The effect of adhesive systems on the pullout strength of a fiberglass-reinforced composite post system in bovine teeth

Purpose: To evaluate the pullout strength of a glass fiber-reinforced composite post (glass FRC) cemented with three different adhesive systems and one resin cement. The null hypothesis was that pullout strengths yielded by the adhesive systems are similar. Materials and Methods: Thirty bovine teeth were selected. The size of the specimens was standardized at 16 mm by sectioning off the coronal portion and part of the root. The specimens were divided into three groups, according to the adhesive system, which were applied following the manufacturers' instructions: G1, ScotchBond Multi-Purpose Plus; G2, Single Bond; G3, Tyrian SPE/One-Step Plus. The glass FRCs (Reforpost) were etched with 37% H3PO4 for 1 min and silanized (Porcelain Primer). Thereafter, they were cemented with the dual resin cement En-Force. The specimens were stored for 24 h, attached to an adapted device, and submitted to the pullout test in a universal testing machine (1 mm/min). The data were submitted to the one-way ANOVA and Tukey's test (α = 0.05). Results: G1 (30.2 ± 5.8 Kgf) displayed the highest pullout strength (p < 0.001) when compared to G2 (18.6 ± 5.8 Kgf) and G3 (14.3 ± 5.8 Kgf), which were statistically similar. Analysis of the specimens revealed that all failures occurred between the adhesive system and the root dentin (pullout of the post cement), regardless of group. Conclusion: The multiple-bottle, total-etch adhesive system provided higher pullout strength of the glass FRC when compared to the single-bottle, total-etch, and single-step self-etching adhesive systems. The null hypothesis was rejected (p < 0.001).

Bond strength of adhesive systems to human tooth enamel

The purpose of this study was to evaluate in vitro three adhesive systems: a total etching single-component system (G1 Prime & Bond 2.1), a self-etching primer (G2 Clearfil SE Bond), and a self-etching adhesive (G3 One Up Bond F), through shear bond strength to enamel of human teeth, evaluating the type of fracture through stereomicroscopy, following the ISO guidance on adhesive testing. Thirty sound premolars were bisected mesiodistally and the buccal and lingual surfaces were embedded in acrylic resin, polished up to 600-grit sandpapers, and randomly assigned to three experimental groups (n = 20). Composite resin cylinders were added to the tested surfaces. The specimens were kept in distilled water (37°C/24 h), thermocycled for 500 cycles (5°C-55°C) and submitted to shear testing at a crosshead speed of 0.5 mm/min. The type of fracture was analyzed under stereomicroscopy and the data were submitted to Anova, Tukey and Chi-squared (5%) statistical analyses. The mean adhesive strengths were G1: 18.13 ± 6.49 MPa, (55% of resin cohesive fractures); G2: 17.12 ± 5.80 MPa (90% of adhesive fractures); and G3: 10.47 ± 3.14 MPa (85% of adhesive fractures). In terms of bond strength, there were no significant differences between G1 and G2, and G3 was significantly different from the other groups. G1 presented a different type of fracture from that of G2 and G3. In conclusion, although the total etching and self-etching systems presented similar shear bond strength values, the types of fracture presented by them were different, which can have clinical implications.

Performance of a New One-step Multi-mode Adhesive on Etched vs Non-etched Enamel on Bond Strength and Interfacial Morphology

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Responses of dental pulp cells to a less invasive bleaching technique applied to adhesive restored teeth

To assess the cytotoxicity of 35% hydrogen peroxide (HP) bleaching gel applied for 15 min to sound or restored teeth with two-step self-etching adhesive systems and composite resin. Materials and Methods: Sound and restored enamel/dentin disks were stored in water for 24 h or 6 months + thermocycling. The disks were adapted to artificial pulp chambers and placed in compartments containing culture medium. Immediately after bleaching, the culture medium in contact with dentin was applied for 1 h to previously cultured odontoblast-like MDPC-23 cells. Thereafter, cell viability (MTT assay) and morphology (SEM) were assessed. Data were analyzed by two-way ANOVA and Tukey's test (a = 5%). Results: In comparison to the negative control group (no treatment), no significant cell viability reduction occurred in those groups in which sound teeth were bleached. However, a significant decrease in cell viability was observed in the adhesive-restored bleached groups compared to negative control. No significant difference among bleached groups was observed with respect to the presence of restoration and storage time. Conclusion: The application of 35% HP bleaching gel to sound teeth for 15 min does not cause toxic effects in pulp cells. When this bleaching protocol was performed in adhesive-restored teeth, a significant toxic effect occurred.

