Effect of pH and oxalic acid on the reduction of Fe(3+) by a biomimetic chelator and on Fe(3+) desorption/adsorption onto wood: Implications for brown-rot decay

Fenton reaction is thought to play an important role in wood degradation by brown-rot fungi. In this context, the effect of oxalic acid and pH on iron reduction by a biomimetic fungal chelator and on the adsorption/desorption of iron to/from wood was investigated. The results presented in this work indicate that at pH 2.0 and 4.5 and in the presence of oxalic acid, the phenolate chelator 2,3-dihydroxybenzoic acid (2,3-DHBA) is capable of reducing ferric iron only when the iron is complexed with oxalate to form Fe mono-oxalate (Fe(C(2)O(4))(+)). Within the pH range tested in this work, this complex formation occurs when the oxalate:Fe(3+) molar ratio is less than 20 (pH 2.0) or less than 10 (pH 4.5). When aqueous ferric iron was passed through a column packed with milled red spruce (Picea rubens) wood equilibrated at pH 2.0 and 4.5. it was observed that ferric iron binds to wood at pH 4.5 but not at pH 2.0, and the bound iron could then be released by application of oxalic acid at pH 4.5. The release of bound iron was dependent on the amount of oxalic acid applied in the column. When the amount of oxalate was at least 20-fold greater than the amount of iron bound to the wood, all bound iron was released. When Fe-oxalate complexes were applied to the milled wood column equilibrated in the pH range of 2-4.5, iron from Fe-oxalate complexes was bound to the wood only when the pH was 3.6 or higher and the oxalate:Fe(3+) molar ratio was less than 10. When 2,3-DHBA was evaluated for its ability to release iron bound to the milled wood, it was found that 2,3-DHBA possessed a greater affinity for ferric iron than the wood as 2,3-DHBA was capable of releasing the ferric iron bound to the wood in the pH range 3.6-5.5. These results further the understanding of the mechanisms employed by brown-rot fungi in wood biodegradation processes. (C) 2009 Elsevier Ltd. All rights reserved.

The influence of microstructure on the maximum load and fracture energy of refractory castables

Refractory castables are composed of fractions of fine to fairly coarse particles. The fine fraction is constituted primarily of raw materials and calcium aluminate cement, which becomes hydrated, forming chemical bonds that stiffen the concrete during the curing process. The present study focused on an evaluation of several characteristics of two refractory castables with similar chemical compositions but containing aggregates of different sizes. The features evaluated were the maximum load, the fracture energy, and the ""relative crack-propagation work"" of the two castables heat-treated at 110, 650, 1100 and 1550 degrees C. The results enabled us to draw the following conclusions: the heat treatment temperature exerts a significant influence on the matrix/aggregate interaction, different microstructures form in the castables with temperature, and a relationship was noted between the maximum load and the fracture energy. (C) 2009 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Spontaneous infiltrations of compound systems of Y(2)O(3), Sm(2)O(3), RE(2)O(3), Al(2)O(3) and AIN in SiC ceramics

Silicon carbide ceramics (SiC) are used in different applications in the engineering area due to the excellent properties, mainly in high temperatures. They are usually obtained by liquid-phase sintering enabling to form volatile products and, consequently, defects. The present work aims at studying the obtention of SiC ceramics by spontaneous infiltration using a eutectic composition of the Al(2)O(3)/Y(2)O(3), AIN/Y(2)O(3), Al(2)O(3)/Sm(2)O(3), AlN/Sm(2)O(3), Al(2)O(3)/RE(2)O(3) and AlN/RE(2)O(3) Systems. RE(2)O(3) is the concentrate of the rare-earth oxide obtained from Xenotime ore. Infiltration tests were carried out in argon atmosphere, graphite crucibles, in several temperatures near the melting point of each system, varying from 2.5 to 60 min. It was observed that Al(2)O(3)/Y(2)O(3), Al(2)O(3)/SM(2)O(3), AlN/SM(2)O(3) and Al(2)O(3)/RE(2)O(3) systems do not infiltrate appropriately and the AlN/Y(2)O(3) and AlN/RE(2)O(3) systems infiltrated spontaneously more than 20 mm; however, the first one presented a higher degree of infiltration, approximately 97%. (C) 2009 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Sensor arrays to detect humic substances and Cu(II) in waters

The interaction between poly(o-ethoxyaniline) (POEA) adsorbed onto solid substrates and humic substances (HS) and Cu(2+) ions has been investigated using UV-vis spectroscopy and atomic force microscopy (AFM). Both HS and Cu(2+) are able to dope POEA and change film morphology. This interaction was exploited in a sensor array made with nanostructured films of POEA, sulfonated lignin and HS, which could detect small concentrations of HS and Cu(2+) in water. (C) 2009 Elsevier B.V. All rights reserved.

