Room temperature ferromagnetism and white light emissive CdS:Cr nanoparticles synthesized by chemical co-precipitation method

Undoped and Cr (3% and 5%) doped CdS nanoparticles were synthesized by chemical co-precipitation method. The synthesized nanocrystalline particles are characterized by energy dispersive X-ray analysis (EDAX), scanning electron microscope (SEM), X-ray Diffraction (XRD), transmission electron microscopy (TEM), diffuse reflectance spectroscopy (DRS), photoluminescence (PL), Electron paramagnetic resonance (EPR), vibrating sample magnetometer (VSM) and Raman spectroscopy. XRD studies indicate that Cr doping in host CdS result a structural change from Cubic phase to mixed (cubic + hexagonal) phase. Due to quantum confinement effect, widening of the band gap is observed for undoped and Cr doped CdS nanoparticles compared to bulk CdS. The average particle size calculated from band gap values is in good agreement with the TEM study calculation and it is around 4-5 nm. A strong violet emission band consisting of two emission peaks is observed for undoped CdS nanoparticles, whereas for CdS:Cr nanoparticles, a broad emission band ranging from 420 nm to 730 nm with a maximum at similar to 587 nm is observed. The broad emission band is due to the overlapped emissions from variety of defects. EPR spectra of CdS:Cr samples reveal resonance signal at g = 2.143 corresponding to interacting Cr3+ ions. VSM studies indicate that the diamagnetic CdS nanoparticles are transform to ferromagnetic for 3% Cr3+ doping and the ferromagnetic nature is diminished with increasing the doping concentration to 5%. (C) 2015 Elsevier B.V. All rights reserved.

Magnetic properties of nanocrystalline Mn1-xZnxFe2O4

Nanocrystalline Mn1-xZnxFe2O4 (x = 0, 0.1, 0.3, 0.5, 0.7, 0.9, 1.0) were prepared via solution combustion method. Structural and morphology of Mn-Zn ferrites were characterized by X-ray diffraction (XRD) and Transmission Electron Microscopy (TEM). Magnetic properties were carried out using vibrating sample magnetometer (VSM) at room temperature (RT) up to maximum field of 1.5 T. The room temperature real and imaginary part of permeability(mu' and mu'') has been measured in the frequency range of 1MHz to 1GHz. The room temperature XRD patterns exhibits the spinel cubic (Fm-3m) structure and broad XRD patterns shows the presence of nanoparticles. The imaginary part of the permeability (mu'') gradually increased with the frequency and took a broad maximum at a certain frequency, where the real permeability (mu') rapidly decreases, which is known as natural resonance. The coercive filed values are low, hence probability of domain rotation is also lower and the magnetization decreased with zinc substitution. The values of mu' and mu'' increases sharply, attained a maximum and then decreases with zinc content.

La estructura y propiedades magnéticos de las nanopartículas de Fe50Ni50 obtenidas mediante el método de explosión eléctrica de hilo

[Es]Actualmente ninguna área científica es ajena a la revolución de la nanociencia; las nanopartículas atraen el interés de muchos investigadores desde el punto de vista de la ciencia fundamental y para sus aplicaciones tecnológicas. Las nanopartículas ofrecen la posibilidad de fabricar sensores que sean capaces de detectar desde un virus hasta concentraciones de substancias patógenas que no pueden ser detectadas por los métodos convencionales. Hoy en día existes 82 tratamientos contra el cáncer basadas en la utilización de nanopartículas y los materiales composite con nanopartículas se utilizan como medio de protección frente la radiación del rango de microondas. En la rama de ciencias ambientales, las nanopartículas metálicas sirven como materiales anticontaminantes. En este trabajo se ha estudiado la estructura y las propiedades magnéticas de las nanopartículas de FeNi preparadas mediante el método de explosión eléctrica de hilo. Con la técnica de Rayos–X(DRX) se ha determinado que las nanopartículas se cristalizan en un sistema cúbico FCC con un parámetro de celda de 3.596 Å, también, se ha obtenido el tamaño de dominio coherente que es de 35 nm. La muestra se ha sometido a un programa de temperatura controlada para seguir la evolución de la estructura cristalina y del tamaño del cristal, tanto en atmósfera oxidante como en vacío. Para el aprendizaje de los microscopios utilizados en este trabajo, se ha asistido al curso “Fundamentos de microscopia electrónica de barrido y microanálisis” impartido por SGIker de la UPV/EHU. Se han empleado los microscopios electrónicos SEM y TEM para obtener imágenes de gran resolución de la muestra y analizar su contenido elemental. Partiendo de las imágenes sacadas por el SEM se ha calculado el valor medio del tamaño de las partículas de la muestra, 58 nm. Mediante el Mastersizer 2000 se ha medido el tamaño de las partículas y/o agregados por método de difracción láser, disgregando la muestra todo lo posible hasta conseguir el tamaño medio que se aproxime al de una sola partícula, 100nm. Por último, para la caracterización magnética se ha servido del VSM que mide el momento magnético de una muestra cuando ésta vibra en presencia de un campo magnético estático, consiguiendo una imanación de saturación de 125 emu/g. Hemos fabricado y caracterizado las nanopartículas magnéticas de hierro-níquel y los resultados obtenidos han sido enviados a un congreso especializado de ciencia de materiales (ISMANAM - 2013, Italia).

