Failure analysis of laminated glass panels subjected to blast loads

This paper presents a rigorous and a reliable analytical procedure using finite element (FE) techniques to study the blast response of laminated glass (LG) panel and predict the failure of its components. The 1st principal stress (σ11) is used as the failure criterion for glass and the von mises stress (σv) is used for the interlayer and sealant joints. The results from the FE analysis for mid-span deflection, energy absorption and the stresses at critical locations of glass, interlayer and structural sealant are presented in the paper. These results compared well with those obtained from a free field blast test reported in the literature. The tensile strength (T) of the glass has a significant influence on the behaviour of the LG panel and should be treated carefully in the analysis. The glass panes absorb about 80% of the blast energy for the treated blast load and this should be minimised in the design.

Numerical modelling and analysis of the blast performance of laminated glass panels and the influence of material parameters

This paper presents a comprehensive numerical procedure to treat the blast response of laminated glass (LG) panels and studies the influence of important material parameters. Post-crack behaviour of the LG panel and the contribution of the interlayer towards blast resistance are treated. Modelling techniques are validated by comparing with existing experimental results. Findings indicate that the tensile strength of glass considerably influences the blast response of LG panels while the interlayer material properties have a major impact on the response under higher blast loads. Initially, glass panes absorb most of the blast energy, but after the glass breaks, interlayer deforms further and absorbs most of the blast energy. LG panels should be designed to fail by tearing of the interlayer rather than failure at the supports to achieve a desired level of protection. From this aspect, material properties of glass, interlayer and sealant joints play important roles, but unfortunately they are not accounted for in the current design standards. The new information generated in this paper will enhance the capabilities of engineers to better design LG panels under blast loads and use better materials to improve the blast response of LG panels.

Response of laminated glass panels to near field blast events

This thesis develops and applies an analytical method to treat the blast response of glass façades and studies the influence of controlling parameters such as all component materials and geometric properties, support conditions and energy absorption, and hence establishes a framework for their design for a credible blast event.

Design guidance for blast-resistant glazing

This paper reviews current design standards and test methods for blast-resistant glazing design and compares a typical design outcome with that from comprehensive finite-element (FE) analysis. Design standards are conservative and are limited to the design of relatively small glazed panels. Standard test methods are expensive, create environmental pollution, and can classify the hazard ratings of only smaller glazed panels. Here the design of a laminated glass (LG) panel is carried out according to an existing design standard, and then its performance is examined using comprehensive FE modeling and analysis. Finite-element results indicate that both glass panes crack, the interlayer yields with little damage, and the sealant joints do not fail for the designed blast load. This failure pattern satisfies some of the requirements for minimal hazard rating in the design standard. It is evident that interlayer thickness and material properties are important during the post-crack stage of an LG panel, but they are not accounted for in the design standards. The new information generated in this paper will contribute toward an enhanced blast design of LG panels.

Novel protective covering to enhance concrete resistance against projectile impact

A novel protective covering with a layered and staggered structure was proposed to protect concrete against projectile impact. Experimental study was conducted to investigate the ballistic behaviour of the concrete targets against 12.7 mm armour-piercing incendiary projectile at velocities ranging from 537.7 to 596.5 m/s. The results showed that the concrete targets with protective covering exhibited superior integrity with no damage on the distal surface, whereas the concrete targets without protective covering were fractured with penetrating cracks throughout the thickness of the target. Moreover, the protected concrete targets displayed significantly reduced penetration depth compared with the concrete targets without protective covering. The protective covering with epoxy adhesive interlayers had a bigger protection factor than that with silicone sealant interlayers, but the former suffered more severe damage than the latter.

