V2O5/TiO2 catalyst xerogels: Method of preparation and characterization

This work describes a modified sol-gel method for the preparation of V2O5/TiO2 catalysts. The samples have been characterized by N-2 adsorption at 77 K, X-ray Diffractometry (XRD), Scanning Electronic Microscopy (SEM/EDX) and Fourier Transform Infrared Spectroscopy (FT-IR). The surface area increases with the vanadia loading from 24 m(2) g(-1) for pure TiO2 to 87 m(2) g(-1) for 9 wt% of V2O5. The rutile form is predominant for pure TiO2 but becomes enriched with anatase phase when vanadia loading is increased. No crystalline V2O5 phase was observed in the diffractograms of the catalysts. Analysis by SEM showed heterogeneous granulation of particles with high vanadium dispersion. Two species of surface vanadium were observed by FT-IR spectroscopy: a monomeric vanadyl and polymeric vanadates. The vanadyl/vanadate ratio remains practically constant. Ethanol oxidation was used as a catalytic test in a temperature range from 350 to 560 K. The catalytic activity starts around 380 K. For the sample with 9 wt% of vanadia, the conversion of ethanol into acetaldehyde as the main product was approximately 90% at 473 K.

Characterization of silica-carbon mesoporous matrix with embedded nickel nanoparticles synthesized by the polymeric precursor method

Nickel nanoparticles into silica-carbon matrix composites were prepared by using the polymeric precursor method. The effects of the polyester type and the time of pyrolysis on the mesoporosity and nickel particle dispersion into non-aqueous amorphous silica-carbon matrix were investigated by thermogravimetric analysis, adsorption/desorption isotherms and TEM. A well-dispersed metallic phase could be only obtained by using ethylene glycol. Weightier polyesters affected the pyrolysis process due to a combination of more amounts of carbonaceous residues and delaying of pyrolysis process. The post-pyrolyzed composites were successfully cleaned at 200 degrees C for I h in oxygen atmosphere leading to an increase in the surface area and without the occurrence of carbon combustion or nickel nanoparticles oxidation. The matrix composites presented predominantly mesoporous with pore size well defined in 38 angstrom, mainly when tetraethylene glycol was used as polymerizing agent. (C) 2007 Elsevier B.V. All rights reserved.

Chemical and structural characterization of V2O5/TiO2 catalysts

A series of V2O5/TiO2 samples was synthesized by sol-gel and impregnation methods with different contents of vanadia. These samples were characterized by x-ray diffraction (XRD), Raman spectroscopy, x-ray photoelectron spectroscopy (XPS), and electronic paramagnetic resonance (EPR). XRD detected rutile as the predominant phase for pure TiO2 prepared by the sol-gel method. The structure changed to anatase when the vanadia loading was increased. Also, anatase was the predominant phase for samples obtained by the impregnation method. Raman measurements identified two species of surface vanadium: monomeric vanadyl (V4+) and polymeric vanadates (V5+). XPS results indicated that Ti ions were in octahedral position surrounded by oxygen ions. The V/Ti atomic ratios showed that V ions were highly dispersed on the vanadia/titania surface obtained by the sol-gel method. EPR analysis detected three V4+ ion types: two of them were located in axially symmetric sites substituting for Ti4+ ions in the rutile structure, and the third one was characterized by magnetically interacting V4+ ions in the form of pairs or clusters. A partial oxidation of V4+ to V5+ was evident from EPR analysis for materials with higher concentrations of vanadium. (C) 2001 American Vacuum Society.