Preparação e avaliação de hidrogéis nanocompósitos à base de alginato na remoção de Cu (II) e Zn (II) de soluções aquosas

Esta dissertação teve como objetivo, a preparação de hidrogéis à base de alginato contendo argila e material magnético em sua estrutura. Foram analisadas as modificações nas características físico-químicas dos hidrogéis preparados com diferentes reticulantes (CaCl2 e FeCl3) e diferentes concentrações de material magnético (1 e 3 % m/m) e argila (1, 5 e 10 %). Após isso, os hidrogéis foram avaliados quanto à capacidade de remoção de íons Cu2+ e Zn2+ de soluções aquosas. As amostras foram caracterizadas quanto à composição química por espectroscopia na região do infravermelho (FTIR), quanto à morfologia por microscopia óptica e microscopia eletrônica de varredura (SEM) e quanto às propriedades magnéticas por magnetometria de amostra vibrante (VSM). Através da técnica de difratometria de raios-X (XRD), foi possível verificar a natureza do material magnético e a dispersão da argila nos hidrogéis. A estabilidade térmica das amostras foi analisada por análise termogravimétrica (TGA). Os resultados mostraram que tanto a argila como o material magnético ficaram bem dispersos nas amostras. De forma geral, foram preparados hidrogéis com morfologia esférica, sendo que os hidrogéis de alginato de cálcio tenderam a apresentar maior resistência térmica do que os hidrogéis de alginato de ferro. Todas as amostras magnéticas apresentaram comportamento superparamagnético, porém as amostras de alginato de ferro mostraram-se quebradiças após o intumescimento em água. O tempo médio de equilíbrio de intumescimento foi de 240 minutos. Os resultados de cinética de adsorção mostraram que os hidrogéis de alginato de cálcio preparados nas condições avaliadas nesta Dissertação foram eficientes na remoção dos íons Cu2+ e Zn2+, sendo que o cobre apresentou maior afinidade pelo hidrogel do que o zinco

Thermal plasma synthesis of superparamagnetic iron oxide nanoparticles

Superparamagnetic iron oxide nanoparticles were synthesized by injecting ferrocene vapor and oxygen into an argon/helium DC thermal plasma. Size distributions of particles in the reactor exhaust were measured online using an aerosol extraction probe interfaced to a scanning mobility particle sizer, and particles were collected on transmission electron microscopy (TEM) grids and glass fiber filters for off-line characterization. The morphology, chemical and phase composition of the nanoparticles were characterized using TEM and X-ray diffraction, and the magnetic properties of the particles were analyzed with a vibrating sample magnetometer and a magnetic property measurement system. Aerosol at the reactor exhaust consisted of both single nanocrystals and small agglomerates, with a modal mobility diameter of 8-9 nm. Powder synthesized with optimum oxygen flow rate consisted primarily of magnetite (Fe 3O 4), and had a room-temperature saturation magnetization of 40.15 emu/g, with a coercivity and remanence of 26 Oe and 1.5 emu/g, respectively. © Springer Science+Business Media, LLC 2011.

Quasi-hexagonal ordered arrays of FePt nanoparticles prepared by a micellar method

Hexagonally ordered arrays of magnetic FePt nanoparticles on Si substrates are prepared by a self assembly of diblock copolymer PS-b-P2VP in toluene, a dip coating process and finally plasma treatment. The as-treated FePt nanoparticles are covered by an oxide layer that can be removed by a 40 s Ar+ sputtering. The effects of the sequence of adding salts on the composition distribution are revealed by x-ray photoelectron spectroscopy measurements. No particle agglomeration is observed after 600 degrees C annealing for the present ordered array of FePt nanoparticles, which exhibits advantages in patterning FePt nanoparticles by a micellar method. Moreover, magnetic properties of the annealed FePt nanoparticles at room temperature are investigated by a vibrating sample magnetometer.

