The effects of substrate water availability on the isolation and growth of fungi

The work reported in this thesis was carried out to contribute to the knowledge of the effects of substrate water availability or water activity (a ) on fungal growth parameters and its implications in the preparationw of materials susceptible to biodeterioration. Fungi were isolated from soils of different ecological sites at a range of substrate aw levels controlled by sodium chloride (NaCl). Three groups of fungi were isolated : firstly, those isolated only at high a (aw about 0.997).secondly, those isolated at high and decreasing aw (aw 0.997 to 0.85) and finally, those isolated at only decreased aw (aw O.95 to 0.80). From these isolations, test fungi were selected to study the effects of pH, temperature, exo-enzyme production and biocide efficacy at decreased aw levels, with glycerol and NaCl as a controlling solutes. The linear extension rates of the fungi increased at all test pH values near optimum a of growth. Test fungi of the Aspergillus glaucus group were found to be most resistant to low aw. Growth and survival of vegetative and fruiting bodies at elevated temperatures were enhanced with the addition of a controlling solutes. A. flavus, A. fumigatus displayed high heat resistance and A. amstelodami, A. versicolor and Penicillium citrinum displayed low heat resistance at high aw levels and vice versa at low aw levels. Amylase, lipase and protease activities were studied at lowered aw , using modifications of the test tube method of Raute11a and Cowling. Amylase and protease production in most xerophilic fungi ceased around 0.80 aw , but lipase production in some xerophilic fungi, including A. glatlcus fungi, was up to and including 0.70 aw with g1ycero1.

Enhanced spectral sensitivity of fibre long period gratings to refractive index of aqueous solutions utilising copper patterned coatings

A set of long period grating devices have been fabricated in photosensitive single mode fibre coated with a series of copper rings (period of 380μm, 50% duty cycle and length of 4cm). The long period gratings were inscribed with a uniform UV-laser exposure across the entire length of the copper ring patterned coating. The devices ranged in copper thickness from 0.5μm to 1.5μm. In addition, a control long period grating was fabricated in the same type of fibre with the same period for comparison. The refractive index and temperature spectral sensitivity of these devices were investigated and it was found that the index and temperature sensitivity is a function of the thickness of the copper rings, as supported by theoretical modelling. Furthermore, the index sensitivity of these devices in the 1.333 index region is greater than the control long period grating. The patterned 0.5μm coated long period grating gave a sensitivity of Δλ/Δn = -74 nm leading to a resolution of 1.4×10-3 compared to the control which had a sensitivity of Δλ/Δn = -32 nm with a resolution of 3.2×10-3 in the index region of 1.320 to 1.380 (aqueous solution regime). This demonstrates a two fold increase in the sensitivity. This novel fibre long period grating device shows potential for increasing the resolution of measurements of the index of aqueous solutions.

Effect of cancer cachexia on triacylglycerol/fatty acid substrate cycling in white adipose tissue

The effect of cancer cachexia on the TAG/FA substrate cycle in white adipose tissue was determined in vivo using the MAC16 murine model of cachexia. When compared with non-tumor-bearing animals, the rate of TAG-glycerol production was found to be increased almost threefold in animals bearing the MAC13 tumor, which does not induce cachexia, but was not further elevated in animals bearing the MAC16 tumor. In both cases TAG-glycerol production and de novo synthesis of TAG-FA were also increased above non-tumor-bearing animals. In animals bearing the MAC16 tumor, the TAG-FA rates were significantly higher than in animals bearing the MAC13 tumor. This suggests that the presence of the tumor alone is sufficient to cause an increase in cycling rate, and in the absence of an elevated energy intake (MAC16) this may contribute to the depletion of adipose tissue.

SHG in a low-loss orientation patterned GaAs waveguide

We demonstrate second harmonic generation at 1621 nm in a low-loss orientation-patterned GaAs waveguide pumped by an optical parametric oscillator system. The losses were estimated to be 2.12 dB/cm.

Second harmonic generation in a low-loss orientation-patterned GaAs waveguide

The technology of low-loss orientation-patterned gallium arsenide (OP-GaAs) waveguided crystals was developed and realized by reduction of diffraction scattering on the waveguide pattern. The propagation losses in the OP-GaAs waveguide were estimated to be as low as 2.1 dB/cm, thus demonstrating the efficient second harmonic generation at 1621 nm under an external pumping. © 2013 Optical Society of America.

Initial nucleation study and new technique for sublimation growth of AlN on SiC substrate

Single crystal platelets of AlN were successfully grown on 6H-SiC(0001) by a novel technique designed to suppress SiC decomposition, promote two-dimensional growth, and eliminate cracking in the AlN. X-ray diffractometry and synchrotron white beam X-ray topography demonstrate that the final AlN single crystal is of high structural quality.

