Chlorhexidine does not increase immediate bond strength of etch-and-rinse adhesive to caries-affected dentin of primary and permanent teeth

The aim of this study was to evaluate the effect of 2% chlorhexidine digluconate (CHX) on immediate bond strength of etch-and-rinse adhesive to sound (SD) and caries-affected (CAD) primary dentin compared with permanent dentin. Flat dentin surfaces from 20 primary molars (Pri) and 20 permanent molars (Perm) were assigned to 8 experimental groups (n=5) according to tooth type (Pri or Perm), dentin condition (SD or CAD - pH-cycling for 14 days) and treatment (control - C or 60 s application of 2% CHX solution after acid etching - CHX). The bonding system (Adper Single Bond 2) was applied according to manufacturer's instructions followed by resin composite application (Filtek Z250). After 24 h water storage, specimens with cross-section area of 0.8 mm² were prepared for being tested under microtensile test (1 mm/min). Data were submitted to ANOVA and Tukey's post hoc test (α=0.05). Failure mode was evaluated using a stereomicroscope at ×400. Treatment with CHX did not result in higher bond strength values than no pre-treatment (C groups), independently of tooth type. Primary teeth and caries-affected dentin showed significantly lower (p<0.05) bond strength means compared with permanent teeth and sound dentin, respectively. Predominance of adhesive/mixed failure was observed for all groups. CHX did not influence the immediate bond strength to sound or caries-affected dentin of primary and permanent teeth.

Influence of alloy microstructure on the microshear bond strength of basic alloys to a resin luting cement

The aim of this study was to evaluate the influence of microstructure and composition of basic alloys on their microshear bond strength (µSBS) to resin luting cement. The alloys used were: Supreme Cast-V (SC), Tilite Star (TS), Wiron 99 (W9), VeraBond II (VBII), VeraBond (VB), Remanium (RM) and IPS d.SIGN 30 (IPS). Five wax patterns (13mm in diameter and 4mm height) were invested, and cast in a centrifugal casting machine for each basic alloy. The specimens were embedded in resin, polished with a SiC paper and sandblasted. After cleaning the metal surfaces, six tygon tubes (0.5 mm height and 0.75 mm in diameter) were placed on each alloy surface, the resin cement (Panavia F) was inserted, and the excess was removed before light-curing. After storage (24 h/37°C), the specimens were subjected to µSBS testing (0.5 mm/min). The data were subjected to a one-way repeated measures analysis of variance and Turkey's test (α=0.05). After polishing, their microstructures were revealed with specific conditioners. The highest µSBS (mean/standard deviation in MPa) were observed in the alloys with dendritic structure, eutectic formation or precipitation: VB (30.6/1.7), TS (29.8/0.9), SC (30.6/1.7), with the exception of IPS (31.1/0.9) which showed high µSBS but no eutectic formation. The W9 (28.1/1.5), VBII (25.9/2.0) and RM (25.9/0.9) showed the lowest µSBS and no eutectic formation. It seems that alloys with eutectic formation provide the highest µSBS values when bonded to a light-cured resin luting cement.

Effect of tin-chloride pretreatment on bond strength of two adhesive systems to dentin

OBJECTIVES: To determine the effect on resin composite-to-dentin bond strength of incorporation of an acidic tin-chloride pretreatment in two adhesive systems. MATERIALS AND METHODS: Human molars were ground to expose mid-coronal dentin. For microtensile bond strength (μTBS) testing, dentin was treated with Optibond FL or Clearfil SE according to one of six protocols (n = 22/group). Group 1: Phosphoric acid etching, Optibond FL Prime, Optibond FL Adhesive (manufacturer's instructions; control); Group 2: Tin-chloride pretreatment, Optibond FL Prime, Optibond FL Adhesive; Group 3: Phosphoric acid etching, tin-chloride pretreatment, Optibond FL Prime, Optibond FL Adhesive; Group 4: Clearfil SE Primer, Clearfil SE Bond (manufacturer's instructions; control); Group 5: Phosphoric acid etching, Clearfil SE Primer, Clearfil SE Bond; and Group 6: Tin-chloride pretreatment, Clearfil SE Primer, Clearfil SE Bond. The molars were then built up with resin composite (Clearfil Majesty Esthetic). After storage (1 week, 100  % humidity, 37 °C) the μTBS was measured and failure mode was determined. Additionally, pretreated dentin surfaces were evaluated using SEM and EDX. The μTBS results were analyzed statistically by a Welch Two Sample t-test and a Kruskal-Wallis test followed by exact Wilcoxon rank sum tests with Bonferroni-Holm adjustment for multiple testing (α = 0.05). RESULTS: When Optibond FL was used, partial or total replacement of phosphoric acid with tin-chloride decreased μTBS significantly. In contrast, when Clearfil SE was used, inclusion of a tin-chloride pretreatment in the adhesive procedure increased μTBS significantly. CONCLUSIONS: Tin-chloride pretreatment had a beneficial influence on the bond promoting capacity of the MDP-containing adhesive system Clearfil SE.

