MECHANISMS OF ABRASIVE WEAR IN A BORONIZED ALLOY STEEL.

This paper describes the effects of abrasive hardness and size on the 2-body abrasive wear mechanisms of a boronized low alloy steel. It is found that the wear resistance of the boronized steel is much greater against alumina abrasive than against silicon carbide. This difference in wear resistance is much enhanced when the particle size or the applied load is increased. Scanning electron microscopy of the worn specimens and of the used abrasive papers revealed that the enhanced difference in wear resistance between coarse alumina and silicon carbide papers is due to a change in the wear mechanism produced by silicon carbide papers with increasing abrasive particle size.

Mechanisms of erosion of unfilled elastomers by solid particle impact

The mechanisms of material removal were studied during the erosion of two unfilled elastomers (natural rubber and epoxidised natural rubber). The effects of impact velocity and of lubrication by silicone oil were investigated. The development of surface features due to single impacts and during the early stages of erosion was followed by scanning electron microscopy. The basic material removal mechanism at impact angles of both 30° and 90° involves the formation and growth of fine fatigue cracks under the tensile surface stresses caused by impact. No damage was observed after single impacts; it was found that many successive impacts are necessary for material removal. It was found that the erosion rate has a very strong dependance on impact velocity above about 50 ms-1.

Solid particle erosion of boronized steels

Boronizing is a thermochemical diffusion-based process for producing iron boride layers in the surface of steel components. The boride layer is wear resistant and is very hard. Large residual stresses are found to exist in the surface layers, which are a function of substrate steel composition and heat treatment. By slow cooling from the boronizing temperature (900°C), a large compressive stress is developed in the boride layer. Hardening the steel by rapid cooling, either directly from the boronizing treatment or after subsequent austenitizing, develops tension in the coating which causes it to fracture. Tempering of the martensite produces compression in the coating, closing but not welding the cracks. The results of solid particle erosion experiments using silicon carbide, quartz, and glass bead erodents on boronized steels are presented.

Transitions in the erosive wear behavior of a glass-ceramic

The mechanisms of material removal were investigated during the erosive wear of a glass-ceramic. The effects of erodent particle shape, velocity and angle were studied. Single impacts and incremental erosion tests were performed, to study the development of surface features and to elucidate the mechanisms of material removal. It was found that transitions in mechanism occurred which depended on the particle shape, impact velocity and impact angle. The mechanisms of material removal, for erosion by silica sand, changed from fine scale fracture and plastic processes below a transition point to large-scale cracking of the surface above. Spherical glass beads caused wear dominated by fatigue, with a very strong dependence of wear rate on the impact conditions. This work indicates that laboratory erosion testing of glass-ceramic and other brittle materials should reflect the conditions present in practice, and that account must be taken of possible changes in wear mechanisms.