Effect of disinfection on adhesion of reline polymers

Cylinders (3.5 x 5.0 mm) of the reline resins Kooliner (K), New Truliner (N), Tokuso Rebase Fast (T), and Ufi Gel Hard (U) were bonded to cylinders (20 x 20 mm) of the denture base resin Lucitone 550 (L), and samples were divided into two controls and four test groups (n = 8). Shear tests (0.5 mm/min) were performed after polymerization or immersion in water (37 degrees C) for 7 days (controls); two or seven cycles of disinfection by immersion in sodium perborate (50 degrees C/10 min) or microwave irradiation (650 W/6 min). Statistical analyses (alpha = 0.05) revealed that two cycles of microwave and chemical disinfection increased the mean bond strengths of materials T (9.08 to 12.93 MPa) and L (18.89 to 23.02 MPa). For resin L, seven cycles of chemical (15.72 MPa) and microwave (17.82 MPa) disinfection decreased the shear bond strength compared with the respective control (21.74 MPa). Resins U (13.12 MPa), K (8.44 MPa), and N (7.98 MPa) remained unaffected.

Linear dimensional changes of denture base and hard chair-side reline resins after disinfection

Objectives: This study evaluated the effect of disinfection by immersion in sodium perborate (50 degrees C/10 min) or microwave irradiation (650 W/6 min) on the linear dimensional change (LDC) of four reline resins (Kooliner-K, New Truliner-N, Tokuso Rebase Fast-T, Ufi Gel Hard-U) and one heat-polymerizing denture base resin (Lucitone 550-L). Methods: Specimens (50.0 mm diameter, 0.5 mm thickness) were made using a split mold with reference points, and divided into two controls and four test groups (u = 8). The distances between the points were measured on the mold (baseline readings), and compared to those obtained from the specimens after: polymerization or immersion in water (37 degrees C) for 7 days (controls); 2 or 7 cycles of disinfection by immersion or microwave irradiation. Results: the two-way ANOVA and Tukey's test (alpha = 0.05) showed that microwave disinfection significantly increased the mean LDC of materials L (-1.43%), N (-1.27%) and K (-1.06%). Material N also exhibited a significant increase in LDC after two cycles of chemical disinfection (-0.73%). For U (-0.47%) and T (-0.21%) materials, no significant changes in LDC were found. Conclusions: Microwave disinfection increases the shrinkage of materials L, N, and K. The dimensional stability of resins U and T was not affected by the disinfection methods evaluated. (c) 2006 Wiley Periodicals, Inc.

The effect of disinfectant solutions on the hardness of acrylic resin denture teeth

This investigation studied the effects of disinfectant solutions on the hardness of acrylic resin denture teeth. The occlusal surfaces of 64 resin denture teeth were ground flat with abrasives up to 400-grit silicon carbide paper. Measurements were made after polishing and after the specimens were stored in water at 37 degreesC for 48 h. The specimens were then divided into four groups and immersed in chemical disinfectants (4% chlorhexidine; 1% sodium hypochlorite and sodium perborate) for 10 min. The disinfection methods were performed twice to simulate clinical conditions and hardness measurements were made. Specimens tested as controls were immersed in water during the same disinfection time. Eight specimens were produced for each group. After desinfection procedures, testing of hardness was also performed after the samples were stored at 37 degreesC for 7, 30, 60, 90 and 120 days. Data were analysed using two-way analysis of variance (anova) and Tukey's test at 95% confidence level. According to the results, no significant differences were found between materials and immersion solutions (P > 0.05). However, a continuous decrease in hardness was noticed after ageing (P < 0.05). It was conclude that the surfaces of both acrylic resin denture teeth softened upon immersion in water regardless the disinfecting solution.

Adherence in vitro of Candida albicans to plasma treated acrylic resin. Effect of plasma parameters, surface roughness and salivary pellicle

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The effect of long-term disinfection procedures on hardness property of resin denture teeth

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effectiveness of chlorhexidine on the disinfection of complete dentures colonised with fluconazole-resistant Candida albicans: in vitro study

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of microwave disinfection on the bond strength of denture teeth to acrylic resins

During microwave disinfection, the dentures are exposed to water at high temperature and this may affect the bond between the denture teeth and the acrylic resin from which dentures are made. In this study, a shear test was used to evaluate the effect of microwave disinfection (650W/6 min) on the bond strength of two types of denture teeth to three acrylic resins, with different polymerization methods. The specimens were submitted to the shear tests (0.5 mm/min) after: immersion in water (37 degrees C) for 48 h or 8 days (controls); two or seven cycles of microwave disinfection (test groups). Data (MPa) were analyzed using three-way ANOVA and Tukey HSD test (alpha = 0.05). Microwave disinfection did not adversely affect the bond strength of all tested materials with the exception of QC-20 bonded to SR Vivodent PE, for which a significant reduction was recorded after seven cycles of irradiation. (C) 2007 Elsevier Ltd. All rights reserved.