Effect of Er:YAG laser and diamond drill on hybrid layer morphology obtained with self-etch adhesive: analysis by SEM and confocal laser scanning microscopy (CLSM)

This study aimed to evaluate the effect of Er:YAG (L) and diamond drills (DD) on: 1) the microshear bond strength (MPa); 2) the adhesive interface of two-step (TS) – Adper Scotchbond Multipurpose and one-step (OS) adhesives – Adper EasyOne, both from 3M ESPE. Material and methods: According to the preparation condition and adhesives, the samples were divided into four groups: DD_TS (control); DD_OS; L_TS and L_OS. 60 bovine incisors were randomly divided into experimental and groups: 40 for microshear bond strength (n = 10) and 20 for the adhesive interface morphology [6 to measure the thickness of the hybrid layer (HL) and length of tags (t) by CLSM (n = 3); 12 to the adhesive interface morphology by SEM (n = 3) and 2 to illustrate the effect of the instruments on dentine by SEM (n = 1)]. To conduct the microshear bond strength test, four cylinders (0.7 mm in diameter and 1 mm in height with area of adhesion of 0.38 mm) were constructed with resin composite (Filtek Z350 XT – 3M ESPE) on each dentin surface treated by either L or DD and after adhesives application. Microshear bond strength was performed in universal testing machine (EMIC 2000) with load cell of 500 kgf and a crosshead speed of 0.5 mm / min. Adhesive interface was characterized by thickness of hybrid layer (HL) and length of tags (t) in nm, with the aid of UTHSCSA ImageTool software. Results: Microshear bond strength values were: L_TS 34.10 ± 19.07, DD_TS 24.26 ± 9.35, L_OS 33.18 ± 12.46, DD_OS 21.24 ± 13.96. Two-way ANOVA resulted in statistically significant differences only for instruments (p = 0.047). Mann-Whitney identified the instruments which determined significant differences for HL thickness and tag length (t). Concerning to the adhesive types, these differences were only observed for (t). Conclusion: It can be concluded that 1) laser Er:YAG results in higher microshear bond strength values regardless of the adhesive system (TS and OS); 2) the tags did not significant affect the microshear bond strength; 3) the adhesive interface was affected by both the instruments for cavity preparation and the type of adhesive system used.

Bonding of simplified adhesive systems to caries-affected dentin of primary teeth.

PURPOSE To evaluate the bonding of simplified adhesive systems to sound and caries-affected dentin of primary teeth with microtensile (µTBS) and nanoleakage (NL) tests. MATERIALS AND METHODS Occlusal cavities were prepared in 36 sound second primary molars. Half of the specimens were submitted to pH cycling to simulate caries-affected dentin. Teeth were randomly restored with one of three materials: the etch-and-rinse adhesive system Adper Single Bond 2 (SB), the two-step self-etching adhesive system Adper SE Plus (SE), and the one-step self-etching adhesive system Adper Easy One (EASY). After storage for 24 h, specimens with cross-sectional areas of 0.8 mm2 were prepared for microtensile testing (1 mm/min). One stick from each tooth was immersed in silver nitrate solution (24 h) and allowed to develop for 8 h in order to score the nano leakage with SEM. The fracture pattern was evaluated using a stereomicroscope (400X). The µTBS means were analyzed by two-way ANOVA and Tukey's post-hoc test. For NL, the Kruskal- Wallis and Mann-Whitney tests were used (α < 0.05). RESULTS SB (35.5 ± 3.5) showed the highest µTBS value to sound dentin, followed by EASY (26.3 ± 1.9) and SE (18.2 ± 6.5) (p < 0.05). No difference among materials was observed for caries-affected dentin (SB: 17.8 ± 4.2; SE: 13.9 ± 3.2; EASY: 14.4 ± 4.2, p > 0.05). For all groups, adhesive/mixed fracture prevailed. Caries affected dentin promoted silver nitrate uptake into the adhesive interface; however, with SE, the nano leakage was more pronounced than in the other adhesive systems, even in sound dentin. CONCLUSION Caries-affected dentin negatively influences the bond strength and nano leakage of the two-step etch-and-rinse and one-step self-etching adhesive systems tested in primary teeth.

Influence of blood contamination on bond strength of a self-etching system.

