Periodic Arrays of Interwoven Quadrifilar Spirals on Ferrite Substrates

The properties of metasurfaces composed of doubly periodic arrays of interwoven quadrifilar spiral conductors on magnetized ferrite substrates have been investigated with the aid of the full-wave electromagnetic simulator. The effects of incident wave polarization and ferrite magnetization on the scattering characteristics have been analysed at both normal and in-plane dc magnetic bias. The features of the fundamental topological resonances in the interwoven spiral arrays on ferrite substrates are illustrated by the simulation results and the effects of ferrite gyrotropy and dispersion on the array resonance response and fractional bandwidth are discussed.

Mechanical behaviour of AISiC nano composites produced by Ball Milling and Spark Plasma Sintering

Neste trabalho foram produzidos nanocompósitos de AlSiC misturando alumínio puro com nano partículas de SiC com diâmetro de 45 – 55 nm, usando, de forma sequencial, a técnica da metalurgia do pó e a compactação por “ Spark Plasma Sintering”. O compósito obtido apresentava grãos com 100 nm de diâmetro, encontrandose as partículas de SiC localizadas, principalmente, nas fronteiras de grão. O nanocompósito sob a forma de provetes cilíndricos foi submetido a testes de compressão uniaxial e a testes de nanoindentação para analisar a influência das nanopartículas de SiC, da fração volúmica de ácido esteárico e do tempo de moagem, nas propriedades mecânicas do material. Para efeitos de comparação, utilizouse o comportamento mecânico do Al puro processado em condições similares e da liga de alumínio AA1050O. A tensão limite de elasticidade do nanocompósito com 1% Vol./Vol. de SiC é dez vezes superior à do AA1050. O refinamento de grão à escala nano constitui o principal mecanismo de aumento de resistência mecânica. Na realidade, o Al nanocristalino sem reforço de partículas de SiC, apresenta uma tensão limite de elasticidade sete vezes superior à da liga AA1050O. A adição de 0,5 % Vol./Vol. e de 1 % Vol./Vol. de SiC conduzem, respetivamente, ao aumento da tensão limite de elasticidade em 47 % e 50%. O aumento do tempo de moagem e a adição de ácido esteárico ao pó durante a moagem conduzem apenas a um pequeno aumento da tensão de escoamento. A dureza do material medida através de testes de nanoindentação confirmaram os dados anteriores. A estabilidade das microestruturas do alumínio puro e do nanocompósito AlSiC, foi testada através de recozimento de restauração realizado às temperaturas de 150 °C e 250 °C durante 2 horas. Aparentemente, o tratamento térmico não influenciou as propriedades mecânicas dos materiais, excepto do nanocompósito com 1 % Vol./Vol. de SiC restaurado à temperatura de 250 °C, para o qual se observou uma redução da tensão limite de elasticidade na ordem dos 13 %. No alumínio nanocristalino, a tensão de escoamento é controlada pelo efeito de HallPetch. As partículas de SiC, são segregadas pelas fronteiras do grão e não contribuem para o aumento de resistência mecânica segundo o mecanismo de Orowan. Alternativamente, as nanopartículas de SiC constituem um reforço das fronteiras do grão, impedindo o seu escorregamento e estabilizando a nanoestrutura. Deste modo, as propriedades mecânicas do alumínio nanocristalino e do nanocompósito de AlSiC poderão estar relacionadas com a facilidade ou dificuldade do escorregamento das fronteiras de grão, embora não seja apresentada prova explícita deste mecanismo à temperatura ambiente.

