Mechanical and thermal cycling effects on the flexural strength of glass ceramics fused to titanium

This study evaluated the effects of mechanical and thermal cycling on the flexural strength (ISO 9693) of three brands of ceramics fused to commercially pure titanium (cpTi). Metallic frameworks of 25 x 3 x 0.5 mm dimensions (N = 84) were cast in cpTi, followed by 150-mu m aluminum oxide airborne particle abrasion at a designated area of the frameworks (8 x 3 mm). Bonder and opaque ceramic were applied on the frameworks, and then the corresponding ceramic (Triceram, Super Porcelain Ti-22, Vita Titankeramik) was fired onto them (thickness: 1 mm). Half of the specimens from each ceramic-metal combination were randomly tested without aging (only water storage at 37 degrees C for 24 hours), while the other half were mechanically loaded (20,000 cycles under 10 N load, immersion in distilled water at 37 degrees C) and thermocycled (3,000 cycles, between 5-55 degrees C, dwell time of 13 seconds). After the flexural strength test, failure types were noted. Mechanical and thermal cycling decreased the mean flexural strength values significantly (p<0.05) for all the three ceramic-cpTi combinations tested when compared to the control group. In all the three groups, failure type was exclusively adhesive at the opaque ceramic-cpTi interfacial zone with no presence of ceramic on the substrate surface except for a visible oxide layer.

Deposition of SiOx Thin Films on Y-TZP by Reactive Magnetron Sputtering: Influence of Plasma Parameters on the Adhesion Properties Between Y-TZP and Resin Cement for Application in Dental Prosthesis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Bond strengths, degree of conversion of the cement and molecular structure of the adhesive-dentine joint in fibre post restorations

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Avaliação da resistência de união metalocerâmica em função de diferentes tempos de oxidação prévia

Avaliou-se a resistência de união metal/porcelana utilizando-se uma liga de Ni-Cr, submetida a diferentes tempos de oxidação prévia com o sistema cerâmico Vita-VMK, através do teste preconizado por CHIODI NETTO3. A análise dos resultados permitiu as seguintes conclusões: a ausência da oxidação prévia possibilitou os melhores resultados, sendo que a diferença foi estatisticamente significante; diferentes tempos de oxidação prévia provocaram redução acentuada nos valores obtidos e foram semelhantes entre si; o grupo submetido ao processo de jateamento após a oxidação prévia por cinco minutos mostrou resultados similares aos grupos que também passaram pelo processo de oxidação e não sofreram jateamento posterior.

Muscle strength assessment among children and adolescents with growing pains and joint hypermobility

OBJETIVO: Avaliar, por meio de teste quantitativo, a força muscular em crianças e adolescentes com dores de crescimento, associada ou não com hipermobilidade articular e comparadas com controles saudáveis. MÉTODO: Quarenta e sete casos de crianças e adolescentes acompanhados por dores de crescimento, sendo 24 com hipermobilidade articular (DC-HA), 23 sem hipermobilidade articular (DC) e 47 controles saudáveis pareados por idade e gênero foram submetidos a dois testes quantitativos para a avaliação da força muscular, o Childhood Myositis Assessment Scale (CMAS) e o Manual Muscle Strength Test (MMT). Os dados antropométricos como altura, peso, índice de massa corporal, prega cutânea tricipital, circunferência média do braço e a área muscular do braço foram comparados entre os três grupos. RESULTADOS: Os três grupos não apresentaram diferença estatística entre as medidas antropométricas. Houve diferença significante entre a mediana da pontuação do CMAS, sendo menores no grupo DC (47, mínimo e máximo 39-52) e DC-HA (46, mínimo e máximo 40-51), comparados com controles (50, mínimo e máximo 45-52; p<0,0001). Dois dos exercícios cronometrados do CMAS, a elevação da cabeça e a duração da elevação das pernas, tiveram menor pontuação nos pacientes comparados aos controles (p<0.0001). A pontuação mediana do MMT no grupo DC (79, mínimo e máximo 73-80) e DC-HA (78, mínimo e máximo 32-80) também apresentou diferença significante, sendo menor nos pacientes que nos controles (80, mínimo e máximo 78-80; p<0,0001). A melhor correlação entre a pontuação do CMAS e MMT foi no grupo DC-HA (Spearman r=0,65; p=0,0007). A aplicação do CMAS e MMT em duas ocasiões apresentou boa concordância e coeficiente de correlação intraclasse de 0,87 (IC 95% 0,64-0,96; p<0,0001) e 0,92 (IC 95% 0,76-0,97; p<0,0001), respectivamente. CONCLUSÃO: Os pacientes com dores de crescimento com ou sem hipermobilidade articular apresentaram fraqueza muscular de leve a moderada quando comparados com controles saudáveis.