Does tin pre-treatment enhance the bond strength of adhesive systems to enamel?

OBJECTIVES The study investigated the modification of composite-to-enamel bond strength by pre-treatment of enamel with a concentrated, acidic SnCl2-solution. METHODS Six groups of flat human enamel specimens (n=44 per group) were treated as follows: OB-H: H3PO4 etching, Optibond FL application (primer+adhesive; manufacturer's instructions); OB-S: SnCl2 pre-treatment, Optibond FL application (primer+adhesive); OB-HS: H3PO4 etching+SnCl2 pre-treatment, Optibond FL application (primer+adhesive); CF-N: Clearfil SE application (primer+bond; manufacturer's instructions); CF-H: H3PO4 etching, Clearfil SE application (primer+bond); CF-S: SnCl2 pre-treatment, Clearfil SE application (primer+bond). Enamel specimens were then built up with resin composite (Clearfil Majesty Esthetic) and stored (100% humidity, 37 °C, 1 week). μTBS-measurement and failure mode analysis of one-half of the specimens were performed immediately after storage, while the other half was analysed after a thermocycling procedure (8500 cycles; 5 °C and 55 °C; dwell time 30s). Additional specimens were prepared for SEM- and EDX-analysis. RESULTS Highest values were measured for OB-H before and after thermocycling, lowest values for CF-N. Compared to OB-H treatment, OB-S treatment reduced μTBS before/after thermocycling by 23%/28% and OB-HS treatment by 8%/24% (except for OB-SH before (n.s.), all p≤0.001 compared to OB-H). In the Clearfil SE treated groups pre-treatment increased μTBS significantly compared to CF-N (before/after: CF-H: +46%/+70%; CF-S: +51%/42%; all p≤0.001). CONCLUSION Pre-treatment with H3PO4 or SnCl2 markedly increased the μTBS of Clearfil SE to enamel. However, thermocycling partly reduced the gain in μTBS obtained by SnCl2 pre-treatment. CLINICAL SIGNIFICANCE The application of an acidic and highly concentrated SnCl2 solution is a good option to increase the μTBS between enamel and a resin composite mediated by an adhesive system containing the multifunctional monomer MDP.

Bonding of simplified adhesive systems to caries-affected dentin of primary teeth.

PURPOSE To evaluate the bonding of simplified adhesive systems to sound and caries-affected dentin of primary teeth with microtensile (µTBS) and nanoleakage (NL) tests. MATERIALS AND METHODS Occlusal cavities were prepared in 36 sound second primary molars. Half of the specimens were submitted to pH cycling to simulate caries-affected dentin. Teeth were randomly restored with one of three materials: the etch-and-rinse adhesive system Adper Single Bond 2 (SB), the two-step self-etching adhesive system Adper SE Plus (SE), and the one-step self-etching adhesive system Adper Easy One (EASY). After storage for 24 h, specimens with cross-sectional areas of 0.8 mm2 were prepared for microtensile testing (1 mm/min). One stick from each tooth was immersed in silver nitrate solution (24 h) and allowed to develop for 8 h in order to score the nano leakage with SEM. The fracture pattern was evaluated using a stereomicroscope (400X). The µTBS means were analyzed by two-way ANOVA and Tukey's post-hoc test. For NL, the Kruskal- Wallis and Mann-Whitney tests were used (α < 0.05). RESULTS SB (35.5 ± 3.5) showed the highest µTBS value to sound dentin, followed by EASY (26.3 ± 1.9) and SE (18.2 ± 6.5) (p < 0.05). No difference among materials was observed for caries-affected dentin (SB: 17.8 ± 4.2; SE: 13.9 ± 3.2; EASY: 14.4 ± 4.2, p > 0.05). For all groups, adhesive/mixed fracture prevailed. Caries affected dentin promoted silver nitrate uptake into the adhesive interface; however, with SE, the nano leakage was more pronounced than in the other adhesive systems, even in sound dentin. CONCLUSION Caries-affected dentin negatively influences the bond strength and nano leakage of the two-step etch-and-rinse and one-step self-etching adhesive systems tested in primary teeth.

Influence of blood contamination on bond strength of a self-etching system.