OBJECTIVES: To detect the influence of blood contamination (BC) on the bond strength (BS) of a self-etching bonding system (SES) to enamel and dentine. METHODS: 25 human molars were longitudinally sectioned on the mesio-distal axis in order to obtain 50 specimens, which were embedded in acrylic resin. At first, the specimens were ground to expose a flat surface of enamel, and a bond strength test was performed. Afterwards, the samples were ground again in order to obtain a flat surface of dentine. Ten groups (total: n=100) were assigned according to substrate (enamel and dentine), step in the bonding sequence when contamination occurred (before the acidic primer and after the bonding resin), and contamination treatment (dry or rinse and dry procedure). Fresh human blood was introduced either before or after SES application (Clearfil SE Bond) and treated with air drying, or by rinsing and drying following application. Composite resin (Filtek Z-250,3M ESPE) was applied as inverted, truncated cured cones that were debonded in tension. RESULTS: The mean tensile BS values (MPa) for enamel/dentine were 19.4/23.0 and 17.1/10.0 for rinse-and-dry treatment (contamination before and after SES, respectively); while the measurements for the dry treatment, 16.2/23.3 and 0.0/0.0 contamination before and after SES, respectively. CONCLUSIONS: It was determined that blood contamination impaired adhesion to enamel and dentine when it occurred after bond light curing. Among the tested contamination treatments, the rinse-and-dry treatment produced the highest bond strength with BC after SES application, but it was not sufficient to recover the BS in the contamination-free group.

Influência da associação de catalisadores químicos na cimentação de pinos pré-fabricados de fibra de vidro

O objetivo deste estudo foi avaliar a Influência da associação de catalisadores químicos junto a diferentes sistemas adesivos autocondicionantes e cimentos resinosos de dupla polimerização, na cimentação de pinos pré-fabricados de fibra de vidro, quanto a sua resistência ao cisalhamento por extrusão - push out, seu grau de conversão e nanoinfiltração. Foram utilizadas trinta raízes bovinas extraídas, que tiveram seus canais obturados com guta-percha termoplastificada, divididas em três grupos: G1 - Adper SE Plus /Rely X ARC; G2- Adper SE Plus / Catalisador Scotchbond + Rely X ARC ; G3- Clearfil SE Bond / ED Primer + Panavia F. Após a cimentação dos pinos foram obtidas fatias das raízes, com 1mm de espessura, dos terços cervical (C), médio (M) e apical (A). O ensaio de resistência ao cisalhamento por extrusão foi realizado em máquina de ensaio universal EMIC D500 com carga de 100KN à velocidade de 1,0 mm/min, até o deslocamento do pino. Os dados obtidos no ensaio foram tabulados e submetidos à análise estatística. A análise de variância a dois critérios mostrou que apenas os fatores grupo e profundidade foram significativos, não sendo significativa a sua interação. O resultado do teste de Tukey (ρ≥0,05), para o fator grupo, mostrou que a menor média de resistência ao cisalhamento por extrusão foi obtida pelo grupo 3, que apresentou diferença estatística significativa para os grupos 1 e 2 que não diferiram entre si. Para o fator Profundidade a maior média foi obtida no terço cervical que apresentou diferença estatística significativa para os terços médio e apical que não diferiram entre si: A análise do grau de conversão foi feita após vinte e quatro horas e os fatores estudados foram os cimentos resinosos Panavia F e Rely X ARC e os catalisadores químicos ED Primer e Catalisador Scotchbond, na forma incorporada ou aplicada superficialmente aos cimentos, formando 10 grupos experimentais. Para o grau de conversão, o teste de Tukey mostrou que o catalisador químico não aumentou o grau de conversão do RelyX ARC, já para o Panavia F, este aumentou significativamente seu grau de conversão. Quanto a análise em MEV da nanoinfiltração para o fator grupo, o resultado do teste de Tukey (ρ≥0,05) mostrou que a maior média foi obtida pelo grupo 3 que apresentou diferença estatística significativa para os grupos 1 e 2, que não diferiram entre si. Para o fator Profundidade a maior média foi obtida no terço apical que apresentou diferença estatística significativa para o terço cervical, que não diferiu do terço médio. Conclusões: 1- A associação de catalisadores químicos não aumentou a resistência ao cisalhamento por extrusão dos pinos de fibra de vidro. 2- O cimento Panavia F é dependente de catalisador aumentar o grau de conversão. 3- A associação de catalisadores químicos não foi capaz de alterar o padrão da camada híbrida, representado pela nanoinfiltração. 4- A nanoinfiltração está associada inversamente ao grau de conversão dos sistemas de cimentação, o que contribui negativamente para a resistência adesiva de pinos de fibra de vidro.