Avaliação da influência dos tipos de tratamento superficial da porcelana glazeada na colagem de braquetes ortodônticos

OBJETIVO: o objetivo deste trabalho foi avaliar a influência do tipo de tratamento superficial da porcelana na resistência adesiva da colagem de braquetes ortodônticos e o modo de fratura após a descolagem. METODOLOGIA:foram confeccionados 80 corpos-de-prova de porcelana, divididos em quatro grupos (n = 18) de acordo com os diferentes tratamentos de superfície: (G1) ponta diamantada; (G2) ponta diamantada e silano; (G3) ácido hidrofluorídrico e (G4) ácido hidrofluorídrico e silano. Após o preparo das superfícies, braquetes Edgewise (Morelli) foram colados com resina (Transbond XT, 3M) e submetidos ao teste de cisalhamento. Os resultados foram avaliados estatisticamente pelo teste de Kruskal-Wallis. RESULTADO: o grupo G1 apresentou uma média de resistência de 3,35, o G2 3,97, o G3 2,56 e o G4 3,10. CONCLUSÃO: constatou-se que não houve diferença estatisticamente significativa na resistência adesiva do braquete entre os tipos de tratamentos estudados (p > 0,05) e os modos de fratura ocorreram, em sua grande maioria, na interface braquete/resina. Este estudo indica que todos os tipos de tratamentos apresentados são eficientes para a colagem.

Adhesives with different pHs: Effect on the MTBS of chemically activated and light-activated composites to human dentin

Purpose: To evaluate the bond strength between human dentin and composites, using two light-activated single-bottle total-etch adhesive systems with different pHs combined with chemically activated and light-activated-composites. The tested hypothesis was that the dentin bond strength is not influenced by an adhesive system of low pH, combined with chemically activated or light-activated composites. Material and Method: Flat dentin surfaces of twenty-eight human third molars were allocated in 4 groups (n=7), depending on the adhesive system: (One Step Plus-OS and Prime & Bond NT-PB) and composite (light-activated Filtek Z-100 [Z100] and chemically activated Bisfil 2B [B2B]). Each adhesive system was applied on acid-etched dentin and then one of the composites was added to form a 5 mm-high resin block. The specimens were stored in tap water (37 degrees C/24 h) and sectioned into two axes, x and y. This was done with a diamond disk under coolant irrigation to obtain beams with a cross-section area of approximately 0.8 mm(2). Each specimen was then attached to a custom-made device and submitted to the microtensile test (1 mm.min(-1)). Data were analyzed using two-way ANOVA and Tukey's tests (p<0.05). Results: the anticipated hypothesis was not confirmed (p<0.0001). The bond strengths (MPa) were not statistically different between the two adhesive systems when light-activated composite was used (OS+Z100 = 24.7 +/- 7.1(a); PB+Z100 = 23.8 +/- 5.7(a)). However, with use of the chemically activated composite (B2B), PB (7.8 +/- 3.6(b) MPa) showed significantly lower dentin bond strengths than OS (32.2 +/- 7.6(a)). Conclusion: the low pH of the adhesive system can affect the bond of chemically activated composite to dentin. on the other hand, under the present conditions, the low pH did not seem to affect the bond of light-activated composites to dentin significantly.