OBJECTIVES: To detect the influence of blood contamination (BC) on the bond strength (BS) of a self-etching bonding system (SES) to enamel and dentine. METHODS: 25 human molars were longitudinally sectioned on the mesio-distal axis in order to obtain 50 specimens, which were embedded in acrylic resin. At first, the specimens were ground to expose a flat surface of enamel, and a bond strength test was performed. Afterwards, the samples were ground again in order to obtain a flat surface of dentine. Ten groups (total: n=100) were assigned according to substrate (enamel and dentine), step in the bonding sequence when contamination occurred (before the acidic primer and after the bonding resin), and contamination treatment (dry or rinse and dry procedure). Fresh human blood was introduced either before or after SES application (Clearfil SE Bond) and treated with air drying, or by rinsing and drying following application. Composite resin (Filtek Z-250,3M ESPE) was applied as inverted, truncated cured cones that were debonded in tension. RESULTS: The mean tensile BS values (MPa) for enamel/dentine were 19.4/23.0 and 17.1/10.0 for rinse-and-dry treatment (contamination before and after SES, respectively); while the measurements for the dry treatment, 16.2/23.3 and 0.0/0.0 contamination before and after SES, respectively. CONCLUSIONS: It was determined that blood contamination impaired adhesion to enamel and dentine when it occurred after bond light curing. Among the tested contamination treatments, the rinse-and-dry treatment produced the highest bond strength with BC after SES application, but it was not sufficient to recover the BS in the contamination-free group.

Influence of increment thickness on microhardness and dentin bond strength of bulk fill resin composites

OBJECTIVES To investigate the influence of increment thickness on Vickers microhardness (HV) and shear bond strength (SBS) to dentin of a conventional and four bulk fill resin composites. METHODS HV and SBS were determined on specimens of the conventional resin composite Filtek Supreme XTE (XTE) and the bulk fill resin composites SDR (SDR), Filtek Bulk Fill (FBF), x-tra fil (XFIL), and Tetric EvoCeram Bulk Fill (TEBF) after 24h storage. HV was measured either as profiles at depths up to 6mm or at the bottom of 2mm/4mm/6mm thick resin composite specimens. SBS of 2mm/4mm/6mm thick resin composite increments was measured to dentin surfaces of extracted human molars treated with the adhesive system OptiBond FL, and the failure mode was stereomicroscopically determined at 40× magnification. HV profiles and failure modes were descriptively analysed whereas HV at the bottom of resin composite specimens and SBS were statistically analysed with nonparametric ANOVA followed by Wilcoxon rank sum tests (α=0.05). RESULTS HV profiles (medians at 2mm/4mm/6mm): XTE 105.6/88.8/38.3, SDR 34.0/35.5/36.9, FBF 36.4/38.7/37.1, XFIL 103.4/103.9/101.9, TEBF 63.5/59.7/51.9. HV at the bottom of resin composite specimens (medians at 2mm/4mm/6mm): XTE (p<0.0001) 105.5>85.5>31.1, SDR (p=0.10) 25.8=21.9=26.0, FBF (p=0.16) 26.6=25.3=28.9, XFIL (p=0.18) 110.5=107.2=101.9, TEBF (p<0.0001) 63.0>54.9>48.2. SBS (MPa, medians at 2mm/4mm/6mm): XTE (p<0.0001) 23.9>18.9=16.7, SDR (p=0.26) 24.6=22.7=23.4, FBF (p=0.11) 21.4=20.3=22.0, x-tra fil (p=0.55) 27.0=24.0=23.6, TEBF (p=0.11) 21.0=20.7=19.0. The predominant SBS failure mode was cohesive failure in dentin. SIGNIFICANCE At increasing increment thickness, HV and SBS decreased for the conventional resin composite but generally remained constant for the bulk fill resin composites.

Restauración de incisivo inferior fracturado mediante procedimientos de invasión mínima : reporte de un caso clínico

