In vitro evaluation of antimicrobial activity of sealers and pastes used in endodontics

The antimicrobial activity of four root canal sealers (AH Plus, Sealapex, Ketac Endo, and Fill Canal), two calcium hydroxide pastes (Calen and Calasept), and a zinc oxide paste was evaluated. Seven bacterial strains were used, six of them standard; Micrococcus luteus ATCC 9341, Staphylococcus aureus ATCC 25923, Pseudomonas aeruginosa ATCC 27853, Staphylococcus epidermidis ATCC 12228, Escherichia coli ATCC 25922, and Enterococcus faecalis ATCC 10541. There was a wild strain of Streptococcus mutans isolated from saliva obtained in an adult dental clinic. Activity was evaluated using the agar diffusion method with Brain Heart Infusion agar and Müller Hinton medium seeded by pour plate. Calcium hydroxide-based sealers and pastes were either placed directly into 4.0 × 4.0 mm wells or by using absorbent paper points. The plates were kept at room temperature for 2 hr for diffusion. After incubation at 37°C for 24 hr, the medium was optimized with 0.05 g% TTC gel and inhibition haloes were measured. All bacterial strains were inhibited by all materials using the well method. However, when the materials were applied with absorbent paper points, Enterococcus faecalis was not inhibited by zinc oxide, and Pseudomonas aeruginosa was not inhibited by AH Plus, Fill Canal, and the zinc oxide-based paste. We conclude that sealers and pastes presented antimicrobial activity in vitro and culture medium optimization with 0.05 g% TTC gel facilitated observation of the inhibition haloes. Copyright © 2000 by The American Association of Endodontists.

Mineral trioxide aggregate repair of lateral root perforations

This study was conducted to observe the healing process of intentional lateral root perforation repaired with mineral trioxide aggregate (MTA). Forty-eight root canals of dogs' teeth were instrumented and filled. After partial removal of the filling, an intentional perforation was made with a bur in the lateral area of the root. The perforations were repaired with MTA or Sealapex (control group). Histological analysis occurred 30 and 180 days after treatment. Results showed no inflammation and deposition of cementum over MTA in the majority of the specimens. In the 180-day period, Sealapex exhibited chronic inflammation in all the specimens and slight deposition of cementum over the material in only three cases. In conclusion, MTA exhibited better results than the control group. Copyright © 2001 by The American Association of Endodontists.

Radiographic evaluation of periradicular repair after endodontic treatment of dog's teeth with induced periradicular periodontitis

Eighty-four root canals of premolars from six dogs were left open for 7 days, and then sealed and followed for 45 days until periradicular periodontitis developed. The root canals were then treated endodontically using 5.25% sodium hypochlorite as the irrigating solution. After instrumentation, all root canals were filled with a calcium hydroxide-based antibacterial dressing (Calen PMCC or Calasept) that was left in place for 30 days. After this period the root canals were filled with gutta-percha cones and a root canal sealer (Sealapex or AH Plus)-group I: Calen PMCC + Sealapex; group II: Calasept + Sealapex; group III: Calen PMCC + AH Plus; and group IV: Calasept + AH Plus. Periapical radiographs of the teeth were made after root canal filling and after 90, 180, 270, and 360 days. Radiographic images were digitalized by scanning, and the Mocha program was used to measure the periapical lesions. Analysis showed that the lesions of groups I to III were statistically similar reduction in size, whereas group IV had a smaller reduction in lesion size (p < 0.05). Copyright © 2001 by The American Association of Endodontists.

Calcium salts deposition in rat connective tissue after the implantation of calcium hydroxide-containing sealers

This study was conducted to observe the rat subcutaneous connective tissue reaction to implanted dentin tubes that were filled with mineral trioxide aggregate, Sealapex, Calciobiotic Root Canal Sealer (CRCS), Sealer 26, and the experimental material, Sealer Plus. The animals were sacrificed after 7 and 30 days, and the specimens were prepared for histological analysis after serial sections with a hard-tissue microtome. The undecalcified sections were examined with polarized light after staining according to the Von Kossa technique for calcium. At the tube openings, there were Von Kossa-positive granules that were birefringent to polarized light. Next to these granulations, there was irregular tissue, like a bridge, that was Von Kossa-positive. The dentin walls of the tubes exhibited a structure highly birefringent to polarized light, usually like a layer, in the tubules. These results were observed with all the studied materials, except the CRCS, which didn't exhibit any kind of mineralized structure. The results suggest that among the materials studied, the CRCS could have the least possibility of encouraging hard tissue deposition.

Apical and periapical repair of dogs' teeth with periapical lesions after endodontic treatment with different root canal sealers.

