Catalytic activities and coking characteristics of oxides-supported Ni catalysts for CH4 reforming with carbon dioxide

Catalytic activities and deactivation characteristics of oxides-supported nickel catalysts for the reaction of methane reforming with carbon dioxide were investigated. The dynamic carbon deposition on various nickel catalysts was also studied by a thermogravimetric method. Among the catalysts prepared, Ni/La2O3, Ni/alpha-Al2O3, Ni/SiO2, and Ni/CeO2 showed very high CH4 and CO2 conversions and moderate deactivation whereas Ni/MgO and Ni/TiO2 had lower conversions when the Ni reduction was conducted at 500 degrees C. When Ni/MgO catalyst was reduced at 800 degrees C, it exhibited not only comparable conversions of CH4 and CO2 with other active catalysts but also much longer period of stability without deactivation. The amount of carbon deposited in Ni-based catalysts varied depending on the nature of support and followed the order of Ni/La2O3 > Ni/alpha-Al2O3 > Ni/SiO2 > Ni/MgO > Ni/CeO2 at 700 degrees C. The carbons formed on the catalyst surface showed different structural and chemical properties, and these in turn affected the catalytic activity of the catalysts.

Reforming of methane with carbon dioxide over Ni/Al2O3 catalysts: Effect of nickel precursor

The catalytic activities of Ni/gamma-Al2O3 catalysts prepared using different nickel precursor compounds were studied for the reaction of methane reforming with CO2. It is found that the nickel precursor employed in the catalyst preparation plays an important role. The catalyst based on nickel nitrate exhibited higher catalytic activity and stability over a 24-h test period than the other two catalysts derived from nickel chloride and nickel acetylacetonate. A comprehensive characterisation of the catalysts showed that the weak interaction between Ni particles and gamma-Al2O3 resulted in more active sites on Ni nitrate-derived Ni/gamma-Al2O3 catalyst. Coking studies showed that carbon deposition on Ni catalysts derived from inorganic precursors (nitrate and chloride) were more severe than on the organic precursor-derived catalyst. However, the Ni nitrate-derived catalyst was found to have the highest stability (or lowest deactivation rate) mainly due to the active carbon species (-C-C-) of the resulting graphitic structure and their close contact with the metal particles. In contrast, the carbon formed on Ni-AA catalyst (from Ni acetylacetonate) is dominated by inactive -CO-C- species, thus leading to a rapid accumulation of carbon in this catalyst and more severe deactivation. (C) 1998 Elsevier Science B.V.

Thermogravimetric analysis of carbon deposition over Ni/gamma-Al2O3 catalysts in carbon dioxide reforming of methane

Carbon formation on Ni/gamma-Al2O3 catalysts and its kinetics during methane reforming with carbon dioxide was studied in the temperature range of 500-700 degrees C using a thermogravimetric analysis technique. The activation energies of methane cracking, carbon gasification in CO2, as well as carbon deposition in CO2-CH4 reforming were obtained. The results show that the activation energy for carbon gasification is larger than that of carbon formation in methane cracking and that the activation energy of coking in CO2-CH4 reforming is also larger than that of methane decomposition to carbon. The dependencies of coking rate on partial pressures of CH4 and CO2 indicate that methane decomposition is the main route for carbon deposition. A mechanism and kinetic model for carbon deposition is proposed.

Role of CeO2 in Ni/CeO2-Al2O3 catalysts for carbon dioxide reforming of methane

Ni catalysts supported on gamma-Al2O3, CeO2 and CeO2-A1(2)O(3) systems were tested for catalytic CO2 reforming of methane into synthesis gas. Ni/CeO2-Al2O3 catalysts showed much better catalytic performance than either CeO2- or gamma-Al2O3-supported Ni catalysts. CeO2 as a support for Ni catalysts produced a strong metal-support interaction (SMSI), which reduced the catalytic activity and carbon deposition. However, CeO2 had positive effect on catalytic activity, stability, and carbon suppression when used as a promoter in Ni/gamma-Al2O3 catalysts for this reaction. A weight loading of 1-5 wt% CeO2 was found to be the optimum. Ni catalysts with CeO2 promoters reduced the chemical interaction between nickel and support, resulting in an increase in reducibility and stronger dispersion of nickel. The stability and less coking on CeO2-promoted catalysts are attributed to the oxidative properties of CeO2. (C) 1998 Elsevier Science B.V. All rights reserved.