Step and flash imprint lithography: Fabrication of patterned media for extremely high density magnetic data storage devices

Currently the data storage industry is facing huge challenges with respect to the conventional method of recording data known as longitudinal magnetic recording. This technology is fast approaching a fundamental physical limit, known as the superparamagnetic limit. A unique way of deferring the superparamagnetic limit incorporates the patterning of magnetic media. This method exploits the use of lithography tools to predetermine the areal density. Various nanofabrication schemes are employed to pattern the magnetic material are Focus Ion Beam (FIB), E-beam Lithography (EBL), UV-Optical Lithography (UVL), Self-assembled Media Synthesis and Nanoimprint Lithography (NIL). Although there are many challenges to manufacturing patterned media, the large potential gains offered in terms of areal density make it one of the most promising new technologies on the horizon for future hard disk drives. Thus, this dissertation contributes to the development of future alternative data storage devices and deferring the superparamagnetic limit by designing and characterizing patterned magnetic media using a novel nanoimprint replication process called "Step and Flash Imprint lithography". As opposed to hot embossing and other high temperature-low pressure processes, SFIL can be performed at low pressure and room temperature. Initial experiments carried out, consisted of process flow design for the patterned structures on sputtered Ni-Fe thin films. The main one being the defectivity analysis for the SFIL process conducted by fabricating and testing devices of varying feature sizes (50 nm to 1 μm) and inspecting them optically as well as testing them electrically. Once the SFIL process was optimized, a number of Ni-Fe coated wafers were imprinted with a template having the patterned topography. A minimum feature size of 40 nm was obtained with varying pitch (1:1, 1:1.5, 1:2, and 1:3). The Characterization steps involved extensive SEM study at each processing step as well as Atomic Force Microscopy (AFM) and Magnetic Force Microscopy (MFM) analysis.

Synthesis and electron emission properties of aligned carbon nanotube arrays

Carbon nanotubes (CNTs) have become one of the most interesting allotropes of carbon due to their intriguing mechanical, electrical, thermal and optical properties. The synthesis and electron emission properties of CNT arrays have been investigated in this work. Vertically aligned CNTs of different densities were synthesized on copper substrate with catalyst dots patterned by nanosphere lithography. The CNTs synthesized with catalyst dots patterned by spheres of 500 nm diameter exhibited the best electron emission properties with the lowest turn-on/threshold electric fields and the highest field enhancement factor. Furthermore, CNTs were treated with NH3 plasma for various durations and the optimum enhancement was obtained for a plasma treatment of 1.0 min. CNT point emitters were also synthesized on a flat-tip or a sharp-tip to understand the effect of emitter geometry on the electron emission. The experimental results show that electron emission can be enhanced by decreasing the screening effect of the electric field by neighboring CNTs. In another part of the dissertation, vertically aligned CNTs were synthesized on stainless steel (SS) substrates with and without chemical etching or catalyst deposition. The density and length of CNTs were determined by synthesis time. For a prolonged growth time, the catalyst activity terminated and the plasma started etching CNTs destructively. CNTs with uniform diameter and length were synthesized on SS substrates subjected to chemical etching for a period of 40 minutes before the growth. The direct contact of CNTs with stainless steel allowed for the better field emission performance of CNTs synthesized on pristine SS as compared to the CNTs synthesized on Ni/Cr coated SS. Finally, fabrication of large arrays of free-standing vertically aligned CNT/SnO2 core-shell structures was explored by using a simple wet-chemical route. The structure of the SnO2 nanoparticles was studied by X-ray diffraction and electron microscopy. Transmission electron microscopy reveals that a uniform layer of SnO2 is conformally coated on every tapered CNT. The strong adhesion of CNTs with SS guaranteed the formation of the core-shell structures of CNTs with SnO2 or other metal oxides, which are expected to have applications in chemical sensors and lithium ion batteries.

Uniquely Identifiable Tamper-Evident Device Using Coupling between Subwavelength Gratings