La odontología está inmersa en un nuevo paradigma: no se puede pensar en ninguna técnica restauradora sin que participen fenómenos de adhesión. El desarrollo de pernos de fibra de vidrio, sumado a los procedimientos de restauraciones adhesivas puede utilizarse como uno de los tantos recursos de la odontología de invasión mínima. Los pernos de fibra de vidrio ofrecen varias ventajas: comportamiento anisótropo, módulo de elasticidad bajo, buena resistencia mecánica, el lecho que aloja al perno de fibra requiere de una mínima preparación y se cementan con cementos adhesivos con carga, permitiendo de esta manera obtener una superficie homogénea que se interpone entre el perno de fibra y los tejidos dentales, conectándolo a los tejidos del conducto y sustituyendo mecánicamente la dentina. El caso clínico que se reporta se presentó para su resolución en la Clínica Integrada III F. O. UNCuyo durante el año lectivo 2009. El paciente presentaba una fractura amelodentinaria desde hacía cuatro años, con compromiso de la vitalidad y un proceso periapical. Durante los procedimientos endodónticos se realizó una perforación de la pared del conducto que se selló mediante la colocación de hidróxido de calcio y la obturación del mismo con conos de gutapercha. Se efectuó el seguimiento clínico y radiográfico del caso en donde se constató la reparación del proceso apical y luego se procedió a la restauración del elemento dentario con resinas compuestas con la ayuda de un poste de fibra de vidrio cementado con cemento resinoso. Dadas las características del tratamiento endodóntico realizado, se decidió dejar más porción del cono de gutapercha a pesar de lo aconsejado por numerosos autores, ya que de esta manera se aseguró el sellado de la perforación radicular para evitar de esta manera la nanofiltración hacia el interior del elemento dentario.

Nucleator-dependent intercellular assembly of adhesive curli organelles in Escherichia coli.

Bacterial adhesion to other bacteria, to eukaryotic cells, and to extracellular matrix proteins is frequently mediated by cell surface-associated polymers (fimbriae) consisting of one or more subunit proteins. We have found that polymerization of curlin to fimbriae-like structures (curli) on the surface of Escherichia coli markedly differs from the prevailing model for fimbrial assembly in that it occurs extracellularly through a self-assembly process depending on a specific nucleator protein. The cell surface-bound nucleator primes the polymerization of curlin secreted by the nucleator-presenting cell or by adjacent cells. The addition of monomers to the growing filament seems to be driven by mass action and guided only by the diffusion gradient between the source of secreted monomer and the surface of monomer condensation.

Synthesis and assembly of self-complementary calix[4]arenes.

A calix[4]arene was designed to reversibly dimerize and form an egg-shaped enclosure. Adhesive interactions in the assembly were provided by four self-associating ureas, which form a cyclic array containing 16 hydrogen bonds. The synthesis was completed in four steps from the previously described O,O',O",O"'-tetrabenzylcalix[4]arene. Evidence for dimerization of the calixarene tetraurea was provided by H NMR, mass spectrometry, and the observation of encapsulated molecules. The resulting cavity was of sufficient size to capture guests such as ethyl benzene and p-xylene.

Self-standing curved crystals for X and Gamma rays focusing

The efficiency of a Laue lens for X and Gamma ray focusing in the energy range 60 ÷ 600 keV is closely linked to the diffraction efficiency of the single crystals composing the lens. A powerful focusing system is crucial for applications like medical imaging and X ray astronomy where wide beams must be focused. Mosaic crystals with a high density, such as Cu or Au, and bent crystals with curved diffracting planes (CDP) are considered for the realization of a focusing system for X rays, owing to their high diffraction efficiency. In this work, a comparison of the efficiency of CDP crystals and mosaic crystals was performed on the basis of the theory of X-ray diffraction. Si, GaAs and Ge CDP crystals with optimized thicknesses and moderate radii of curvature of several tens of metres demonstrate comparable or superior performance with respect to the higher atomic number mosaic crystals generally used. A simplified approach for calculating the integrated reflectivity of the crystals is applied. A bending technique used during this work to realize CDP crystals consists in a controlled surface damaging induced by a mechanical lapping process. A compressive strained layer of few micrometres in thickness is generated and causes the convex curvature of the damaged side of the crystal. Another new bending technique is developed and the main results are shown. The process consists on a film deposition of a selected bi-component epoxy resin on one side of crystal, made uniform in thickness by mean of a spin-coater. Choosing the speed of spin-coating, so changing the thickness of the film, a control of radius of curvature can be obtained. Moreover the possibility to combine the two bending technique to obtain CDP crystal with a stronger curvature in rather thick crystals was demonstrated. Detailed characterization of Si, and GaAs CDP crystals at low and high x-ray energies are performed on flat and bent crystals obtained with the damaging and the resin deposition technique. As expected an increase of diffraction efficiency in asymmetrical diffraction geometry in CDP crystals with respect to the flat ones is observed. On the other hand an unexpected increase of the integrated intensity in symmetrical geometry, not predicted by the theory, is observed in all the measurements performed with different set up. The experimental trend of the integrated reflectivity as a function of the radius of curvature is in a good agreement with that predicted by the theory of bent perfect crystals, so it is possible to conclude that the surface damage has a limited effect on the crystal reflectivity. A study of the integrated reflectivity in the energy range of interest (100÷350 keV) in CDP crystals realized with damaging and resin deposition technique at symmetrical and asymmetrical geometries was performed at ILL Institute. Also at these energies the diffraction efficiency of bent crystals was much larger (a 12 time increase is observed for bent crystals in asymmetrical 111 geometry) than that measured in flat crystals. The diffraction efficiency of CDP crystals realized with both techniques tends to coincide with that of flat crystals at very high energies (> 200 keV). This suggesting that also real flat perfect crystals can be considered as strongly bent or mosaic crystals at very high X ray energies.