Arresting occlusal enamel caries lesions with pit and fissure sealants

The aim of this study was to evaluate the feasibility of pit and fissure sealants and the effectiveness of the two sealant methods applied in every-day practice in public dental health care in Finland. Two sealant methods were evaluated according to their effectiveness in preventing dentin caries and sealant retention. Application time with these sealant methods was compared. The survival rate of sealed first and second molars was followed for nine and 13 year periods, respectively. Caries risk evaluation and observed increased caries risk were the basis for considering sealant application. A questionnaire, sent to all public dental health centers in Finland, monitored the attitudes of the dental profession towards sealant application and explored the current policies used as well as changes noted in the sealant application protocol. DMFT (Decayed, Missing or Filled Teeth) index values collected from the health centers were evaluated. The difference in caries rate between two methods investigated was highly significant. When compared to the glass ionomer sealant method (GIC), the effectiveness of the resin-based method (RB) in preventing dentin caries was 74% and the rate difference 3%. The relative risk for RB-sealed surfaces vs. GIC-sealed surfaces of having detectable dentin caries was 0.3 (95% CI 0.12, 0.57). The retention rate of sealants was higher with RB than GIC (P<0.001). Application of RB sealant material was less time-consuming than application of GIC sealant. Occlusal dentin caries lesions were found in 4% and proximal caries in less than 2% of sealed teeth. The majority of respondents reported application of sealants on a systematic basis along with caries-risk evaluation. Those health centers sealing over suspected or detected enamel caries had lower average DMFT index values (1.0) when compared to DMFT values (1.2) of health centers applying sealants by alternative criteria. It is concluded that the RB sealant method is more effective than the GIC sealant method in preventing dentin caries. Sealant maintenance may increase the costs of a sealant program. Occlusal caries management may be improved if the applied sealant policies are changed towards an interceptive approach i.e. applying the sealants over detected or suspected enamel caries lesions instead of sealing sound teeth in a preventive manner.

Cicatrização de anastomose colônica reforçada por esponja de colágeno revestida com fatores de coagulação (TachoSil) em ratos submetidos à quimioterapia intraperitoneal perioperatória precoce com 5-fluorouracil

A administração intraperitoneal de 5-fluorouracil (5-FU) no pós-operatório imediato reduz a recorrência local e prolonga a sobrevida dos pacientes com câncer colônico. Contudo, esse tratamento também pode prejudicar a cicatrização das anastomoses intestinais. O objetivo deste estudo foi determinar os efeitos da quimioterapia (QT) intraperitoneal (IP) pós-operatória (PO) precoce com o 5-FU e da selagem anastomótica com o TachoSil sobre o processo de cicatrização de anastomoses colônicas. Quarenta ratos foram divididos em quatro grupos (I - IV, com dez ratos em cada) e submetidos à secção do cólon esquerdo seguida por anastomose. As anastomoses dos ratos dos grupos II e IV foram cobertas com o TachoSil. Solução salina (2 ml/dia grupos I e II) ou 5-FU (20 mg/kg/dia grupos III e IV) foi administrado por via IP uma vez ao dia, desde do procedimento cirúrgico até a morte programada dos animais no quarto dia pós-operatório. Foram realizadas medidas da pressão de ruptura e análise histopatológica das anastomoses. A perda relativa de peso foi significativamente maior nos animais do grupo III comparado a todos os demais grupos (p=0,0004). Não houve diferença significativa entre os grupos no que se refere à presença de fístulas, coleções perianastomóticas, sinais de dilatação intestinal pré-anastomótica ou aderências pós-operatórias. A pressão de ruptura foi significativamente menor no grupo III comparada a todos os demais grupos (p=0,001). A neoangiogênese foi significativamente menor no grupo III comparada aos grupos I e II (p=0,05). A infiltração fibroblástica foi significativamente maior no grupo I e em comparação ao grupo III (p=0,035). Não ocorreu diferença significativa entre os grupos no que concerne à presença de infiltração de células inflamatórias e deposição de colágeno. Os dados obtidos permitem concluir que a QT IP precoce com 5-FU afetou negativamente a fase inicial da cicatrização de anastomoses colônicas. Contudo, a selagem com o TachoSil foi capaz de reverter alguns dos efeitos adversos decorrentes da QT.