Reliability and sensitive information protection are critical aspects of integrated circuits. A novel technique using near-field evanescent wave coupling from two subwavelength gratings (SWGs), with the input laser source delivered through an optical fiber is presented for tamper evidence of electronic components. The first grating of the pair of coupled subwavelength gratings (CSWGs) was milled directly on the output facet of the silica fiber using focused ion beam (FIB) etching. The second grating was patterned using e-beam lithography and etched into a glass substrate using reactive ion etching (RIE). The slightest intrusion attempt would separate the CSWGs and eliminate near-field coupling between the gratings. Tampering, therefore, would become evident. Computer simulations guided the design for optimal operation of the security solution. The physical dimensions of the SWGs, i.e. period and thickness, were optimized, for a 650 nm illuminating wavelength. The optimal dimensions resulted in a 560 nm grating period for the first grating etched in the silica optical fiber and 420 nm for the second grating etched in borosilicate glass. The incident light beam had a half-width at half-maximum (HWHM) of at least 7 µm to allow discernible higher transmission orders, and a HWHM of 28 µm for minimum noise. The minimum number of individual grating lines present on the optical fiber facet was identified as 15 lines. Grating rotation due to the cylindrical geometry of the fiber resulted in a rotation of the far-field pattern, corresponding to the rotation angle of moiré fringes. With the goal of later adding authentication to tamper evidence, the concept of CSWGs signature was also modeled by introducing random and planned variations in the glass grating. The fiber was placed on a stage supported by a nanomanipulator, which permitted three-dimensional displacement while maintaining the fiber tip normal to the surface of the glass substrate. A 650 nm diode laser was fixed to a translation mount that transmitted the light source through the optical fiber, and the output intensity was measured using a silicon photodiode. The evanescent wave coupling output results for the CSWGs were measured and compared to the simulation results.

The dual effect of normobaric hypoxia on heart rate variability and substrate partitioning following interval cycling

Recent studies have shown the importance of the beat-by-beat changes in heart rate influenced by the autonomic nervous system (ANS), or heart rate variability (HRV). The purpose of this study was to examine the lasting effects of hypoxic exercise on HRV, and its influences on substrate usage. Results from this study could lead an increased understanding on this topic. Eight active healthy males (age: 31±11 years; height: 180±7 cm; weight: 83±8 kg; VO₂max (maximal oxygen consumption): 4.4±0.6 L•min⁻¹) underwent normoxic and hypoxic (FᵢO₂= 0.15) conditions during high-intensity interval (HIIT) cycling (70%-high interval, 35%-rest interval). Cycling intensity was determined by a peak power output cycling test. Each experimental session consisted of a basal metabolic rate determination, up to 45-minutes of HIIT cycling, and three 30-minute post-exercise metabolic rate measurements (spanning 3 hours and 15 minutes after exercise). During exercise, RPE was higher (p<0.01) and LAC (lactate) increased (p=0.001) at each point of time in hypoxia, with no change in normoxia. After hypoxic exercise, the SNS/PNS ratio (overall ANS activity) was significantly higher (p<0.01) and significantly decreased through time in both conditions (p<0.01). In addition, a significant interaction between time and conditions (p<0.02) showed a decrease in LAC concentration through time post-hypoxic exercise. The findings showed that a single bout of hypoxic exercise alters ANS activity post-exercise along with shifting substrate partitioning from glycolytic to lipolytic energy production. The significant decrease in LAC concentration post-hypoxic exercise supports the notion that hypoxic HIIT induces a greater muscle glycogen depletion leading to increased fat oxidation to sustain glycogenesis and gluconeogenesis to maintain blood glucose level during recovery.

Benthic and substrate cover data derived from photo-transect surveys in Lizard Island Reef conducted on December 10-15, 2011

Underwater georeferenced photo-transect surveys were conducted on December 10-15, 2011 at various sections of the reef at Lizard Island, Great Barrier Reef. For this survey a snorkeler or diver swam over the bottom while taking photos of the benthos at a set height using a standard digital camera and towing a GPS in a surface float which logged the track every five seconds. A standard digital compact camera was placed in an underwater housing and fitted with a 16 mm lens which provided a 1.0 m x 1.0 m footprint, at 0.5 m height above the benthos. Horizontal distance between photos was estimated by three fin kicks of the survey diver/snorkeler, which corresponded to a surface distance of approximately 2.0 - 4.0 m. The GPS was placed in a dry-bag and logged the position as it floated at the surface while being towed by the photographer. A total of 5,735 benthic photos were taken. A floating GPS setup connected to the swimmer/diver by a line enabled recording of coordinates of each benthic photo (Roelfsema 2009). Approximation of coordinates of each benthic photo was conducted based on the photo timestamp and GPS coordinate time stamp, using GPS Photo Link Software (www.geospatialexperts.com). Coordinates of each photo were interpolated by finding the GPS coordinates that were logged at a set time before and after the photo was captured. Benthic or substrate cover data was derived from each photo by randomly placing 24 points over each image using the Coral Point Count for Microsoft Excel program (Kohler and Gill, 2006). Each point was then assigned to 1 of 78 cover types, which represented the benthic feature beneath it. Benthic cover composition summary of each photo scores was generated automatically using CPCE program. The resulting benthic cover data of each photo was linked to GPS coordinates, saved as an ArcMap point shapefile, and projected to Universal Transverse Mercator WGS84 Zone 55 South.