Effect of Sm3+-Gd3+ on structural, electrical and magnetic properties of Mn-Zn ferrites synthesized via combustion route

Nanocrystalline Mn0.4Zn0.6SmxGdyFe2-(x+y)O4 (x = y = 0.01, 0.02, 0.03, 0.04 and 0.05) were synthesized by combustion route. The detailed structural studies were carried out through X-ray diffractometer (XRD), Fourier transform infrared spectroscopy (FTIR), transmission electron microscopy (TEM). The results confirms the formation of mixed spine phase with cubic structure due to the distortion created with co-dopants substitution at Fe site in Mn-Zn ferrite lattice. Further, the crystallite size increases with an increase of Sm3+-Gd3+ ions concentration while lattice parameter and lattice strain decreases. Furthermore, the effect of Sm-Gd co-doping in Mn-Zn ferrite on the room temperature electrical (dielectric studies) studies were carried out in the wide frequency range 1 GHz-5 GHz. The magnetic studies were carried out using vibrating sample magnetometer (VSM) under applied magnetic field of 1.5T and also room temperature electron paramagnetic resonance (EPR) spectra's were recorded. From the results of dielectric studies, it shows that the real and imaginary part of permittivities are increasing with variation of Gd3+ and Sm3+ concentration. The magnetic studies reveal the decrease of remnant, saturation magnetization and coercivity with increasing of Sm3+-Gd3+ ion concentration. The g-value, peak-to-peak line width and spin concentration evaluated from EPR spectra correlated with cations occupancy. The electromagnetic properties clearly indicate that these materials are the good candidates which are useful at L and C band frequency. (C) 2015 Elsevier B.V. All rights reserved.

MnFe2O4-Fe3O4 core-shell nanoparticles as a potential contrast agent for magnetic resonance imaging

In recent years, magnetic core-shell nanoparticles have received widespread attention due to their unique properties that can be used for various applications. We introduce here a magnetic core-shell nanoparticle system for potential application as a contrast agent in magnetic resonance imaging (MRI). MnFe2O4-Fe3O4 core-shell nanoparticles were synthesized by the wet-chemical synthesis method. Detailed structural and compositional charaterization confirmed the formation of a core-shell microstructure for the nanoparticles. Magnetic charaterization revealed the superparamagnetic nature of the as-synthesized core-shell nanoparticles. Average size and saturation magnetization values obtained for the as-synthesized core-shell nanoparticle were 12.5 nm and 69.34 emu g(-1) respectively. The transverse relaxivity value of the water protons obtained in the presence of the core-shell nanoparticles was 184.1 mM(-1) s(-1). To investigate the effect of the core-shell geometry towards enhancing the relaxivity value, transverse relaxivity values were also obtained in the presence of separately synthesized single phase Fe3O4 and MnFe2O4 nanoparticles. Average size and saturation magnetization values for the as-synthesized Fe3O4 nanoparticles were 12 nm and 65.8 emu g(-1) respectively. Average size and saturation magnetization values for the MnFe2O4 nanoparticles were 9 nm and 61.5 emu g(-1) respectively. The transverse relaxivity value obtained in the presence of single phase Fe3O4 and MnFe2O4 nanoparticles was 96.6 and 83.2 mM(-1) s(-1) respectively. All the nanoparticles (core-shell and single phase) were coated with chitosan by a surfactant exchange reaction before determining the relaxivity values. For similar nanoparticle sizes and saturation magnetization values, the highest value of the transverse relaxivity in the case of core-shell nanoparticles clearly illustrated that the difference in the magnetic nature of the core and shell phases in the core-shell nanoparticles creates greater magnetic inhomogeneity in the surrounding medium yielding a high value for proton relaxivity. The MnFe2O4-Fe3O4 core-shell nanoparticles exhibited extremely low toxicity towards the MCF-7 cell line. Taken together, this opens up new avenues for the use of core-shell nanoparticles in MRI.

