Synthesis of a functionalized europium complex and deposition of luminescent Langmuir-Blodgett (LB) films

The synthesis, characterization and formation of Langmuir-Blodgett (LB)films for the luminescent [(C12H25)(2)(CH3)(2)N][Eu(tta)(4)] complex, where [(C12H25)(2)(CH3)(2)](N+) is didodecyldimethylammonium and the tta ligand is thenoyltrifluoroacetone, are reported. The coordination of tta ligands to the Eu3+ ion was confirmed by FTIR spectroscopy and the emission spectrum comprised bands corresponding to D-5(0) -> F-7(0-4) transitions. The lifetime (tau) from the emission state (D-5(0))was 0.41 ms, measured by monitoring the hypersensitive D-5(0) -> F-7(2) transition, with the curve being fitted with a first-order exponential function. The surface pressure-area isotherm indicated that the anionic complex may form condensed structures at the air-water interface due to the amphiphilic properties of the counter ion and the beta-diketone ligand. Y-type LB films of [(C12H25)(2)(CH3)(2)N][Eu(tta)(4)] were deposited on quartz substrates, with preserved luminescence and a band assigned to the D-5(0) -> F-7(2) transition. The molecular arrangement at the air/water interface and the preserved luminescence in LB films are consistent with theoretical predictions using a semi-empirical Sparkle/AM1 calculation method for the molecule in vacuum. These tools were used for the first time to predict the behavior of organized films.

Effect of the vanadium(V) concentration on the spectroscopic properties of nanosized europium-doped yttrium phosphates

Nanosized rare earth phosphovanadate phosphors (Y(P,V)O-4:Eu3+) have been prepared by applying the organic-inorganic polymeric precursors methodology. Luminescent powders with tetragonal structure and different vanadate concentrations (0%, 1%, 5%, 10%, 20%, 50%, and 100%, with regard to the phosphate content) were then obtained for evaluation of their structural and spectroscopic properties. The solids were characterized by scanning electron microscopy, X-ray diffractometry, vibrational spectroscopy (Raman and infrared), and electronic spectroscopy (emission, excitation, luminescence lifetimes, chromaticity, quantum efficiencies, and Judd-Ofelt intensity parameters). The solids exhibited very intense D-5(0) -> F-7(J) Eu3+ transitions, and it was possible to control the luminescent characteristics, such as excitation maximum, lifetime and emission colour, through the vanadium(V) concentration. The observed luminescent properties correlated to the characteristics of the chemical environments around the Eu3+ ions with respect to the composition of the phosphovanadates. The Eu3+ luminescence spectroscopy results indicated that the presence of larger vanadium(V) amounts in the phosphate host lattice led to more covalent and polarizable chemical environments. So, besides allowing for control of the luminescent properties of the solids, the variation in the vanadate concentration in the obtained YPO4:Eu3+ phosphors enabled the establishment of a strict correlation between the observable spectroscopic features and the chemical characteristics of the powders.

Effects of EDTA and Sodium Citrate on hormone measurements by fluorometric (FIA) and immunofluorometric (IFMA) methods

Abstract Background Measurements of hormonal concentrations by immunoassays using fluorescent tracer substance (Eu3+) are susceptible to the action of chemical agents that may cause alterations in its original structure. Our goal was to verify the effect of two types of anticoagulants in the hormone assays performed by fluorometric (FIA) or immunofluorometric (IFMA) methods. Methods Blood samples were obtained from 30 outpatients and were drawn in EDTA, sodium citrate, and serum separation Vacutainer®Blood Collection Tubes. Samples were analyzed in automatized equipment AutoDelfia™ (Perkin Elmer Brazil, Wallac, Finland) for the following hormones: Luteinizing hormone (LH), Follicle stimulating homone (FSH), prolactin (PRL), growth hormone (GH), Sex hormone binding globulin (SHBG), thyroid stimulating hormone (TSH), insulin, C peptide, total T3, total T4, free T4, estradiol, progesterone, testosterone, and cortisol. Statistical analysis was carried out by Kruskal-Wallis method and Dunn's test. Results No significant differences were seen between samples for LH, FSH, PRL and free T4. Results from GH, TSH, insulin, C peptide, SHBG, total T3, total T4, estradiol, testosterone, cortisol, and progesterone were significant different between serum and EDTA-treated samples groups. Differences were also identified between serum and sodium citrate-treated samples in the analysis for TSH, insulin, total T3, estradiol, testosterone and progesterone. Conclusions We conclude that the hormonal analysis carried through by FIA or IFMA are susceptible to the effects of anticoagulants in the biological material collected that vary depending on the type of assay.