Study on Granular Dynamics in Vertically Vibrated Beds using Tracking Technique

The study of granular material is of great interest to many researchers in both engineering and science communities. The importance of such a study derives from its complex rheological character and also its significant role in a wide range of industrial applications, such as coal, food, plastics, pharmaceutical, powder metallurgy and mineral processing. A number of recent reports have been focused on the physics of non-cohesive granular material submitted to vertical vibration in either experimental or theoretical approaches. Such a kind of system can be used to separate, mix and dry granular materials in industries. It exhibits different instability behaviour on its surface when under vertical vibration, for example, avalanching, surface fluidization and surface wave, and these phenomena have attracted particular interest of many researchers. However, its fundamental understanding of the instability mechanism is not yet well-understood. This paper is therefore to study the dynamics of granular motion in such a kind of system using Positron Emission Particle Tracking (PEPT), which allows the motion of a single tracer particle to be followed in a non-invasive way. Features of the solids motion such as cycle frequency and dispersion index were investigated via means of authors’ specially-written programmes. Regardless of the surface behaviour, particles are found to travel in rotational movement in horizontal plane. Particle cycle frequency is found to increase strongly with increasing vibration amplitude. Particle dispersion also increased strongly with vibration amplitude. Horizontal dispersion is observed to always exceed vertical dispersion.

Contribución metodológica en técnicas de diseñar para fabricación

En el proceso de diseño se toman decisiones que pueden afectar a la fabricabilidad del producto. Cuando el diseñador es experto, considera las limitaciones, las propiedades y el coste de fabricación en la fase de materialización o de detalle. El problema surge cuando el diseñador no es experto o cuando no hay suficiente información y conocimiento de fabricación disponible. Tomando como referencia la teoría de Diseño Axiomático y las técnicas de DFM, se propone una metodología para identificar, definir y formalizar la información de fabricación que debería estar disponible en el diseño para diseñar para fabricar (DFM). También se propone un prototipo de modelo de información para desarrollar una futura herramienta informática que facilitaría la aplicación de esta metodología y que permitiría guiar al diseñador durante el diseño. La metodología ha sido aplicada a una biela de un motor de combustión interna alternativo (MCIA), y a los procesos que se están usando actualmente para fabricarla: forja en matriz cerrada y forja de polvo de metal.

Estudo e desenvolvimento de um capacitor eletrolítico de nióbio

It seeks to find an alternative to the current tantalum electrolytic capacitors in the market due to its high cost. Niobium is a potential substitute, since both belong to the same group of the periodic table and because of this have many similar physical and chemical properties. Niobium has several technologically important applications, and Brazil has the largest reserves, around 96%. There are including niobium in reserves of tantalite and columbite in Rio Grande do Norte. These electrolytic capacitors have high capacitance specifies, ie they can store high energy in small volumes compared to other types of capacitors. This is the main attraction of this type of capacitor because is growing demand in the production of capacitors with capacitance specifies increasingly high, this because of the miniaturization of various devices such as GPS devices, televisions, computers, phones and many others. The production route of the capacitor was made by powder metallurgy. The initial niobium powder supplied by EEL-USP was first characterized by XRD, SEM, XRF and laser particle size, to then be sieved into three particle size, 200, 400 e 635mesh. The powders were then compacted and sintered at 1350, 1450 and 1550°C using two sintering time 30 and 60min. Sintering is one of the most important parts of the process as it affects properties as porosity and surface cleaning of the samples, which greatly affected the quality of the capacitor. The sintered samples then underwent a process of anodic oxidation, which created a thin film of niobium pentóxido over the whole porous surface of the sample, this film is the dielectric capacitor. The oxidation process variables influence the performance of the film and therefore the capacitor. The samples were characterized by electrical measurements of capacitance, loss factor, ESR, relative density, porosity and surface area. After the characterizations was made an annealing in air ate 260ºC for 60min. After this treatment were made again the electrical measurements. The particle size of powders and sintering affected the porosity and in turn the specific area of the samples. The larger de area of the capacitor, greater is the capacitance. The powder showed the highest capacitance was with the smallest particle size. Higher temperatures and times of sintering caused samples with smaller surface area, but on the other hand the cleaning surface impurities was higher for this cases. So a balance must be made between the gain that is achieved with the cleaning of impurities and the loss with the decreased in specific area. The best results were obtained for the temperature of 1450ºC/60min. The influence of annealing on the loss factor and ESR did not follow a well-defined pattern, because their values increased in some cases and decreased in others. The most interesting results due to heat treatment were with respect to capacitance, which showed an increase for all samples after treatment