Polymerization shrinkage: effects of boundary conditions and filling technique of resin composite restorations

Objective: To evaluate the linear polymerization shrinkage (LPS) and the effect of polymerization shrinkage of a resin composite and resin-dentin bond strength under different boundary conditions and filling techniques.Methods: Two cavities (4 x 4 x 2 MM) were prepared in bovine incisors (n = 30). The teeth were divided into three groups, according to boundary conditions: In group TE, the total-etch technique was used. In group EE, only enamel was conditioned, and in group NE, none of the watts of the cavities were conditioned. A two-step adhesive system was applied to all cavities. The resin composite was inserted in one (B) or three increments (1), and tight-cured with 600 mW/cm(2) (80 s). The LPS (%) was measured in the top-bottom direction, by placing a probe in contact with resin composite during curing. Enamel and total mean gap widths were measured (400 x) in three slices obtained after sectioning the restorations. Then, the slices were sectioned again, either to obtain sticks from the adhesive interface from the bottom of the cavity or to obtain resin composite sticks (0.8 mm(2)) to be tested for tensile strength (Kratos machine, 0.5 mm/min). The data was subjected to a two-way repeated measures ANOVA and Tukey's test for comparison of the means (alpha = 0.05).Results: the highest percentage of LPS was found for the TE when bulk fitted, and the lowest percentage of LPS was found in the Hand NE when incrementally fitted. The resin dentin bond strength was higher and the total mean gap width was tower for TE group; no significant effect was detected for the main factor fitting techniques. No difference was detected for the tensile strength of resin composite among the experimental groups.Conclusions: the filling technique is not able to minimize effects of the polymerization shrinkage, and bonding to the cavity watts is necessary to assure reduced mean gap width and high bond strength values. (C) 2004 Elsevier Ltd. All rights reserved.

The effect of ceramic surface treatment on bonding to densely sintered alumina ceramic

Statement of problem. Ceramic surface treatment is crucial for bonding to resin. High crystalline ceramics are poorly conditioned using traditional procedures.Purpose. The purpose of this study was to evaluate the effect of silica coating on a densely sintered alumina ceramic relative to its bond strength to composite, using a resin luting agent.Material and methods. Blocks (6 X 6 X 5 mm) of ceramic and composite were made. The ceramic (Procera AllCeram) surfaces were polished, and the blocks were divided into 3 groups (n = 5): SB, airborne-particle abrasion with 110-mu m Al(2)O(3); RS, silica coating using Rocatec System; and CS, silica coating using CoJet System. The treated ceramic blocks were luted to the composite (W3D Master) blocks using a resin luting agent (Panavia F). Specimens were stored in distilled water at 37 degrees C for 7 days and then Cut in 2 axes, x and y, to obtain specimens with a bonding area of approximately 0.6 mm(2) (n = 30). The specimens were loaded to failure in tension in a universal testing machine, and data were statistically analyzed using a randomized complete block design analysis of variance and Tukey's test (alpha=.05). Fractured surfaces were examined using light microscopy and scanning electron microscopy to determine the type of failure. Energy-dispersive spectroscopy was used for surface compositional analysis.Results. Mean bond strength values (MPa) of Groups RS (17.1 +/- 3.9) (P = .00015) and CS (18.5 +/- 4.7) (P=.00012) were significantly higher than the values of Group SB (12.7 +/- 2.6). There was no statistical difference between Groups RS and CS. All failures occurred at the adhesive zone.Conclusion. Tribochemical silica coating systems increased the tensile bond strength values between Panavia F and Procera AllCeram ceramic.