Measurement and model calculation of the temperature dependence of ligand-to-metal energy transfer rates in lanthanide complexes

Temperature dependent transient curves of excited levels of a model Eu3+ complex have been measured for the first time. A coincidence between the temperature dependent rise time of the 5D0 emitting level and decay time of the 5D1 excited level in the [Eu(tta)3(H2O)2] complex has been found, which unambiguously proves the T1→5D1→5D0 sensitization pathway. A theoretical approach for the temperature dependent energy transfer rates has been successfully applied to the rationalization of the experimental data.

Petrografia e geochimica delle vulcaniti del Monte dei Porri di Salina (Isole Eolie)

E’ stata indagata dal punto di vista stratigrafico, geochimico e petrografico la successione di vulcaniti appartenenti alle formazioni Rocce di Barcone (Tufi Grigi dei Porri o Grey Porri Tuffs – GPT), Punta Sallustro, Punta di Megna e Serro dello Sciarato (Lucchi et al., 2013a, b), riferibili all’Epoca Eruttiva 5 (~70 - 57 ka) dell’evoluzione vulcanologica dell’isola Salina (isole Eolie), durante la quale si realizza l’edificazione della porzione medio-basale dello stratocono del Monte dei Porri. Attraverso un approccio basato sull’integrazione e correlazione di metodologie stratigrafiche, petrografiche e geochimiche si è giunti ad una ricostruzione dei meccanismi eruttivi, deposizionali e petrogenetici che sottendono la successione di eventi vulcanici responsabili dell’edificazione dello stratocono suddetto. Utilizzando l’analisi di litofacies si è giunti, anche attraverso le correlazioni stratigrafiche estese sull’isola di Lipari, alla definizione di cinque unità eruttive (EU1-EU5), rappresentanti il riferimento stratigrafico per la campionatura necessaria per caratterizzarle sia petrograficamente che geochimicamente. Il significato vulcanologico delle EU1-5 ha permesso di evidenziare che il Monte dei Porri è costituito, in larga parte, da un’articolata alternanza di depositi da caduta e da correnti piroclastiche (formati sia da pomici che da scorie), alla quale si intercalano colate laviche; all’interno dell’unità i prodotti analizzati evidenziano composizione dei magmi da trachi-dacitica (EU1), a basaltica e andesitico basaltica (EU2), a francamente andesitico basaltica (EU3); quest’ultima composizione caratterizza la EU4 (che evolve anche verso termini andesitici), e la EU5. In conclusione, l’integrazione di tutti i dati (stratigrafici, petrografici e geochimici) permette di affermare che l’attività vulcanica responsabile della messa in posto delle EU1-5 cominci con una fase di apertura del condotto eruttivo (fase esplosiva pliniana) accompagnata dall’emissione dei magmi più evoluti (EU1), residenti al top di una camera magmatica zonata. Ad essa presumibilmente segue il coinvolgimento dei livelli più profondi del reservoir magmatico dove risiedono i magmi più mafici (EU2 e EU3). La ripresa dell’attività vulcanica (dopo una stasi durante il quale i magmi mafici evolvono verso composizioni mediamente evolute) vede infatti l’emissione di prodotti andesitici (EU4) seguita da magmi meno evoluti (EU5) che porta ad un progressivo svuotamento del sistema.

Luminescence Enhancement after Adding Stoppers to Europium(III) Nanozeolite L

Stopper molecules attached to nanozeolite L (NZL) boost the luminescence of confined Eu3+-β-diketonate complexes. The mechanism that is responsible was elucidated by comparing two diketonate ligands of different pKa and two aromatic imines, and by applying stationary and time resolved spectroscopy. The result is that the presence of the imidazolium based stopper is favorable to the sustainable formation of Eu3+-β-diketonate complexes with high coordination by decreasing the proton strength inside the channels of NZL. A consequence is that strongly luminescent transparent films can be prepared using aqueous suspension of the stopper modified composites.

Diseño y síntesis de materiales nanoestructurados basados en aluminatos de estroncio con propiedades fotoluminiscentes

