Evaluation of the physicochemical properties and push-out bond strength of mta-based root canal cement

Aim: This study investigated the flowability, setting time, pH, calcium release and bond strength of a MTA-based cement (MTA Fillapex®) compared to AH Plus and Sealapex. Materials and methods: For the flowability test, the ISO 6876:2001 specification was utilized and for the setting time test, the ASTM C266-03 specification was utilized. For the pH and calcium release measurements, 10 samples were prepared for each group and analyzed for several different periods. For the push-out test, dentin disks were distributed into three groups, according to the cement utilized and into three subgroups, according to the root third (n = 10). After obturation, the specimens underwent push-out testing. The data were compared statistically using a significance level of 5%. Results: The flowability of all materials was found to be similar (p > 0.05). The setting times were different among the groups tested (MTA Fillapex < Sealapex < AH Plus) (p < 0.05). At days 7 and 28, the MTA Fillapex presented the higher pH values (p < 0.05). At 24 hours and at 14 days, the calcium release of the MTA Fillapex was similar to that of Sealapex (p > 0.05). AH Plus presented the lowest pH and calcium release values (p < 0.05). In all root thirds, the adhesion to the dentin of the MTA Fillapex and Sealapex were significantly lower than that of AH Plus (p < 0.05). Conclusion: MTA Fillapex and Sealapex presented several similar properties and both were found to be different than AH Plus. Clinical significance: This study evaluated the physicochemical and mechanical properties of new MTA-based root canal cement, in order to use this scaler in root canal fillings. MTA Fillapex showed satisfactory properties for clinical use.

Qualitative SEM/EDS analysis of microleakage and apical gap formation of adhesive root-filling materials

Objective: The aim of this study was to compare the correspondence between gap formation and apical microleakage in root canals filled with epoxy resin-based (AH Plus) combined or not with resinous primer or with a dimethacrylate-based root canal sealer (Epiphany). Material and Methods: Thirty-nine lower single-rooted human premolars were filled by the lateral condensation technique (LC) and immersed in a 50-wt% aqueous silver nitrate solution at 37 degrees C (24 h). After longitudinal sectioning, epoxy resin replicas were made from the tooth specimens. Both the replicas and the specimens were prepared for scanning electron microscopy (SEM). The gaps were observed in the replicas. Apical microleakage was detected in the specimens by SEM/energy dispersive spectroscopy (SEM/EDS). The data were analyzed statistically using an Ordinal Logistic Regression model and Analysis of Correspondence (alpha=0.05). Results: Epiphany presented more regions containing gaps between dentin and sealer (p<0.05). There was correspondence between the presence of gaps and microleakage (p<0.05). Microleakage was similar among the root-filling materials (p>0.05). Conclusions: The resinous primer did not improve the sealing ability of AH Plus sealer and the presence of gaps had an effect on apical microleakage for all materials.

Periapical repair after root canal filling with different root canal sealers

The aim of this study was to evaluate periapical repair after root canal filling with different endodontic sealers. Sixty-four root canals from dog´s teeth were filled, divided into 4 groups (n=16). Root canals were instrumented with K-type files and irrigated with 1% sodium hypochlorite solution. Root canals were filled in the same session by active lateral condensation of the cones and sealers: Intrafill, AH Plus, Roeko Seal and Resilon/Epiphany System. After 90 days, the animals were euthanized and the tissues to be evaluated were processed and stained with hematoxylin and eosin. For histopathological analysis, the following parameters were evaluated: inflammatory process, mineralized tissue resorption, and apical mineralized tissue deposition. Histopathological analysis demonstrated that Intrafill had less favorable results in terms of apical and periapical repair, compared to the other sealers (p<0.05). AH Plus, Roeko Seal, and Epiphany sealers had similar and satisfactory results (p>0.05). In conclusion, AH Plus and the materials Roeko Seal and Epiphany are good options for clinical use in Endodontics.