智能涂胶机控制系统设计

本文介绍了一种新型涂胶机控制系统的设计,详细描述了系统的原理和硬件功能。涂胶机是汽车变速箱装配流水线上最重要的部分之一。该机除具有自动涂胶功能、自动检测报警功能外,还能与装配管理系统联网,实现网络化管理与控制功能。整个系统采用运动控制器、伺服电机等控制部件,为变速箱涂胶提供了安全可靠的质量保证。

变速箱智能涂胶机系统设计及实现

目前变速箱涂胶主要采用人工作业，本项目是为实现了该类设备的自动化而研制的智能控制系统。本文根据株州齿轮厂提出的设计要求，在查阅大量有关文献基础上，分析了涂胶的全部工艺，设计并开发了经济实用数控涂胶机，符合国情，推动了我国变速箱自动化装配线的发展。本文完成了以下研究工作和创新性成果： 系统采用一种基于PC机和运动控制卡的开放式、模块化的智能控制系统方案，用运动控制卡和交流伺服组成闭环控制系统，实现了在线编程和运动控制的并行处理。 采用模块化的结构对涂胶机实行分层控制，涂胶机采用手动和自动两种工作方式，应用先进的示教方法实现涂胶机的开放性，并且对整个涂胶机实现实时监控以及智能保护。 论文提出了一种智能保护系统方案。通过胶嘴定位系统进行位置检测，利用红外传感器进行生产区域安全防护，对伺服报警信号进行监控和设计三重限位保护等方法，切实增强了系统的安全性和稳定性。 开发了数控系统的仿真器，使用户在涂胶前就可以看到胶线的轨迹，防止发生浪费。同时开发了数控系统的执行控制器。实现了数控程序的编辑和管理，以及通过RS232串行接口接收用户离线编写的数控程序。在智能涂胶机上进行实际涂胶，涂胶效果良好。 课题开发的涂胶系统的速度为4.8米/分钟，涂胶精度为0.01毫米，已经远远超过了现场要求的涂胶精度，而且在制造和维护成本上占有很大优势，获得了用户好评。

Hydrogen-permeation characteristics of a SrCeO3-based ceramic separation membrane:Thermal, ageing and surface-modification effects

Dense ceramics with mixed protonic-electronic conductivity are of considerable interest for the separation and purification of hydrogen and as electrochemical reactors. In this work, the hydrogen permeability of a Sr_0.97Ce_0.9Yb_0.1O_{3 - δ} (SCYb) membrane with a porous Pt catalytic layer on the hydrogen feed-exposed side has been studied over the temperature range 500-804 °C employing Ar as the permeate sweep gas. A SiO₂-B₂O₃-BaO-MgO-ZnO-based glass-ceramic sealant was successfully employed to seal the membrane to the dual-chamber reactor. After 14 h of exposure to 10% H₂:90% N₂ at 804 °C, the H₂ flux reached a maximum of 33 nmol cm^{- 2} s^{- 1}, over an order of magnitude higher than that obtained on membranes of similar thickness without surface modification. The permeation rate then decreased slowly and moderately on annealing at 804 °C over a further 130 h. Thereafter, the flux was both reproducible and stable on thermal cycling in the range 600-804 °C. The results indicate an important role of superficial activation processes in the flux rate and suggest that hydrogen fluxes can be further optimised in cerate-based perovskites. © 2009 Elsevier B.V. All rights reserved.

Alkaline-earth aluminosilicate-based glass and glass-ceramic sealants for functional applications