Flyash as support for Ni catalysts in carbon dioxide reforming of methane

A series of Ni catalysts supported on flyash treated by various chemical methods was tested for carbon dioxide reforming of methane. Ni catalyst on the flyash treated with CaO (Ni/Ash-CaO) shows high conversion and stability, being close to those of the well-reported Ni/Al2O3 and Ni/SiO2 catalysts with conversions approaching thermodynamic equilibrium levels.

A comprehensive study on carbon dioxide reforming of methane over Ni/gamma-Al2O3 catalysts

Carbon dioxide reforming of methane into syngas over Ni/gamma-Al2O3 catalysts was systematically studied. Effects of reaction parameters on catalytic activity and carbon deposition over Ni/gamma-Al2O3 catalysts were investigated. It is found that reduced NiA1204, metal nickel, and active species of carbon deposited were the active sites for this reaction. Carbon deposition on Ni/gamma Al2O3 varied depending on the nickel loading and reaction temperature and is the major cause of catalyst deactivation. Higher nickel loading produced more coke on the catalysts, resulting in rapid deactivation and plugging of the reactor. At 5 wt % Ni/gamma-Al2O3 catalyst exhibited high activity and much lesser magnitude of deactivation in 140 h. Characterization of carbon deposits on the catalyst surface revealed that there are two kinds of carbon species (oxidized and -C-C-) formed during the reaction and they showed different reactivities toward hydrogenation and oxidation. Kinetic studies showed that the activation energy for CO production in this reaction amounted to 80 kJ/mol and the rate of CO production could be described by a Langmuir-Hinshelwood model.

Protective effect of carbon dioxide against bacterial peritonitis induced in rats

Carbon dioxide (CO(2)) has been used in the food industry as an antimicrobial agent. This study aimed to investigate whether CO(2) pneumoperitoneum might act similarly as an antimicrobial agent in the infected peritoneal cavity. Peritonitis was induced in 58 rats by intraabdominal injection of an Escherichia coli inoculum (6 x 105 colony-forming units [CFU]/ml). Control rats were injected with saline solution. The rats were randomly divided into four groups: rat control (RC, n = 15), bacterial inoculation control (BIC, n = 10), bacterial inoculation and laparotomy (BIL, n = 17), and bacterial inoculation and CO(2) pneumoperitoneum (BIP, n = 16). The survival rates and histopathologic changes in the abdominal wall muscles, spleen, liver, intestines, and omentum were evaluated, and the samples were classified as ""preserved"" or ""inflamed"" (acute inflammation or tissue regeneration). The survival rates for the four groups were as follows: RC (100%), BIP (75%), BIL (53%), and BIC (30%). With regard to survival rates, statistically significant differences were observed between the following groups: RC and BIC (p = 0.0009), RC and BIL (p = 0.0045), BIP and BIC (p = 0.0332), and RC and BIP (p = 0.0470). No significant differences regarding survival rates were observed between the BIL and BIC groups or between the BIP and BIL groups. With regard to the number of inflamed samples per group, a statistically significant difference was observed between the BIC and RC groups and the BIL and RC groups (p = 0.05). Carbon dioxide pneumoperitoneum has a protective effect against bacterial peritonitis induced in rats.

A study of actinic cheilitis treatment by two low-morbidity CO(2) laser vaporization one-pass protocols

Therapeutic approaches to chronic actinic cheilitis focus on the removal or destruction of diseased epithelium. The CO(2) laser has become an important therapeutic alternative, achieving clinical resolution in around 90% of patients. Although many laser physical parameters have been reported, some are known for their low potential for scar induction without compromising the success of the results. The aim of this clinicohistological study was to compare the therapeutic responses to two low-morbidity protocols involving a single laser pass. A total of 40 patients with chronic multicentric and microscopically proven disease were randomly submitted to two conservative CO(2) laser protocols using a bilateral comparative model. The degree of histological atypia of the epithelium was determined in 26 patients both pre- and postoperatively for both protocols. Other histological phenomena were assessed in addition to this central analysis parameter. Clinical recurrence occurred in 12.5% of patients for each protocol, together with a significant reduction in the degree of epithelial atypia (p < 0.001), which was occasionally complete. However, no difference was found between the protocols (p > 0.05). Using these morphological parameters it was not possible to determine whether postoperative epithelial atypias in part of the sample were reactive or residual in nature. A few patients may show minor postoperative lesions. Due to their potential to achieve clinical and importantly microscopic resolution, the studied protocols may be used for mild through moderate dysplastic epithelium and clinically diffuse disease.