Selection of new glass-forming compositions in Al-La system using a combination of topological instability and thermodynamic criteria

A combination of an extension of the topological instability ""lambda criterion"" and a thermodynamic criterion were applied to the Al-La system, indicating the best range of compositions for glass formation. Alloy compositions in this range were prepared by melt-spinning and casting in an arc-melting furnace with a wedge-section copper mold. The GFA of these samples was evaluated by X-ray diffraction, differential scanning calorimetry and scanning electron microscopy. The results indicated that the gamma* parameter of compositions with high GFA is higher, corresponding to a range in which the lambda parameter is greater than 0.1, which are compositions far from Al solid solution. A new alloy was identified with the best GFA reported so far for this system, showing a maximum thickness of 286 mu m in a wedge-section copper mold. Crown Copyright (C) 2009 Published by Elsevier B.V. All rights reserved.

Concretes and mortars recycled with water treatment sludge and construction and demolition rubble

There are about 7500 water treatment plants in Brazil. The wastes these plants generate in their decantation tanks and filters are discharged directly into the same brooks and rivers that supply water for treatment. Another serious environmental problem is the unregulated disposal of construction and demolition rubble, which increases the expenditure of public resources by degrading the urban environment and contributing to aggravate flooding and the proliferation of vectors harmful to public health. In this study, an evaluation was made of the possibility of recycling water treatment sludge in construction and demolition waste recycling plants. The axial compressive strength and water absorption of concretes and mortars produced with the exclusive and joint addition of these two types of waste was also determined. The ecoefficiency of this recycling was evaluated by determining the concentration of aluminum in the leached extract resulting from the solubilization of the recycled products. The production of concretes and mortars with the joint addition of water treatment sludge and recycled concrete rubble aggregates proved to be a viable recycling alternative from the standpoint of axial compression strength, modulus of elasticity, water absorption and tensile strength by the Brazilian test method. (C) 2008 Elsevier Ltd. All rights reserved.

Co-electrodeposition and characterization of Cu-Si(3)N(4) composite coatings

Smooth copper coatings containing well-distributed silicon nitride particles were obtained by co-electrodeposition in acidic sulfate bath. The cathodic current density did not show significant influence on incorporated particle volume fraction, whereas the increase of particle concentration in the bath led to its decrease. The increase of stirring rate increased the amount of embedded particles. The microhardness of the composite layers was higher than that of pure copper deposits obtained under the same conditions due to dispersion-strengthening and copper matrix grain refinement and increased with the increase of incorporated particle volume fraction. The microhardness of composites also increased with the increase of current density due to copper matrix grain refining. The composite coatings presented higher strength but lower ductility than pure copper layers. Pure copper and composite coatings showed the same corrosion resistance in 0.5 wt.% H(2)SO(4) solution at room temperature. (C) 2011 Elsevier B.V. All rights reserved.

Mechanical properties and cytotoxicity of 3Y-TZP bioceramics reinforced with Al(2)O(3) particles

The influence of Al(2)O(3) addition and sintering parameters on the mechanical properties and cytotoxicity of tetragonal ZrO(2)-3 mol% Y(2)O(3) ceramics was evaluated. Samples containing 0, 10, 20 and 30 wt.% of Al(2)O(3) particles were prepared by cold uniaxial pressing (80 MPa) and sintered in air at 1500, 1550 and 1600 degrees C for 120 min. The effects of the sintering conditions on the microstructure were analyzed by X-ray diffraction analysis and scanning electron microscopy. Hardness and fracture toughness were determined by the Vickers indentation method and the mechanical resistance by four-point bending tests. As a preliminary biological evaluation, ""in vitro"" cytotoxicity tests were realized to determine the cytotoxic level of the ZrO(2)-Al(2)O(3) composites, using the neutral red uptake method with NCTC clones L929 from the American Type Culture Collection (ATCC) bank. Fully dense ceramic materials were obtained with a hardness ranging between 1340 HV and 1585 HV, depending on the amount of Al(2)O(3) in the ZrO(2) matrix. On the other hand, no significant influence of the Al(2)O(3) addition on fracture toughness was observed, exhibiting values near 8 MPa m(1/2) for all compositions and sintering conditions studied. The non-cytotoxic behavior, the elevated fracture toughness, the good bending strength (sigma(f) = 690 MPa) and the elevated Weibull`s modulus (m = 11) exhibited by the material, show that these ceramic composites are highly suitable biomaterials for dental implant applications. (C) 2008 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Properties of Y-TZP/Al(2)O(3) ceramic nanocomposites obtained by high-energy ball milling

