The influence of storage condition and duration on the resistance to fracture of different fiber post systems

Purpose: To evaluate the effects of storage condition and duration on the resistance to fracture of different fiber post systems (and to morphologically assess the post structure before and after storage. Methods: Three types of fiber posts (DT Light Post, GC Post, FRC Postect Plus) were divided in different groups (n=12) according to the storage condition (dry at 37 degrees C; saline water at 37 degrees C; mineral oil at 37 degrees C and storage inside the roots of extracted human teeth immersed in saline water at 37 degrees C and duration (6, 12 months). A universal testing machine loading at a 90 degrees angle was employed for the three-point bending test. The test was carried out until fracture of the post. A 3-way ANOVA and Tukey`s test (alpha= 0.05) were used to compare the effect of the experimental factors on the fracture strength. Two posts of each group were observed before and after the storage using a scanning electron microscope. Results: Storage condition and post type had a significant effect on post fracture strength (P< 0.05). The interaction between these factors was significant (P< 0.05). Water storage significantly decreased the fracture strength, regardless of the post type and the storage duration. Storage inside roots, in oil, and at dry conditions did not significantly affect post fracture strength. SEM micrographs revealed voids between fibers and resin matrix for posts stored in water. Posts stored under the other conditions showed a compact matrix without porosities. (Am J Dent 2009;22:366-370).

Bond strength of Epiphany (TM) Sealer combined with different adhesive systems photo-activated with LED and QTH

The Epiphany (TM) Sealer is a new dual-curing resin-based sealer and has been introduced as an alternative to gutta-percha and traditional root canal sealers. The canal filling is claimed to create a seal with the dentinal tubules within the root canal system producing a `monoblock` effect between the sealer and dentinal tubules. Therefore, considering the possibility to incorporate the others adhesive systems, it is important to study the bond strength of the resulting cement. Forty-eight root mandibular canines were sectioned 8-mm below CEJ. The dentine discs were prepared using a tapered diamond bur and irrigated with 1% NaOCl and 17% EDTA. Previous the application Epiphany (TM) Sealer, the Epiphany (TM) Primer, AdheSE, and One Up Bond F were applied to the root canal walls. The LED and QTH (Quartz Tungsten Halogen) were used to photo-activation during 45 s with power density of 400 and 720 mW/cm(2), respectively. The specimens were performed on a universal testing machine at a cross-head speed of 1 mm/min until bond failure occurred. The force was recorded and the debonding values were used to calculate Push-out bond strength. The analysis of variance (ANOVA) and Tukey`s post-hoc tests showed significant statistical differences (P < 0.05) to Epiphany (TM) Sealer/Epiphany (TM) Primer/QTH and EpiphanyTM Sealer/AdheSE/QTH, which had the highest mean values of bond strength. The efficiency of resin-based filling materials are dependent the type of light curing unit used including the power density, the polymerization characteristics of these resin-based filling materials, depending on the primer/adhesive used.

Influence of different endodontic filling materials on root fracture susceptibility

Objective: To evaluate the influence of different endodontic materials on root fracture susceptibility. Methods: Seventy-two mandibular incisors were sectioned 1 mm below the cementoenamel junction to obtain roots of 12 mm length. Roots were submitted to chemomechanical preparation with the rotary instruments of Profile system. The obturation of root canals were performed with the following filling materials (n = 12): GI, unfilled teeth (control); GII, Endofill + gutta-percha; GIII, Sealer 26 + gutta-percha; GIV, AH Plus + gutta-percha; GV, Epiphany + gutta-percha; GVI, Epiphany + Resilon. After the sealers setting time, each root was embedded in acrylic resin. The specimens were then submitted to fracture resistance test using an Instron testing machine at 1 mm/min. Results: The ANOVA test showed no significant statistical difference (p > .05) among GI (162.16 +/- 41.4N), GII (168.46 +/- 37.5N), GIII (164.83 +/- 35.7N), GIV (168.29 +/- 38.7N), GV (172.36 +/- 20.6N) and GVI (193.11 +/- 42.8N). Conclusion: The core materials (gutta-percha or Resilon) combined with the tested endodontic sealers are not able to increase the root fracture resistance in canals submitted to chemomechanical preparation. (c) 2007 Elsevier Ltd. All rights reserved.