Formation and magnetic properties of Fe16N2 films prepared by ion-beam-assisted deposition

Fe-N films containing the Fe16N2 phase were prepared in a high-vacuum system of ion-beam-assisted deposition (IBAD). The composition and structure of the films were analysed by Auger electron spectroscopy (AES) and X-ray diffraction (XRD), respectively. Magnetic properties of the films were measured by a vibrating sample magnetometer (VSM). The phase composition of Fe-N films depend sensitively on the N/Fe atomic arrival ratio and the deposition temperature. An Fe16N2 film was deposited successfully on a GaAs (1 0 0) substrate by IBAD at a N/Fe atomic arrival ratio of 0.12. The gram-saturation magnetic moment of the Fe16N2 film obtained is 237 emu/g at room temperature, the possible cause has been analysed and discussed. Hysteresis loops of Fe16N2 have been measured, the coercive force H-c is about 120 Oe, which is much larger than the value for Fe, this means the Fe16N2 sample exhibits a large uniaxial magnetocrystalline anisotropy. (C) 1998 Elsevier Science B.V. All rights reserved.

Formation and magnetic properties of Fe16N2 films prepared by ion-beam-assisted deposition

Fe-N films containing the Fe16N2 phase were prepared in a high-vacuum system of ion-beam-assisted deposition (IBAD). The composition and structure of the films were analysed by Auger electron spectroscopy (AES) and X-ray diffraction (XRD), respectively. Magnetic properties of the films were measured by a vibrating sample magnetometer (VSM). The phase composition of Fe-N films depend sensitively on the N/Fe atomic arrival ratio and the deposition temperature. An Fe16N2 film was deposited successfully on a GaAs (1 0 0) substrate by IBAD at a N/Fe atomic arrival ratio of 0.12. The gram-saturation magnetic moment of the Fe16N2 film obtained is 237 emu/g at room temperature, the possible cause has been analysed and discussed. Hysteresis loops of Fe16N2 have been measured, the coercive force H-c is about 120 Oe, which is much larger than the value for Fe, this means the Fe16N2 sample exhibits a large uniaxial magnetocrystalline anisotropy. (C) 1998 Elsevier Science B.V. All rights reserved.

Studies on the magnetism of cobalt ferrite nanocrystals synthesized by hydrothermal method

Fe-Co/CoFe2O4 nanocomposite and CoFe2O4 nanopowders were prepared by the hydrothermal method. The structure of magnetic powders were characterized by X-ray diffraction diffractometer (XRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), thermal gravity analysis (TGA) and differential thermal analysis (DTA) analysis, X-ray photoelectron spectrometry (XPS), and Fourier transform infrared spectra (FTIR) techniques, while magnetic properties were determined by using a vibrating sample magnetometer (VSM) at room temperature.

Preparation of Ni0.65Zn0.35Cu0.1Fe1.9O4/SiO2 nanocomposites by sol-gel method

(Ni0.65Zn035Cu0.1Fe1.904)-Cu-./SiO2 natiocomposites were fabricated by the sol-gel method using tetraethylorthosilicate as a precursor of silica, and metal nitrates as precursors of NiZnCu ferrite. With infrared spectra, X-ray diffraction, transmission electron microscope, Raman spectra, Mossbauer spectroscopy and vibrating sample magnetometer measurements, the formation of single phase nanocrystalline NiZnCu ferrites dispersed in silica matrix is confirmed when the sample is annealed at 550degreesC. The transition from the paramagnetic to the ferromagnetic state is observed as the annealing temperature increases from 750degreesC to 1150degreesC. The magnetic properties of these nanocomposites are clearly size dependent. The saturation magnetization increases with the annealing temperature.

Preparation of nanocrystalline NiZnCu ferrite particles by sol-gel method and their magnetic properties

Polyvinyl alcohol (PVA) was first used as chelating agent and metal nitrates as precursor of ferrite in the fabrication of nanocrystalline Ni0.65Zn0.35Cu0.1Fe1.9O4 particles by the sol-gel method. The thermal decomposition process of dried gel was studied by thermogravimetry (TG), differential thermal analysis (DTA) and infrared spectra (IR). The structural and magnetic properties of resultant particles were investigated by X-ray diffraction (XRD), transmission electron microscope (TEM), vibrating sample magnetometer (VSM) and Mossbauer spectroscopy. The dependence of the decomposition of dried gel, the formation of spinel structured NiZnCu ferrite, the sizes of annealed particles, the saturation magnetization and coercivity of annealed particles on annealing temperature is presented.

