Contraction stress determinants in dimethacrylate composites

The influence of composite organic content on polymerization stress development remains unclear. It was hypothesized that stress was directly related to differences in degree of conversion, volumetric shrinkage, elastic modulus, and maximum rate of polymerization encountered in composites containing different BisGMA (bisphenylglycidyl dimethacrylate) concentrations and TEGDMA ( triethylene glycol dimethacrylate) and/or BisEMA ( ethoxylated bisphenol-A dimethacrylate) as co-monomers. Stress was determined in a tensilometer. Volumetric shrinkage was measured with a mercury dilatometer. Elastic modulus was obtained by flexural test. We used fragments of flexural specimens to determine degree of conversion by FT-Raman spectroscopy. Reaction rate was determined by differential scanning calorimetry. Composites with lower BisGMA content and those containing TEGDMA showed higher stress, conversion, shrinkage, and elastic modulus. Polymerization rate did not vary significantly, except for the lower value of the 66% TEGDMA composite. We used linear regressions to evaluate the association between polymerization stress and conversion (R-2 = 0.905), shrinkage ( R-2 = 0.825), and modulus ( R-2 = 0.623).

The role of surface sealants in the roughness of composites after a simulated toothbrushing test

Objectives: To evaluate the influence of two surface sealants (BisCover/Single Bond) and three application techniques (unsealed/conventional/co-polymerization) on the roughness of two composites (Filtek Z250/Z350) after the toothbrushing test. Methods: Seventy-two rectangular specimens (5 mm x 10 mm x 3 mm) were fabricated and assigned into 12 groups (n = 6). Each sample was subjected to three random roughness readings at baseline, after 100,000 (intermediate), and 200,000 (final) toothbrushing strokes. Roughness (R) at each stage was obtained by the arithmetic mean of the reading of each specimen. Sealant removal was qualitatively examined (optical microscope) and classified into scores (0-3). Data were analyzed by Student`s paired t-test, two-way ANOVA/Tukey`s test, and by Wilcoxon, Kruskal-Wallis and Miller`s test (alpha = 0.05). Results: Z250 groups at baseline did not differ statistically from each other. Unsealed Z350 at baseline had lower R values. All the unsealed groups presented gradual decrease in R from baseline to final brushing. From baseline to the inter-mediate stage, Z250 co-polymerized groups presented a significant reduction in R (score 3). Conventionally sealed groups had no significant changes in R (scores 2-0.8). From baseline to the intermediate stage, the conventionally sealed Z350 Single Bond group had an increase in R (score 1.5). In the final stage, all the conventionally sealed groups presented a reduction in R (scores 0.7-0). Co-polymerized Single Bond groups had a significant reduction in R (scores 2.5-2.7), and co-polymerized BisCover groups an increase in R (scores 2.8-3). Conclusions: At any brushing stage, sealed composites presented superior performance when compared with unsealed composites. (C) 2009 Elsevier Ltd. All rights reserved.

Effect of different surface treatments on the repair bond strength of indirect composites

Purpose: To evaluate the tensile bond strength of indirect composites repaired with different surface treatments and direct composites. Methods: 180 specimens were prepared with Targis, belleGlass HP and Sculpture indirect composites, light-activated and post-cured according to the manufacturers` recommendations. The specimens were stored in distilled water for 24 hours at 37 degrees C. The bonding surfaces were prepared with air abrasion, hydrofluoric acid or hydrofluoric acid followed by a neutralizing solution. All the treated surfaces were subject to the application of a silane and a bonding agent before the repair procedures with Tetric Ceram and Tetric Flow for the Targis specimens, Herculite XRV and Revolution for the belleGlass HP specimens and Sculp-It and Flow-It for Sculpture specimens. The tensile bond strength tests were carried out using a universal testing machine at cross-head speed of 0.5 mm/minute. The type of fracture was observed under a light microscope at x40 magnification. Data were analyzed by a two-way ANOVA and Tukey`s post-hoc tests (P<0.05). Results: Targis showed a statistically higher repair bond strength than belleGlass HP and Sculpture, which were not significantly different from each other. Air abrasion increased the repair bond strength of belleGlass HP and Sculpture. For Targis, all the surface treatments resulted in similar repair bond strength. The different viscosity of repair composites did not affect the repair of indirect composites. Fractured surfaces showed mostly adhesive failures, mainly with hydrofluoric acid treatment.