Ultrafine graphene oxide-CoFe2O4 nanoparticle composite as T-1 and T-2 contrast agent for magnetic resonance imaging

Graphene oxide-CoFe2O4 nanoparticle composites were synthesized using a two step synthesis method in which graphene oxide was initially synthesized followed by precipitation of CoFe2O4 nanoparticles in a reaction mixture containing graphene oxide. Samples were extracted from the reaction mixture at different times at 80 degrees C. All the extracted samples contained CoFe2O4 nanoparticles formed over the graphene oxide. It was observed that the increase in the reflux time significantly increased the saturation magnetization value for the superparamagnetic nanoparticles in the composite. It was also noticed that the size of the nanoparticles increased with increase in the reflux time. Transverse relaxivity of the water protons increased monotonically with increase in the reflux time. Whereas, the longitudinal relaxivity value initially increased and then decreased with the reflux time. Graphene oxide-CoFe2O4 nanoparticle composites also exhibit biocompatibility towards the MCF-7 cell line.

The effect of carbon encapsulation on the magnetic properties of Ni nanoparticles produced by arc discharge in de-ionized water

Despite intensive research on optimizing the methods for depositing carbon encapsulated ferromagnetic nanoparticles, the effect of the carbon cages remains unclear. In the present work, the effect of the graphitic cages on the magnetization of the ferromagnetic core has been studied by comparing the magnetic properties of pure and carbon encapsulated Ni particles of the same size. The carbon encapsulated Ni particles were formed using an electric arc discharge in de-ionized water between a solid graphite cathode and an anode consisting of Ni and C in a mass ratio of Ni:C = 7:3. This method is shown to have potential for low cost production of carbon encapsulated Ni nanoparticle samples with narrow particle size distributions. X-ray diffraction (XRD) and high resolution transmission electron microscopy (HRTEM) analysis were used to study the crystallography, morphology, and size distribution of the encapsulated and pure Ni nanoparticle samples. The availability of encapsulated particles with various sizes allowed us to elucidate the role of carbon cages in size-dependent properties. Our data suggest that even though encapsulation is beneficial for protection against hostile chemical environments and for avoiding low proximity phenomena, it suppresses the saturation magnetization of the Ni cores.

Structural and magnetic properties of insulating Zn1-xCoxO thin films

Cobalt-doped ZnO (Zn1-xCoxO) thin films were fabricated by reactive magnetron cosputtering. The processing conditions were carefully designed to avoid the occurrence of Co precipitations. The films are c-axis oriented, and the solubility limit of Co in ZnO is less than 17%, determined by x-ray diffraction. X-ray photoemission spectroscopy measurements show Co ions have a chemical valance of 2+. In this paper, hysteresis loops were clearly observed for Zn1-xCoxO films at room temperature. The coercive field, as well as saturation magnetization per Co atom, decreases with increasing Co content, within the range of 0.07

La estructura y propiedades magnéticos de las nanopartículas de Fe50Ni50 obtenidas mediante el método de explosión eléctrica de hilo