Durante la última década, se han llevado acabo numeroso estudios sobre la síntesis de materiales fotoluminiscentes sub-micrónicos, en gran medida, al amplio número de aplicaciones que demandan este tipo de materiales. En concreto dentro de los materiales fosforescentes o también denominados materiales con una prolongada persistencia de la luminiscencia, los estudios se han enfocado en la matriz de SrAl2O4 dopada con Europio (Eu2+) y Disprosio (Dy3+) dado que tiene mayor estabilidad y persistencia de la fosforescencia con respecto a otras matrices. Estos materiales se emplean mayoritariamente en pinturas luminiscentes, tintas, señalización de seguridad pública, cerámicas, relojes, textiles y juguetes fosforescentes. Dado al amplio campo de aplicación de los SrAl2O4:Eu, Dy, se han investigado múltiples rutas de síntesis como la ruta sol-gel, la síntesis hidrotermal, la síntesis por combustión, la síntesis láser y la síntesis en estado sólido con el fin de desarrollar un método eficiente y que sea fácilmente escalable. Sin embargo, en la actualidad el método que se emplea para el procesamiento a nivel industrial de los materiales basados en aluminato de estroncio es la síntesis por estado sólido, que requiere de temperaturas de entre 1300 a 1900oC y largos tiempos de procesamiento. Además el material obtenido tiene un tamaño de partícula de 20 a 100 μm; siendo este tamaño restrictivo para el empleo de este tipo de material en determinadas aplicaciones. Por tanto, el objetivo de este trabajo es el desarrollo de nuevas estrategias que solventen las actuales limitaciones. Dentro de este marco se plantean una serie de objetivos específicos: Estudio de los parámetros que gobiernan los procesos de reducción del tamaño de partícula mediante molienda y su relación en la respuesta fotoluminiscente. Estudio de la síntesis por combustión de SrAl2O4:Eu, Dy, evaluando el efecto de la temperatura y la cantidad de combustible (urea) en el proceso para la obtención de partículas cristalinas minimizando la presencia de fases secundarias. Desarrollo de nuevas rutas de síntesis de SrAl2O4:Eu, Dy empleando el método de sales fundidas. Determinación de los mecanismos de reacción en presencia de la sal fundida en función de los parámetros de proceso que comprende la relación de sales y reactivos, la naturaleza de la alúmina y su tamaño, la temperatura y atmósfera de tratamiento. Mejora de la eficiencia de los procesos de síntesis para obtener productos con propiedades finales óptimas en procesos factibles industrialmente para su transferencia tecnológica. Es este trabajo han sido evaluados los efectos de diferentes procesos de molienda para la reducción del tamaño de partícula del material de SrAl2O4:Eu, Dy comercial. En el proceso de molienda en medio húmedo por atrición se observa la alteración de la estructura cristalina del material debido a la reacción de hidrólisis generada incluso empleando como medio líquido etanol absoluto. Con el fin de solventar las desventajas de la molienda en medio húmedo se llevo a cabo un estudio de la molturación en seco del material. La molturación en seco de alta energía reduce significativamente el tamaño medio de partícula. Sin embargo, procesos de molienda superiores a una duración de 10 minutos ocasionan un aumento del estado de aglomeración de las partículas y disminuyen drásticamente la respuesta fotoluminiscente del material. Por tanto, se lleva a cabo un proceso de molienda en seco de baja energía. Mediante este método se consigue reducir el tamaño medio de partícula, d50=2.8 μm, y se mejora la homogeneidad de la distribución del tamaño de partícula evitando la amorfización del material. A partir de los resultados obtenidos mediante difracción de rayos X y microscopia electrónica de barrido se infiere que la disminución de la intensidad de la fotoluminiscencia después de la molienda en seco de alta energía con respecto al material inicial se debe principalmente a la reducción del tamaño de cristalito. Se observan menores variaciones en la intensidad de la fotoluminiscencia cuando se emplea un método de molienda de baja de energía ya que en estos procesos se preserva el dominio cristalino y se reduce la amorfización significativamente. Estos resultados corroboran que la intensidad de la fotoluminiscencia y la persistencia de la luminiscencia de los materiales de SrAl2O4:Eu2+, Dy3+ dependen extrínsecamente de la morfología de las partículas, del tamaño de partícula, el tamaño de grano, los defectos superficiales e intrínsecamente del tamaño de cristalito. Siendo las características intrínsecas las que dominan con respecto a las extrínsecas y por tanto tienen mayor relevancia en la respuesta fotoluminiscente. Mediante síntesis por combustión se obtuvieron láminas nanoestructuradas de SrAl2O4:Eu, Dy de ≤1 μm de espesor. La cantidad de combustible, urea, en la reacción influye significativamente en la formación de determinadas fases cristalinas. Para la síntesis del material de SrAl2O4:Eu, Dy es necesario incluir un contenido de urea mayor que el estequiométrico (siendo m=1 la relación estequiométrica). La incorporación de un exceso de urea (m>1) requiere de la presencia de un agente oxidante interno, HNO3, para que la reacción tenga lugar. El empleo de un mayor contenido de urea como combustible permite una quelación efectiva de los cationes en el sistema y la creación de las condiciones reductoras para obtener un material de mayor cristalinidad y con mejores propiedades fotoluminiscentes. El material de SrAl2O4:Eu, Dy sintetizado a una temperatura de ignición de 600oC tiene un tamaño medio 5-25 μm con un espesor de ≤1 μm. Mediante procesos de molturación en seco de baja energía es posible disminuir el tamaño medio de partícula ≈2 μm y homogenizar la distribución del tamaño de partícula pero hay un deterioro asociado de la respuesta luminiscente. Sin embargo, se puede mejorar la respuesta fotoluminiscente empleando un tratamiento térmico posterior a 900oC N2-H2 durante 1 hora que no supone un aumento del tamaño de partícula pero si permite aumentar el tamaño de cristalito y la reducción del Eu3+ a Eu2+. Con respecto a la respuesta fotoluminiscente, se obtiene valores de la intensidad de la fotoluminiscencia entre un 35%-21% con respecto a la intensidad de un material comercial de referencia. Además la intensidad inicial del decaimiento de la fosforescencia es un 20% de la intensidad del material de referencia. Por tanto, teniendo en cuenta estos resultados, es necesario explorar otros métodos de síntesis para la obtención