Surface conditioning of a composite used for inlay/onlay restorations: Effect on mu TBS to resin cement

Purpose: To assess the effect of the composite surface conditioning on the microtensile bond strength of a resin cement to a composite used for inlay/onlay restorations.Materials and Methods: Forty-two blocks (6 x 6 x 4 mm) of a microfilled composite (Vita VMLC) were produced and divided into 3 groups (N = 14) by composite surface conditioning methods: Gr1 - etching with 37% phosphoric acid, washing, drying, silanization; Gr2 - air abrasion with 50-Im Al203 particles, silanization; Gr3 - chairside tribochemiCal silica coating (CoJet System), silanization. Single-Bond (one-step adhesive) was applied on the conditioned surfaces and the two resin blocks treated with the same method were cemented using RelyX ARC (dual-curing resin cement). The specimens were stored for 7 days in water at 37 degrees C and then sectioned to produce nontrimmed beam samples, which were submitted to microtensile bond strength testing (mu TBS). For statistical analysis (one-way ANOVA and Tukey's test, = 0.05), the means of the beam samples from each luted specimen were calculated (n = 7).Results: mu TBS values (MPa) of Gr2 (62.0 +/- 3.9a) and Gr3 (60.5 +/- 7.9a) were statistically similar to each other and higher than Gr1 (38.2 +/- 8.9b). The analysis of the fractured surfaces revealed that all failures occurred at the adhesive zone.Conclusion: Conditioning methods with 50-Im Al203 or tribochemical silica coating allowed bonding between resin and composite that was statistically similar and stronger than conditioning with acid etching.

Microleakage and nanoleakage: Influence of laser in cavity preparation and dentin pretreatment

Objective: the purpose of this study was to verify if the application of the Nd:YAG laser following pretreatment of dentin with adhesive systems that were not light cured in class V cavities and were prepared with Er:YAG laser would promote better sealing of the gingival margins when compared to cavities prepared the conventional way. Background Data: Previous studies had shown that the pretreatment of dentin with laser irradiation after the application of an adhesive system is efficient in achieving higher shear bond and tensile bond strength. Materials and Methods: Er:YAG laser (Kavo-Key, Germany) with 350 mJ, 4 Hz, and 116.7 J/cm(2) was used for cavity preparation. The conventional preparation was made with diamond bur mounted in high-speed turbine. Dentin treatment was accomplished using an Nd:YAG laser (Pulse Master 1000, ADT. USA) at 60 mJ, 10 Hz, and 74.65/cm(2) following application of the adhesive system. The cavities were stored with Single Bond/Z100 and Prime & Bond NT/TPH. Eighty bovine incisors were used, and class V preparations were done at buccal and lingual surfaces divided into eight groups: (1) Er:YAG preparation + Prime & Bond NT + TPH; (2) Er:YAG preparation + Single Bond + Z100; (3) Er:YAG preparation + Single Bond + Nd:YAG + Z100; (4) Er:YAG preparation + Prime & Bond NT + Nd:YAG + TPH; (5) conventional preparation + Prime & Bond NT + TPH; (6) conventional preparation + Single Bond + Z100; (7) conventional preparation + Single Bond + Nd:YAG + Z100; (8) conventional preparation + Prime & Bond NT + Nd:YAG + TPH. All specimens were thermocycled for 300 full cycles between 5 degreesC +/- 2 degreesC and 55 degreesC +/- 2 degreesC (dwell time of 30 sec), and stored in 50% silver nitrate solution for 24 h soaked in photodeveloping solution and exposed to fluorescent light for 6 h. After this procedure, the specimens were sectioned longitudinally in 3 portions and the extension of microleakage at the gingival wall was determined following a criteria ranging from 0 to 4 using scanning electron microscopy (SEM). The medium portion sectioned of each specimen was polished and prepared for nanoleakage avaliation by SEM. Results: Kruskall-Wallis and Miller statistical tests determined that group 3 presented less microleakage and nanoleakage. Conclusion: Application of the Nd:YAG laser following pretreatment of dentin with adhesive Single Bond non-photocured Single Bond adhesive in cavities prepared with Er:YAG promote better sealing of the gingival margins.