[Es]Actualmente ninguna área científica es ajena a la revolución de la nanociencia; las nanopartículas atraen el interés de muchos investigadores desde el punto de vista de la ciencia fundamental y para sus aplicaciones tecnológicas. Las nanopartículas ofrecen la posibilidad de fabricar sensores que sean capaces de detectar desde un virus hasta concentraciones de substancias patógenas que no pueden ser detectadas por los métodos convencionales. Hoy en día existes 82 tratamientos contra el cáncer basadas en la utilización de nanopartículas y los materiales composite con nanopartículas se utilizan como medio de protección frente la radiación del rango de microondas. En la rama de ciencias ambientales, las nanopartículas metálicas sirven como materiales anticontaminantes. En este trabajo se ha estudiado la estructura y las propiedades magnéticas de las nanopartículas de FeNi preparadas mediante el método de explosión eléctrica de hilo. Con la técnica de Rayos–X(DRX) se ha determinado que las nanopartículas se cristalizan en un sistema cúbico FCC con un parámetro de celda de 3.596 Å, también, se ha obtenido el tamaño de dominio coherente que es de 35 nm. La muestra se ha sometido a un programa de temperatura controlada para seguir la evolución de la estructura cristalina y del tamaño del cristal, tanto en atmósfera oxidante como en vacío. Para el aprendizaje de los microscopios utilizados en este trabajo, se ha asistido al curso “Fundamentos de microscopia electrónica de barrido y microanálisis” impartido por SGIker de la UPV/EHU. Se han empleado los microscopios electrónicos SEM y TEM para obtener imágenes de gran resolución de la muestra y analizar su contenido elemental. Partiendo de las imágenes sacadas por el SEM se ha calculado el valor medio del tamaño de las partículas de la muestra, 58 nm. Mediante el Mastersizer 2000 se ha medido el tamaño de las partículas y/o agregados por método de difracción láser, disgregando la muestra todo lo posible hasta conseguir el tamaño medio que se aproxime al de una sola partícula, 100nm. Por último, para la caracterización magnética se ha servido del VSM que mide el momento magnético de una muestra cuando ésta vibra en presencia de un campo magnético estático, consiguiendo una imanación de saturación de 125 emu/g. Hemos fabricado y caracterizado las nanopartículas magnéticas de hierro-níquel y los resultados obtenidos han sido enviados a un congreso especializado de ciencia de materiales (ISMANAM - 2013, Italia).

Preparação e caracterização de microesferas poliméricas à base de metacrilato de glicidila e divinilbenzeno com propriedades magnéticas

Nesta Dissertação, foram sintetizadas microesferas poliméricas com propriedades magnéticas à base de metacrilato de glicidila e divinilbenzeno pela técnica de polimerização em suspensão. O material utilizado para conferir as propriedades magnéticas ao copolímero foi magnetita sintetizada no laboratório. Foram estudados os efeitos da modificação da magnetita com ácido oleico, da velocidade de agitação, do teor de agente reticulante, do teor de material magnético adicionado e do teor de agente de suspensão sobre as características das partículas poliméricas obtidas. As microesferas foram caracterizadas quanto ao seu aspecto morfológico, à estabilidade térmica, à incorporação de material magnético e quanto às suas propriedades magnéticas. A quantidade de partículas de ferro incorporadas foi afetada pela velocidade de agitação durante a síntese, pelo teor de material magnético adicionado, pela fase de dispersão do material magnético e pelo teor de monômeros no copolímero. A estabilidade térmica dos copolímeros foi afetada, principalmente, pelo teor de material magnético incorporado e pelo teor de monômeros, levando em consideração resinas com a mesma quantidade de material magnético adicionado. A magnetização de saturação para as microesferas foi afetada pelo teor de material magnético incorporado. A modificação da superfície da magnetita com ácido oleico foi considerada importante para a incorporação do material magnético na matriz do copolímero.Partículas poliméricas magnéticas com comportamento superparamagnéticos foram obtidas com morfologia esférica e magnetização de saturação de 7,11 (emu/g), utilizando razão molar de monômeros de 50/50 %, 1 % de PVA, 20 % de magnetita modificada com ácido oleico adicionada à fase orgânica e velocidade de agitação mecânica de 500 rpm

Síntese e caracterização de copolímeros à base de poli(metacrilato de metila) e divinilbenzeno com propriedades magnéticas