Influence of the length of remaining root canal filling and post space preparation on the coronal leakage of Enterococcus faecalis

This study evaluated the sealing ability of different lengths of remaining root canal filling and post space preparation against coronal leakage of Enterococcus faecalis. Forty-one roots of maxillary incisors were biomechanically prepared, maintaining standardized canal diameter at the middle and coronal thirds. The roots were autoclaved and all subsequent steps were undertaken in a laminar flow chamber. The canals of 33 roots were obturated with AH Plus sealer and gutta-percha. The root canal fillings were reduced to 3 predetermined lengths (n=11): G1=6 mm, G2=4 mm and G3=2 mm. The remaining roots served as positive and negative controls. Bacterial leakage test apparatuses were fabricated with the roots attached to Eppendorf tubes keeping 2 mm of apex submerged in BHI in glass flasks. The specimens received an E. faecalis inoculum of 1 x 107 cfu/mL every 3 days and were observed for bacterial leakage daily during 60 days. Data were submitted to ANOVA, Tukey's test and Fisher's test. At 60 days, G1 (6 mm) and G2 (4 mm) presented statistically similar results (p>0.05) (54.4% of specimens with bacterial leakage) and both groups differed significantly (p<0.01) from G3 (2 mm), which presented 100% of specimens with E. faecalis leakage. It may be concluded that the shortest endodontic obturation remnant leaked considerably more than the other lengths, although none of the tested conditions avoids coronal leakage of E. faecalis.

In vitro analysis of thermocompaction time and gutta-percha type on quality of main canal and lateral canals filling

The aim of this study was to evaluate the quality of filling in main and lateral root canals performed with the McSpadden technique, regarding the time spent on the procedure and the type of gutta-percha employed. Fifty simulated root canals, made with six lateral canals placed two apiece in the cervical, middle and apical thirds of the root, were divided into 5 groups. Group A: McSpadden technique with conventional gutta-percha, performed with sufficient time for canal filling; Group B: McSpadden technique with conventional gutta-percha, performed in twice the mean time used in Group A; Group C: McSpadden technique with TP gutta-percha, performed with sufficient time for canal filling; Group D: McSpadden technique with TP gutta-percha, performed in twice the mean time used in Group C; Group E: lateral condensation technique. Images of the filled root canals were taken using a stereomicroscope and analyzed using the Leica QWIN Pro software for filling material flow, gutta-percha filling extension and sealer flow. Data were analyzed by analysis of variance (ANOVA) and Tukey test (p < 0.05). The best values of penetration in lateral canals in the middle third occurred in the groups where TP gutta-percha was used. However, in the apical third, group B showed the best values. Although a longer time of compactor use allows greater penetration of the filling material into the lateral canals, the presence of voids resulted in bad quality radiographic images, suggesting porosity. The best quality of filling material was observed in Group A (McSpadden technique with conventional Gutta-Percha, performed with sufficient time for root canal filling).

pH, Calcium Ion Release, and Setting Time of an Experimental Mineral Trioxide Aggregate-based Root Canal Sealer

Introduction: An experimental mineral trioxide aggregate sealer (MTAS) has been developed for use as a root canal sealer. The aim of this study was to evaluate the setting time, pH, and calcium ion release of MTAS compared with white Portland cement (CPB-40; Votorantin Cimentos, Camargo Correa SA, Pedro Leopoldo, MG, Brazil), white MTA Angelus (MTA; Angelus, Londrina, PR, Brazil), and AH Plus (Dentsply DeTrey, Konstanz, Germany). Methods: For the evaluation of setting time, each material was analyzed using Gilmore-type needles. Polyethylene tubes with the materials were immersed in distilled water for the measurement of pH (digital pH meter) and calcium release (atomic absorption spectrophotometry). The evaluations were performed at 3, 6, 12, 24, and 48 hours and 7, 14, and 28 days. Data were analyzed by analysis of variance and the Tukey test at 5% significance level. Results: MTAS showed higher calcium release at all experimental periods, a greater increase in pH up to 48 hours and the longest setting time. Conclusions: MTAS presented favorable properties for its indication as a root canal sealer. (J Endod 2011;37:844-846)

Evaluation of pH and Calcium Ion Release of Root-end Filling Materials Containing Calcium Hydroxide or Mineral Trioxide Aggregate