Shear Bond Strength of A Sealant to Contaminated-Enamel Surface: Influence of Erbium : Yttrium-Aluminum-Garnet Laser Pretreatment

Salivary contamination is one of the factors that can disturb the sealing process and interfere in the longevity of pit and fissure sealants. Erbium : yttrium-aluminum-garnet (Er : YAG) laser could influence the bond strength of enamel and increase the acid resistance. To evaluate the influence of Er : YAG laser on the shear bond strength of a sealant to a salivary contaminated enamel surface. Twenty-four third molars had the roots sectioned 2 mm coronal to the cementoenamel junction. The crowns were mesiodistally sectioned providing 48 halves that were embedded in polyester resin. Enamel was flattened and a 2-mm diameter bonding area was demarcated. Specimens were randomly assigned to two groups according to the superficial pretreatment-37% phosphoric acid (A) and Er : YAG laser (80 mJ/2 Hz) + phosphoric acid (L), which were subdivided into two groups (N = 12), without salivary contamination (C) and with salivary contamination (SC). To contaminate the specimens, 0.25 mL of human fresh saliva was applied for 20 seconds and then dried. Fluroshield sealant was applied in all specimens. After storage, shear bond strength of samples were tested in a universal testing machine. Means in MPa were: AC-14.61 (+/- 2.52); ASC-6.66 (+/- 2.34); LC-11.91 (+/- 1.34); and LSC-2.22 (+/- 0.66). Statistical analysis revealed that surfaces without salivary contamination and with acid treatment had the highest mean (p < 0.05). The group with salivary contamination treated by Er : YAG laser followed by phosphoric acid application presented the lowest bond values (p < 0.05). The phosphoric acid etching under dry condition yielded better bonding performance. Er : YAG laser was not able to increase the effectiveness of conventional acid etching of enamel in the bond of sealants in both dry and wet conditions. Under the conditions of this study, the conventional etching protocol (phosphoric acid without salivary contamination) is still preferable to laser-conditioning enamel surface prior to sealant application.

Effects of Ethanol on the Surface and Bulk Properties of a Microwave-Processed PMMA Denture Base Resin

Purpose: This study evaluated the effect of different concentrations of ethanol on hardness, roughness, flexural strength, and color stability of a denture base material using a microwave-processed acrylic resin as a model system. Materials and Methods: Sixty circular (14 x 4 mm) and 60 rectangular microwave-polymerized acrylic resin specimens (65 x 10 x 3 mm(3)) were employed in this study. The sample was divided into six groups according to the ethanol concentrations used in the immersion solution, as follows: 0% (water), 4.5%, 10%, 19%, 42%, and 100%. The specimens remained immersed for 30 days at 37 degrees C. The hardness test was performed by a hardness tester equipped with a Vickers diamond penetrator, and a surface roughness tester was used to measure the surface roughness of the specimens. Flexural strength testing was carried out on a universal testing machine. Color alterations (Delta E) were measured by a portable spectrophotometer after 12 and 30 days. Variables were analyzed by ANOVA/Tukey`s test (alpha = 0.05). Results: For the range of ethanol-water solutions for immersion (water only, 4.5%, 10%, 19.5%, 42%, and 100%), the following results were obtained for hardness (13.9 +/- 2.0, 12.1 +/- 0.7, 12.9 +/- 0.9, 11.2 +/- 1.5, 5.7 +/- 0.3, 2.7 +/- 0.5 VHN), roughness (0.13 +/- 0.01, 0.15 +/- 0.07, 0.13 +/- 0.05, 0.13 +/- 0.02, 0.23 +/- 0.05, 0.41 +/- 0.19 mu m), flexural strength (90 +/- 12, 103 +/- 18, 107 +/- 16, 90 +/- 25, 86 +/- 22, 8 +/- 2 MPa), and color (0.8 +/- 0.6, 0.8 +/- 0.3, 0.7 +/- 0.4, 0.9 +/- 0.3, 1.3 +/- 0.3, 3.9 +/- 1.5 Delta E) after 30 days. Conclusions: The findings of this study showed that the ethanol concentrations of tested drinks affect the physical properties of the investigated acrylic resin. An obvious plasticizing effect was found, which could lead to a lower in vivo durability associated with alcohol consumption.