de los materiales bajo estudio. Por esta razón, en este trabajo se desarrollo una ruta de síntesis novedosa para sintetizar SrAl2O4:Eu, Dy mediante el método de sales fundidas para la obtención de materiales de gran cristalinidad con tamaños de cristalito del orden nanométrico. Se empleo como sal fundente la mezcla eutéctica de NaCl y KCl, denominada (NaCl-KCl)e. La principal ventaja de la incorporación de la mezcla es el incremento la reactividad del sistema, reduciendo la temperatura de formación del SrAl2O4 y la duración del tratamiento térmico en comparación con la síntesis en estado sólido. La formación del SrAl2O4 es favorecida ya que se aumenta la difusión de los cationes de Sr2+ en el medio líquido. Se emplearon diferentes tipos de Al2O3 para evaluar el papel del tamaño de partícula y su naturaleza en la reacción asistida por sales fundidas y por tanto en la morfología y propiedades del producto final. Se obtuvieron partículas de morfología pseudo-esférica de tamaño ≤0.5 μm al emplear como alúmina precursora partículas sub-micrónicas ( 0.5 μm Al2O3, 0.1 μm Al2 O3 y γ-Al2O3). El mecanismo de reacción que tiene lugar se asocia a procesos de disolución-precipitación que dominan al emplear partículas de alúmina pequeñas y reactivas. Mientras al emplear una alúmina de 6 μm Al2O3 prevalecen los procesos de crecimiento cristalino siguiendo un patrón o plantilla debido a la menor reactividad del sistema. La nucleación y crecimiento de nanocristales de SrAl2O4:Eu, Dy se genera sobre la superficie de la alúmina que actúa como soporte. De esta forma se desarrolla una estructura del tipo coraza-núcleo («core-shell» en inglés) donde la superficie externa está formada por los cristales fosforescentes de SrAl2O4 y el núcleo está formado por alúmina. Las partículas obtenidas tienen una respuesta fotoluminiscente diferente en función de la morfología final obtenida. La optimización de la relación Al2O3/SrO del material de SrAl2O4:Eu, Dy sintetizado a partir de la alúmina de 6 μm permite reducir las fases secundarias y la concentración de dopantes manteniendo la respuesta fotoluminiscente. Comparativamente con un material comercial de SrAl2O4:Eu, Dy de referencia, se han alcanzado valores de la intensidad de la emisión de hasta el 90% y de la intensidad inicial de las curvas de decaimiento de la luminiscencia de un 60% para el material sintetizado por sales fundidas que tiene un tamaño medio ≤ 10μm. Por otra parte, es necesario tener en cuenta que el SrAl2O4 tiene dos polimorfos, la fase monoclínica que es estable a temperaturas inferiores a 650oC y la fase hexagonal, fase de alta temperatura, estable a temperaturas superiores de 650oC. Se ha determinado que fase monoclínica presenta propiedades luminiscentes, sin embargo existen discordancias a cerca de las propiedades luminiscentes de la fase hexagonal. Mediante la síntesis por sales fundidas es posible estabilizar la fase hexagonal empleando como alúmina precursora γ-Al2O3 y un exceso de Al2O3 (Al2O3/SrO:2). La estabilización de la fase hexagonal a temperatura ambiente se produce cuando el tamaño de los cristales de SrAl2O4 es ≤20 nm. Además se observó que la fase hexagonal presenta respuesta fotoluminiscente. El diseño de materiales de SrAl2O4:Eu,Dy nanoestructurados permite modular la morfología del material y por tanto la intensidad de la de la fotoluminiscencia y la persistencia de la luminiscencia. La disminución de los materiales precursores, la temperatura y el tiempo de tratamiento significa la reducción de los costes económicos del material. De ahí la viabilidad de los materiales de SrAl2O4:Eu,Dy obtenidos mediante los procesos de síntesis propuestos en esta memoria de tesis para su posterior escalado industrial. ABSTRACT The synthesis of sub-micron photoluminescent particles has been widely studied during the past decade because of the promising industrial applications of these materials. A large number of matrices has been developed, being SrAl2O4 host doped with europium (Eu2+) and dysprosium (Dy3+) the most extensively studied, because of its better stability and long-lasting luminescence. These functional inorganic materials have a wide field of application in persistent luminous paints, inks and ceramics. Large attention has been paid to the development of an efficient method of preparation of SrAl2O4 powders, including solgel method, hydrothermal synthesis, laser synthesis, combustion synthesis and solid state reaction. Many of these techniques are not compatible with large-scale production and with the principles of sustainability. Moreover, industrial processing of highly crystalline powders usually requires high synthesis temperatures, typically between 1300 a 1900oC, with long processing times, especially for solid state reaction. As a result, the average particle size is typically within the 20-100 μm range. This large particle size is limiting for current applications that demand sub-micron particles. Therefore, the objective of this work is to develop new approaches to overcome these limitations. Within this frame, it is necessary to undertake the following purposes: To study the parameters that govern the particle size reduction by milling and their relation with the photoluminescence properties. To obtain SrAl2O4:Eu, Dy by combustion synthesis, assessing the effect of the temperature and the amount of fuel (urea) to synthesize highly crystalline particles minimizing the presence of secondary phases. To develop new synthesis methods to obtain SrAl2O4:Eu, Dy powders. The molten salt synthesis has been proposed. As the method is a novel route, the reaction mechanism should be determine as a function of the salt mixture, the ratio of the salt, the kind of Al2O3 and their particle size and the temperature and the atmosphere of the thermal treatment. To improve the efficiency of the synthesis process to obtain SrAl2O4:Eu, Dy powders with optimal final properties and easily scalable. On the basis of decreasing the particle size by using commercial product SrAl2O4:Eu2+, Dy3+ as raw material, the effects of different milling methods have been evaluated. Wet milling can significantly alter the structure of the material through hydrolysis reaction even in ethanol media. For overcoming the drawbacks of wet milling, a dry milling-based processes are studied. High energy dry milling process allows a great reduction of the particle size, however milling times above 10 min produce agglomeration and accelerates the decrease of the photoluminescence feature. To solve these issues the