights reserved.

Spectral properties and stability of Er3+-doped TeO2-WO3 glass

Er3+-doped TeO2-WO3 glass was fabricated and characterized by absorption spectrum, fluorescence spectrum, Raman spectrum and stability. The Judd-Ofelt parameter ohm(t)(t = 2, 4, 6) were calculated from the absorption spectrum by the Judd-Ofelt theory. The fluorescence spectrum indicates that the fluorescence width at half-maximum (FWHM) is 66nm. The stimulated emission cross-section of Er3+ in TeO2-WO3 glass at 1532 nm was calculated to be 0.80 x 10(-20) cm(2) by McCumber theory. The phonon energy of TeO2-WO3 glass is found to be 931 cm(-1). The difference between crystallization onset temperature and glass transition temperature Delta T is 112 degrees C. These results show that Er3+-doped TeO2-WO3 glass has higher stability and good spectral properties, which were useful for broadband amplifier. (c) 2005 Elsevier B.V. All rights reserved.

荧光俘获效应对掺铒氧化物玻璃光谱性质的影响

测试了不同掺杂浓度和样品厚度下掺铒磷酸盐和碲酸盐玻璃的吸收光谱、荧光光谱和荧光寿命，计算了Er^3＋离子在1．53μm处的吸收截面（σa）、发射截面（σe）、自发辐射跃迁概率（Arad）、辐射跃迁寿命（τrad）、以及辐射跃迁量子效率（η）等光谱参数．讨论了荧光俘获效应对掺铒磷酸盐和碲酸盐玻璃光谱性质及光谱参数的影响．结果表明即使在铒离子低掺杂浓度（0．1mol％Er2O3）下，荧光俘获效应也普遍存在于掺铒玻璃材料中，使得荧光寿命（τt）和荧光半高宽（FWHM）随样品的厚度和铒离子掺杂浓度增加而增大，导致

The influence of OH groups on laser performance in phosphate glasses

Because of the influence of OH groups in phosphate glasses on the radiation of rare-earth ions, the laser performance is degraded. The laser efficiency and the small signal gain experiment of several phosphate glass samples have been done, the concentration of OH groups in glasses was calculated from the measured absorption coefficient at 3.47 μm. It is shown that the concentration of OH groups in phosphate glasses can seriously influence the laser output characteristics, and the OH groups have worse influence on the laser amplifier than laser oscillator.

掺铒磷酸盐玻璃波导放大器的特性研究

研究了掺铒磷酸盐玻璃波导放大器的特性。利用重叠因子将980nm光抽运的掺铒玻璃波导放大器四能级模型的速率-传输方程进行化简，在考虑上转换效应和放大自发发射的情况下．利用数值模拟的方法，得到了掺铒玻璃波导放大器的增益与Er^3+离子浓度、抽运功率、波导长度等参量之间的关系曲线；同时模拟出放大自发发射曲线并与实验测量结果进行比较。结果表明在考虑上转换效应和放大自发发射的情况下,理论结果和实验测量结果是一致的。同时看到，选择合适的铒离子浓度是制作掺铒玻璃波导放大器的关键；并且为了全面发挥掺铒玻璃波导放大器的性能

Fabrication and amplified spontaneous emission spectrum of Er3+-doped tellurite glass fiber with D-shape cladding

Tellurite glass is proposed as a host for broadband erbium-doped fiber amplifiers because of their excellent optical and chemical properties. A single-mode Er3+-doped tellurite glass fiber with D-shape cladding was fabricated in this work. The characterization of amplified spontaneous emission (ASE) from this newly fabricated Er3+-doped tellurite fibers are exhibited. When pumped at 980 nm, a very broad erbium ASE nearly 150 nm around 1.53 mum is observed. The changes in ASE with regard to fiber lengths and pumping power were measured and discussed. The output of 2 mW from Er3+-doped tellurite fiber ASE source was obtained under the pump power of 660 mW. The broad 1.53 mum emission of Er3+ in tellurite glass fiber can be used as host material for potential broadband optical amplifier and tunable fiber lasers. (C) 2004 Elsevier B.V. All rights reserved.

