Relationship between wearer prickle response with fibre and garment properties and Wool ComfortMeter assessment

The prickle evoked by 48 knitted fabrics was assessed by wearers under a defined evaluation protocol. The relationship between the average wearer prickle score and known properties of constituent fibre, yarns and fabrics and fabric evaluation using the Wool ComfortMeter (WCM) was determined using linear modelling. After log transformation, the best model accounted for 87.7% of the variance. The major share of variation could be attributed to differences between mean fibre diameter (MFD) and WCM values. Low prickle scores were linearly associated with lower MFD, lower WCM and lower yarn linear density. There was an indication that yarn twist affected prickle scores and that fabrics composed of cotton evoked less prickle. Measures of fibre diameter distribution or coarse fibre incidence and other fabric properties were not significant. The analysis indicates that wool garments can be constructed to keep wearer assessed prickle to barely detectable levels and textile designers can manipulate a range of parameters to achieve similar wearer comfort responses.

A simple and effective method to ameliorate the interfacial properties of cellulosic fibre based bio-composites using poly (ethylene glycol) based amphiphiles

In order to overcome interfacial incompatibility issues in natural fibre reinforced polymer bio-composites, surface modifications of the natural fibres using complex and environmentally unfriendly chemical methods is necessary. In this paper, we demonstrate that the interfacial properties of cellulose-based bio-composites can be tailored through surface adsorption of polyethylene glycol (PEG) based amphiphilic block copolymers using a greener alternative methodology. Mixtures of water or water/acetone were used to form amphiphilic emulsions or micro-crystal suspensions of PEG based amphiphilic block copolymers, and their deposition from solution onto the cellulosic substrate was carried out by simple dip-coating. The findings of this study evidence that, by tuning the amphiphilicity and the type of building blocks attached to the PEG unit, the flexural and dynamic thermo-mechanical properties of cellulose-based bio-composites comprised of either polylactide (PLA) or high density polyethylene (HDPE) as a matrix, can be remarkably enhanced. The trends, largely driven by interfacial effects, can be ascribed to the combined action of the hydrophilic and hydrophobic components of these amphiphiles. The nature of the interactions formed across the fibre-matrix interface is discussed. The collective outcome from this study provides a technological template to significantly improve the performance of cellulose-based bio-composite materials.

Exposure to As(III) and As(V) changes the Ca²⁺-activation properties of the two major fibre types from the chelae of the freshwater crustacean Cherax destructor

Arsenic is a known carcinogen found in the soil in gold mining regions at concentrations thousands of times greater than gold. Mining releases arsenic into the environment and surrounding water bodies. The main chemical forms of arsenic found in the environment are inorganic arsenite (As(III)) and arsenate (As(V)). Yabbies (Cherax destructor) accumulate arsenic at levels comparable to those in the sediment of their environment but the effect on their physiological function is not known. The effects of arsenic exposure (10 ppm sodium arsenite, AsNaO2 - 5.7 ppm As(III)) and 10 ppm arsenic acid, Na2HAsO4·7H2O - 2.6 ppm As(V)) for 40 days on the contractile function of the two major fibre types from the chelae were determined. After exposure, individual fibres were isolated from the chela, "skinned" (membrane removed) and attached to the force recording apparatus. Contraction was induced in solutions containing increasing [Ca(2+)] until a maximum Ca(2+)-activation was obtained. Submaximal force responses were plotted as a percentage of the maximum Ca(2+)-activated force. As(V) exposure resulted in lower levels of calcium required for activation than As(III) indicating an increased sensitivity to Ca(2+) after long term exposure to arsenate compared to arsenite. Myosin heavy chain and tropomyosin content in individual fibres was also decreased as a result of arsenic exposure. Single fibres exposed to As(V) produced significantly more force than muscle fibres from control animals. Long-term exposure of yabbies to arsenic alters the contractile function of the two major fibre types in the chelae.

Fabric handle properties of superfine wool fabrics with different fibre curvature, cashmere content and knitting tightness

The handle properties of single jersey fabrics composed of superfine wools (17 μm) of different fibre curvature (114 vs. 74 °/mm) in blends with cashmere (fibre curvature 49 °/mm) were investigated. There were four blend ratios of cashmere (0, 25, 50, 75%) plus 100% cashmere. Each of the nine fibre blend combinations were replicated three times, and each was knitted into three tightness factors. The 81 fabrics were evaluated using the Wool HandleMeter, which measures seven primary handle attributes and Overall handle, and have been calibrated using a panel of experts and a wide variety of commercial fabrics. Results were analysed by ANOVA and general linear modelling. Tightness factor significantly affected all Wool HandleMeter attribute values, with the effect of tightness factor varying according to handle attribute. The Wool HandleMeter was able to detect differences between fabrics composed of superfine wool differing in fibre curvature, with lower fibre curvature wool fabrics having more preferred Overall handle and softer, looser, cooler, lighter and less dry handle attributes at some or all tightness factors compared with fabrics composed of higher fibre curvature superfine wool. Progressively blending cashmere with wool significantly improved Overall handle, increased soft and smooth handle, reduced dry, heavy and tight handle. Linear regression modelling indicated that fabric mass per unit area explained more than 50% of the variance in overall fabric handle and in combination with variations in fabric thickness and yarn elongation could explain 71% of the variance in Overall handle.