low energy dry milling process proposed effectively reduces the particle size to d50=2.8 μm, and improves the homogeneity avoiding the amorphization in comparison with previous methods. The X-ray diffraction and scanning electron microscope characterization allow to infer that the large variations in PL (Photoluminescence) values by high energy milling process are a consequence mainly of the crystallite size reduction. The lesser variation in PL values by low energy milling proces is related to the coherent crystalline domain preservation and the unnoticeable amorphization. These results corroborate that the photoluminescence intensity and the persistent luminescence of the SrAl2O4:Eu2+, Dy3+ powders depend extrinsically on the morphology of the particles such as particle size, grain size, surface damage and intrinsically on the crystallinity (crystallite size); being the intrinsically effects the ones that have a significant influence on the photoluminescent response. By combustion method, nanostructured SrAl2O4:Eu2+, Dy3+ sheets with a thickness ≤1 μm have been obtained. The amount of fuel (urea) in the reaction has an important influence on the phase composition; urea contents larger than the stoichiometric one require the presence of an oxidant agent such as HNO3 to complete the reaction. A higher amount of urea (excess of urea: denoted m>1, being m=1 the stoichiometric composition) including an oxidizing agent produces SrAl2O4:Eu2+,Dy3+ particles with persistent luminescence due to the effective chelation of the cations and the creation of suitable atmospheric conditions to reduce the Eu3+ to Eu2+. Therefore, optimizing the synthesis parameters in combustion synthesis by using a higher amount of urea and an internal oxidizing agent allows to complete the reaction. The amount of secondary phases can be significantly reduced and the photoluminescence response can be enhanced. This situation is attributed to a higher energy that improves the crystallinity of the powders. The powders obtained have a particle size c.a. 5-25 μm with a thickness ≤1 μm and require relatively low ignition temperatures (600oC). It is possible to reduce the particle size by a low energy dry milling but this process implies the decrease of the photoluminescent response. However, a post-thermal treatment in a reducing atmosphere allows the improvement of the properties due to the increment of crystallinity and the reduction of Eu3+ to Eu2+. Compared with the powder resulted from solid state method (commercial reference: average particle size, 20 μm and heterogeneous particle size distribution) the emission intensity of the powder prepared by combustion method achieve the values between 35% to 21% of the reference powder intensity. Moreover, the initial intensity of the decay curve is 20% of the intensity of the reference powder. Taking in account these results, it is necessary to explore other methods to synthesize the powders For that reason, an original synthetic route has been developed in this study: the molten salt assisted process to obtain highly crystalline SrAl2O4 powders with nanometric sized crystallites. The molten salt was composed of a mixture of NaCl and KCl using a 0.5:0.5 molar ratio (eutectic mixture hereafter abbreviated as (NaCl-KCl)e). The main advantages of salt addition is the increase of the reaction rate, the significant reduction of the synthesis temperature and the duration of the thermal treatment in comparison with classic solid state method. The SrAl2O4 formation is promoted due to the high mobility of the Sr2+ cations in the liquid medium. Different kinds of Al2O3 have been employed to evaluate the role of the size and the nature of this precursor on the kinetics of reaction, on the morphology and the final properties of the product. The SrAl2O4:Eu2+, Dy3+ powders have pseudo-spherical morphology and particle size ≤0.5 μm when a sub-micron Al2O3 ( 0.5 μm Al2O3, 0.1 μm Al2O3 and γ-Al2O3) has been used. This can be attributed to a higher reactivity in the system and the dominance of dissolution-precipitation mechanism. However, the use of larger alumina (6 μm Al2O3) modifies the reaction pathway leading to a different reaction evolution. More specifically, the growth of SrAl2O4 sub-micron particles on the surface of hexagonal platelets of 6μm Al2O3 is promoted. The particles retain the shape of the original Al2O3 and this formation process can be attributed to a «core-shell» mechanism. The particles obtained exhibit different photoluminescent response as a function of the final morphology of the powder. Therefore, through this study, it has been elucidated the reaction mechanisms of SrAl2O4 formation assisted by (NaCl-KCl)e that are governed by the diffusion of SrCO3 and the reactivity of the alumina particles. Optimizing the Al2O3/SrO ratio of the SrAl2O4:Eu, Dy powders synthesized with 6 μm Al2O3 as a precursor, the secondary phases and the concentration of dopant needed can be reduced keeping the photoluminescent response of the synthesized powder. Compared with the commercial reference powder, up to 90% of the emission intensity of the reference powder has been achieved for the powder prepared by molten salt method using 6μm Al2O3 as alumina precursor. Concerning the initial intensity of the decay curve, 60% of the initial intensity of the reference powder has been obtained. Additionally, it is necessary to take into account that SrAl2O4 has two polymorphs: monoclinic symmetry that is stable at temperatures below 650oC and hexagonal symmetry that is stable above this temperature. Monoclinic phase shows luminescent properties. However, there is no clear agreement on the emission of the hexagonal structure. By molten salt, it is possible to stabilize the hexagonal phase of SrAl2O4 employing an excess of Al2O3 (Al2O3/SrO: 2) and γ-Al2O3 as a precursor. The existence of nanometric crystalline domains with lower size (≤20 nm) allows the stabilization of the hexagonal phase. Moreover, it has been evidenced that the hexagonal polymorph exhibits photoluminescent response. To sum up, the design of nanostructured SrAl2O4:Eu2+, Dy3+ materials allows to obtain different morphologies and as consequence different photoluminescent responses. The reduction of temperature, duration of the thermal treatment and the precursors materials needed imply the decrease of the economic cost of the material. Therefore, the viability, suitability and scalability of the synthesis strategy developed in this work to process SrAl2O4:Eu2+, Dy3+ are demonstrated.