Nesta dissertação, foram sintetizados copolímeros à base de poli(metacrilato de metila) (PMMA), divinilbenzeno (DVB) com propriedades magnéticas pela técnica de polimerização em suspensão. O material utilizado para conferir propriedade magnética foi o ferro. Foi estudada a influência das variáveis reacionais para a formação de microesferas (ordem de adição das fases orgânica e aquosa e a dispersão do ferro antes e após a pré-polimerização), o efeito da concentração de ferro adicionado na polimerização, a influência da razão molar MMA/DVB na formação do copolímero, o efeito do tipo de agente de suspensão e a velocidade de agitação para a síntese dos copolímeros. Os copolímeros foram caracterizados quanto à morfologia, estabilidade térmica, teor de ferro incorporado, distribuição de tamanho de partículas, propriedades magnéticas, área superficial, volume e tamanho de poros. As análises de propriedades magnéticas mostraram que os materiais obtidos não apresentaram ciclos de histerese, estando assim próximos de um material com propriedades superparamagnéticas, com magnetização de saturação entre 8,0 e 13,0 emu/g. Os copolímeros sintetizados com velocidade de agitação 500 RPM, temperaturade 90 C, tempo de polimerização de 24h, monômeros MMA/DVB 50/50 (% molar); razão volumétrica fase orgânica/fase aquosa 1/3, diluente heptano, grau de diluição 100% apresentaram melhor controle morfológico, melhor magnetização de saturação, tamanho de partículas menores e maior tamanho de poros

Spin wave resonance in ferromagnetic films

The objective of this investigation has been a theoretical and experimental understanding of ferromagnetic resonance phenomena in ferromagnetic thin films, and a consequent understanding of several important physical properties of these films. Significant results have been obtained by ferromagnetic resonance, hysteresis, torque magnetometer, He ion backscattering, and X-ray fluorescence measurements for nickel-iron alloy films.

Taking into account all relevant magnetic fields, including the applied, demagnetizing, effective anisotropy and exchange fields, the spin wave resonance condition applicable to the thin film geometry is presented. On the basis of the simple exchange interaction model it is concluded that the normal resonance modes of an ideal film are expected to be unpinned. The possibility of nonideality near the surface of a real film was considered by means of surface anisotropy field, inhomogeneity in demagnetizing field and inhomogeneity of magnetization models. Numerical results obtained for reasonable parameters in all cases show that they negligibly perturb the resonance fields and the higher order mode shapes from those of the unpinned modes of ideal films for thicknesses greater than 1000 Å. On the other hand for films thinner than 1000 Å the resonance field deviations can be significant even though the modes are very nearly unpinned. A previously unnoticed but important feature of all three models is that the interpretation of the first resonance mode as the uniform mode of an ideal film allows an accurate measurement of the average effective demagnetizing field over the film volume. Furthermore, it is demonstrated that it is possible to choose parameters which give indistinguishable predictions for all three models, making it difficult to uniquely ascertain the source of spin pinning in real films from resonance measurements alone.

Spin wave resonance measurements of 81% Ni-19% Fe coevaporated films 30 to 9000 Å thick, at frequencies from 1 to 8 GHz, at room temperature, and with the static magnetic field parallel and perpendicular to the film plane have been performed. A self-consistent analysis of the results for films thicker than 1000 Å, in which multiple excitations can be observed, shows for the first time that a unique value of exchange constant A can only be obtained by the use of unpinned mode assignments. This evidence and the resonance behavior of films thinner than 1000 Å strongly imply that the magnetization at the surfaces of permalloy films is very weakly pinned. However, resonance measurements alone cannot determine whether this pinning is due to a surface anisotropy, an inhomogeneous demagnetizing field or an inhomogeneous magnetization. The above analysis yields a value of 4πM=10,100 Oe and A = (1.03 ± .05) x 10^-6 erg/cm for this alloy. The ability to obtain a unique value of A suggests that spin wave resonance can be used to accurately characterize the exchange interaction in a ferromagnet.

In an effort to resolve the ambiguity of the source of pinning of the magnetization, a correlation of the ratio of magnetic moment and X-ray film thickness with the value of effective demagnetizing field 4πNM as determined from resonance, for films 45 to 300 Å has been performed. The remarkable agreement of both quantities and a comparison with the predictions of five distinct models, strongly imply that the thickness dependence of both quantities is related to a thickness dependent average saturation magnetization, which is far below 10,100 Oe for very thin films. However, a series of complementary experiments shows that this large decrease of average saturation magnetization cannot be simply explained by either oxidation or interdiffusion processes. It can only be satisfactorily explained by an intrinsic decrease of the average saturation magnetization for very thin films, an effect which cannot be justified by any simple physical considerations.