Spectroscopic properties of Er3+ doped TeO2-BaO (Li2O, Na2O)-La2O3 glasses for 1.5-mu m optical amplifiers

This paper reports on the optical spectroscopic properties and thermal stability of Er3+-doped TeO2-BaO (Li2O,NaO)-La2O3 glasses for developing 1.5-mu m fiber amplifiers. Upon excitation at 977 nm laser diode, an intense 1.53-mu m infrared fluorescence has been observed with a broad full width at half maximum (FWHM) of about 60 nm for the Er3+-doped TeO2-BaO (Li2O, Na2O)-La2O3 glass with 10 mol% of BaO. The calculated fluorescence lifetime and the emission cross-sections of the 1.53-mu m transition are 2.91 ms and similar to 9.97 x 10(-21) cm(2), respectively. It is noted that the gain bandwidth, a, x FWHM, of the TeO2-BaO-La2O3Er2O3 glass is about 600, which is significantly higher than that in silicate and phosphate glasses. Meanwhile, it is interesting to note that the TeO2-BaO-La2O3-Er2O3 glass has shown a high glass thermal stability and good infrared transmittance. As a result, TeO2-BaO (Li2O, Na2O)-La2O3 glass with 10 mol% of BaO has been considered to be more useful as a host for broadband optical fiber amplifier. (c) 2005 Elsevier B.V. All rights reserved.

Property studies of optical waveguide formed by 6.0 MeV carbon ion implantation into Nd : silicate glass

Nd:silicate glass was implanted at room temperature by 6.0 MeV C3+ ions with a dose of 2.0 x 10(15) ions cm(-2). A waveguide with thickness of about 6.3 mu m was formed. The prism-coupling method was used to observe the dark modes of the waveguide at 633 nm and 1539 nm, respectively. There are three dark modes at 633 nm, of which one is the enhanced-index mode. The propagation loss of the enhanced-index mode in the waveguide measured at 633 nm is 0.42 dB cm(-1) after annealing at 217 degrees C for 35 min. The reflectivity calculation method was applied to simulate the refractive index profiles in the waveguide. The mode optical near-field output at 633 nm was presented.

Enhanced luminescence from transparent Ni2+-doped MgO-Al2O3-SiO2 glass ceramics by Ga2O3 addition

Transparent Ni2+-doped MgO-Al2O3-SiO2 glass ceramics without and with Ga2O3 were synthetized. The precipitation of spinel nanocrystals, which was identified as solid solutions in the glass ceramics, could be favored by Ga2O3 addition and their sizes were about 7.6 nm in diameter. The luminescent intensity of the Ni2+-doped glass ceramics was largely enhanced by Ga2O3 addition which could mainly be caused by increasing of Ni2+ in the octahedral sites and the reduction of the mean frequency of phonon density of states in the spinel nanocrystals of solid solutions. The full width at half maximum (FWHM) of emissions for the glass ceramics with different Ga2O3 content was all more than 200 nm. The emission lifetime increased with the Ga2O3 content and the longest lifetime is about 250 mu s. The Ni2+-doped transparent glass ceramics with Ga2O3 addition have potential application as broadband optical amplifier and laser materials. (C) 2007 Elsevier Ltd. All rights reserved.

High Er3+ concentration low refractive index fluorophosphate glass for evanescent wave optical amplifiers

This is about the first reported laser glass with very low no, high Er3+ concentration and no quenching. In this work, a series of high Er3+ concentration (10.6-12.2 x 10(20) ions/cm(3)), low refractive index (n(1550) < 1.47) and relatively high fluorescence lifetime (6.8-12.6 ms) fluorophosphate glasses were made. A cw-pumping evanescent wave optical amplifier experiment was performed with it, and a relative gain of around 2dB at 1550 nm wavelength was achieved while the noise level was almost unchanged. To our knowledge, this is the first successful relative gain in evanescent wave optical amplifiers (EWOA) demonstrated with cw pumping. It is a valuable study of specially designed fluorophosphate glass suitable for EWOA communication experiment. (C) 2008 Elsevier B.V. All rights reserved.

碱金属和碱土金属氟化物对掺Er^3＋氟磷酸盐玻璃光谱性质的影响

研究了碱金属和碱土金属离子修饰的掺Er^3＋氟磷酸盐玻璃的光谱性质，讨论了碱金属和碱土金属对铒氟磷玻璃的吸收和发射截面、荧光半高宽，Judd-Ofelt强度参数和上转换发光强度等光谱性质的影响，并与一些传统氧化物玻璃系统进行了比较．研究表明碱金属K^＋和碱土金属Sr^2＋掺杂高的玻璃更适宜用作光放大器基质．含12mol％K^＋的氟磷玻璃展现出7．83×10^-21cm^2的高发射截面和最小的荧光上转换强度；含23mol％Sr^2＋的氟磷玻璃则有7．58×10^-21cm^2的高发射截面、65nm的荧光半高