Nanomateriais luminescentes de terras raras utilizando complexos de benzenotricarboxilatos como precursores

O material Y2O3:Eu3+ vem sendo usado comercialmente como luminóforo vermelho desde da década de 1960, em uma grande variedade de aplicações devido ao seu elevado rendimento quântico (próximo de 100 %), elevada pureza de cor e boa estabilidade. Portanto, este trabalho propõe um novo método de síntese baseado nos complexos benzenotricarboxilatos (BTC) de terras raras trivalentes (RE3+) dopados com íons Eu3+. O objetivo principal é produzir materiais luminescente RE2O3:Eu3+ a temperatura mais baixa (500 °C) e em escala nanométrica. Os complexos precursores [RE(BTC):Eu3+] e [RE(TLA)·n(H2O):Eu3+], onde RE3+: Y, Gd e Lu; BTC: ácido trimésico (TMA) e ácido trimelítico (TLA) foram calcinados em diferentes temperaturas de 500 a 1000 °C, a fim de obter os materiais luminescentes RE2O3:Eu3+. Os complexos foram caracterizados por análise elementar de carbono e hidrogênio, analise térmica (TG), espectroscopia de absorção no infravermelho (FTIR), difração de raios-X - método do pó (XPD) e microscopia eletrônica de varredura (SEM). Todos os complexos são cristalinos e termo estáveis até 460 °C. Dados de fosforescência dos complexos de Y, Gd e Lu mostram que o nível T1 do aníon BTC3- tem energia acima do nível emissor 5D0 do íon Eu3+, indicando que os ligantes podem atuar como sensibilizadores de energia intramolecular. O estudo das propriedades fotoluminescentes dos complexos dopados foi baseado nos espectros de excitação e emissão e curvas de decaimento de luminescência. Ademais, foram determinados os parâmetros de intensidades experimentais (Ωλ), tempos de vida (τ), taxas de decaimentos radiativo (Arad) e não-radiativo (Anrad). Os materiais luminescentes RE2O3:Eu3+ foram sintetizados de forma bem sucedida por meio do método benzenotricarboxilatos calcinados a 500, 600, 700, 800, 900 e 1000 °C, apresentando alta homogeneidade química e controle de tamanho de cristalito. Os nanomateriais foram caracterizados pelas técnicas de FTIR, XPD SEM e TEM revelando a obtenção dos materiais C-RE2O3:Eu3+ mesmo a 500 °C. Os dados de XPD dos materiais confirmaram um aumento do tamanho dos cristalitos de 5 até 52 nm (equação de Scherrer) de em função da temperatura de calcinação de 500 a 1000 °C, respectivamente, corroborados pelas técnicas de SEM e TEM. Os espectros de emissão de RE2O3:Eu3+ mostram uma banda larga atribuída a transição interconfiguracional de transferência de carga ligante-metal (LMCT) em 260 nm, i.e. O2-(2p)&#8594Eu3+(4f6). Além disso, foram observadas linhas finas de absorção devido as transições intraconfiguracionais 4f do íon európio (7F0,1&#85945LJ; J: 0, 1, 2, 3 e 4), como esperado. As propriedades fotoluminescentes dos luminóforos foram baseadas nos espectros (excitação e emissão) e curvas de decaimento luminescente. Os parâmetros de intensidade experimental, tempos de vida, assim como as taxas de decaimentos radiativos e não radiativos foram calculados. As propriedades fotônicas dos nanomateriais são consistentes com o sítio de baixa simetria C2 ocupado pelo íon Eu3+ no C-RE2O3:Eu3+, produzindo emissão vermelha dominada pela transição hipersensível 5D0&#85947F2 do íon Eu3+ no sitio C2, ao invés do sítio centrossimétrico S6. Além disso, os nanomateriais Y2O3:Eu3+ exibem características espectroscópicas semelhantes e elevados valores de eficiência quântica (η~91 %), compatível com os luminóforos comerciais disponíveis no mercado. Este novo método pode ser utilizado para o desenvolvimento de novos nanomateriais contendo íons terras raras, assim como outros íons metálicos.