Effects of Strength Training on Running Economy

The objective of this study was to compare the effect of different strength training protocols added to endurance training on running economy (RE). Sixteen well-trained runners (27.4 +/- 4.4 years; 62.7 +/- 4.3 kg; 166.1 +/- 5.0 cm), were randomized into two groups: explosive strength training (EST) (n = 9) and heavy weight strength training (HWT) (n = 7) group. They performed the following tests before and after 4 weeks of training: 1) incremental treadmill test to exhaustion to determine of peak oxygen uptake and the velocity corresponding to 3.5 mM of blood lactate concentration; 2) submaximal constant-intensity test to determine RE; 3) maximal countermovernent jump test and; 4) one repetition maximal strength test in leg press. After the training period, there was an improvement in RE only in the HWT group (HWT = 47.3 +/- 6.8 vs. 44.3 +/- 4.9 ml.kg(-1) -min(-1); EST = 46.4 +/- 4.1 vs. 45.5 +/- 4.1 ml.kg(-1) .min(-1)). In conclusion, a short period of traditional strength training can improve RE in well-trained runners, but this improvement can be dependent on the strength training characteristics. When comparing to explosive training performed in the same equipment, heavy weight training seems to be more efficient for the improvement of RE.

An In Vitro Comparison of Different Cementation Strategies on the Pull-out Strength of a Glass Fiber Post

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

The slippery slope - Critical perspectives on in vitro research methodologies

Objectives. This paper attempts to provide critical perspectives on common in vitro research methodologies, including shear bond testing, wear testing, and load-to-failure tests. Origins of interest in high-quality laboratory data is reviewed, in vitro data is categorized into property and simulation protocols, and two approaches are suggested for establishing clinical validity. It is hoped that these insights will encourage further progress toward development of in vitro tests that are validated against clinical performance and/or by producing clinically validated failure or damage mechanisms.Materials and methods. Published shear and tensile bond data (macro and micro) is examined in light of published finite element analyses (FEA). This data is subjected to a Weibull scaling analysis to ascertain whether scaling is consistent with failure from the bonded interface or not. Wear tests results are presented in light of the damage mechanism(s) operating. Quantitative wear data is re-examined as being dependent upon contact pressure. Load-to-failure test results are re-analyzed by calculating contact stresses at failure for 119 tests from 54 publications over more than 25 years.Results. FEA analyses and reported failure modes (adhesive, mixed, cohesive) are consistent with failure not involving interfacial "shear stresses" as calculated in published work. Weibull scaling clearly suggests failure involving external surfaces of specimens, not interfacial origins. Contact stresses (pressures) are clearly an important variable in wear testing and are not well-controlled in published work. Load-to-failure tests create damage not seen clinically due to excessively high contact stresses. Most contact stresses in the 119 tests examined were calculated to be between 1000 MPa and 5000 MPa, whereas clinical contact stresses at wear facets have been measured not to exceed 40 MPa.Conclusions. Our community can do a much better job of designing in vitro tests that more closely simulate clinical conditions, especially when contact is involved. Journals are encouraged to thoughtfully consider a ban on publishing papers using bond tests and load-to-failure methods that are seriously flawed and have no clinical relevance. (C) 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Influência de diferentes agentes de fixação na resistência de união, por tração, de ligas metálicas fixadas à dentina.

They were casted pieces using three kinds of alloy (Ni-Cr, Ag-Sn and Cu-Al) with circular and smooth surface. They were cemented to human teeth, on occlusal surface, grounded at dentin level, through three different materials kind (zinc polycarboxylate cement, glassionomer cement and composite). After 24 hours storing, the samples were subjected to the tensile test. The results showed that the samples cemented with composite and the casts made with Ag-Sn alloy had higher bond strength.