In situ evaluation of anticancer drug methotrexate-DNA interaction using a DNA-electrochemical biosensor and AFM characterization

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Ultrastructural characterization of CD133(+) stem cells bound to superparamagnetic nanoparticles: possible biotechnological applications

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Characterization of native and oxidized starches of two varieties of Peruvian carrot (Arracacia xanthorrhiza, B.) from two production areas of Paraná state, Brazil

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Novel production method of porous surface Ti samples for biomedical application

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of interface characterization and adhesion of glass ceramics to commercially pure titanium and gold alloy after thermal- and mechanical-loading

Objectives. This study evaluated the effect of thermal- and mechanical-cycling on the shear bond strength of three low-fusing glassy matrix dental ceramics to commercial pure titanium (cpTi) when compared to conventional feldspathic ceramic fused to gold alloy.Methods. Metallic frameworks (diameter: 5 min, thickness: 4 mm) (N = 96, n = 12 per group) were cast in cpTi and gold alloy, airborne particle abraded with 150 mu m aluminum oxide. Low-fusing glassy matrix ceramics and a conventional feldspathic ceramic were fired onto the alloys (thickness: 4mm). Four experimental groups were formed; Gr1 (control group): Vita Omega 900-Au-Pd alloy; Gr2: Ticeram-cpTi; Gr3: Super Porcelain Ti-22-cpTi and G4: Vita Titankeramik-cpTi. While half of the specimens from each ceramic-metal combination were randomly tested without aging (water storage at 37 C for 24h only), the other half were first thermocycled (6000 cycles, between 5 and 55 C, dwell time: 13 s) and then mechanically loaded (20,000 cycles under SON load, immersion in distilled water at 37 C). The ceramic-alloy interfaces were loaded under shear in a universal test machine (cross-head speed: 0.5 mm/min) until failure occur-red. Failure types were noted and the interfaces of the representative fractured specimens from each group were examined with stereo microscope and scanning electron microscope (SEM). in an additional study (N = 16, n = 2 per group), energy dispersive X-ray spectroscopy (EDS) analysis was performed from ceramic-alloy interfaces. Data were analyzed using ANOVA and Tukey's test.Results. Both ceramic-metal combinations (p < 0.001) and aging conditions (p < 0,001) significantly affected the mean bond strength values. Thermal- and mechanical-cycling decreased the bond strength (MPa) results significantly for Gr3 (33.4 +/- 4.2) and Gr4 (32.1 +/- 4.8) when compared to the non-aged groups (42.9 +/- 8.9, 42.4 +/- 5.2, respectively). Gr1 was not affected significantly from aging conditions (61.3 +/- 8.4 for control, 60.7 +/- 13.7 after aging) (p > 0.05). Stereomicroscope images showed exclusively adhesive failure types at the opaque ceramic-cpTi interfacial zone with no presence of ceramic on the substrate surface but with a visible dark titanium oxide layer in Groups 2-4 except Gr1 where remnants of bonder ceramic was visible. EDS analysis from the interfacial zone for cpTi-ceramic groups showed predominantly 34.5-85.1% O(2) followed by 1.1-36.7% Aland 0-36.3% Si except for Super Porcelain Ti-22 where a small quantity of Ba (1.4-8.3%), S (0.7%) and Sn (35.3%) was found. In the Au-Pd alloy-ceramic interface, 56.4-69.9% O(2) followed by 15.6-26.2% Si, 3.9-10.9% K, 2.8-6% Na, 4.4-9.6% Al and 0-0.04% Mg was observed.Significance. After thermal-cycling for 6000 times and mechanical-cycling for 20,000 times, Triceram-cpTi combination presented the least decrease among other ceramic-alloy combinations when compared to the mean bond strength results with Au-Pd alloy-Vita Omega 900 combination. (c) 2008 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Structural and dielectric characterization of praseodymium-modified lead titanate ceramics synthesized by the OPM route

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural characterization of phase transition of Al2O3 nanopowders obtained by polymeric precursor method

Nanocrystalline Al(2)O(3)powders have been synthesized by the polymeric precursor method. A study of the evolution of crystalline phases of obtained powders was accomplished through X-ray diffraction, micro-Raman spectroscopy and refinement of the structures through the Rietveld method. The results obtained allow the identification of three steps on the gamma-Al2O3 to alpha-Al2O3 phase transition. The single-phase alpha-Al2O3 Powder was obtained after heat-treatment at 1050 degrees C for 2 h. A study of the morphology of the particles was accomplished through measures of crystallite size, specific surface area and transmission electronic microscopy. The particle size is closely related to gamma-Al2O3 to alpha-Al2O3 phase transition. (c) 2007 Elsevier B.V. All rights reserved.