Recognizing that this decrease of average saturation magnetization could be due to an oxidation process, a correlation of resonance measurements, He ion backscattering, X-ray fluorescence and torque magnetometer measurements, for films 40 to 3500 Å thick has been performed. On basis of these measurements it is unambiguously established that the oxide layer on the surface of purposefully oxidized 81% Ni-19% Fe evaporated films is predominantly Fe-oxide, and that in the oxidation process Fe atoms are removed from the bulk of the film to depths of thousands of angstroms. Extrapolation of results for pure Fe films indicates that the oxide is most likely α-Fe₂O₃. These conclusions are in agreement with results from old metallurgical studies of high temperature oxidation of bulk Fe and Ni-Fe alloys. However, X-ray fluorescence results for films oxidized at room temperature, show that although the preferential oxidation of Fe also takes place in these films, the extent of this process is by far too small to explain the large variation of their average saturation magnetization with film thickness.

Effects of magnetostriction and superlattice formation in ferromagnetic thin films

The contribution to the magnetic uniaxial perpendicular anisotropy which arises from substrate constraint through magnetostrictive effects has been measured in Ni-Fe and Ni-Co thin films evaporated on substrates at room temperature. This was accomplished by measuring the perpendicular anisotropy before and after removal of the film from the substrate. Data are given for the fcc crystal structure regions of both alloy systems, but data for Ni-Co include compositions with less than 60% Ni which have a small percentage of the hcp phase mixed with the fcc phase. The constraint contribution to the perpendicular anisotropy correlates well with the value of the bulk magnetostriction constant using the equation ∆K_˔=3/2λ_sσ. Measured values of isotropic stress for films thicker than 600 Å were 1.6 x 10¹⁰ dyn/cm². In films less than 600 Å thick the isotropic stress decreased with decreasing thickness. After removal of the films from the substrates, the measured perpendicular anisotropy deviated from the expected geometrical shape anisotropy near pure Ni in both alloys. This indicates that additional significant sources of anisotropy exist at these compositions.

The effect of substrate constraint on the crystalline anisotropy K₁ of Ni-Fe epitaxial films has been studied by use of a film removal technique, which involves the evaporation of an epitaxial layer of LiF on MgO, the epitaxial growth of the metallic film on the LiF, and the stripping of the film with water soluble tape. Films ranging in composition from 50% to 100% Ni have been studied. For compositions below 90% Ni the experimental values agree reasonably well with the first order theoretical prediction, ∆K₁=[-9/4(C₁₁-C₁₂)λ² 100+9/2C₄₄λ²111].

In order to compare the magnetic properties of epitaxial thin films more completely with the properties of bulk single crystals, Ni-Fe films ranging in composition from 60% to 90% Ni, which were evaporated epitaxially on (100) MgO substrates, have been subsequently annealed at 400°C in a vacuum of less than 10^-7 Torr to form the ordered Ni₃Fe structure near the 75% composition. This ordered structure has been confirmed by electron diffraction.

The saturation magnetization at Ni₃Fe increased about 6% with ordering which is in good agreement with previous bulk data. Measurements of the magnetocrystalline anisotropy energy K₁ for the epitaxial films show the same large changes with ordering as observed in bulk single crystal samples. In the (001) plane the magnetostriction constants ^λ100, ^λ111 are directly related to the induced anisotropy due to a uniform uniaxial strain in the [100] and [110] directions respectively. Assuming that the elastic constants of a film are the same as in bulk material and are unchanged by ordering, the changes in strain sensitivity with ordering for the epitaxial films are found to be in good agreement with values predicted from bulk data. The exchange constant A as measured by ferromagnetic resonance has been measured at the Ni₃Fe composition and found to increase 25% with ordering. This seems to indicate a significant increase in the Curie temperature which has only been inferred indirectly for bulk material.

