Polymerization of photocurable commercial dental methacrylate-based composites - Photocalorimetry study

Due to their excellent aesthetics, photopolymers have been extensively used in several dentistry applications. However, several problems are reported, e.g. low mechanical and abrasion resistance, shrinkage during polymerization, etc. Properties of the final restorations are intrinsically related to the polymerization stage, which can be conveniently studied by photocalorimetry. In the present work the polymerization reaction and the filler content of different photocurable commercial dental methacrylate-based composites were studied by means of photocalorimetry and thermogravimetry, respectively. The results show that the values of curing rate, the heat of polymerization and the filler content vary significantly from one composite to another.

Effect of calcium pre-rinse and fluoride dentifrice on remineralisation of artificially demineralised enamel and on the composition of the dental biofilm formed in situ

Objective: This in situ blind crossover study investigated the effect of calcium (Ca) rinse prior to the use fluoride (F) dentifrice on remineralisation of artificially demineralised enamel and on the composition of biofilm. Design: During four phases of 14 days, 10 volunteers wore appliances containing two artificially demineralised bovine enamel blocks. Three times a day, they rinsed with 10 mL, of Ca (150 mM) or placebo rinse (1 min). A slurry (1:3, w/v) of F (1030 ppm) or placebo dentifrice was dripped onto the blocks. During I min, the volunteers brushed their teeth with the respective dentifrice. The appliance was replaced into the mouth and the volunteers rinsed with water. The biofilm formed on the blocks was analysed for F and Ca. Enamel alterations were evaluated by the percentage of surface microhardness change (%SMHC), cross-sectional microhardness (% mineral volume) and alkali-soluble F analysis. Data were analysed by ANOVA (p < 0.05). Results: the use of the Ca pre-rinse before the F dentifrice produced a six- and four-fold increase in biofilm F and Ca concentrations, respectively. For enamel, the remineralisation was significantly improved by the Ca pre-rinse when compared to the other treatments. There was a significantly higher concentration of alkali-soluble F in enamel when the F dentifrice was used, but the Ca pre-rinse did not have any significant additive effect. Conclusions: According to our protocol, the Ca pre-rinse significantly increased biofilm F concentration and, regardless the use of F dentifrice, significantly enhanced the remineralisation of artificially demineralised enamel. (c) 2007 Elsevier Ltd. All rights reserved.

Spectroscopic study of ejected dental tissue after Er : YAG laser ablation

By means of IR spectroscopy, we determined the teeth ablation mechanism by an Er:YAG laser oscillating at 2.94 mum. Ejected dental material, ablated by the laser from human teeth, was deposited on an IR window and the absorption spectra were measured in the range 2500-20,000 nm. Sound teeth were used, and the corresponding film spectra were compared to spectra obtained by traditional methods. The films spectra obtained do not differ appreciably from those obtained by the traditional method for sound teeth, indicating that the material ejected by an Er:YAG represents the tooth condition.The obtained results confirm that a spectroscopic analysis of a tooth treated with an Er:YAG laser can be done measuring the absorbance of a film composed of ejected material without the need to slice it. In addition, we could determine that the laser absorption occurs mainly by the interstitial water, and the temperature elevation of the ejected material does not exceed 60degreesC. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Different methods of finishing and polishing enamel

Statement of problem. Highly polished enamel surfaces arc recommended for axial tooth surfaces that will serve as guiding planes and be contacted by component parts of a removable partial denture. There is little evidence to support the assumption that this tooth modification will provide accurate adaptation of the framework and prevent build-up of plaque.Purpose. The aim of this investigation was to evaluate the surface roughness of the tooth enamel, prepared to serve as guiding planes, with different polishing systems.Material and methods. Four different methods (designated A, B, C, and D) for finishing and polishing the prepared enamel surfaces of 20 freshly extracted third molar teeth were studied. Each method involved 3, 4, or 5 different steps. The roughness of each specimen was measured at the start of each method before recontouring, after recontouring, and after each step of the 4 finishing and polishing procedures. The 4 experimental finishing methods were applied after recontouring the axial surfaces (buccal, lingual, and proxinial) of each tooth. Thus the 20 teeth (60 surfaces) were finished and polished by use of 1 of the experimental methods. Surface roughness was measured with a profilometer (mum); the readings of the unpolished enamel Surfaces were recorded as control measurements. Results were statistically analyzed with one-way analysis of variance followed by Tukey's test at the 95% level of confidence.Results. The highest roughness mean values (14.41 mum to 16.44 mum) were found when the diamond bur was used at a high speed for tooth preparation. A significant decrease in roughness values was observed with the diamond bur at a low speed (P<.05). Analysis of the roughness values revealed that all polishing methods produced surface roughness similar to that of the corresponding control teeth.Conclusion. Within the limitations of this study, all finishing procedures tested effectively promoted an enamel surface similar to the original unpolished enamel.

Influence of age on the behavior of dental pulp of dog teeth after capping with an adhesive system or calcium hydroxide

This study evaluated histomorphologically the influence of chronological age of the dog on the dental pulp-healing process after capping with the All Bond 2 system or with calcium hydroxide paste. The animals were divided according to age into young and adult groups. Class 5-type cavities were prepared, and the pulp was submitted to an exposure of a diameter of 0.5 mm. The pulp of the teeth was then protected with the adhesive system or with a calcium hydroxide paste. Sixty days after treatment, the results obtained with the adhesive system in the young group were significantly better than those in the adult group. With calcium hydroxide, the results were similar for both groups. The pulp treated with calcium hydroxide exhibited a complete hard tissue bridge and a pulp without inflammatory reaction, a fact not observed when the adhesive system was used. In conclusion, the chronological age of the pulp influenced the comparative results only for the adhesive system (P = 0.1), and the total results were better with calcium hydroxide than with the All Bond 2 system (P = 0.01).