The aim of this study was to evaluate the apical and periapical repair after root canal treatment of dogs' teeth with pulp necrosis and chronic periapical lesion using different root canal sealers. After periapical lesion induction, forty-four root canals of 3 dogs were submitted to biomechanical preparation using 5.25% sodium hypochlorite as an irrigating solution. A calcium hydroxide dressing (Calen PMCC) was applied for 15 days and the root canals were filled using the lateral condensation technique with gutta-percha points and Sealapex, AH Plus or Sealer Plus for sealing. After 180 days, the animals were sacrificed by anesthetic overdose and the obtained histological sections were stained with hematoxylin-eosin for optical microscopic analysis of the apical and periapical repair. The groups filled with Sealapex and AH Plus had better histological repair (p < 0.05) than the group filled with Sealer Plus, that had unsatisfactory results.

In vitro evaluation of apical microleakage using different root-end filling materials

The objective of this study was to evaluate the apical leakage of retrograde cavities filled with Portland Cement (Concrebrás S/A-MG-Brazil), ProRoot MTA™ (Dentsply International, Johnson City, TN, USA) and Sealapex (Kerr Corporation, Orange, California, USA) with addition of zinc oxide (Odahcam Herpo Produtos Dentários Ltda, Rio de Janeiro, RJ, Brazil). Forty-two extracted single-rooted human teeth were decoronated and used for this study. The root canals were instrumented at 1.0mm short of the apical foramen using the step-back technique to an apical ISO size 60. The roots were obturated with gutta-percha points and sealer Sealapex (Kerr Corporation-USA) and then 3mm of each root apex was sectioned at a 90° angle. Ultrasonic retrograde preparation was performed with a diamond tip to 3mm depth and the roots were randomly divided into 3 groups according to the filling material: G1-Portland, G2-ProRoot MTA, G3- Sealapex zinc oxide-added cement. The root surfaces were covered with nail varnish up to 2mm from the apical foramen, immersed in simulated tissue fluid for 30 days, and then immersed in 0.2% Rhodamine B solution for 24 hours for evaluation of marginal leakage. The results showed mean leakage of 0.75, 0.35 and 0.35 for groups 1, 2 and 3, respectively; however, Kruskal-Wallis test revealed that there was no statistically significant difference among the results (p>0.05).

In vitro antimicrobial activity of endodontic sealers, MTA-based cements and Portland cement.

The aim of this study was to evaluate the antimicrobial activity of different root-end filling materials - Sealer 26, Sealapex with zinc oxide, zinc oxide and eugenol, white and gray Portland cement, white and gray MTA-Angelus, and gray Pro Root MTA - against six different microorganism strains. The agar diffusion method was used. A base layer was made using Müller-Hinton agar (MH) and wells were formed by removing the agar. The materials were placed in the wells immediately after manipulation. The microorganisms used were: Micrococcus luteus (ATCC9341), Staphylococcus aureus (ATCC6538), Escherichia coli (ATCC10538), Pseudomonas aeruginosa (ATCC27853), Candida albicans (ATCC 10231), and Enterococcus faecalis (ATCC 10541). The plates were kept at room temperature for 2 h for prediffusion and then incubated at 37 degrees C for 24 h. Triphenyltetrazolium chloride 0.05% gel was added for optimization, and the zones of inhibition were measured. Data were subjected to the Kruskal-Wallis and Dunn tests at a 5% significance level. The results showed that all materials had antimicrobial activity against all the tested strains. Analysis of the efficacy of the materials against the microbial strains showed that Sealapex with zinc oxide, zinc oxide and eugenol and Sealer 26 created larger inhibition halos than the MTA-based and Portland cements (P < 0.05). On the basis of the methodology used, it may be concluded that all endodontic sealers, MTA-based and Portland cements evaluated in this study possess antimicrobial activity, particularly the endodontic sealers.

The effect of endodontic materials on the optical density of dyes used in marginal leakage studies

The aim of this study was to determine the effect of the exposure of different endodontic materials to different dye solutions by evaluating the optical density of the dye solutions. Seventy-five plastic tubes were filled with one of the following materials: AH Plus, Sealapex, Portland cement, MTA (Angelus and Pro Root) and fifteen control plastic tubes were not. Each specimen of material and control was immersed in a container with 1 ml of each dye solution. A 0.1 ml-dye solution aliquote was removed before immersion and after 12, 24, 48 and 72 hours of each specimen immersion to record its optical density (OD) in a spectrophotometer. Statistical analysis was performed with ANOVA and Tukey tests (5%). No significant difference was found among any of the solution OD values for AH Plus cement. Portland cement promoted different OD values after 12 hours of immersion. MTA-Angelus cement presented different OD values only for 2% rhodamine B and the MTA-Pro Root cement presented different OD values in all 2% rhodamine B samples. Sealapex cement promoted a reduction in the India Ink OD values. Dye evaluation through OD seems to be an interesting method to select the best dye solution to use in a given marginal leakage study.