The planar design of solid oxide fuel cell (SOFC) is the most promising one due to its easier fabrication, improved performance and relatively high power density. In planar SOFCs and other solid-electrolyte devices, gas-tight seals must be formed along the edges of each cell and between the stack and gas manifolds. Glass and glass-ceramic (GC), in particular alkaline-earth alumino silicate based glasses and GCs, are becoming the most promising materials for gas-tight sealing applications in SOFCs. Besides the development of new glass-based materials, new additional concepts are required to overcome the challenges being faced by the currently existing sealant technology. The present work deals with the development of glasses- and GCs-based materials to be used as a sealants for SOFCs and other electrochemical functional applications. In this pursuit, various glasses and GCs in the field of diopside crystalline materials have been synthesized and characterized by a wide array of techniques. All the glasses were prepared by melt-quenching technique while GCs were produced by sintering of glass powder compacts at the temperature ranges from 800−900 ºC for 1−1000 h. Furthermore, the influence of various ionic substitutions, especially SrO for CaO, and Ln2O3 (Ln=La, Nd, Gd, and Yb), for MgO + SiO2 in Al-containing diopside on the structure, sintering and crystallization behaviour of glasses and properties of resultant GCs has been investigated, in relevance with final application as sealants in SOFC. From the results obtained in the study of diopside-based glasses, a bilayered concept of GC sealant is proposed to overcome the challenges being faced by (SOFCs). The systems designated as Gd−0.3 (in mol%: 20.62MgO−18.05CaO−7.74SrO−46.40SiO2−1.29Al2O3 − 2.04 B2O3−3.87Gd2O3) and Sr−0.3 (in mol%: 24.54 MgO−14.73 CaO−7.36 SrO−0.55 BaO−47.73 SiO2−1.23 Al2O3−1.23 La2O3−1.79 B2O3−0.84 NiO) have been utilized to realize the bi-layer concept. Both GCs exhibit similar thermal properties, while differing in their amorphous fractions, revealed excellent thermal stability along a period of 1,000 h. They also bonded well to the metallic interconnect (Crofer22APU) and 8 mol% yttrium stabilized zirconium (8YSZ) ceramic electrolyte without forming undesirable interfacial layers at the joints of SOFC components and GC. Two separated layers composed of glasses (Gd−0.3 and Sr−0.3) were prepared and deposited onto interconnect materials using a tape casting approach. The bi-layered GC showed good wetting and bonding ability to Crofer22APU plate, suitable thermal expansion coefficient (9.7–11.1 × 10–6 K−1), mechanical reliability, high electrical resistivity, and strong adhesion to the SOFC componets. All these features confirm the good suitability of the investigated bi-layered sealant system for SOFC applications.

Seguimiento de áreas cruentas cubiertas con queratinocitos autólogos cultivados en suero autólogo: Estudio multicéntrico en Bogotá

En 2009 se presento la estandarización de cultivos de queratinocitos autólogos cultivados en suero autólogo. En este estudio los autores describen la efectividad de estos parches de regeneración de piel, para la cobertura de áreas cruentas con indicación de injerto de piel parcial. El porcentaje de epitelización del área cruenta fue el punto principal. Métodos: 47 pacientes fueron incluidos consecutivamente, equivalentes a 78 áreas cruentas. Las áreas fueron estratificadas según la profundidad: grupo 1:IIA (n=8) grupo 2: IIB (n=39); grupo 3,III (n=24) y grupo 4, etiología diferente: Otras (n=7). Todas las áreas fueron tratadas con injertos de queratinocitos autólogos cultivados en suero autólogo y se realizo registro fotográfico y del porcentaje de epitelización al día 5, 7, 15 y 30. Resultados: La efectividad de los injertos de queratinocitos autólogos es de 53.16% ± 46.46%. El porcentaje de epitelización es mayor para el grupo 1 (100%) y grupo 2 (62.79%) que para el grupo 3 (27.57%) y el grupo 4 (33.86%). Se encontró relación entre la interacción de las medianas del porcentaje de epitelización entre área corporal y grado de quemadura (p<0.001 KW) siendo mayor para el grupo 1 en todas las áreas, grupo 2 en cara, grupo 3 en tronco y grupo 4 en cara; y el menor porcentaje de epitelización en el grupo 3 y grupo 4 de las áreas ubicadas tronco. Conclusión: Los injertos de queratinocitos autólogos cultivados en suero autólogo son un método de cobertura eficaz para áreas cruentas producidas por quemaduras IIA y IIB independientemente del tamaño y la localización , y para las áreas cruentas pequeñas (<9cm2) de etiología diferente o grado III de profundidad. Palabras Clave: Cultivo queratinocitos, cobertura áreas cruentas, efectividad.