In vitro wear, surface roughness and hardness of propanal-containing and diacetyl-containing novel composites and copolymers based on bis-GMA analogs

Objective. To evaluate the effect of two additives, aldehyde or diketone, on the wear, roughness and hardness of bis-GMA-based composites/copolymers containing TEGDMA, propoxylated bis-GMA (CH(3)bis-GMA) or propoxylated fluorinated bis-GMA (CF(3)bis-GMA). Methods. Fifteen experimental composites and 15 corresponding copolymers were prepared combining bis-GMA and TEGDMA, CH3bis-GMA or CF3bis-GMA, with aldehyde (24mol% and 32 mol%) or diketone (24 mol% and 32 mol%) totaling 30 groups. For composites, hybrid treated filler (barium aluminosilicate glass/pyrogenic silica; 60 wt%) was added to monomer mixtures. Photopolymerization was affected by 0.2 wt% each of camphorquinone and N,N-dimethyl-p-toluidine. Wear (W) test was conducted in a toothbrushing abrasion machine (n = 6) and quantified using a profilometer. Surface roughness (R) changes, before and after abrasion test, were determined using a rugosimeter. Microhardness (H) measurements were performed for dry and wet samples using a Knoop microindenter (n = 6). Data were analyzed by one-way ANOVA and Tukey`s test (alpha = 0.05). Results. Incorporation of additives led to improved W and H values for bis-GMA/TEGDMA and bis-GMA/CH(3)bis-GMA systems. Additives had no significant effect on the W and H changes of bis-GMA/CF(3)bis-GMA. With regard to R changes, additives produced decreased values for bis-GMA/CH3bis-GMA and bis-GMA/CF3bis-GMA composites. Bis-GMA/TEGDMA and bis-GMA/CH(3)bis-GMA copolymers with additives became smoother after abrasion test. Significance. The findings correlate with additives ability to improve degree of conversion of some composites/copolymers thereby enhancing mechanical properties. Published by Elsevier Ltd on behalf of Academy of Dental Materials

Clinical evaluation of two packable posterior composites A five-year follow-up

Background. Research has suggested that packable resin-based composites inserted with a placement technique similar to amalgam condensation can reduce the sensitivity associated with posterior restorations. The authors evaluated the clinical performance, including associated sensitivity, of two packable composites in a randomized five-year clinical trial. Methods. A single operator randomly placed two restorations in each of 33 patients: one restoration consisting of Alert (Jeneric/Pentron, Wallingford, Conn.) and the other consisting of SureFil (Dentsply/Caulk, Milford, Del.). There were 30 Class I and 36 Class II restorations. Two independent evaluators evaluated the restorations by using modified U.S.; Public Health Service criteria. The authors analyzed data by means of the Fisher, chi(2) and McNemar tests at P < .05. Results. Of 60 restorations evaluated at five years, two Class II restorations (one SureFil, one Alert) failed. All other restorations received the highest score possible for sensitivity and vitality. The only difference between the composites at the five-year recall was the significantly better surface texture of SureFil. The authors observed significantly different scores between the baseline and at five years for marginal discoloration (Alert and SureFil), surface texture (Alert and SureFil) and color (SureFil). Conclusions. Both packable resin-based composites showed excellent durability during the five-year follow-up. Clinical Implications. The investigated resin-based composites are suitable for posterior restorations.