Physical Properties of an Acrylic Resin after Incorporation of an Antimicrobial Monomer

Purpose: This study evaluated the effect of the incorporation of the antimicrobial monomer methacryloyloxyundecylpyridinium bromide (MUPB) on the hardness, roughness, flexural strength, and color stability of a denture base material. Materials and Methods: Ninety-six disk-shaped (14-mm diameter x 4-mm thick) and 30 rectangular (65 x 10 x 3.3 mm(3)) heat-polymerized acrylic resin specimens were divided into three groups according to the concentration of MUPB (w/w): (A) 0%, (B) 0.3%, (C) 0.6%. Hardness was assessed by a hardness tester equipped with a Vickers diamond penetrator. Flexural strength and surface roughness were tested on a universal testing machine and a surface roughness tester, respectively. Color alterations (Delta E) were measured by a portable spectrophotometer after 12 and 36 days of immersion in water, coffee, or wine. Variables were analyzed by ANOVA/Tukey HSD test (alpha = 0.05). Results: The following mean results (+/-SD) were obtained for hardness (A: 15.6 +/- 0.6, B: 14.6 +/- 1.7, C: 14.8 +/- 0.8 VHN; ANOVA: p = 0.061), flexural strength (A: 111 +/- 17, B: 105 +/- 12, C: 88 +/- 12 MPa; ANOVA: p = 0.008), and roughness (A: 0.20 +/- 0.11, B: 0.20 +/- 0.11, C: 0.24 +/- 0.08 mu m; ANOVA: p = 0.829). Color changes of immersed specimens were significantly influenced by solutions and time (A: 9.1 +/- 3.1, B: 14.8 +/- 7.5, C: 13.3 +/- 6.1 Delta E; ANOVA: p < 0.05). Conclusions: The incorporation of MUPB affects the mechanical properties of a denture base acrylic resin; however, the only significant change was observed for flexural strength and may not be critical. Color changes were slightly higher when resin containing MUPB was immersed in wine for a prolonged time; however, the difference has debatable clinical relevance.

Evaluation of the Bond Strength of Denture Base Resins to Acrylic Resin Teeth: Effect of Thermocycling

Purpose: The purpose of this study was to evaluate the thermocycling effects and shear bond strength of acrylic resin teeth to denture base resins. Materials and Methods: Three acrylic teeth (Biotone, Trilux, Ivoclar) were chosen for bonding to four denture base resins: microwave-polymerized (Acron MC), heat-polymerized (Lucitone 550 and QC-20), and light-polymerized (Versyo. bond). Twenty specimens were produced for each denture base/acrylic tooth combination and were divided into two groups (n = 10): without thermocycling (control groups) and thermocycled groups submitted to 5000 cycles between 4 and 60 degrees C. Shear strength tests (MPa) were performed with a universal testing machine at a crosshead speed of 1 mm/min. Statistical analysis of the results was carried out with three-way ANOVA and Bonferroni`s multiple comparisons post hoc analysis for test groups (alpha = 0.05). Results: The shear bond strengths of Lucitone/Biotone, Lucitone/Trilux, and Versyo/Ivoclar specimens were significantly decreased by thermocycling, compared with the corresponding control groups (p < 0.05). The means of Acron/Ivoclar and Lucitone/Ivoclar specimens increased after thermocycling (p < 0.05). The highest mean shear bond strength value was observed with Lucitone/Biotone in the control group (14.54 MPa) and the lowest with QC-20/Trilux in the thermocycled group (3.69 MPa). Conclusion: Some acrylic tooth/denture base resin combinations can be more affected by thermocycling; effects vary based upon the materials used.