Rapid synthesis of Mn0.65Zn0.35Fe2O4/SiO2 homogeneous nanocomposites by modified sol-gel auto-combustion method

MnZn-ferrite/SiO2 nanocomposites with different silica content were successfully fabricated by a novel modified sol-gel auto-combustion method using citric acid as a chelating agent and tetraethyl orthosilicate (TEOS) as the source of silica matrix. The auto-combustion nature of the dried gel was studied by X-ray diffraction (XRD), Infrared spectra (IR), thermogravimetry (TG) and differential thermal analysis (DTA). Transmission electron microscope (TEM) observation shows that the MnZn-ferrite particles are homogeneously dispersed in silica matrix after auto-combustion of the dried gels. The magnetic properties vary with the silica content. The transition from the ferromagnetic to paramagnetic state is observed by Mossbauer spectra measurement with the increasing silica content. Vibrating sample magnetometer (VSM) shows that the magnetic properties of Mn0.65Zn0.35Fe2O4/SiO2 nanocomposites strongly depend on the silica content.

Synthesis of nanocrystalline Ba(CoxZn1-x)(2)Fe16O27 by sol-gel auto-combustion method

The synthesis of nanocrystalline W-type hexaferrites Ba(CoxZn1-x)(2)Fe16O27 powders by sol-gel auto-combustion method has been investigated. The thermal decomposition process of dried gel was studied by thermogravimetry (TG), differential thermal analysis (DTA) and infrared spectra (IR). The structural and magnetic properties of resultant particles were investigated by X-ray diffraction (XRD), transmission electron microscope (TEM), and vibrating sample magnetometer (VSM). The results reveal that the dried gel exhibits auto-combustion behavior. After combustion, pure nanocrystalline W-type hexaferrite phase starts to appear at the calcination temperature of 800 degrees C. The crystallinity and the grain size increase at higher temperature. The saturation magnetization and coercivity clearly depend on calcination temperature and Co content X.

Assessment of microInductors for DC-DC converters

There are increasing demands on the power density and efficiency of DC-DC power converters due to the soaring functionality and operational longevity required for today's electronic products. In addition, DC-DC converters are required to operate at new elevated frequencies in the MHz frequency regime. Typical ferrite cores, whose useable flux density falls drastically at these frequencies, have to be replaced and a method of producing compact component windings developed. In this study, two types of microinductors, pot-core and solenoid, for DC-DC converter applications have been analyzed for their performance in the MHz frequency range. The inductors were manufactured using an adapted UV-LIGA process and included electrodeposited nickel-iron and the commercial alloy Vitrovac 6025 as core materials. Using a vibrating sample magnetometer (VSM) and a Hewlett Packard 4192A LF- impedance analyzer, the inductor characteristics such as power density, efficiency, inductance and Q-factor were recorded. Experimental, finite element and analytical results were used to assess the suitability of the magnetic materials and component geometries for low MHz operation.

Application of citrate-stabilized gold-coated ferric oxide composite nanoparticles for biological separations

Gold-coated magnetic nanoparticles were synthesized with size ranging from 15 to 40 nm using sodium citrates as the reducing agent. Oxidized magnetites (Fe3O4) fabricated by co-precipitation of Fe2+ and Fe3+ in strong alkaline solution were used as magnetic cores. The structures of gold (Au) shell and magnetic core (Au–Fe) were studied by transmission electron microscopy (TEM) image and energy dispersive spectroscopy (EDS) spectrum. Results from high-resolution X-ray diffraction (HR XRD) show that the Au–Fe oxide nanoparticles have a face-centered cubic shape with the crystalline faces of {1 1 1}. The Au-coated magnetic nanoparticles exhibited a surface plasmon resonance peak at 528 nm. The nanoparticles are well dispersed in distilled water. A 3000 G permanent magnet was successfully used for the separation of the functionalized nanoparticles. Magnetic properties of the nanoparticles were determined by magnetic force microscope (MFM) in nanometric resolution and vibrating sample magnetometer (VSM). Magnetic separation of biological molecules using Au-coated magnetic oxide composite nanoparticles was examined after attachment of protein immunoglobulin G (IgG) through electrostatic interactions. Using this method, separation was achieved with a maximum yield of 35% at an IgG concentration of 400 ng/ml.