Preparação e caracterização de microesferas poliméricas com morfologia casca-núcleo e propriedades magnéticas à base de estireno e divinilbenzeno

Foram sintetizadas microesferas poliméricas com propriedades magnéticas e morfologia casca-núcleo por meio da técnica de polimerização em suspensão em duas etapas. O núcleo foi constituído por poli(estireno-co-divinilbenzeno) e magnetita modificada com ácido oleico. Foi avaliada a influência da velocidade de agitação e da concentração de iniciador sobre as características das microesferas utilizadas como núcleo (morfologia, tamanho de partículas, propriedades magnéticas e estabilidade térmica). A casca foi constituída por poli(estireno-co-divinilbenzeno) sem material magnético. Foi avaliado o método de adição da emulsão dos monômeros formadores da casca e o tempo de inchamento dos núcleos na emulsão. As microesferas casca-núcleo foram caracterizadas quanto ao seu aspecto morfológico e à estabilidade térmica. Os núcleos não apresentaram ciclos de histerese, estando assim próximos de um material com propriedades superparamagnéticas. O copolímero sintetizado com a maior velocidade de agitação e a menor concentração de iniciador foi o que apresentou o maior teor de ferro incorporado (3,317 %), a maior magnetização de saturação (2,99 emu/g) e o menor diâmetro médio de partículas (81 m). As microesferas casca-núcleo apresentaram apenas um estágio de degradação e as suas Tmáx foram menores do que a do núcleo. O mapa composicional de ferro confirmou a presença de magnetita na superfície das microesferas casca-núcleo

Síntese e caracterização de microesferas poliméricas reticuladas à base de poli(ácido metacrílico) contendo nanopartículas magnéticas de ferritas de manganês

As nanopartículas de ferritas de manganês (MnFe2O4) tem sido de grande interesse por causa de suas notáveis propriedades magnéticas doces (baixa coercividade e moderada magnetização de saturação) acompanhada com boa estabilidade química e dureza mecânica. A formação de materiais híbridos/compósito estabiliza as nanopartículas magnéticas (NPMs) e gera funcionalidades aos materiais. Entretanto, não foi encontrada na literatura uma discussão sobre a síntese e as propriedades de polímeros polares reticulados à base de ácido metacrílico contendo ferritas de manganês na matriz polimérica. Assim, o objetivo desta Dissertação foi produzir partículas esféricas poliméricas reticuladas, com boas propriedades magnéticas, à base de ácido metacrílico, estireno, divinilbenzeno e ferritas de manganês. Neste trabalho, foram sintetizados compósitos de ferrita de manganês (MnFe2O4) dispersa em copolímeros de poli(ácido-metacrílico-co-estireno-co-divinilbenzeno), via polimerização em suspensão e em semi-suspensão. Foram variados os teores de ferrita (1% e 5%) e a concentração do agente de suspensão (0,2% e 5%). Além disso, foram testadas sínteses contendo a fase orgânica pré-polimerizada, e também a mistura da ferrita na fase orgânica (FO), antes da etapa da polimerização em suspensão. Os copolímeros foram analisados quanto as suas morfologias - microscopia óptica; propriedades magnéticas e distribuição das ferritas na matriz polimérica - VSM, SEM e EDS-X; propriedades térmicas TGA; concentração de metais presentes na matriz polimérica absorção atômica. As ferritas foram avaliadas quanto à cristalografia XRD. A matriz polimérica foi avaliada pela técnica de FTIR. As amostras que foram pré-polimerizadas e as que além de pré-polimerizadas foram misturadas as ferritas de manganês na FO, apresentaram as melhores propriedades magnéticas e uma incorporação maior da ferrita na matriz polimérica. Essas rotas sintéticas fizeram com que os copolímeros não apresentassem aglomeração, e também minimizou a presença de ferritas na superfície das microesferas. Em geral, todos os copolímeros obtidos apresentaram as características de materiais magneticamente doces além do superparamagnetismo. Foi constatado que o aumento da concentração do PVA e a diminuição da concentração da ferrita fazem com que os diâmetros das microesferas decresçam. Os resultados de TGA e DTG mostraram que ao misturar as ferritas na FO, a concentração de material magnético na matriz polimérica aumenta cerca de 10%. Entretanto, somente a amostra PM2550, pré-polimerizada e com as ferritas misturadas na FO (5% de ferrita e 0,2% de PVA), apresentou potencial aplicação. Isso porque as ferritas não ficaram expostas na superfície das microesferas, ou seja, o material magnético fica protegido de qualquer ação externa