INFLUENCE OF LASER RADIATION IN NERVE REGENERATION IN DIFFERENT TREATMENT SITES

Objective: This study seeks to determine, through functional gait assessment in different irradiation sites, the influence of a low-intensity GaAsAl laser beam on an injury caused by crushing the peroneal nerve in rats. Methods: 53 rats were used, which were divided into six groups: normal, injured and untreated, injured and treated using placebo, injured and treated in the bone marrow, injured and treated in the nerve, and injured and treated in both (nerve and bone marrow). The peroneal nerve was crushed using a pair of tweezers, and subsequently treated with laser for 28 consecutive days. The functional gait evaluation analyzed the footprints, which were recorded with a video camera on an acrylic bridge in the preoperative period, and on postoperative days 14, 21 and 28, and assessed using PFI formula software. Results: In the functional gait evaluation, significant differences were found only on postoperative day 14. Conclusion: Based on the functional gait evaluation, low-intensity GaAs AI irradiation was able to accelerate and reinforce the process of peripheral nerve regeneration in rats on postoperative day 14, both in the bone marrow- and in the nerve-treated groups.

Magnetic resonance imaging quantification of regional cerebral blood flow and cerebrovascular reactivity to carbon dioxide in normotensive and hypertensive rats

Hypertension afflicts 25% of the general population and over 50% of the elderly. In the present work, arterial spin labeling MRI was used to non-invasively quantify regional cerebral blood flow (CBE), cerebrovascular resistance and CO(2) reactivity in spontaneously hypertensive rats (SHR) and in normotensive Wistar Kyoto rats (WKY), at two different ages (3 months and 10 months) and under the effects of two anesthetics, alpha-chloralose and 2% isoflurane (1.5 MAC). Repeated CBE measurements were highly consistent, differing by less than 10% and 18% within and across animals, respectively. Under alpha-chloralose, whole brain CBE at normocapnia did not differ between groups (young WKY: 61 3 ml/100 g/min; adult WKY: 62 +/- 4 ml/100 g/min; young SHR: 70 +/- 9 ml/100 g/min: adult SHR: 69 8 ml/100 g/min), indicating normal cerebral autoregulation in SHR. At hypercapnia, CBE values increased significantly, and a linear relationship between CBE and PaCO(2) levels was observed. In contrast, 2% isoflurane impaired cerebral autoregulation. Whole brain CBE in SHR was significantly higher than in WKY rats at normocapnia (young SHR: 139 +/- 25 ml/100 g/min; adult SHR: 104 +/- 23 ml/100 g/min; young WKY: 55 +/- 9 ml/100 g/min; adult WKY: 71 +/- 19 ml/100 g/min). CBE values increased significantly with increasing CO(2): however, there was a clear saturation of CBF at PaCO(2) levels greater than 70 mm Hg in both young and adult rats, regardless of absolute CBE values, suggesting that isoflurane interferes with the vasoclilatory mechanisms of CO(2). This behavior was observed for both cortical and subcortical structures. Under either anesthetic, CO(2) reactivity values in adult SHR were decreased, confirming that hypertension, when combined with age, increases cerebrovascular resistance and reduces cerebrovascular compliance. Published by Elsevier Inc.

Dentine caries inhibition through CO(2) laser (10.6 mu m) irradiation and fluoride application, in vitro