Electrochemical and structural characterization of heat-treated Cr3C2-NiCr coatings

The influence of heat-treatments on the electrochemical behavior of thermal spray Cr3C2-NiCr coatings prepared by high velocity oxygen fuel (HVOF) was studied in NaCl solution, at 25 degrees C, using open-circuit potential (E-OC) and electrochemical impedance spectroscopy (EIS) measurements. Coating characterization were performed before and after the heat-treatments and electrochemical tests by scanning electron microscopy, X-ray diffraction, and Auger electron spectroscopy. In addition to the changes in the original powder composition occurring during HVOF process, heat-treatment performed at 450 degrees C caused no significant changes in electrochemical response compared with untreated sample, and at 760 degrees C the main difference was the formation of a thin and defective layer of Cr2O3 at the coating surface, which increased the total impedance at the first day of immersion. Higher influence on the electrochemical was noted for samples treated at 880 degrees C, which also showed higher E-OC and total impedance, and lower corrosion current. This behavior was interpreted considering the formation of a chromium oxide layer on the coating surface, dissolution and decomposition of smaller carbide particles and their surface enrichment with Cr due to C diffusion and dissolution into the matrix, and possible Ni, Cr, and Fe diffusion to coating/substrate interface. (c) 2006 the Electrochemical Society.

NiTiO3 powders obtained by polymeric precursor method: Synthesis and characterization

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Electrochemical and spectroscopic characterization of screen-printed gold-based electrodes modified with self-assembled monolayers and Tc85 protein

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Poly(glutamic acid) nanofibre modified glassy carbon electrode: Characterization by atomic force microscopy, voltammetry and electrochemical impedance

Glassy carbon electrodes (GCE) were modified with poly(glutamic acid) acid films prepared using three different procedures: glutamic acid monomer electropolymerization (MONO), evaporation of poly(glutamic acid) (PAG) and evaporation of a mixture of poly(glutamic acid)/glutaraldehyde (PAG/GLU). All three films showed good adherence to the electrode surface. The performance of the modified GCE was investigated by cyclic voltammetry and differential pulse voltammetry, and the films were characterized by atomic force microscopy (AFM) and electrochemical impedance spectroscopy (EIS). The three poly(glutamic acid) modified GCEs were tested using the electrochemical oxidation of ascorbic acid and a decrease of the overpotential and the improvement of the oxidation peak current was observed. The PAG modified electrode surfaces gave the best results. AFM morphological images showed a polymeric network film formed by well-defined nanofibres that may undergo extensive swelling in solution, allowing an easier electron transfer and higher oxidation peaks. (C) 2007 Elsevier Ltd. All rights reserved.

Preparation and Characterization of Graphite-Epoxy Composite Modified with Zinc Hexacyanoferrate and Their Electrochemical Behaviour in Presence of Substituted Anilines

The growth of zinc hexacyanoferrate (ZnHCF) hybrid film on the surface of graphite-epoxy composite (GEC) electrodes was demonstrated by cyclic voltammetry. Surface morphology of the hybrid film was investigated by using scanning electron microscopy. The effect of the type of monovalent cations on the redox behaviour of hybrid film was also studied. This effect indicated that the radius of the hydrated cation mainly determines the ion permeability of the film.The electrochemical behavior of the substituted anilines (procaine and sulfamerazine) in 1 M KCl of the modified GEC electrode showed a decrease of the cathodic currents while increasing the concentration of these analytes. The developed sensor also showed excellent stability for long time usage, higher sensitivity and cost-effective fabrication.