Multifunctional cement composites strain and damage sensors applied on reinforced concrete (RC) structural elements

In this research, strain-sensing and damage-sensing functional properties of cement composites have been studied on a conventional reinforced concrete (RC) beam. Carbon nanofiber (CNFCC) and fiber (CFCC) cement composites were used as sensors on a 4 m long RC beam. Different casting conditions (in situ or attached), service location (under tension or compression) and electrical contacts (embedded or superficial) were compared. Both CNFCC and CFCC were suitable as strain sensors in reversible (elastic) sensing condition testing. CNFCC showed higher sensitivities (gage factor up to 191.8), while CFCC only reached gage factors values of 178.9 (tension) or 49.5 (compression). Furthermore, damage-sensing tests were run, increasing the applied load progressively up to the RC beam failure. In these conditions, CNFCC sensors were also strain sensitive, but no damage sensing mechanism was detected for the strain levels achieved during the tests. Hence, these cement composites could act as strain sensors, even for severe damaged structures near to their collapse.

An improved procedure for obtaining and maintaining well characterized partial water saturation states on concrete samples to be used for mass transport tests

A conditioning procedure is proposed allowing to install into the concrete specimens any selected value of water saturation degree with homogeneous moisture distribution. This is achieved within the least time and the minimum alteration of the concrete specimens. The protocol has the following steps: obtaining basic drying data at 50 °C (water absorption capacity and drying curves); unidirectional drying of the specimens at 50 °C until reaching the target saturation degree values; redistribution phase in closed containers at 50 °C (with measurement of the quasi-equilibrium relative humidities); storage into controlled environment chambers until and during mass transport tests, if necessary. A water transport model is used to derive transport parameters of the tested materials from the drying data, i.e., relative permeabilities and apparent water diffusion coefficients. The model also allows calculating moisture profiles during isothermal drying and redistribution phases, thus allowing optimization of the redistribution times for obtaining homogeneous moisture distributions.

Recommendation of RILEM TC 178-TMC: Testing and modelling chloride penetration in concrete

This RILEM Technical Recommendation intends to give a general description of methods of sampling for obtaining chloride concentration profiles in concrete, applicable both for laboratory cast concrete specimens, for concrete cores taken from structures and for testing on site. These sampling procedures may be applied for obtaining concentration profiles of any other chemical species present in concrete.

Efficiency of a conductive cement-based anodic system for the application of cathodic protection, cathodic prevention and electrochemical chloride extraction to control corrosion in reinforced concrete structures

This article describes the research carried out regarding the application of cathodic protection (CP) and cathodic prevention (CPrev), in some cases with a pre-treatment of electrochemical chloride extraction (ECE), on representative specimens of reinforced concrete structures, using an anodic system consisting of a graphite-cement paste applied as a coating on the surface. The aim of this research is to find out the competence of this anode for the aforementioned electrochemical treatments. The efficiency of this anode has been clearly demonstrated, as well as its capability to apply a combined process of ECE and after CP.

Procedure for calculating the chloride diffusion coefficient and surface concentration from a profile having a maximum beyond the concrete surface

Chlorides induce local corrosion in the steel reinforcements when reaching the bar surface. The measurement of the rate of ingress of these ions, is made by mathematically fitting the so called “error function equation” into the chloride concentration profile, obtaining so the diffusion coefficient and the chloride concentration at the concrete surface. However, the chloride profiles do not always follow Fick’s law by having the maximum concentration at the concrete surface, but often the profile shows a maximum concentration more in the interior, which indicates a different composition and performance of the most external concrete layer with respect to the internal zones. The paper presents a procedure prepared during the time of the RILEM TC 178-TMC: “Testing and modeling chloride penetration in concrete”, which suggests neglecting the external layer where the chloride concentration increases and using the maximum as an “apparent” surface concentration, called C max and to fit the error function equation into the decreasing concentration profile towards the interior. The prediction of evolution should be made also from the maximum.

Acoustic properties of porous concrete made from arlite and vermiculite lightweight aggregates

The use of sustainable materials is becoming a common practice for noise abatement in building and civil engineering industries. In this context, many applications have been found for porous concrete made from lightweight aggregates. This work investigates the acoustic properties of porous concrete made from arlite and vermiculite lightweight aggregates. These natural resources can still be regarded as sustainable since they can be recycled and do not generate environmentally hazardous waste. The experimental basis used consists of different type specimens whose acoustic performance is assessed in an impedance tube. Additionally, a simple theoretical model for granular porous media, based on parameters measurable with basic experimental procedures, is adopted to predict the acoustic properties of the prepared mixes. The theoretical predictions compare well with the absorption measurements. Preliminary results show the good absorption capability of these materials, making them a promising alternative to traditional porous concrete solutions.