Color stability of silorane-based composites submitted to accelerated artificial ageing-An in situ study

Objectives: To assess the in situ color stability, surface and the tooth/restoration interface degradation of a silorane-based composite (P90, 3M ESPE) after accelerated artificial ageing (AAA), in comparison with other dimethacrylate monomer-based composites (Z250/Z350, 3M ESPE and Esthet-X, Dentsply). Methods: Class V cavities (25 mm(2) x 2 mmdeep) were prepared in 48 bovine incisors, which were randomly allocated into 4 groups of 12 specimens each, according to the type of restorative material used. After polishing, 10 specimens were submitted to initial color readings (Easyshade, Vita) and 2 to analysis by scanning electronic microscopy (SEM). Afterwards, the teeth were submitted to AAA for 384 h, which corresponds to 1 year of clinical use, after which new color readings and microscopic images were obtained. The values obtained for the color analysis were submitted to statistical analysis (1-way ANOVA, Tukey, p < 0.05). Results: With regard to color stability, it was verified that all the composites showed color alteration above the clinically acceptable levels (Delta E >= 3.3), and that the silorane-based composite showed higher Delta E (18.6), with a statistically significant difference in comparison with the other composites (p < 0.05). The SEM images showed small alterations for the dimethacrylate-based composites after AAA and extensive degradation for the silorane-based composite with a rupture at the interface between the matrix/particle. Conclusion: It may be concluded that the silorane-based composite underwent greater alteration with regard to color stability and greater surface and tooth/restoration interface degradation after AAA. (C) 2011 Elsevier Ltd. All rights reserved.

Freeform fabrication of aluminum metal-matrix composites

A series of metal-matrix composites were formed by extrusion freeform, fabrication of a sinterable aluminum alloy in combination with silicon carbide particles and whiskers, carbon fibers, alumina particles, and hollow flyash cenospheres. Silicon carbide particles were most successful in that the composites retained high density with up to 20 vol% of reinforcement and the strength approximately doubles over the strength of the metal matrix alone. Comparison with simple models suggests that this unexpectedly high degree of reinforcement can be attributed to the concentration of small silicon carbide particles around the larger metal powder. This fabrication method also allows composites to be formed with hollow spheres that cannot be formed by other powder or melt methods.

Novel composites of TiO2 (anatase) and silicate nanoparticles

Thermally stable composite nanostructures of titanium dioxide (anatase) and silicate nanoparticles were prepared from Laponite clay and a sol of titanium hydrate in the presence of poly(ethylene oxide) (PEO) surfactants. Laponite is a synthetic clay that readily disperses in water and exists as exfoliated silicate layers of about 1-nm thick in transparent dispersions of high pH. The acidic sol solution reacts with the clay platelets and leaches out most of the magnesium in the clay, while the sol particles hydrolyze further due to the high pH of the clay dispersion. As a result, larger precursors of TiO2 nanoparticles form and condense on the fragmentized pieces of the leached silicate. Introducing PEO surfactants into the synthesis can significantly increase the porosity and surface area of the composite solids. The TiO2 exists as anatase nanoparticles that are separated by silicate fragments and voids such that they are accessible to organic molecules. The size of the anatase particle can be tailored by manipulating the experimental parameters at various synthesis stages. Therefore, we can design and engineer composite nanostructures to achieve better performance. The composite solids exhibit superior properties as photocatalysts for the degradation of Rhodamine 6G in aqueous solution.

Mechanical, electrical and electro-mechanical properties of thermoplastic elastomer styrene–butadiene–styrene/multiwal carbon nanotubes composites

Composites of styrene–butadiene–styrene (SBS) block copolymer with multiwall carbon nanotubes were processed by solution casting to investigate the influence of filler content, the different ratios of styrene/butadiene in the copolymer and the architecture of the SBS matrix on the electrical, mechanical and electro-mechanical properties of the composites. It was found that filler content and elastomer matrix architecture influence the percolation threshold and consequently the overall composite electrical conductivity. Themechanical properties aremainly affected by the styrene and filler content. Hopping between nearest fillers is proposed as the main mechanism for the composite conduction. The variation of the electrical resistivity is linear with the deformation. This fact, together with the gauge factor values in the range of 2–18, results in appropriate composites to be used as (large) deformation sensors.