Determinação de propriedades mecânicas através de ensaios de provetes miniatura, "Small Punch"

Trabalho Final de Mestrado para obtenção do grau de Mestre em Engenharia Mecânica

Stress Ratio Effects on the fatigue Properties of Biaxially Loaded Tubular FRP-Specimens – Experimental Study

In this work tubular fiber reinforced specimens are tested for fatigue life. The specimens are biaxially loaded with tension and shear stresses, with a load angle β of 30° and 60° and a load ratio of R=0,1. There are many factors that affect fatigue life of a fiber reinforced material and the main goal of this work is to study the effects of load ratio R by obtaining S-N curves and compare them to the previous works (1). All the other parameters, such as specimen production, fatigue loading frequency and temperature, will be the same as for the previous tests. For every specimen, stiffness, temperature of the specimen during testing, crack counting and final fracture mode are obtained. Prior to testing, a study if the literature regarding the load ratio effects on composites fatigue life and with that review estimate the initial stresses to be applied in testing. In previous works (1) similar specimens have only been tested for a load ratio of R=-1 and therefore the behaviour of this tubular specimens for a different load ratio is unknown. All the data acquired will be analysed and compared to the previous works, emphasizing the differences found and discussing the possible explanations for those differences. The crack counting software, developed at the institute, has shown useful before, however different adjustments to the software parameters lead to different cracks numbers for the same picture, and therefore a better methodology will be discussed to improve the crack counting results. After the specimen’s failure, all the data will be collected and stored and fibre volume content for every specimen is also determinate. The number of tests required to make the S-N curves are obtained according to the existent standards. Additionally are also identified some improvements to the testing machine setup and to the procedures for future testing.

Estudo da delaminação em compósitos

As excelentes propriedades mecânicas, associadas ao seu baixo peso, fazem com que os materiais compósitos sejam atualmente dos mais interessantes da nossa sociedade tecnológica. A crescente utilização destes materiais e a excelência dos resultados daí provenientes faz com que estes materiais sejam utilizados em estruturas complexas de responsabilidade, pelo que a sua maquinagem se torna necessária de forma a possibilitar a ligação entre peças. O processo de furação é o mais frequente. O processo de maquinagem de compósitos terá como base os métodos convencionais utilizados nos materiais metálicos. O processo deverá, no entanto, ser convenientemente adaptado, quer a nível de parâmetros, quer a nível de ferramentas a utilizar. As características dos materiais compósitos são bastante particulares pelo que, quando são sujeitos a maquinagem poderão apresentar defeitos tais como delaminação, fissuras intralaminares, arrancamento de fibras ou dano por sobreaquecimento. Para a detecção destes danos, por vezes a inspeção visual não é suficiente, sendo necessário recorrer a processos específicos de análise de danos. Existem já, alguns estudos, cujo âmbito foi a obtenção de furos de qualidade em compósitos, com minimização do dano, não se podendo comparar ainda com a informação existente, no que se refere à maquinagem de materiais metálicos ou ligas metálicas. Desta forma, existe ainda um longo caminho a percorrer, de forma a que o grau de confiança na utilização destes materiais se aproxime aos materiais metálicos. Este trabalho experimental desenvolvido nesta tese assentou essencialmente na furação de placas laminadas e posterior análise dos danos provocados por esta operação. Foi dada especial atenção à medição da delaminação causada pela furação e à resistência mecânica do material após ser maquinado. Os materiais utilizados, para desenvolver este trabalho experimental, foram placas compósitas de carbono/epóxido com duas orientações de fibras diferentes: unidireccionais e em “cross-ply”. Não se conseguiu muita informação, junto do fornecedor, das suas características pelo que se levaram a cabo ensaios que permitiram determinar o seu módulo de elasticidade. Relativamente á sua resistência â tração, como já foi referido, a grande resistência oferecida pelo material, associada às limitações da máquina de ensaios não permitiu chegar a valores conclusivos. Foram usadas três geometrias de ferramenta diferentes: helicoidal, Brad e Step. Os materiais utilizados nas ferramentas, foram o aço rápido (HSS) e o carboneto de tungsténio para as brocas helicoidais de 118º de ângulo de ponta e apenas o carboneto de tungsténio para as brocas Brad e Step. As ferramentas em diamante não foram consideradas neste trabalho, pois, embora sejam reconhecidas as suas boas características para a maquinagem de compósitos, o seu elevado custo não justifica a sua escolha, pelo menos num trabalho académico, como é o caso. As vantagens e desvantagens de cada geometria ou material utilizado foram avaliadas, tanto no que diz respeito à delaminação como á resistência mecânica dos provetes ensaiados. Para a determinação dos valores de delaminação, foi usada a técnica de Raio X. Algum conhecimento já existente relativamente a este processo permitiu definir alguns parâmetros (por exemplo: tempo de exposição das placas ao liquido contrastante), que tornaram acessível o procedimento de obtenção de imagens das placas furadas. Importando estas imagens para um software de desenho (no caso – AutoCad), foi possível medir as áreas delaminadas e chegar a valores para o fator de delaminação de cada furo efetuado. Terminado este processo, todas as placas foram sujeitas a ensaios de esmagamento, de forma a avaliar a forma como os parâmetros de maquinagem afectaram a resistência mecânica do material. De forma resumida, são objetivos deste trabalho: - Caracterizar as condições de corte em materiais compósitos, mais especificamente em fibras de carbono reforçado com matriz epóxida (PRFC); - Caracterização dos danos típicos provocados pela furação destes materiais; - Desenvolvimento de análise não destrutiva (RX) para avaliação dos danos provocados pela furação; - Conhecer modelos existentes com base na mecânica da fratura linear elástica (LEFM); - Definição de conjunto de parâmetros ideais de maquinagem com o fim de minimizar os danos resultantes da mesma, tendo em conta os resultados provenientes dos ensaios de força, da análise não destrutiva e da comparação com modelos de danos existentes e conhecidos.