In this work, the synthesis of Y(2)O(3) stabilized tetragonal zirconia polycrystals (Y-TZP)-alumina (Al(2)O(3)) powder mixture was performed by high-energy ball milling and the sintering behavior of this composite was investigated. In order to understand the phase transformations occurring during ball milling, samples were collected after different milling times, from 1 to 60 h. The milled powders were compacted by cold uniaxial pressing and sintered at 1400 and 1600 degrees C. Both powders and sintered samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometry analysis (EDS) and mechanical properties. Fully dense samples were obtained after sintering at 1600 degrees C, while the samples sintered at 1400 degrees C presented a full density for powder mixtures milled for 30 and 60 h. Fracture toughness and Vickers hardnessvalues of the Y-T-ZP/Al(2)O(3) nanocomposite were improved due to dispersed Al(2)O(3) grains and reduced ZrO(2) grain size. Samples sintered at 1400 degrees C, based on powders milled for 60 h, presented high K(IC) and hardness values near to 8.0 Mpan(1/2) and 15 GPa, respectively (C) 2008 Elsevier B.V. All rights reserved

Crystallographic characterization of silicon nitride ceramics sintered with Y(2)O(3)-Al(2)O(3) or E(2)O(3)-Al(2)O(3) additions

Silicon nitride ceramics were sintered using Y(2)O(3)-Al(2)O(3) or E(2)O(3)-Al(2)O(3) (E(2)O(3) denotes a mixed oxide Of Y(2)O(3) and rare-earth oxides) as sintering additives. The intergranular phases formed after sintering was investigated using high-resolution X-ray diffraction (HRXRD). The use of synchrotron radiation enabled high angular resolution and a high signal to background ratio. Besides the appearance Of beta-Si(3)N(4) phase the intergranular phases Y(3)Al(5)O(12) (YAG) and Y(2)SiO(5) were identified in both samples. The refinement of the structural parameters by the Rietveld method indicated similar crystalline structure Of beta-Si(3)N(4) for both systems used as sintering additive. On the other hand, the intergranular phases Y(3)Al(5)O(12) and Y(2)SiO(5) shown a decrease of the lattice parameters, when E(2)O(3) was used as additive, indicating the formation of solid solutions of E(3)Al(5)O(12) and E(2)SiO(5), respectively. (C) 2007 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Magnetostriction of Fe-Sn polycrystalline alloys

In the present work we study the magnetostriction of Fe(91)Sn(9) and Fe(80)Sn(20) polycrystalline samples produced by arc melting and heat treated at temperatures of 1153 K for 6 h and 1023 K for 24 h, looking for high values of magnetostriction as in Fe-Ga alloys. Magnetostriction, as well as saturation magnetization measurements, was carried out at temperatures close to 203 K in the magnetic field interval 0 to 1.5 T. Results of magnetostriction on sample Fe(91)Sn(9), which has almost pure alpha-phase, show magnitude and behavior similar to pure Fe. The two additional Fe(80)Sn(20) samples have a combination of alpha-phase plus either Fe(5)Sn(3) or Fe(3)Sn(2) and show a peculiar behavior of the magnetostriction for mu(0)H < 0.3 T the magnetostriction grows from zero to saturation of the alpha-phase. Following, for mu(0)H > 0.3 T, the magnetostriction starts again to grow linearly with the field, but saturation was not observed up to 5 T. This behavior was attributed to the presence of Fe(5)Sn(3) or Fe(3)Sn(2) phases in these samples that are also ferromagnetic as the alpha-phase is. (c) 2008 Elsevier B.V. All rights reserved.