GdFeCo／TbFeCo磁超分辨磁光记录薄膜研究

用磁控溅射法制备了GdFeCo／TbFeCo交换耦合两层薄膜，利用不同温度的克尔磁滞回线和VSM磁滞回线研究了读出层（GdFeCo）变温磁化方向变化过程．结果表明，随温度升高读出层从平面磁化转变为垂直磁化，交换耦合两层薄膜具有中心孔探测磁超分辨的基本性能．转变过程主要受饱和磁化强度（Ms）的影响，在GdFeCo的补偿温度附近，读出层的磁化强度较小，退磁场能也较小，在交换耦合的作用下，使读出层（GdFeCo）的磁化方向发生转变．磁化方向的转变在75℃～125℃的温度范围内变化较快．

Synthesis and characterization of room-temperature ferromagnetism in Fe- and Ni-co-doped In2O3

Observation of room-temperature ferromagnetisin in Fe- and Ni-co-doped In2O3 samples (In0.9Fe0.1-xNix)(2)O-3 (0 <= x <= 0.1) prepared by citric acid sol-gel auto-igniting method is reported. All of the samples with intermediate x values are ferromagnetic at roomtemperature. The highest saturation magnetization (0.453 mu B/Fe + Ni ions) moment is reached in the sample with x = 0.04. The highest solubility of Fe and Ni ions in the In2O3 lattice is around 10 and 4 at%, respectively. The 10 at% Fe-doped sample is found to be weakly ferromagnetic, while the 10at% Ni-doped sample is paramagnetic. Extensive structure including Extended X-ray absorption fine structure (EXAFS), magnetic and magneto-transport including Hall effects studies on the samples indicate the observed ferromagnetism is intrinsic rather than from the secondary impurity phases. (c) 2007 Elsevier Ltd. All rights reserved.

Optimizing the Curie temperature of pseudo-binary RxR2-x ' Fe-17 (R, R ' = rare earth) for magnetic refrigeration

Several pseudo-binary RxR2-x'Fe-17 alloys (with R = Y, Ce, Pr, Gd and Dy) were synthesized with rhombohedral Th2Zn17-type crystal structure determined from x-ray and neutron powder diffraction. The choice of compositions was done with the aim of tuning the Curie temperature (T-C) in the 270 +/- 20 K temperature range, in order to obtain the maximum magneto-caloric effect around room temperature. The investigated compounds exhibit broad isothermal magnetic entropy changes, Delta S-M(T), with moderate values of the refrigerant capacity, even though the values of Delta S-M(Peak) are relatively low compared with those of the R2Fe17 compounds with R = Pr or Nd. The reduction on the Delta S-M(Peak) is explained in terms of the diminution in the saturation magnetization value. Furthermore, the Delta S-M(T) curves exhibit a similar caret-like behavior, suggesting that the magneto-caloric effect is mainly governed by the Fe-sublattice. A single master curve for Delta S-M/Delta S-M(Peak)(T) under different values of the magnetic field change are obtained for each compound by rescaling of the temperature axis.