Desenvolvimento de materiais nanoestruturados à base de SiO2-Nb2O5 preparados por uma nova rota sol-gel com aplicações em fotônica

Este trabalho concentra-se na preparação e caracterizações estrutural e espectroscópica de materiais nanoestruturados à base de SiO2-Nb2O5 dopados e codopados com íons Er3+, Yb3+ e Eu3+ na forma de pós e guias de onda planares. Os nanocompósitos foram preparados através de uma nova rota sol-gel utilizando óxido de nióbio como precursor em substituição ao alcóxido de nióbio. A correlação estrutura propriedades luminescentes foi estudada por difração de raios X, microscopia eletrônica de transmissão, espectroscopia vibracional de absorção no infravermelho, espectroscopia vibracional de espalhamento Raman, análise térmica, reflectância difusa e especular, espectroscopia de fotoluminescência e acoplamento M-line. Inicialmente foi avaliado a influência da concentração de nióbio nas propriedades estruturais e luminescentes de nanocompósitos (100-x)Si-xNb dopados e codopados com íons Er3+, Yb3+ e Eu3+ tratados termicamente a 900 °C por 3h. A cristalização do Nb2O5 foi dependente da concentração de Nb na matriz, com a distribuição dos íons lantanídeos preferencialmente no Nb2O5, afetando as propriedades luminescentes. Para os nanocompósitos codopados com íons Er3+ e Yb3+ foram obtidos valores de largura de banda a meia altura (FWHM) da ordem de 70 nm na região de 1550 nm e tempos de vida de até 5,2 ms. A emissão na região do visível, decorrente de processos de conversão ascendente, revelou-se dependente da concentração de nióbio. Foi verificada emissão preferencial na região do verde para menores concentrações de Nb. Enquanto que, para as maiores concentrações, processos de relaxação cruzada levaram a um aumento relativo na intensidade de emissão na região do vermelho. A eficiência quântica de emissão dos nanocompósitos (100-x)Si-xNb dopados com Eu3+ variou com o comprimento de onda de excitação, refletindo os diferentes sítios de simetria ocupados por este íons nesta estrutura complexa. A influência da temperatura de tratamento térmico no processo de cristalização do Nb2O5 em nanocompósitos 70Si:30Nb codopados com íons Er3+ e Yb3+ foi avaliada. Material amorfo foi obtido a 700 °C enquanto que a 900 e 1100 °C foram identificas as fases ortorrômbica (fase T) e monoclínica (fase M) do Nb2O5. Intensa emissão na região de 1550 nm com valores de FWHM de 52 e 67 nm e tempos de vida de 5,6 e 5,4 ms foram verificados a 700 e 900 °C sob excitação em 977 nm, respectivamente. Por fim, foram obtidos guias de onda planares com excelentes propriedades ópticas e com grande potencial de aplicação em dispositivos de amplificação óptica. Especificamente, materiais fotônicos com banda larga de emissão na região do infravermelho foram preparados, indicando fortemente a potencialidade para a aplicação em telecomunicações envolvendo não somente a banda C como também as bandas L e S em materiais contendo somente íons Er3+ como centros emissores.