HARDNESS and SURFACE ROUGHNESS of RELINE and DENTURE BASE ACRYLIC RESINS AFTER REPEATED DISINFECTION PROCEDURES

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Changes in roughness of denture base and reline materials by chemical disinfection or microwave irradiation: Surface roughness of denture base and reline materials

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of fungal adherence to plasma-modified polymethylmethacrylate

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Leachability of degradation products from hard chairside reline resins in artificial saliva: effect of water-bath post-polymerization treatment

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of water-bath post-polymerization on the mechanical properties, degree of conversion, and leaching of residual compounds of hard chairside reline resins

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Titanium surface topography after brushing with fluoride and fluoride-free toothpaste simulating 10 years of use

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of dentin conditioning time on nanoleakage

Objectives: To study the nanoleakage pattern in the dentin hybrid layer by using different dentin adhesives. The null hypotheses tested in this study were: 1) dentin conditioning time does not affect nanoleakage within the hybrid layer; 2) the type of dentin adhesive used does not affect nanoleakage. Methods: Standardized Class V cavities were prepared in 30 intact human molars on the buccal and lingual surfaces. The specimens were randomly assigned to 2 total-etch dentin adhesives (OptiBond SOLO Plus [OPS, Kerr] and One-Step [ONS, BISCO Inc]) and 2 self-etch dentin adhesives (Clearfil SE Bond [CSE, Kuraray] and Adper Prompt L-Pop [APL, 3M ESPE]). The specimens were etched or conditioned for 15 seconds, 30 seconds or 60 seconds. Upon restoration of the Class V cavities with the proprietary resin composite, the specimens were isolated with nail polish except for a 2.0-mm rim around the restoration, and they were immersed in 50 wt% ammoniacal silver nitrate solution (pH=9.5) for 24 hours followed by 8 hours of immersion in photo-developing solution to reduce the silver ions to metallic silver. The specimens were fixed, dehydrated and processed for FESEM and TEM. Silver penetration was measured along the cervical wall, and data were analyzed with Kruskal-Wallis non-parametric tests at a significance level of 95%. Results: There were no statistically significant differences among the experimental groups for the factor conditioning time (p>0.926). There were significant differences for the variable dentin adhesive (p<0.0001). The least amount of nanoleakage within the hybrid layer occurred with CSE, while ONS resulted in the greatest penetration of silver ions. The adhesives OPS and APL ranked in the intermediary subset. Under TEM, all adhesives resulted in some degree of nanoleakage within the hybrid layer. Both spotted/reticular and water-tree nanoleakage patterns were observed. Significance: Longer conditioning times did not increase nanoleakage within the hybrid layer. Nanoleakage varied with the type of adhesive used.

Marginal adaptation of Class 2 adhesive restorations

Objective: Control of microleakage represents a challenge for posterior composite restorations. The technique for composite placement may reduce microleakage. The null hypothesis of this in vitro study was that centripetal incremental insertion of composite resin would result in less microleakage than that obtained with the oblique incremental technique or bulk technique. Method and Materials: Standardized Class 2 preparations were made in 60 caries-free extracted third molars and randomly assigned to 3 groups ( n = 20): ( 1) oblique incremental insertion technique ( control), ( 2) centripetal incremental insertion technique, and ( 3) bulk insertion. The teeth were restored with a total-etch adhesive and micro-hybrid composite resin. The specimens were isolated with nail varnish except for a 2-mm-wide area around the restoration and then thermocycled ( 1,000 thermal cycles, 5 degrees C/ 55 degrees C; 30-second dwell time). The specimens were immersed in an aqueous solution of 50% silver nitrate for 24 hours, followed by 8 hours of immersion in a photo-developing solution and subsequently evaluated for leakage. The microleakage scores ( 0 to 4) obtained from the occlusal and cervical walls were analyzed with median nonparametric tests ( P <.05). Results: The null hypothesis was rejected. All techniques attained statistically similar dentin microleakage scores ( P =.15). The centripetal insertion technique displayed significantly less microleakage than the oblique technique at the enamel margins ( P =.04). Conclusion: None of the techniques eliminated marginal microleakage in Class 2 preparations. However, in occlusal areas, the centripetal technique performed significantly better than the other techniques.