Mechanical, electrical and electro-mechanical properties of thermoplastic elastomer styrene–butadiene–styrene/multiwall carbon nanotubes composites

Composites of styrene–butadiene–styrene (SBS) block copolymer with multiwall carbon nanotubes were processed by solution casting to investigate the influence of filler content, the different ratios of styrene/butadiene in the copolymer and the architecture of the SBS matrix on the electrical, mechanical and electro-mechanical properties of the composites. It was found that filler content and elastomer matrix architecture influence the percolation threshold and consequently the overall composite electrical conductivity. The mechanical properties are mainly affected by the styrene and filler content. Hopping between nearest fillers is proposed as the main mechanism for the composite conduction. The variation of the electrical resistivity is linear with the deformation. This fact, together with the gauge factor values in the range of 2–18, results in appropriate composites to be used as (large) deformation sensors.

On the origin of the electrical response of vapor grown carbon nanofiber + epoxy composites

The origin of the electrical response of vapor grown carbon nanofiber (VGCNF) + epoxy composites is investigated by studying the electrical behavior of VGCNF with resin, VGCNF with hardener and cured composites, separately. It is demonstrated that the onset of the conductivity is associated to the emergence of a weak disorder regime. It is also shown that the weak disorder regime is related to a hopping depending on the physical properties of the polymer matrix.

Temperature dependence of the electrical conductivity of vapor grown carbon nanofiber/epoxy composites with different filler dispersion levels

The influence of the dispersion of vapor grown carbon nanofibers (VGCNF) on the electrical properties of VGCNF/epoxy composites has been studied. A homogeneous dispersion of the VGCNF does not imply better electrical properties. The presence of well distributed clusters appears to be a key factor for increasing composite conductivity. It is also shown that the main conduction mechanism has an ionic nature for concentrations below the percolation threshold, while above the percolation threshold it is dominated by hopping between the fillers. Finally, using the granular system theory it is possible to explain the origin of conduction at low temperatures.

Modeling Carbon Nanotube Electrical Properties in CNT/Polymer Composites

In this work it is demonstrated that the capacitance between two cylinders increases with the rotation angle and it has a fundamental influence on the composite dielectric constant. The dielectric constant is lower for nematic materials than for isotropic ones and this can be attributed to the effect of the filler alignment in the capacitance. The effect of aspect ratio in the conductivity is also studied in this work. Finally, based on previous work and by comparing to results from the literature it is found that the electrical conductivity in this type of composites is due to hopping between nearest fillers resulting in a weak disorder regime that is similar to the single junction expression.

Electro-mechanical properties of triblock copolymer styrene-butadiene-styrene / carbon nanotube composites for large deformation sensor applications

Thermoplastic elastomer/carbon nanotube composites are studied for sensor applications due to their excellent mechanical and electrical properties. Piezoresisitive properties of tri-block copolymer styrene-butadiene-styrene (SBS)/ carbon nanotubes (CNT) prepared by solution casting have been investigated. Young modulus of the SBS/CNT composites increases with the amount of CNT filler content present in the samples, without losing the high strain deformation on the polymer matrix (~1500 %). Further, above the percolation threshold these materials are unique for the development of large deformation sensors due to the strong piezoresistive response. Piezoresistive properties evaluated by uniaxial stretching in tensile mode and 4-point bending showed a Gauge Factors up to 120. The excellent linearity obtained between strain and electrical resistance makes these composites interesting for large strain piezoresistive sensors applications.

Applying complex network theory to the understanding of high-aspect-ratio carbon-filled composites

This work demonstrates that the theoretical framework of complex networks typically used to study systems such as social networks or the World Wide Web can be also applied to material science, allowing deeper understanding of fundamental physical relationships. In particular, through the application of the network theory to carbon nanotubes or vapour-grown carbon nanofiber composites, by mapping fillers to vertices and edges to the gap between fillers, the percolation threshold has been predicted and a formula that relates the composite conductance to the network disorder has been obtained. The theoretical arguments are validated by experimental results from the literature.