Chemical and Morphological Features of Dental Composite Resin: Influence of Light Curing Units and Immersion Media

Aims: The study evaluated the influence of light curing units and immersion media on superficial morphology and chemistry of the nanofilled composite resin Supreme XT (3M) through the EDX analysis and SEM evaluation. Light curing units with different power densities and mode of application used were XL 3000 (480 mW/cm(2)), Jet Lite 4000 Plus (1230mW/cm(2)), and Ultralume Led 5 (790 mW/cm(2)) and immersion media were artificial saliva, Coke(R), tea and coffee, totaling 12 experimental groups. Specimens (10 mm X 2 mm) were immersed in each respective Solution for 5 min, three times a day, during 60 days and stored in artificial saliva at 37 degrees C +/- 1 degrees C between immersion periods. Topography and chemical analysis was qualitative. Findings: Groups immersed in artificial saliva, showed homogeneous degradation of matrix and deposition of calcium at the material surface. Regarding coffee, there was a reasonable chemical degradation with loss of load particles and deposition of ions. For tea, superficial degradation occurred in specific areas with deposition of calcium, carbon. potassium and phosphorus. For Coke(R), excessive matrix degradation and loss of load particles with deposition of calcium, sodium, and potassium. Conclusion: Light curing units did not influence the superficial morphology of composite resin tested, but the immersion beverages did. Coke(R) affected material`s surface more than did the other tested drinks. Microsc. Res. Tech. 73:176-181, 2010. (c) 2009 Wiley-Liss Inc.

Estudo da viabilidade do sistema LZAS para uso como selante de PaCOS

Cells the solid oxide fuel are systems capable to directly convert energy of a chemical reaction into electric energy in clean, quiet way and if its components in the solid state differentiate of excessively the techniques for having all. Its more common geometric configurations are: the tubular one and to glide. Geometry to glide beyond the usual components (anode, cathode and electrolyte) needs interconnect and sealant. E the search for materials adjusted for these components is currently the biggest challenge found for the production of the cells. The sealants need to present chemical stability in high temperatures, to provoke electric isolation, to have coefficient of compatible thermal expansion with the excessively component ones. For presenting these characteristics the glass-ceramics materials are recommended for the application. In this work the study of the partial substitution of the ZrO2 for the Al2O3 in system LZS became it aiming at the formation of system LZAS, this with the addition of natural spodumene with 10, 20 and 30% in mass. The compositions had been casting to a temperature of 1500°C and later quickly cooled with the objective to continue amorphous. Each composition was worn out for attainment of a dust with average diameter of approximately 3μm and characterized by the techniques of DRX, FRX, MEV, dilatometric analysis and particle size analysis. Later the samples had been conformed and treated thermally with temperatures in the interval between 700-1000 °C, with platform of 10 minutes and 1 hour. The analyses for the treated samples had been: dilatometric analysis, DRX, FRX, electrical conductivity and tack. The results point with respect to the viability of the use of system LZAS for use as sealant a time that had presented good results as isolating electric, they had adhered to a material with similar α of the components of a SOFC and had presented steady crystalline phases

Avaliação da eficácia de selante ionomérico modificado por resina e escovação dentária na preservação de cárie oclusal

The purpose of this study was to evaluate the effectiveness during a twelve-month period, of resin-modified glass ionomer (Vitremer@) used as fissure sealants compared to supervised teeth brushing in the prevention of oclusal caries in permarient molars of pubIlc school children from 5 to 7 years of age. A total of 91 children participated in the study, being randomly divided up into three groups of investigation: group with sealant (n=31), group of supervised brushing (m=30), and control gorup (n=30). After 12 months, a total of 28.5% of tosses in the sample of 26 children was registered, and although there wasn t a significant diference between these losses and the groups studles (p = 0.6355), there was a considerable reduction in the sample. The results showed that none of the independentIy studied variables (present caries experience, biofilm, bleeding, sealant retention, position of the tooth in the arch, and sex) interfered in the final results, and that there was no significant difference between applying the sealant in question, perfornling supervised dental brushing, or not intervening at alI (p=0.542). These results could have been a consequence of the limitations found alI through the study, especially relating to the losses occurred because of school evasion, transfer, or because of the accident in the Marise Paiva Municipal School, Keeping students away for approximately one semester, so tht a new reseach had to be developed sos as to better clarify the effects among the treatments done there