Estudo da sinterização de cavacos de aço ferritico

This research studies the sintering of ferritic steel chips from the machining process. Were sintered metal powder obtained from machining process chips for face milling of a ferritic steel. The chip was produced by machining and characterized by SEM and EDS, and underwent a process of high energy mill powder characterized also by SEM and EDS. Were constructed three types of matrixes for uniaxial compression (relation l / d greater than 2.5). The differences in the design of the matrixes were essentially in the direction of load application, which for cylindrical case axial direction, while for the rectangular arrays, the longer side. Two samples were compressed with different geometries, a cylindrical and rectangular with the same compaction pressure of 700 MPa. The samples were sintered in a vacuum resistive furnace, heating rate 20 °C / min., isotherm 1300 °C for 60 minutes, and cooling rate of 25 °C / min to room temperature. The starting material of the rectangular sample was further annealed up to temperature of 800 ° C for 30 min. Sintered samples were characterized by scanning electron microscopy, optical microscopy and EDS. The sample compressed in the cylindrical matrix did not show a regular density reflecting in the sintered microstructure revealed by the irregular geometry of the pores, characterizing that the sintering was not complete, reaching only the second phase. As for the specimen compacted in the rectangular array, the analysis performed by scanning electron microscopy, optical microscopy and EDS indicate a good densification, and homogeneous microstructure in their full extent. Additionally, the EDS analyzes indicate no significant changes in chemical composition in the process steps. Therefore, it is concluded that recycling of chips, from the processed ferritic steel is feasible by the powder metallurgy. It makes possible rationalize raw material and energy by manufacture of known properties components from chips generated by the machining process, being benefits to the environment

Estudo da sinterabilidade de ligas de níquel obtidas por meio dos portadores de liga sic, si3n4 ou si metálico com grafita

Nickel alloys are frequently used in applications that require resistance at high temperatures associated with resistance to corrosion. Alloys of Ni-Si-C can be obtained by means of powder metallurgy in which powder mixtures are made of metallic nickel powders with additions of various alloying carriers for such were used in this study SiC, Si3N4 or Si metal with graphite. Carbonyl Ni powder with mean particle size of 11 mM were mixed with 3 wt% of SiC powders with an average particle size of 15, 30 and 50 μm and further samples were obtained containing 4 to 5% by mass of SiC with average particle size of 15 μm. Samples were also obtained by varying the carrier alloy, these being Si3N4 powder with graphite, with average particle size of 1.5 and 5 μm, respectively. As a metallic Si graphite with average particle size of 12.5 and 5 μm, respectively. The reference material used was nickel carbonyl sintered without adding carriers. Microstructural characterization of the alloys was made by optical microscopy and scanning electron microscopy with semi-quantitative chemical analysis. We determined the densities of the samples and measurement of microhardness. We studied the dissociation of carriers alloy after sintering at 1200 ° C for 60 minutes. Was evaluated also in the same sintering conditions, the influence of the variation of average particle size of the SiC carrier to the proportion of 3% by mass. Finally, we studied the influence of variation of the temperatures of sintering at 950, 1080 and 1200 ° C without landing and also with heights of 30, 60, 120 and 240 minutes for sintering where the temperature was 950 °C. Dilatometry curves showed that the SiC sintered Ni favors more effectively than other carriers alloy analyzed. SiC with average particle size of 15 μm active sintering the alloy more effectively than other SiC used. However, with the chemical and morphological analyzes for all leagues, it was observed that there was dissociation of SiC and Si3N4, as well as diffusion of Si in Ni matrix and carbon cluster and dispersed in the matrix, which also occurred for the alloys with Si carriers and metallic graphite. So the league that was presented better results containing Si Ni with graphite metallic alloy as carriers, since this had dispersed graphite best in the league, reaching the microstructural model proposed, which is necessary for material characteristic of solid lubricant, so how we got the best results when the density and hardness of the alloy