Determinação das propriedades mecânicas à tração de adesivos estruturais frágeis e dúcteis

A crescente evolução na tecnologia das juntas coladas conferiu um potencial atractivo às ligações adesivas, com aplicações nas mais variadas indústrias. Isto deve-se não só aos aspetos económicos, tais como a melhoria da cadência de produção mas também à resistência mecânica que estas proporcionam. A possibilidade de ligar facilmente materiais distintos, a distribuição mais uniforme das tensões, a melhor resistência à fadiga e a elevada capacidade de amortecimento de vibrações estão entre as principais vantagens da utilização deste tipo de ligação. Estas propriedades transformam as juntas coladas numas das preferidas no momento de seleção de meios de união. O trabalho desenvolvido nesta dissertação enquadra-se no âmbito das ligações adesivas e tem como principais objetivos a produção de uma ferramenta para a produção de provetes de adesivo, assim como a determinação das propriedades mecânicas à tração dos mesmos para testar o desempenho do molde fabricado. Para tal, utilizou-se um adesivo frágil (Araldite® AV 138), um dúctil (Araldite® 2015) e um muito dúctil (SikaForce® 7888). Paralelamente é selecionado o método mais adequado na obtenção destes provetes, designadamente escolhendo entre a moldação em molde aberto e a injeção em molde fechado. Com vista à obtenção dos provetes, foi projetado e construído um molde em aço. Recorrendo à máquina de tração Shimadzu AG – X 100, realizaram-se os respetivos ensaios de tração, para a determinação de todas as propriedades mecânicas dos adesivos. Para efeitos de comparação de resultados foram utilizados dois tipos de extensómetros, um mecânico e um ótico. Os resultados experimentais permitiram observar que a presença de vazios afetou especialmente a deformação de rotura e a tensão de rotura. Detetaram-se pequenas discordâncias, comparativamente com os estudos publicados, de algumas características mecânicas obtidas dos diversos adesivos utilizados. Constatou-se também um ligeiro desfasamento entre os valores adquiridos com os dois tipos de extensómetros utilizados.