Weathering, fibre strength and colour properties of processed white cashmere

Weathering refers to the degradation of wool fibres that occur during growth from exposure of the fleece to sunlight, water and air. Weathering damage to Merino wool reduces quantities of fibre that are harvested, reduces length in both raw and processed wools, reduces spinning performance and dyeing outcomes. This work aimed to aimed to quantify if and to what extent weathering occurred in 38 lots of commercial dehaired white cashmere and cashmere top sourced from traditional and new origins of production and the extent of any association between weathering and tensile strength properties of the dehaired cashmere and cashmere top. The cashmere was tested for physical properties, bundle tenacity and extension, tristimulus values brightness (Y) and yellowness (Y-Z) and reflectance. Dye uptake was used as an index of weathering. Linear models, relating to weathering, bundle tenacity and Y-Z were fitted to origin and other objective measurements. Mean attributes (range) were: mean fibre diameter, 17.0 μm (13.5–21.3 μm); bundle tenacity of tops, 10.3 cN/tex (8.3–12.9 cN/tex), for dehaired fibre, 10.1 cN/tex (9.1–11.4 cN/tex). Stain uptake varied from 0.92 to 6.34 mg/g fibre indicating a six-fold variation in the extent of weathering. Both the extent of weathering and the bundle tenacity of commercial lots of cashmere were affected by the origin of the cashmere. Increased weathering reduced bundle tenacity, bundle extension, increased the yellowness and reduced reflectance of white cashmere. Bundle tenacity of cashmere declined as fibre diameter variability increased from 20 to 22.5%. For the samples tested, the cashmere from China, Mongolia, Afghanistan and Iran showed more weathering than cashmere from Australia, New Zealand and the USA. The differences in the extent of weathering and of bundle tenacity between cashmere from different origins were of commercial significance.

Refractive index sensing properties of long-period fibre grating with sol-gel derived coatings

Long-period fibre gratings (LPGs) have previously been used to detect quantities such as temperature, strain and refractive index (RI). The responsivity to surrounding refractive index means that, potentially, LPGs could be realised as optical biosensors for applications in biochemical and biomedical application areas. We report here to our best knowledge the first investigation on refractive index sensing properties of LPGs with sol-gel derived titanium and silicon oxide coatings. It is revealed that the RI sensitivity of an LPG is affected by both the thickness and the index value of the coating; the coating with higher index and thickness will enhance the LPG RI sensitivity significantly. The surrounding refractive index induced LPG resonance shift has been evaluated over the LPGs’ most sensitive RI region from 1.42 to 1.44. We have identified that, in this region, the uncoated LPG has an RI sensitivity of (-673.0±0.4)nm/uri (unit of refractive index) while the LPG coated with titanium oxide exhibits a sensitivity as high as (-1067.15±0.04)nm/uri.

Thermal properties of fibre Bragg gratings inscribed point-by-point by infrared femtosecond laser

Direct, point-by-point inscription of fibre Bragg gratings by an infrared femtosecond laser has been reported recently. Response of these gratings to annealing at temperatures in the range 500 to 1050°C is studied for the first time. Gratings inscribed by infrared femtosecond lasers were thermally stable at temperatures up to 900°C, representing a significant improvement in comparison with the 'common', UV-inscribed, gratings. Annealing at temperatures up to 700°C increased grating reflectivity. © IEE 2005.

Effects of fibre reinforcement on the mechanical properties of brushite cement

In this study the effect of structure and amount of polyglactin fibre incorporation into a brushite forming calcium phosphate cement system and the effect of mechanical compaction on the fibre modified system were investigated. In comparison the effect of resorbable polycaprolactone surface coating of cement specimens was investigated. The results showed that, apart from the mechanical properties of the reinforcing material, the structure of the incorporated fibres, regular or random, is crucial for the resulting flexural strength and modulus of elasticity. Fibre reinforcement could also be combined with mechanical compaction of the cement/fibre composite paste leading to a possible 7-fold increase in flexural strength or an almost 5-fold increase in modulus of elasticity. Reinforcement of the tensile surface of cement grafts may ultimately improve strength where required, especially in conjunction with bone fixation devices. © 2005 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Refractive index sensing properties of long-period fibre grating with sol-gel derived coatings

Long-period fibre gratings (LPGs) have previously been used to detect quantities such as temperature, strain and refractive index (RI). The responsivity to surrounding refractive index means that, potentially, LPGs could be realised as optical biosensors for applications in biochemical and biomedical application areas. We report here to our best knowledge the first investigation on refractive index sensing properties of LPGs with sol-gel derived titanium and silicon oxide coatings. It is revealed that the RI sensitivity of an LPG is affected by both the thickness and the index value of the coating; the coating with higher index and thickness will enhance the LPG RI sensitivity significantly. The surrounding refractive index induced LPG resonance shift has been evaluated over the LPGs’ most sensitive RI region from 1.42 to 1.44. We have identified that, in this region, the uncoated LPG has an RI sensitivity of (-673.0±0.4)nm/uri (unit of refractive index) while the LPG coated with titanium oxide exhibits a sensitivity as high as (-1067.15±0.04)nm/uri.

Revealing statistical properties of quasi-CW fibre lasers in bandwidth-limited measurements

We introduce a general technique how to reveal in experiments of limited electrical bandwidth which is lower than the optical bandwidth of the optical signal under study, whether the statistical properties of the light source obey Gaussian distribution or mode correlations do exist. To do that one needs to perform measurements by decreasing the measurement bandwidth. We develop a simple model of bandwidth-limited measurements and predict universal laws how intensity probability density function and intensity auto-correlation function of ideal completely stochastic source of Gaussian statistics depend on limited measurement bandwidth and measurement noise level. Results of experimental investigation are in good agreement with model predictions. In particular, we reveal partial mode correlations in the radiation of quasi-CW Raman fibre laser.