Comportamento da adição do carbeto de nióbio (nBC) na matriz metálica do aço ferrítico 15kH2mfa

The 15Kh2MFA steel is a kind of Cr-Mo-V family steels and can be used in turbines for energy generation, pressure vessels, nuclear reactors or applications where the range of temperature that the material works is between 250 to 450°C. To improve the properties of these steels increasing the service temperature and the thermal stability is add a second particle phase. These particles can be oxides, carbides, nitrites or even solid solution of some chemical elements. On this way, this work aim to study the effect of addition of 3wt% of niobium carbide in the metallic matrix of 15Kh2MFA steel. Powder metallurgy was the route employed to produce this metallic matrix composite. Two different milling conditions were performed. Condition 1: milling of pure 15Kh2MFA steel and condition 2: milling of 15Kh2MFA steel with addition of niobium carbide. A high energy milling was carried out during 5 hours. Then, these two powders were sintered in a vacuum furnace (10-4torr) at 1150 and 1250°C during 60 minutes. After sintering the samples were normalized at 950°C per 3 minutes followed by air cooling to obtain a desired microstructure. Results show that the addition of niobium carbide helps to mill faster the particles during the milling when compared with that steel without carbide. At the sintering, the niobium carbide helps to sinter increasing the density of the samples reaching a maximum density of 7.86g/cm³, better than the melted steel as received that was 7,81g/cm³. In spite this good densification, after normalizing, the niobium carbide don t contributed to increase the microhardness. The best microhardness obtained to the steel with niobium carbide was 156HV and to pure 15Kh2MFA steel was 212HV. It happened due when the niobium carbide is added to the steel a pearlitic structure was formed, and the steel without niobium carbide submitted to the same conditions reached a bainitic structure

Desenvolvimento e caracterização de um compósito matriz metálica (CMM): aço EUROFER97 reforçado com Carbeto de Tântalo - TaC

Steel is an alloy EUROFER promising for use in nuclear reactors, or in applications where the material is subjected to temperatures up to 550 ° C due to their lower creep resistance under. One way to increase this property, so that the steel work at higher temperatures it is necessary to prevent sliding of its grain boundaries. Factors that influence this slip contours are the morphology of the grains, the angle and speed of the grain boundaries. This speed can be decreased in the presence of a dispersed phase in the material, provided it is fine and homogeneously distributed. In this context, this paper presents the development of a new material metal matrix composite (MMC) which has as starting materials as stainless steel EUROFER 97, and two different kinds of tantalum carbide - TaC, one with average crystallite sizes 13.78 nm synthesized in UFRN and another with 40.66 nm supplied by Aldrich. In order to improve the mechanical properties of metal matrix was added by powder metallurgy, nano-sized particles of the two types of TaC. This paper discusses the effect of dispersion of carbides in the microstructure of sintered parts. Pure steel powders with the addition of 3% TaC UFRN and 3% TaC commercial respectively, were ground in grinding times following: a) 5 hours in the planetary mill for all post b) 8 hours of grinding in the mill Planetary only for steel TaC powders of commercial and c) 24 hours in the conventional ball mill mixing the pure steel milled for 5 hours in the planetary mill with 3% TaC commercial. Each of the resulting particulate samples were cold compacted under a uniaxial pressure of 600MPa, on a cylindrical matrix of 5 mm diameter. Subsequently, the compressed were sintered in a vacuum furnace at temperatures of 1150 to 1250 ° C with an increment of 20 ° C and 10 ° C per minute and maintained at these isotherms for 30, 60 and 120 minutes and cooled to room temperature. The distribution, size and dispersion of steel and composite particles were determined by x-ray diffraction, scanning electron microscopy followed by chemical analysis (EDS). The structures of the sintered bodies were observed by optical microscopy and scanning electron accompanied by EDS beyond the x-ray diffraction. Initial studies sintering the obtained steel EUROFER 97 a positive reply in relation to improvement of the mechanical properties independent of the processing, because it is obtained with sintered microhardness values close to and even greater than 100% of the value obtained for the HV 333.2 pure steel as received in the form of a bar