Targetless image-based method for measuring displacements and strains on concrete surfaces with a consumer camera

Measurement of concrete strain through non-invasive methods is of great importance in civil engineering and structural analysis. Traditional methods use laser speckle and high quality cameras that may result too expensive for many applications. Here we present a method for measuring concrete deformations with a standard reflex camera and image processing for tracking objects in the concretes surface. Two different approaches are presented here. In the first one, on-purpose objects are drawn on the surface, while on the second one we track small defects on the surface due to air bubbles in the hardening process. The method has been tested on a concrete sample under several loading/unloading cycles. A stop-motion sequence of the process has been captured and analyzed. Results have been successfully compared with the values given by a strain gauge. Accuracy of our methods in tracking objects is below 8 μm, in the order of more expensive commercial devices.

Comparison Between Dcrit Considering the Abrupt Variation and Inflexion in the Concrete Mercury Intrusion Porosimetry Curve

Mercury intrusion porosimetry (MIP) has been widely used to evaluate the quality of concrete through the pore size distribution parameters. Two of these parameters are the critical pore diameter (Dcrit) and the percentage of the most interconnected net of pores compared to the total volume of pores. Some researchers consider Dcrit as the diameter obtained from the inflexion point of the cumulative mercury intrusion curve while others consider Dcrit as the diameter obtained from the point of abrupt variation in the same curve. This study aims to analyze two groups of concretes of varying w/c ratios, one cast with pozzolanic cement and another with high initial strength cement, in order to determine which of these diameters feature a better correlation with the quality parameters of the concretes. The concrete quality parameters used for the evaluations were (1) the w/c ratios and (2) chloride diffusion coefficients measured at approximately 90 days. MIP cumulative distributions of the same concretes were also measured at about 90 days, and Dcrit values were determined (1) from the point of abrupt variation and alternatively, (2) from the inflexion point of each of these plots. It was found that Dcrit values measured from the point of abrupt variation were useful indicators of the quality of the concrete, but the Dcrit values based on the inflexion points were not. Hence, it is recommended that Dcrit and the percentage of the most interconnected volume of pores should be obtained considering the point of abrupt variation of the cumulative curve of pore size distribution.

Highly Conductive Carbon Fiber Reinforced Concrete for Icing Prevention and Curing

This paper aims to study the feasibility of highly conductive carbon fiber reinforced concrete (CFRC) as a self-heating material for ice formation prevention and curing in pavements. Tests were carried out in lab ambient conditions at different fixed voltages and then introduced in a freezer at −15 °C. The specimens inside the freezer were exposed to different fixed voltages when reaching +5 °C for prevention of icing and when reaching the temperature inside the freezer, i.e., −15 °C, for curing of icing. Results show that this concrete could act as a heating element in pavements with risk of ice formation, consuming a reasonable amount of energy for both anti-icing (prevention) and deicing (curing), which could turn into an environmentally friendly and cost-effective deicing method.

The incorporation of construction and demolition wastes as recycled mixed aggregates in non-structural concrete precast pieces

Concern for the environment has lately heightened awareness about the need for recycling in the construction industry. However, some standards, such as the Spanish standard, only accept the recycling of aggregates derived from concrete, which limits the extensive use of construction and demolition waste, which are produced in much bigger volumes. The aim of this work was to explore the possibility of using recycled mixed aggregates (RMA) in the preparation of precast non-structural concretes. To that end different percentages of natural aggregate were replaced by RMA in non-structural elements (25, 50, 75 and 100%). Contents of cement, water, and the dosages commonly used by companies were unchanged by the introduction of RMA. The characterization of the prepared elements has been done using the specific tests for each type of non-structural element (terrazzo for indoor use, hollow tiles, kerbstones and paving blocks): compression and flexural strength, water absorption, dimensional tolerances, abrasion and slipping resistance. The paving blocks, kerbstones, and hollow tiles prepared were tested for 360 days. The stability of the tested properties confirmed the possibility of using these wastes on an industrial scale satisfying the standard requirements. However, the surface of terrazzo with RMA is not as good as that prepared with natural aggregate.

Compressive behaviour of a tire recycled steel and textil fiber concrete subjected to fire

The use of rubber aggregates, steel and textile fibres recycled from tires in concrete is a solution that it is being studied by several authors around the world. A few works have been carried out at room temperature but very scarce at high temperatures. This paper presents the results of a research with the aim to evaluate the behaviour at high temperatures of a concrete made with different amounts of recycled textile and steel fibres from tires. The study considered five concrete compositions, with the same water/cement ratio (W/C=0.43), differing only in the type and quantity of fibers incorporated in the mixture. Thus, a reference composition (0% fiber), two compositions with 30 and 70kg/m3 of steel fibers and a composition with 2 and 4kg/m3 of textile fibers from tires were tested. The concrete was tested for a load level of 0.5fcd and different maximum temperature levels (20, 300, 500 and 700ºC).