Introduction: To evaluate calcium ion release and pH of Sealer 26 (S26) (Dentsply, Rio de Janeiro, RJ, Brazil), white mineral trioxide aggregate (MTA), Endo CPM Sealer (CPM1) (EGEO SRL Bajo licencia MTM Argentina SA, Buenos Aires, Argentina), Endo CPM Sealer in a thicker consistency (CPM 2), and zinc oxide and eugenol cement (ZOE). Methods: Material samples (n = 10) were placed in polyethylene tubes and immersed in 10 mL of distilled water. After 3, 6,12,24, and 48 hours and 7,14, and 28 days, the water pH was determined with a pH meter, and calcium release was assessed by atomic absorption spectrophotometry. An empty tube was used as the control group. Results: The control group presented a pH value of 6.9 at all studied periods and did not show the presence of calcium ion. S26 presented greater hydroxyl ion release up to 12 hours (p < 0.05). From 24 hours until 28 days, S26, MTA, CPM1, and CPM2 had similar results. in ail periods, ZOE presented the lowest hydroxyl ion release. CPM1, followed by CPM2, released the most calcium ions until 24 hours (p < 0.05). Between 48 hours and 7 days, CPM1 and CPM2 had the highest release. A greater calcium ion release was observed for CPM2, followed by CPM1 at 14 days and for S26, CPM1, and CPM2 at 28 days. ZOE released the least calcium ions in all periods. Conclusion: Sealer 26, MTA, and Endo CPM sealer at normal or thicker consistency release hydroxyl and calcium ions. Endo CPM sealer may be an alternative as root-end filling material. (J Endod 2009;35:1418-1421)

Physicochemical Properties of Methacrylate Resin-based Root Canal Sealers

Introduction: This study assessed in vitro the physicochemical properties of 2 methacrylate resin-based sealers (Epiphany SE and Hybrid Root SEAL), comparing the results with a well-established epoxy resin-based sealer (AH Plus). Methods: Five samples of each material were used for each test (setting time, flow, radiopacity, dimensional change after setting, and solubility) according to American National Standards Institute/American Dental Association (ANSI/ADA) Specification 57. The samples were assigned to 3 groups: I, AH Plus; II, Epiphany SE; and III, Hybrid Root SEAL. The distilled and deionized water used at the solubility test was submitted to atomic absorption spectrometry to observe the presence of Ca2+, K+, Ni2+, and Zn2+ ions. In addition, the surface morphology of the specimens was analyzed by means of scanning electron microscopy (SEM). Statistical analysis was performed by using one-way analysis of variance and Tukey-Kramer test (P < .05). Results: Flow, radiopacity, and solubility of all sealers were in accordance with ANSI/ADA. The setting time of Hybrid Root SEAL did not agree with ANSUADA requirements. The dimensional change of all sealers was greater than the values considered acceptable by ANSI/ADA. The spectrometry analysis showed significant Ca2+ ions release for AH Plus. In SEM analysis, Hybrid Root SEAL presented spherical monomers with inferior size than AH Plus and Epiphany SE. Conclusions: It might be concluded that physicochemical properties of the tested sealers conformed to ANSI/ADA (2000) standardization, except for the setting time of Hybrid Root SEAL and the dimensional change of all sealers, which did not fulfill the ANSI/ADA requirements. (J Endod 2010;36:1531-1536)

Push-out strength of methacrylate resin-based sealers to root canal walls

P>Aim To assess the push-out strength of Epiphany SE, Epiphany and Hybrid Root SEAL to the dentine walls of root canals. Methodology Sixty roots of canines were prepared and distributed to six groups (n = 10) according to the filling material: GI - Epiphany SE, GII - Epiphany primer and sealer, GIII - Epiphany primer, sealer and resinous solvent, GIV - Clearfil DC Bond and Epiphany sealer, GV - Clearfil, Epiphany sealer and solvent and GVI - Hybrid Root SEAL. Resilon cones were used in all groups. Roots were sectioned transversally to obtain three slices from each third. One slice was subjected to the push-out test (MPa), and results were analysed by anova and Tukey`s test (P < 0.05). The other two slices were prepared for scanning electron microscopy (SEM). Failure mode was also analysed. Results A statistically significant difference (P < 0.05) occurred between Hybrid Root SEAL (5.27 +/- 2.07) and the other materials, GI (0.40 +/- 0.23), GII (0.78 +/- 0.45), GIII (0.57 +/- 0.28), GIV (0.40 +/- 0.24) and GV (0.50 +/- 0.41), which did not differ significantly from each other (P > 0.05). Adhesive failures predominated in groups I, II, IV and V, whilst mixed and cohesive failures were the most frequent in groups III and VI, respectively. There were gaps in the adhesive interface of GI and GII, continuity areas of the filling material with dentine in GIV and GV and good adaptation of the interface of GVI. Conclusion Hybrid Root SEAL had greater push-out strength to root canal dentine than Epiphany SE and Epiphany. The use of primer, solvent and adhesive system did not influence the adhesion of Epiphany.