Antimicrobial activity of endodontic sealers based on calcium hydroxide and MTA.

The aim of this study was to evaluate the antimicrobial activity of a new root canal sealer containing calcium hydroxide (Acroseal) and the root canal sealer based on MTA (Endo CPM Sealer), in comparison with traditional sealers (Sealapex, Sealer 26 and Intrafill) and white MTA-Angelus, against five different microorganism strains. The materials and their components were evaluated after manipulation, employing the agar diffusion method. A base layer was made using Müller-Hinton agar (MH) and wells were made by removing agar. The materials were placed into the wells immediately after manipulation. The microorganisms used were: Micrococcus luteus (ATCC9341), Staphylococcus aureus (ATCC6538), Pseudomonas aeruginosa (ATCC27853), Candida albicans (ATCC 10231), and Enterococcus faecalis (ATCC 10541). The plates were kept at room temperature for 2 h for prediffusion and then incubated at 37 degrees C for 24 h. The results showed that Sealapex and its base paste, Sealer 26 and its powder, Endo CPM Sealer and its powder, white MTA and its powder all presented antimicrobial activity against all strains. Intrafill and its liquid presented antimicrobial activity against all strains except P. aeruginosa and Acroseal was effective only against M. luteus and S. aureus.

Radiopacity evaluation of root canal sealers containing calcium hydroxide and MTA

The purpose of this study was to evaluate the radiopacity of root canal sealers containing calcium hydroxide and MTA (Acroseal, Sealer 26, Sealapex, Endo CPM Sealer, Epiphany and Intrafill). Five disc-shaped specimens (10 x 1 mm) were fabricated from each material, according to the ISO 6876/2001 standard. After setting of the materials, radiographs were taken using occlusal film and a graduated aluminum stepwedge varying from 2 to 16 mm in thickness. The dental X-ray unit (GE1000) was set at 50 kVp, 10 mA, 18 pulses/s and distance of 33.5 cm. The radiographs were digitized and the radiopacity compared to that of the aluminum stepwedge using VIXWIN-2000 software (Gendex). The data (mmAl) were analyzed statistically by ANOVA and Tukey's test at the 5% significance level. Epiphany and Intrafill presented the highest radiopacity values (8.3 mmAl and 7.5 mmAl respectively, p < 0.05) followed by Sealer 26 (6.3 mmAl), Sealapex (6.1 mmAl) and Endo CPM Sealer (6 mmAl). Acroseal was the least radiopaque material (4 mmAl, p < 0.05). In conclusion, the calcium hydroxide- and MTA-containing root canal sealers had different radiopacities. However, all materials presented radiopacity values above the minimum recommended by the ISO standard. © 2009 Sociedade Brasileira de Pesquisa Odontológica.

Sealing ability of MTA used as a root end filling material: Effect of the sonic and ultrasonic condensation

Despite the excellent properties of mineral trioxide aggregate (MTA), the condensation technique may have some influence in its sealing ability. The purpose of this study was to compare the sealing ability of sonic and ultrasonic setting of MTA. Thirty-four extracted human teeth had their canals prepared and filled with Sealapex sealer and gutta-percha using the active lateral condensation technique. The teeth were rendered waterproof and apicoectomy performed at 3 mm from the apex. Root-end cavities (3.0 mm deep and 1.4 mm diameter) were prepared with diamond ultrasonic tips. The root-end cavities were filled with Pro-Root MTA® with ultrasonic vibration, sonic vibration or no vibration. The positive control group did not receive any material while the negative control group was totally rendered waterproof. After material set, the specimens were immersed in Rodhamine B for 24 h, under vacuum in the first 15 min, then washed, dried and split longitudinally for evaluating the infiltration at the dentin/material interface. Data were analyzed using ANOVA and Tukey's tests at 5% significance level. Sonic vibration promoted the lowest infiltration values (p<0.05). It was concluded that sonic vibration could be considered an efficient aid to improve the sealing ability of MTA when used as root-end filling material.