Análise in vitro da morfologia e da resistência de união da resina composta à dentina erodida e irradiada com laser de Er:YAG com largura de pulso super curta

Lesões dentais por erosão têm sido cada vez mais presentes na prática clínica. A restauração direta com resina composta é uma das opções de tratamento para lesões severas, em que há comprometimento estético/funcional. Com o aprimoramento da tecnologia, a utilização do laser para pré-tratamento da superfície dentinária, antes do condicionamento ácido, tem sido considerada como método alternativo para melhorar a adesão das resinas compostas às superfícies erodidas. Assim, o objetivo deste estudo in vitro foi avaliar a influência da irradiação com laser de Er:YAG (2,94 ?m), de pulso super-curto, na adesão da resina composta à superfície dentinária erodida. Quarenta e seis discos de dentina foram obtidos a partir de 46 dentes terceiros molares humanos. A dentina oclusal planificada de 40 molares humanos teve metade de sua face protegida com fita UPVC (dentina hígida), enquanto na outra metade foi produzida uma lesão de erosão através da ciclagem em ácido cítrico (0,05 M, pH 2,3, 10 minutos, 6x/dia) e solução supersaturada (pH 7,0, 60 minutos entre os ataques ácidos). Metade das amostras foi irradiada com o laser de Er:YAG (50 ?s, 2 Hz, 80 mJ, 12,6 J/cm2) e a outra não (grupo controle). Em cada grupo de tratamento (laser ou controle) (n=10), um sistema adesivo autocondicionante foi utilizado e, então, confeccionados 2 cilindros de resina composta, tanto do lado erodido como no hígido (total de 4 cilindros), os quais foram submetidos à avaliação da Resistência de União através do ensaio de microcisalhamento (1 mm/min), após armazenamento em saliva artificial por 24 h. A análise do padrão de fratura foi realizada em microscópio óptico (40x). Por meio da Microscopia Eletrônica de Varredura (MEV), a morfologia das superfícies dentinárias hígida e submetida ao desafio erosivo, antes e após o tratamento com laser de Er:YAG (n=3), foi avaliada. Os valores obtidos de resistência de união (MPa) foram submetidos ao teste ANOVA e de comparações múltiplas de Tukey (p<0,05) e as análises das eletromicrografias foram feitas de forma descritiva. A análise morfológica da superfície mostrou alterações significativas na dentina hígida irradiada e na submetida à ciclagem erosiva, irradiada ou não. Quanto à resistência de união, houve diferença entre os 4 substratos analisados, sendo: dentina hígida irradiada (12,77±5,09 A), dentina hígida não irradiada (9,76±3,39 B), dentina erodida irradiada (7,62±3,39 C) e dentina erodida não irradiada (5,12±1,72 D). Houve predominância de padrão de fratura do tipo adesiva. Com base nos resultados e nos parâmetros de irradiação utilizados neste estudo, pode-se concluir que a erosão reduz a adesão em dentina e que o tratamento da superfície dentinária com laser de Er:YAG de largura de pulso super curta aumenta a adesão no substrato erodido ou hígido.

Self-sensing properties of alkali activated blast furnace slag (BFS) composites reinforced with carbon fibers

In recent years, several researchers have shown the good performance of alkali activated slag cement and concretes. Besides their good mechanical properties and durability, this type of cement is a good alternative to Portland cements if sustainability is considered. Moreover, multifunctional cement composites have been developed in the last decades for their functional applications (self-sensing, EMI shielding, self-heating, etc.). In this study, the strain and damage sensing possible application of carbon fiber reinforced alkali activated slag pastes has been evaluated. Cement pastes with 0, 0.29 and 0.58 vol % carbon fiber addition were prepared. Both carbon fiber dosages showed sensing properties. For strain sensing, function gage factors of up to 661 were calculated for compressive cycles. Furthermore, all composites with carbon fibers suffered a sudden increase in their resistivity when internal damages began, prior to any external signal of damage. Hence, this material may be suitable as strain or damage sensor.

A practical treatise on the preparation, combination and application of calcareous and hydraulic limes and cements : compiled and arranged from the best authorities, and from the practical experience of the compiler during a long professional career /

Includes index.