Objective: The purpose of the study was to investigate whether dentine irradiation with a pulsed CO(2) laser (10.6 mu m) emitting pulses of 10 ms is capable of reducing dentine calcium and phosphorus losses in an artificial caries model. Design: The 90 dentine slabs obtained from bovine teeth were randomly divided into six groups (n = 15): negative control group (GC); positive control group, treated with fluoride 1.23% (GF); and laser groups irradiated with 8 J/cm(2) (L8); irradiated as in L8 + fluoride 1.23% (L8F); irradiated with 11j/cm(2) (L11); irradiated as in L11 + fluoride 1.23% (L11F). After laser irradiation the samples were submitted to a pH-cycling model for 9 days. The calcium and phosphorous contents in the de- and remineralization solutions were measured by means of inductively coupled plasma optical emission spectrometer - ICP-OES. Additionally intra-pulpal temperature measurements were performed. The obtained data were analysed by means of ANOVA and Tukey`s test (alpha = 0.05). Results: In the demineralization solutions the groups L11F and GF presented significantly lower means of calcium and phosphorous losses than the control group; and in L11F means were significantly lower than in the fluoride group. Both irradiation parameters tested caused intrapulpal temperature increase below 2 degrees C. Conclusion: It can be concluded that under the conditions of this study, CO(2) laser irradiation (10.6 mu m) with 11J/cm(2) (540 mJ and 10 Hz) of fluoride treated dentine surfaces decreases the loss of calcium and phosphorous in the demineralization process and does not cause excessive temperature increase inside the pulp chamber. (C) 2010 Elsevier Ltd. All rights reserved.

CO(2) Laser (10.6 mu m) Parameters for Caries Prevention in Dental Enamel

Although CO(2) laser irradiation can decrease enamel demineralisation, it has still not been clarified which laser wavelength and which irradiation conditions represent the optimum parameters for application as preventive treatment. The aim of the present explorative study was to find low-fluence CO(2) laser (lambda = 10.6 mu m) parameters resulting in a maximum caries-preventive effect with the least thermal damage. Different laser parameters were systematically evaluated in 3 steps. In the first experiment, 5 fluences of 0.1, 0.3, 0.4, 0.5 and 0.6 J/cm(2), combined with high repetition rates and 10 mu s pulse duration, were chosen for the experiments. In a second experiment, the influence of different pulse durations (5, 10, 20, 30 and 50 mu s) on the demineralisation of dental enamel was assessed. Finally, 3 different irradiation times (2, 5 and 9 s) were tested in a third experiment. In total, 276 bovine enamel blocks were used for the experiments. An 8-day pH-cycling regime was performed after the laser treatment. Demineralisation was assessed by lesion depth measurements with a polarised light microscope, and morphological changes were assessed with a scanning electron microscope. Irradiation with 0.3 J/cm(2), 5 mu s, 226 Hz for 9 s (2,036 overlapping pulses) increased caries resistance by up to 81% compared to the control and was even significantly better than fluoride application (25%, p < 0.0001). Scanning electron microscopy examination did not reveal any obvious damage caused by the laser irradiation. Copyright (C) 2009 S. Karger AG, Basel

Ultrastructural Analysis of Radicular Dentine Surface Submitted to CO(2) Laser at Different Parameters

Background: There are no reported studies comparing different parameter settings of the CO(2) laser and irradiation direction considering their effect on the morphology of radicular dentine surface. Purpose: To evaluate the alterations of radicular dentine (cervical, middle, and apical thirds) irradiated with CO(2) laser at different potencies and irradiation directions. Study Design: Roots of 35 canines were prepared and randomly distributed according to the laser potency: GI: no laser treatment (control) (n = 5); GII, 2 W (n = 10); GIII: 4 W (n = 10); GIV: 6 W (n = 10). Each group (excepting GI) was divided in two subgroups according to the irradiation distance (n = 5): (A) parallel and (B) perpendicular to the root canal walls. The roots were splited longitudinally and analyzed by scanning electron microscopy in a qualiquatitative way. The scores were submitted to Kruskal-Wallis and Dunn`s tests. Results: No significant statistical differences were observed among root canal thirds (P > 0.05). The specimens irradiated with 2 W were statistically different (P < 0.05) from those irradiated with 4 and 6 W, which were statistically similar between themselves (P > 0.05). With 2, 4, and 6 W at in parallel irradiation and 2 W in perpendicular direction, the surface showed a fissured aspect. With 4 W in perpendicular direction and 6 W in parallel and perpendicular direction, surface was modified by laser action and exhibited fused areas. Conclusions: The intensity of the effects is dependent on the laser-irradiation dosimetries. Alterations were more intense when higher parameters were used. Microsc. Res. Tech. 72:737-743, 2009. (C) 2009 Wiley-Liss, Inc.