Effect of MTA-based sealer on the healing of periapical lesions

Some manufacturers have recently added specific components to improve the ease of handling and insertion material properties of MTA in order to create MTA-based sealers. Objective: The aim of this study was to evaluate the healing of periapical lesions in canine teeth after a single session of endodontic treatment with MTA Fillapex® compared with Sealapex® or Endo-CPM-Sealer®. Material and Methods: Sixty-two root canals were performed on two 1-year-old male dogs. After coronal access and pulp extirpation, the canals were exposed to the oral cavity for 6 months in order to induce periapical lesions. The root canals were prepared, irrigated with a solution of 2.5% sodium hypochlorite and filled with gutta-percha and different sealers, according to the following groups: 1) Sealapex®; 2) Endo-CPM-Sealer®; and 3) MTA Fillapex®. Some teeth with periapical lesions were left untreated for use as positive controls. Healthy teeth were used as negative controls. After 6 months, the animals were sacrificed and serial sections from the roots were prepared for histomorphologic analysis and stained with hematoxylin and eosin and the Brown and Brenn technique. The lesions were scored according to pre-established histomorphologic parameters and the scores statistically analyzed using the Kruskal-Wallis test. Results: All 3 materials produced similar patterns of healing (p>0.05); in particular, persistent inflammation and absence of complete periapical tissue healing were consistently noted. Conclusions: Preparation of the infected root canals followed by filling with the materials studied was insufficient to provide complete healing of the periapical tissues.

Antibiofilm activity, pH and solubility of endodontic sealers

Aim: To evaluate antibiofilm activity against Enterococcus faecalis, pH and solubility of AH Plus, Sealer 26, Epiphany SE, Sealapex, Activ GP, MTA Fillapex (MTA-F) and an experimental MTA-based Sealer (MTA-S). Methodology: Sealer samples were manipulated and stored for 2 or 7 days. Prepared sealers were evaluated by a modified direct contact test (DCT) for 5 h, 10 h or 15 h with biofilm previously induced on bovine dentine for 14 days. In the control group, the biofilm was not exposed to the sealers. The number of colony-forming units (CFU mL-1) in the remaining biofilm was determined. Sealer solubility was assessed by the percentage of mass loss after 15 h of immersion in distilled water. Sealer pH was measured at 5 h, 10 h and 15 h. Statistical analysis was performed using Kruskal-Wallis and Dunn or anova and Tamhane's T2 tests, at 5% significance. Results: At 2 days post-manipulation, the DCT showed that Sealapex and MTA-F were associated with a reduction in the number of bacteria in all 3 contact periods evaluated, compared with the control group (P < 0.05). At 7 days, Sealapex had the greatest antibiofilm action at 10 h and 15 h. Sealapex had the highest pH values 2 and 7 days post-manipulation. Regarding the solubility, at 2 days the highest values were observed for MTA-F, MTA-S, Sealapex and Activ GP (P < 0.05). At 7 days, MTA-S and MTA-F had greater solubility than the other materials (P < 0.05). AH Plus had the lowest solubility for both post-manipulation periods (P < 0.05). Conclusion: Sealapex and MTA-F were associated with a reduction in the number of bacteria in biofilms and had greater solubility. The high solubility and pH may be related to the antibacterial activity of these materials. © 2012 International Endodontic Journal.

Physicochemical and mechanical properties of zirconium oxide and niobium oxide modified Portland cement-based experimental endodontic sealers

Aim: To evaluate the physicochemical and mechanical properties of Portland cement-based experimental sealers (ES) with different radiopacifying agents (zirconium oxide and niobium oxide micro- and nanoparticles) in comparison with the following conventional sealers: AH Plus, MTA Fillapex and Sealapex. Methodology: The materials were tested for setting time, compressive strength, flow, film thickness, radiopacity, solubility, dimensional stability and formaldehyde release. Data were subjected to anova and Tukey tests (P < 0.05). Results: MTA Fillapex had the shortest setting time and lowest compressive strength values (P < 0.05) compared with the other materials. The ES had flow values similar to the conventional materials, but higher film thickness (P < 0.05) and lower radiopacity (P < 0.05). Similarly to AH Plus, the ES were associated with dimensional expansion (P > 0.05) and lower solubility when compared with MTA Fillapex and Sealapex (P < 0.05). None of the endodontic sealers evaluated released formaldehyde after mixing. Conclusion: With the exception of radiopacity, the Portland cement-based experimental endodontic sealers presented physicochemical properties according to the specifications no 57 ANSI/ADA (ADA Professional Product Review, 2008) and ISO 6876 (Dentistry - Root Canal Sealing Materials, 2012, British Standards Institution, London, UK). The sealers had setting times and flow ability that was adequate for clinical use, satisfactory compressive strength and low solubility. Additional studies should be carried out with the purpose of decreasing the film thickness and to determine the ideal ratio of radiopacifying agents in Portland cement-based root canal sealers. © 2013 International Endodontic Journal.

Sistema adesivo na obturação de canais radiculares: biocompatibilidade e infiltração coronária (reparação apical e periapical em dentes de cães)

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)