Luminescence of delafossite-type CuAlO2 fibers with Eu substitution for Al cations

CuAlO2 has been examined as a potential luminescent material by substituting Eu for Al cations in the delafossite structure. CuAlO2:Eu3+ nanofibers have been prepared via electrospinning for the ease of mitigating synthesis requirements and for future optoelectronics and emerging applications. Single-phase CuAlO2 fibers could be obtained at a temperature of 1100 °C in air. The Eu was successfully doped in the delafossite structure and two strong emission bands at ~405 and 610 nm were observed in the photoluminescence spectra. These bands are due to the intrinsic near-band-edge transition of CuAlO2 and the f-f transition of the Eu3+ activator, respectively. Further electrical characterization indicated that these fibers exhibit semiconducting behavior and the introduction of Eu could act as band-edge modifiers, thus changing the thermal activation energies. In light of this study, CuAlO2:Eu3+ fibers with both strong photoluminescence and p-type conductivity could be produced by tailoring the rare earth doping concentrations.

Development of Zirconia based phosphors for application in lighting and as luminescent bioprobes

The strong progress evidenced in photonic and optoelectronic areas, accompanied by an exponential development in the nanoscience and nanotechnology, gave rise to an increasing demand for efficient luminescent materials with more and more exigent characteristics. In this field, wide band gap hosts doped with lanthanide ions represent a class of luminescent materials with a strong technological importance. Within wide band gap material, zirconia owns a combination of physical and chemical properties that potentiate it as an excellent host for the aforementioned ions, envisaging its use in different areas, including in lighting and optical sensors applications, such as pressure sensors and biosensors. Following the demand for outstanding luminescent materials, there is also a request for fast, economic and an easy scale-up process for their production. Regarding these demands, laser floating zone, solution combustion synthesis and pulsed laser ablation in liquid techniques are explored in this thesis for the production of single crystals, nanopowders and nanoparticles of lanthanides doped zirconia based hosts. Simultaneously, a detailed study of the morphological, structural and optical properties of the produced materials is made. The luminescent characteristics of zirconia and yttria stabilized zirconia (YSZ) doped with different lanthanide ions (Ce3+ (4f1), Pr3+ (4f2), Sm3+ (4f5), Eu3+ (4f6), Tb3+ (4f8), Dy3+ (4f9), Er3+ (4f11), Tm3+ (4f12), Yb3+ (4f13)) and co-doped with Er3+,Yb3+ and Tm3+,Yb3+ are analysed. Besides the Stokes luminescence, the anti- Stokes emission upon infrared excitation (upconversion and black body radiation) is also analysed and discussed. The comparison of the luminescence characteristics in materials with different dimensions allowed to analyse the effect of size in the luminescent properties of the dopant lanthanide ions. The potentialities of application of the produced luminescent materials in solid state light, biosensors and pressure sensors are explored taking into account their studied characteristics.