Novel auxetic structures from basalt braided composites for structural applications

Auxetic materials are a class of materials behaves unusual way compared to regular materials i.e. possess negative Poisson’s ratio. This paper reports, the development of auxetic structures based on re-entrant hexagon design from braided composite materials and testing of the mechanical properties (tensile property, auxetic property and work of rupture). The structure developed from glass and basalt braided composite rods and properties were compared between them. Later, the basic re-entrant hexagon design was modified with vertical straight rods to improve their mechanical behavior and their auxetic property was studied. Auxetic behavior of these structures was studied in a tensile testing machine taking video during testing by Digital camera, later the video converted into images to measure the strain values using simple software, ImageJ. Along with experimental work, analytical model was used to calculate the Poisson’s ratio of basic structure and results were compared

Processamento e caracterização de compósitos de Ti-HAP para aplicações biomédicas

Dissertação de mestrado integrado em Engenharia de Materiais

Development of a Model for the Ice Scraping Process, October 1996

A laboratory study has been conducted with two aims in mind. The first goal was to develop a description of how a cutting edge scrapes ice from the road surface. The second goal was to investigate the extent, if any, to which serrated blades were better than un-serrated or "classical" blades at ice removal. The tests were conducted in the Ice Research Laboratory at the Iowa Institute of Hydraulic Research of the University of Iowa. A specialized testing machine, with a hydraulic ram capable of attaining scraping velocities of up to 30 m.p.h. was used in the testing. In order to determine the ice scraping process, the effects of scraping velocity, ice thickness, and blade geometry on the ice scraping forces were determined. Higher ice thickness lead to greater ice chipping (as opposed to pulverization at lower thicknesses) and thus lower loads. Behavior was observed at higher velocities. The study of blade geometry included the effect of rake angle, clearance angle, and flat width. The latter were found to be particularly important in developing a clear picture of the scraping process. As clearance angle decreases and flat width increases, the scraping loads show a marked increase, due to the need to re-compress pulverized ice fragments. The effect of serrations was to decrease the scraping forces. However, for the coarsest serrated blades (with the widest teeth and gaps) the quantity of ice removed was significantly less than for a classical blade. Finer serrations appear to be able to match the ice removal of classical blades at lower scraping loads. Thus, one of the recommendations of this study is to examine the use of serrated blades in the field. Preliminary work (by Nixon and Potter, 1996) suggests such work will be fruitful. A second and perhaps more challenging result of the study is that chipping of ice is more preferable to pulverization of the ice. How such chipping can be forced to occur is at present an open question.

Development of a Model for the Ice Scraping Process Iowa Department of Transportation Project HR 361 Final Report, October 1996

A laboratory study has been conducted with two aims in mind. The first goal was to develop a description of how a cutting edge scrapes ice from the road surface. The second goal was to investigate the extent, if any, to which serrated blades were better than un-serrated or "classical" blades at ice removal. The tests were conducted in the Ice Research Laboratory at the Iowa Institute of Hydraulic Research of the University of Iowa. A specialized testing machine, with a hydraulic ram capable of attaining scraping velocities of up to 30 m.p.h. was used in the testing. In order to determine the ice scraping process, the effects of scraping velocity, ice thickness, and blade geometry on the ice scraping forces were determined. Higher ice thickness lead to greater ice chipping (as opposed to pulverization at lower thicknesses) and thus lower loads. S~milabr ehavior was observed at higher velocities. The study of blade geometry included the effect of rake angle, clearance angle, and flat width. The latter were found to be particularly important in developing a clear picture of the scraping process. As clearance angle decreases and flat width increases, the scraping loads show a marked increase, due to the need to re-compress pulverized ice fragments. The effect of serrations was to decrease the scraping forces. However, for the coarsest serrated blades (with the widest teeth and gaps) the quantity of ice removed was significantly less than for a classical blade. Finer serrations appear to be able to match the ice removal of classical blades at lower scraping loads. Thus, one of the recommendations of this study is to examine the use of serrated blades in the field. Preliminary work (by Nixon and Potter, 1996) suggests such work will be fruitful. A second and perhaps more challenging result of the study is that chipping of ice is more preferable to pulverization of the ice. How such chipping can be forced to occur is at present an open question.