Laboratory evaluation of the physicochemical properties of a new root canal sealer based on Copaifera multijuga oil-resin

Aim To compare a new root canal sealer based on Copaifera multijuga oil-resin (Biosealer) using three other established sealers (Sealer 26 (R), Endofill (R) and AH plus (R)) in terms of their physicochemical properties. Methodology The study was carried out according to the requirements of Specification Number 57 of the American Dental Association (ADA) and consisted of the following tests: setting time, flow, film thickness, dimensional stability, radiopacity and solubility/disintegration. Data were analysed statistically using anova and Tukey`s test for multiple comparisons. The significance level was set at 5% for all analyses. Results Sealer 26 (R) and AH Plus (R) had the longest setting time (P < 0.05). All materials presented flow in with the ADA`s guidelines. Regarding film thick-ness, Sealer 26 (R) did not have a satisfactory performance, as it had a higher mean value than the maximum allowed by the ADA (0.05 mm), being significantly different from the other materials (P < 0.05), which had mean values for film thickness in accordance with the ADA`s recommendations. Regarding the solubility and disintegration, only Endofill (R) did not meet the ADA`s specifications and presented the worst results of all materials (P < 0.05). Sealer 26 (R) presented the greatest dimensional changes and differed significantly from all other sealers (P < 0.05). Biosealer had the lowest radiopacity values and was significantly different from the other sealers (P < 0.05). Conclusion The experimental sealer based on Copaifera multijuga oil-resin presented satisfactory results in the physicochemical tests required by the ADA.

Apical limit of root canal filling and its relationship with success on endodontic treatment of a mandibular molar: 11-year follow-up

Objective. This article discusses the relationship between apical limit of root canal filling and success on endodontic treatment of a mandibular molar. Study design. A mandibular right first molar with vital pulp was endodontically treated, and 3 years later periapical lesions on mesial and distal roots were detected. The canals were retreated and obturated to the same levels as in the previous treatment. Results. An 8-year radiographic follow-up showed repair of the periapical lesions on both roots. Conclusions. Results suggest that the apical limit of obturation seems to have no influence in the repair of periapical tissues in mandibular molars. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2011; 112: e48-e50)

Assessment of the biocompatibility of Epiphany root canal sealer in rat subcutaneous tissues

Objective. The aim of this study was to evaluate the biocompatibility of the root canal sealer Epiphany in rat subcutaneous tissues. Study design. Polyethylene tubes were filled with the sealer (I: Epiphany; II: photoactivated Epiphany; III: Epiphany associated with self-etch primer; IV: photoactivated Epiphany associated with primer; and V: control group) and later implanted into 4 different regions of the dorsum of 15 adult male rats (Rattus novergicus, Albinus Wistar). After 7, 21, and 42 days, 5 animals were killed, obtaining 4 samples per group, in addition to the control group, at each analyzed time. Results. In all periods, Epiphany induced a mild inflammatory reaction. However, in group II, in which the primer was not used, extensive necrosis and a moderate to intense inflammatory reaction were observed, mainly after 7 and 21 days. Conclusion. Epiphany sealer appears biocompatible when tested on rat subcutaneous tissues.

Histopathological and histomicrobiological study of root canal therapy medication, comparison of calcium hydroxide versus gutta-percha with zinc oxide/eugenol in the teeth of dogs

The presence of microorganisms in dental structures with experimentally induced necrosis was evaluated. The materials were tested to evaluate their antimicrobial activity and tissue repair efficacy. Four dogs were used in this experiment, with a total of 64 roots of premolar teeth, divided into three groups. The root canals of Group I were filled with gutta-percha and zinc oxide/eugenol cement; Group II were filled with calcium hydroxide, and Group III were not filled. All animals were clinically and radiographically examined 15 days after surgery andthen again every subsequent 15 days until 120 days, when the teeth were extracted en bloc.Histopathological analysis showed inflammatory infiltration, cement and bone resorption andnecrotic tissue in the apical delta in different proportions. Histomicrobiological analysis showedthe presence of microorganisms inside the teeth structures, with different concentrationsaccording to the treatment used. There was statistical significance between the groups(p>0.05). Gutta-percha with zinc oxide/eugenol demonstrated good antimicrobial activity;calcium hydroxide was not efficient. The conclusion of this study is that gutta-percha withzinc oxide/eugenol is the better protocol for filling root canals in dogs.