Use of sugarcane bagasse as biomaterial for cell immobilization for xylitol production

This study provides a preliminary contribution to the development of a bioprocess for the contintious production of xylitol from hemicellulosic hydrolyzate utilizing Candida guilliermondii cells immobilized onto natural sugarcane bagasse fibers. To this purpose, cells of this yeast were submitted to batch tests of ""in situ"" adsorption onto crushed and powdered sugarcane bagasse after treatment with 0.5 M NaOH. The results obtained on a xylose-based semi-synthetic medium were evaluated in terms of immobilization efficiency, cell retention and specific growth rates of suspended, immobilized and total cells. The first two parameters were shown to increase along the immobilization process, reached maximum values of 50.5% and 0.31 g immobilized cells/g bagasse after 21 h and then sharply decreased. The specific growth rate of suspended cells continuously increased during the immobilization tests, while that of the immobilized ones, after an initial growth, exhibited decreasing values. Under the conditions selected for cell immobilization, fermentation also took place with promising results. The yields of xylitol and biomass on consumed xylose were 0.65 and 0.18 g/g, respectively, xylitol and biomass productivities 0.66 and 0.13 g L-1 h(-1), and the efficiency of xylose-to-xylitol bioconversion was 70.8%. (C) 2007 Elsevier Ltd. All rights reserved.

Toughened ZrO2 ceramics sintered with a La2O3-rich glass as additive

In this study, the influence of the glass addition and sintering parameters on the densification and mechanical properties of tetragonal zirconia polycrystals (3Y-TZP) ceramics were evaluated. High-purity tetragonal ZrO2 powder and La2O3-rich glass were used as starting powders. Two compositions based on ZrO2 and containing 5wt.% and 10wt.% of La2O3-rich glass were studied in this work. The starting powders were mixed/milled by planetary milling, dried at 90 degrees C for 24 h, sieved through a 60 mesh screen and uniaxially cold pressed under 80 MPa. The samples were sintered in air at 1200 degrees C, 1300 degrees C, 1400 degrees C for 60 min and at 1450 degrees C for 120 min, with heating and cooling rates of 10 degrees C/min. Sintered samples were characterized by relative density, X-ray diffraction (XRD) and scanningelectron microscopy (SEM). Hardness and fracture toughness were obtained by Vickers indentation method. Dense sintered samples were obtained for all conditions. Furthermore, only tetragonal-ZrO2 was identified as crystalline phase in sintered samples, independently of the conditions studied. Samples sintered at 1300 degrees C for 60 min presented the optimal mechanical properties with hardness and fracture toughness values near to 12 GPa and 8.5 MPa m(1/2) respectively. (c) 2007 Elsevier B.V, All rights reserved.

Mechanical properties of concrete produced with a composite of water treatment sludge and sawdust

In developing countries such as Brazil, the wastes generated in the decanters and filters of water treatment plants are discharged directly into the same rivers and streams that supply water for treatment. Another environmental problem is the unregulated discard of wood wastes. The lumber and wood products industry generates large quantities of this waste, from logging to the manufacture of the end product. Brazil has few biomass plants and therefore only a minor part of these wastes are reused. This paper presents the results of the first study involving a novel scientific and technological approach to evaluate the possibility of combining these two types of wastes in the production of a light-weight composite for concrete. The concrete produced with cement:sand:composite:water mass ratios of 1:2.5:0.67:0.6 displayed an axial compressive strength of 11.1 MPa, a compressive and diametral tensile strength of 1.2 MPa, water absorption of 8.8%, and a specific mass of 1.847 kg/m(3). The mechanical properties obtained with this concrete render it suitable for application in non-structural elements. (C) 2010 Elsevier Ltd. All rights reserved.

Infiltration of Al2O3/Y2O3 mix into SiC ceramic preforms

Silicon carbide ceramics are very interesting materials to engineering applications because of their properties. These ceramics are produced by liquid phase sintering (LPS), where elevated temperature and time are necessary, and generally form volatile products that promote defects and damage their mechanical properties. In this work was studied the infiltration process to produce SiC ceramics, using shorter time and temperature than LPS, thereby reducing the undesirable chemical reactions. SiC powder was pressed at 300 MPa and pre-sintered at 1550 degrees C for 30 min. Unidirectional and spontaneous infiltration of this preform by Al2O3/Y2O3 liquid was done at 1850 degrees C for 5, 10, 30 and 60 min. The kinetics of infiltration was studied, and the infiltration equilibrium happened when the liquid infiltrated 12 mm into perform. The microstructures show grains of the SiC surrounded by infiltrated additives. The hardness and fracture toughness are similar to conventional SiC ceramics obtained by LPS. (c) 2007 Elsevier Ltd and Techna Group S.r.l. All rights reserved.