Compósitos de matriz metálica à base níquel com adição de TaC e NbC produzidos via metalurgia do pó

Carbide reinforced metallic alloys potentially improve some important mechanical properties required for the overall use of important engineering materials such as steel and nickel. Nevertheless, improved performance is achieved not only by composition enhancement but also by adequate processing techniques, such as novel sintering methods in the case of powder metallurgy. The method minimizes energy losses in addition to providing uniform heating during sintering. Thus, the general objective of this study was to evaluate the density, hardness, flexural strength, dilatometric behavior and to analyze the microstructure of metal matrix composites based nickel with addition of carbides of tantalum and / or niobium when sintered in a conventional furnace and Plasma assisted debinding and sintering (PADS). Initially, were defineds best parameters of granulation, screening and mixing procedure. After, mixtures of carbonyl Ni and 5%, 10% and 15 wt.% NbC and TaC were prepared in a Y-type mixer under wet conditions during 60 minutes. The mixtures were then dried and granulated using 1.5 wt. % paraffin diluted in hexane. Granulates were cold pressed under 600 MPa. Paraffin was then removed from the pressed pellets during a pre-sintering process carried out in a tubular furnace at 500 °C during 30 min. The heating rate was 3 ºC/min. The pellets were then sintered using either a plasma assisted reactor or a conventional resistive tubular furnace. For both methods, the heating rate was set to 8 ºC/min up to 1150 °C. The holding time was 60 minutes. The microstructure of the sintered samples was evaluated by SEM. Brinell hardness tests were also carried out. The results revealed that higher density and higher hardness values were observed in the plasma-assisted sintered samples. Hardness increased with the concentration of carbides in the Ni-matrix. The flexural strength also increased by adding the carbides. The decline was larger for the sample with addition of 5% 5% TaC and NbC. In general, compositions containing added carbide 10% showed less porous and more uniform distribution of carbides in the nickel matrix microstructural appearance. Thus, both added carbide and plasma sintering improved density, hardness, flexural strength and microstructural appearance of the composites

Obtenção de cerâmicas à base de tricálcio fosfatos utilizando óxido de manganês como aditivo

The calcium phosphate ceramics have been very investigated as material for bone implants. The tricalcium phosphate (β-TCP) had a great potential for application in temporary implants like a resorbable bioceramic. This material presents a limitation in its sintering temperature due to occurrence of the allotropic transformation β → α at temperatures around 1200°C, not allowing the attainment of dense ceramic bodies. This transformation also causes cracks, what diminishes the mechanical strength, limiting its use to applications of low mechanical requests. This work studies the influence of the addition of manganese oxide in the sintering of β-TCP. Two processing routes were investigated. The first was the powder metallurgy conventional process. The test bodies (samples) were pressed and sintering at temperatures of 1200 and 1250°C. The second route was uniaxial hot pressing and its objective was to obtain samples with high relative density. The samples were physically characterized through density and porosity measurements. The thermal behavior was studied through dilatometric, thermal differential and thermogravimetric analysis. The mechanical properties were characterized by three point flexure test and Vickers microhardness measurements. The microstructure was analyzed by scanning electron microscopy. The addition of manganese oxide caused an improvement of the mechanical strength in relation to the material without additive and promoting the stabilization of β-TCP to greater temperatures

Three-Dimensional Characterization of Pores in Ti-6Al-4V Alloy

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Novel production method of porous surface Ti samples for biomedical application

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)