Biocompatibility of resin-based materials used as pulp-capping agents

Aim To evaluate and compare the response of pulps of rats capped with resin-modified glass-ionomer cement (RMGIC) or self-etching adhesive system.Methodology Class I cavities were prepared on the occlusal surface of 54 maxillary first molars of 27 rats. Pulp exposure was performed on the cavity floor. The following resin-based materials were applied as pulp-capping agents: G1, Clearfil Liner Bond 2V (CLB 2V; Kuraray Co., Japan); G2, Vitrebond (VIT; 3M/ESPE, USA). In group 3 (control group), a calcium hydroxide/saline paste (CH; Labsynth, Brazil) was used. The cavities were restored with amalgam. After 7, 30 and 60 days, the animals were sacrificed and the jaws were processed for microscopic evaluation.Results Despite the inflammatory response caused by the experimental and the control materials at 7 days, pulpal healing associated with calcified barrier formation was observed at 60 days following the pulp therapy. Both resin-based materials promoted a large zone of cell-rich fibrodentine matrix deposition on the pulp horn related to the pulp exposure site, which was larger to VIT than to CLB 2V specimens. Tertiary dentine underneath the fibrodentine matrix was deposited by a layer of elongated pulpal cells. The remaining pulpal tissue exhibited normal histological characteristics. In the control group, healing and dentine-bridge formation was observed at 30 days. Pulpal breakdown occurred only when bacterial infection occurred.Conclusion Both experimental pulp-capping agents allowed pulpal healing characterized by cell-rich fibrodentine and tertiary dentine deposition as well as calcified barrier formation.

Bond Strength of Two Resin Cements on Dentin Using Different Cementation Strategies

Purpose:This study evaluated the microtensile bond strength of two resin cements to dentin either with their corresponding self-etching adhesives or employing the three-step etch-and-rinse technique. The null hypothesis was that the etch-and-rinse adhesive system would generate higher bond strengths than the self-etching adhesives.Materials and Methods:Thirty-two human molars were randomly divided into four groups (N = 32, n = 8/per group): G1) ED Primer self-etching adhesive + Panavia F; G2) All-Bond 2 etch-and-rinse adhesive + Panavia F; G3) Multilink primer A/B self-etching adhesive + Multilink resin cement; G4) All-Bond 2 + Multilink. After cementation of composite resin blocks (5 x 5 x 4 mm), the specimens were stored in water (37 degrees C, 24 hours), and sectioned to obtain beams (+/- 1 mm2 of adhesive area) to be submitted to microtensile test. The data were analyzed using 2-way analysis of variance and Tukey's test (alpha = 0.05).Results:Although the cement type did not significantly affect the results (p = 0.35), a significant effect of the adhesive system (p = 0.0001) was found on the bond strength results. Interaction terms were not significant (p = 0.88751). The etch-and-rinse adhesive provided significantly higher bond strength values (MPa) with both resin cements (G2: 34.4 +/- 10.6; G4: 33.0 +/- 8.9) compared to the self-etching adhesive systems (G1: 19.8 +/- 6.6; G3: 17.8 +/- 7.2) (p < 0.0001). Pretest failures were more frequent in the groups where self-etching systems were used.Conclusion:Although the cement type did not affect the results, there was a significant effect of changing the bonding strategy. The use of the three-step etch-and-rinse adhesive resulted in significantly higher bond strength for both resin cements on dentin.CLINICAL SIGNIFICANCEDual polymerized resin cements tested could deliver higher bond strength to dentin in combination with etch-and-rinse adhesive systems as opposed to their use in combination with self-etching adhesives.(J Esthet Restor Dent 22:262-269, 2010).

Estudo das propriedades mecânicas da interface adesiva criada por sistemas adesivos convencional e autocondicionante, associados ou não ao laser Nd:YAG, utilizando a técnica da nanoindentação

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influência do tipo de preparo e sistema adesivo na resistência de união à dentina bovina

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Inter-relação do comprimento dos prolongamentos resinosos (tags) e da espessura da camada híbrida de adesão, com a resistência de união de sistemas adesivos ao tecido dentinário

Pós-graduação em Odontologia - FOA

Resistência adesiva de sistemas autocondicionante e convencional frente a diferentes substratos e associação ao laser Nd:YAG: estudo in vitro

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo comparativo da influência do condicionamento do esmalte humano e bovino com laser de Er:YAG sobre a resistência de união de um sistema adesivo convencional e de um sistema adesivo autocondicionante

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)